CN105419389B - 一种高牢度分散蓝染料组合物和染料制品 - Google Patents
一种高牢度分散蓝染料组合物和染料制品 Download PDFInfo
- Publication number
- CN105419389B CN105419389B CN201510731091.0A CN201510731091A CN105419389B CN 105419389 B CN105419389 B CN 105419389B CN 201510731091 A CN201510731091 A CN 201510731091A CN 105419389 B CN105419389 B CN 105419389B
- Authority
- CN
- China
- Prior art keywords
- component
- composition
- formula
- weight
- mass percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种高牢度分散蓝染料组合物和染料制品，所述分散蓝染料组合物包含组分A和组分B，所述组分A选自式(Ⅰ)所示的化合物中的一种或多种，所述组分B选自式(Ⅱ)所示的化合物中的一种或多种，基于所述的组分A和组分B，组分A的质量百分含量为1～99％，组分B的质量百分含量为1～99％。本发明还提供了一种分散蓝染料制品，其主要含有所述的分散蓝染料组合物和助剂。本发明的染料应用于疏水性纤维材料染色时，具有提升力好、上染率高、耐汗渍和耐水洗牢度优异等特点。
Description
(一)技术领域
本发明涉及一种蓝色分散染料组合物和染料制品，尤其是一种适合印染疏水性纤维材料的高牢度蓝色分散染料组合物和染料制品。
(二)背景技术
随着生活水平的不断提高，人们对于服装面料的功能性要求也越来越多，民众期待更加新颖有活力的服装面料出现，涤纶/氨纶织物因其具有较高的弹性和优良的回弹性能，手感柔软，穿着舒适，易吸汗且不会产生静电等优点，在国内外市场上十分流行，该涤/氨面料主要采用分散染料进行染色，但现有的分散染料对氨纶沾染严重，导致湿处理牢度如耐皂洗牢度、耐水色牢度及耐汗渍牢度等性能较差，无法满足中高档涤纶/氨纶面料的印染要求。
目前客户要求测试的标准以中国国家标准(GB/T系列)及美国染化家协会标准(AATCC系列)居多，但这两项标准的差异较大，例如相同的产品在AATCC系列中测试的耐汗渍、耐水洗色牢度等级明显低于国标中的色牢度等级。因此，有必要开发一类能达到AATCC标准3-4级以上要求的高牢度分散染料，满足高档聚酯以及涤纶/氨纶织物的染色要求。现有文献CN101289414提供了一种各项坚牢度优良的新型染料化合物，但在涤/氨面料的染色上仍有进一步改善的空间。
(三)发明内容
为解决上述问题，本发明提供了一种高牢度分散蓝染料组合物和染料制品，应用于疏水性纤维材料染色时，具有提升力好、上染率高以及耐汗渍和耐水洗牢度优异等特点。
本发明采用的技术方案是：
一种分散蓝染料组合物，包含组分A和组分B，所述组分A选自式(Ⅰ)所示的化合物中的一种或多种，所述组分B选自式(Ⅱ)所示的化合物中的一种或多种，基于所述的组分A和组分B，组分A的质量百分含量为1～99％，组分B的质量百分含量为1～99％；
式(Ⅰ)中：
R1、R2各自独立为C1～C4烷基；
R3为C1～C4烷基、烯丙基、或-CH2COR8，R8为C1～C4烷基；
R4为苄基或C1～C4烷基；
式(Ⅱ)中：
R5、R6各自独立为C1～C4烷基；
R7为C1～C4烷基或烯丙基。
上述组分A、组分B为本发明分散蓝染料组合物的主要组成，在本领域技术人员熟知的范围内，本发明组合物还可添加其它可应用于复配的染料单体，例如C.I.分散蓝366、C.I.分散蓝165、C.I.分散紫33等，通过上述改变获得的复配染料组合物，同样在本发明的保护范围之内。
优选的，所述分散蓝染料组合物由组分A和组分B组成。
优选的，基于所述的组分A和组分B，所述组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
更优选的，基于所述的组分A和组分B，所述组分A的质量百分含量为30～70％，组分B的质量百分含量为30～70％。
本发明中，所述的C1～C4烷基可以是甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基。
进一步，R1、R2各自独立为甲基或乙基。
进一步，R3为甲基、乙基、正丙基、烯丙基、或-CH2COR8，R8为甲基；
进一步，R4为苄基或乙基。
进一步，R5、R6各自独立为甲基或乙基。
更进一步，所述组分A优选自下式之一或其中两种以上的混合物：
上式中，Ph代表苯基。
再更进一步，所述组分A选自式(Ⅰ-1)、(Ⅰ-2)、(Ⅰ-5)、(Ⅰ-8)中的至少一种。
再再更进一步，所述组分A选自式(Ⅰ-1)、(Ⅰ-8)中的一种或两种。
更进一步，所述组分B优选自下式之一或其中两种以上的混合物：
再更进一步，所述组分B选自式(Ⅱ-1)、(Ⅱ-2)、(Ⅱ-4)中的至少一种。
再再更进一步，所述组分B选自式(Ⅱ-1)、(Ⅱ-2)中的一种或两种。
本发明所述的分散蓝染料组合物，优选包含组分A和组分B，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-2)、(Ⅰ-5)、(Ⅰ-8)中的至少一种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)、(Ⅱ-4)中的至少一种；
基于组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
本发明所述的分散蓝染料组合物，进一步优选包含组分A和组分B，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-8)中的一种或两种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)中的一种或两种；
基于组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
本发明所述的分散蓝染料组合物，特别优选由组分A和组分B组成，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-8)中的一种或两种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)中的一种或两种；
基于组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
本发明所述的分散蓝染料组合物，作为商品出售或应用于纺织材料着色时，通常还需要加入助剂进行后处理。因此，本发明还提供了一种分散蓝染料制品，其主要含有所述的分散蓝染料组合物和助剂，助剂和分散染料组合物的重量之比为0.2～5:1。进一步，本发明优选所述分散蓝染料制品由所述分散蓝染料组合物和助剂组成。所述的助剂为分散染料复配时常用的分散剂、扩散剂及其它表面活性剂等，优选自下列之一或其中两种以上的混合物：萘磺酸甲醛缩合物、木质素磺酸盐、烷基萘磺酸甲醛缩合物(如甲基萘磺酸甲醛缩合物(分散剂MF))、萘磺酸甲醛缩合物(扩散剂NNO)、苄基萘磺酸甲醛缩合物(扩散剂CNF)、木质素磺酸钠(木质素85A、木质素83A)等。
本发明具体推荐所述分散蓝染料制品由重量比为1:0.2～5的分散蓝染料组合物和助剂组成，其中分散蓝染料组合物包含组分A和组分B，组分A选自式(Ⅰ-1)～(Ⅰ-8)中的一种或多种；组分B选自式(Ⅱ-1)～(Ⅱ-6)中的一种或多种；基于所述的组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
本发明进一步推荐所述分散蓝染料制品由重量比为1:0.2～5的分散蓝染料组合物和助剂组成，其中分散蓝染料组合物由组分A和组分B组成，组分A选自式(Ⅰ-1)～(Ⅰ-8)中的一种或多种；组分B选自式(Ⅱ-1)～(Ⅱ-6)中的一种或多种；基于所述的组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
本发明所述的分散蓝染料制品的制备方法如下：
将组成分散蓝染料组合物的染料单体化合物(原染料)按配比混合后，在助剂、水的存在下用砂磨机或研磨机等粉碎机进行微粒子化；另外也可将染料单体化合物分别在助剂、水的存在下用砂磨机或研磨机等粉碎机进行微粒子化处理后按比例进行混合。本发明所述的分散蓝染料制品，用砂磨机或研磨机研磨后为液状，喷雾干燥后可为粉状、颗粒状，这是本领域技术人员公知的制备方法。
本发明所使用的式(I)和式(Ⅱ)的染料单体化合物可分别参照专利200780037613.0、EP0439057中所述的方法或类似的方法制备，也可采用市售商品。
利用本发明的染料组合物制成的染料，可按行业内惯用方式对疏水性纤维材料(如聚酯织物或其混纺织物)进行染色，如采用普通浸染法进行染色，也可用于直接印花。其中，普通浸染法如将疏水性纤维材料进行预处理，放入染缸中进行浸染，染毕，冷水清洗至中性，绞干，再进行还原清洗，烘干；直接印花如将织物进行染前处理，烘干，定形，在印花机上印分散染料色浆，再进行蒸化，利用汽蒸方式使织物上的染料固色，最后水洗，拉幅定型。
本发明的有益效果在于：使用本发明分散蓝染料上染疏水性纤维材料时，染色残液清、浮色少；通过调整不同组分间的比例，可获得得色量高、上染速度快，具有优异的耐水洗牢度和耐汗渍牢度的蓝色染织物，非常适用于中高档聚酯面料特别是涤/氨面料的上染。
(四)附图说明
图1是提升力对比图。
图2是上染率对比图。
(五)具体实施方式
下面结合具体实施例对本发明进行进一步描述，但本发明的保护范围并不仅限于此：
实施例1：
将60克式(Ⅰ-1)化合物、40克式(Ⅱ-1)化合物和200克的分散剂MF，加水650克拼混后，研磨分散并干燥，即得成品，该染料能提供给织物各项牢度性能优良的蓝色。
实施例2：
将50克式(Ⅰ-1)化合物、50克式(Ⅱ-2)化合物和200克的分散剂MF，加水650克拼混后，研磨分散并干燥，即得成品，该染料能提供给织物各项牢度性能优良的蓝色。
实施例3～22：
按照实施例1或2所述的方法，不同的是采用表1中组分A、B的结构和重量，加入助剂185克(分散剂MF为150克，木质素磺酸钠为35克)，加水650克拼混后制成浆液，研磨分散，干燥，制得成品，该染料能提供给织物各项牢度性能优良的蓝色。
表1
对比例：
将专利CN101289414A中的实施例8、实施例455作为对比例1、对比例2；
将专利CN103627207A中的实施例1作为对比例3；
将专利CN102002259A中的实施例1作为对比例4。
染色实施例：
分别选取上述实施例1～22、对比例1～4制得的分散染料，采用常规高温高压染色法处理涤纶/氨纶织物，处理过程中，控制染色深度(o.w.f)4.0％，浴比1∶25，调染浴pH值4.5～5，室温入染，以1℃/min升温至125℃，保温35min，按常法还原净洗、水洗、干燥，得到蓝色的染织物。按照AATCC 15、AATCC 61-2A分别测试耐汗渍和耐水洗色牢度，结果见下表2：
表2
由上可知，本发明中的分散蓝染料组合物，其耐水洗沾色牢度明显优于对比例1～4，能够满足高牢度要求面料的印染。
提升力试验：
按照染色实施例中所述的方法，采用本发明实施例1和对比例1中制备的染料，在染色浓度1.0％～10.0％范围内、PH4.5条件下对涤纶布进行染色，按照GB/T2397中所述的方法测试其提升力，所得提升力结果如图1所示。从图1中可直观的看出本申请的分散染料的提升性明显优于对比实施例1。
上染率试验：
按照染色实施例中所述的方法，采用本发明实施例1和对比例1中制备的染料，在染色温度70～130℃范围内、PH 4.5条件下对涤纶布进行染色，按照GB/T 9337中所述的方法测试其上染率，所得上染率结果如图2所示。从图2中可直观的看出本申请的分散染料的上染率明显优于对比实施例1。
Claims (10)
1.一种分散蓝染料组合物，包含组分A和组分B，所述组分A选自式(Ⅰ)所示的化合物中的一种或多种，所述组分B选自式(Ⅱ)所示的化合物中的一种或多种，基于所述的组分A和组分B，组分A的质量百分含量为1～99％，组分B的质量百分含量为1～99％；
式(Ⅰ)中：
R1、R2各自独立为C1～C4烷基；
R3为C1～C4烷基、烯丙基、或-CH2COR8，R8为C1～C4烷基；
R4为苄基或C1～C4烷基；
式(Ⅱ)中：
R5、R6各自独立为C1～C4烷基；
R7为C1～C4烷基或烯丙基。
2.如权利要求1所述的分散蓝染料组合物，其特征在于：所述组分A选自下式之一或其中两种以上的混合物：
其中，Ph代表苯基。
3.如权利要求1或2所述的分散蓝染料组合物，其特征在于：所述组分B选自下式之一或其中两种以上的混合物：
4.如权利要求1所述的分散蓝染料组合物，其特征在于：所述的分散蓝染料组合物包含组分A和组分B，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-2)、(Ⅰ-5)、(Ⅰ-8)中的至少一种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)、(Ⅱ-4)中的至少一种；
基于组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％；
5.如权利要求4所述的分散蓝染料组合物，其特征在于：所述的分散蓝染料组合物包含组分A和组分B，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-8)中的一种或两种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)中的一种或两种；
基于以上组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
6.如权利要求5所述的分散蓝染料组合物，其特征在于：所述的分散蓝染料组合物由组分A和组分B组成，其中：
组分A选自式(Ⅰ-1)、(Ⅰ-8)中的一种或两种；
组分B选自式(Ⅱ-1)、(Ⅱ-2)中的一种或两种；
基于以上组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％。
7.一种分散蓝染料制品，含有如权利要求1所述的分散蓝染料组合物和助剂，助剂和分散染料组合物的重量之比为0.2～5:1。
8.如权利要求7所述的分散蓝染料制品，其特征在于：所述的助剂选自下列之一或其中两种以上的混合物：木质素磺酸盐、烷基萘磺酸甲醛缩合物、萘磺酸甲醛缩合物、苄基萘磺酸甲醛缩合物。
9.如权利要求8所述的分散蓝染料制品，其特征在于：所述的分散蓝染料制品由分散蓝染料组合物和助剂组成。
10.如权利要求9所述的分散蓝染料制品，其特征在于：所述分散蓝染料制品由重量比为1:0.2～5的分散蓝染料组合物和助剂组成，其中分散蓝染料组合物由组分A和组分B组成，组分A选自式(Ⅰ-1)～(Ⅰ-8)中的一种或多种；组分B选自式(Ⅱ-1)～(Ⅱ-6)中的一种或多种；基于所述的组分A和组分B，组分A的质量百分含量为10～90％，组分B的质量百分含量为10～90％；
其中，Ph代表苯基。