CN105419691A - Environment-friendly corrosion-resistant adhesive - Google Patents
Environment-friendly corrosion-resistant adhesive Download PDFInfo
- Publication number
- CN105419691A CN105419691A CN201510902469.9A CN201510902469A CN105419691A CN 105419691 A CN105419691 A CN 105419691A CN 201510902469 A CN201510902469 A CN 201510902469A CN 105419691 A CN105419691 A CN 105419691A
- Authority
- CN
- China
- Prior art keywords
- parts
- friendly corrosion
- sizing agent
- corrosion protection
- water glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly corrosion-resistant adhesive which comprises, by weight parts, 15-20 parts of polyvinyl alcohol, 10-15 parts of acrylic-styrene emulsion, 10-20 parts of trimethyl methyl silane, 5-10 parts of sodium salt, 1-5 parts of silica sol, 1-5 parts of potash water glass and 2-6 parts of isocyanate. The adhesive has the advantages of being good in adhesion effect, high in adhesive strength, good in corrosion resistance, non-toxic and environmentally friendly.
Description
Technical field
The present invention relates to Material Field, particularly relate to a kind of environment friendly corrosion protection sizing agent.
Background technology
Although one time foam tableware brings convenience to the life of people, its difficult degradation, can cause serious white pollution to environment.Although there is the difficult degradation problem that some starch-based degrading materials solve expanded plastic and cause in recent years on the market, these degradable materials, due to bad mechanical strength, poor plasticity, thus can not be applied widely.
Therefore, prior art also needs to further develop and improve.
Summary of the invention
The object of the present invention is to provide a kind of environment friendly corrosion protection sizing agent, be intended to solve current degradable plastics poor plasticity, the problem of bad mechanical strength.
Technical scheme of the present invention is as follows:
A kind of environment friendly corrosion protection sizing agent, wherein, it is composed of the following components by weight:
Polyvinyl alcohol 15 ~ 20 parts;
Propyl benzene emulsion 10 ~ 15 parts;
Methyltrimethylsilane 10 ~ 20 parts;
Sodium salt 5 ~ 10 parts;
Silicon sol 1 ~ 5 part;
Potash water glass 1 ~ 5 part;
Isocyanic ester 2 ~ 6 parts.
Described environment friendly corrosion protection sizing agent, wherein, it is composed of the following components by weight:
Polyvinyl alcohol 15 parts;
Propyl benzene emulsion 12 parts;
Methyltrimethylsilane 15 parts;
Sodium salt 10 parts;
Silicon sol 5 parts;
Potash water glass 5 parts;
Isocyanic ester 4 parts.
Described environment friendly corrosion protection sizing agent, wherein: the consumption proportion of silicon sol and potash water glass is 1:1.
Beneficial effect: the invention provides a kind of environment friendly corrosion protection sizing agent, sizing agent of the present invention has that plybonding effect is good, bonding force is strong, preservative property are good, the feature of asepsis environment-protecting.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of environment friendly corrosion protection sizing agent, wherein, it is composed of the following components by weight:
Polyvinyl alcohol 15 ~ 20 parts;
Propyl benzene emulsion 10 ~ 15 parts;
Methyltrimethylsilane 10 ~ 20 parts;
Sodium salt 5 ~ 10 parts;
Silicon sol 1 ~ 5 part;
Potash water glass 1 ~ 5 part;
Isocyanic ester 2 ~ 6 parts.
Wherein, it is preferred that the consumption proportion of silicon sol and potash water glass is 1:1.
Technical solution of the present invention is set forth further below by embodiment.
Embodiment 1
Described environment friendly corrosion protection sizing agent, wherein, it is composed of the following components by weight:
Polyvinyl alcohol 15 parts;
Propyl benzene emulsion 12 parts;
Methyltrimethylsilane 15 parts;
Sodium salt 10 parts;
Silicon sol 5 parts;
Potash water glass 5 parts;
Isocyanic ester 4 parts.
Preparation method:
(1), each component is taken by weight ratio;
(2), polyvinyl alcohol and propyl benzene emulsion are added in agitator, mix, then methyltrimethylsilane, silicon sol and sodium salt is added, stir 30min, then add other component, when being heated with stirring to 80 DEG C ~ 90 DEG C of temperature, keep stirring 30min, then stop heating, naturally cool to room temperature, namely obtain described anticorrosive adhesive stick.
Embodiment 2
Described environment friendly corrosion protection sizing agent, wherein, it is composed of the following components by weight:
Polyvinyl alcohol 20 parts;
Propyl benzene emulsion 15 parts;
Methyltrimethylsilane 20 parts;
Sodium salt 10 parts;
Silicon sol 5 parts;
Potash water glass 5 parts;
Isocyanic ester 6 parts.
Preparation method:
(1), each component is taken by weight ratio;
(2), polyvinyl alcohol and propyl benzene emulsion are added in agitator, mix, then methyltrimethylsilane, silicon sol and sodium salt is added, stir 30min, then add other component, when being heated with stirring to 80 DEG C ~ 90 DEG C of temperature, keep stirring 30min, then stop heating, naturally cool to room temperature, namely obtain described anticorrosive adhesive stick.
The invention provides a kind of environment friendly corrosion protection sizing agent, sizing agent of the present invention has that plybonding effect is good, bonding force is strong, preservative property are good, the feature of asepsis environment-protecting.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (3)
1. an environment friendly corrosion protection sizing agent, is characterized in that, it is composed of the following components by weight:
Polyvinyl alcohol 15 ~ 20 parts;
Propyl benzene emulsion 10 ~ 15 parts;
Methyltrimethylsilane 10 ~ 20 parts;
Sodium salt 5 ~ 10 parts;
Silicon sol 1 ~ 5 part;
Potash water glass 1 ~ 5 part;
Isocyanic ester 2 ~ 6 parts.
2. environment friendly corrosion protection sizing agent according to claim 1, it is characterized in that, it is composed of the following components by weight:
Polyvinyl alcohol 15 parts;
Propyl benzene emulsion 12 parts;
Methyltrimethylsilane 15 parts;
Sodium salt 10 parts;
Silicon sol 5 parts;
Potash water glass 5 parts;
Isocyanic ester 4 parts.
3. environment friendly corrosion protection sizing agent according to claim 1, is characterized in that: the consumption proportion of silicon sol and potash water glass is 1:1.