CN105419160A - Formula of novel wood plastic composite - Google Patents

Formula of novel wood plastic composite Download PDF

Info

Publication number
CN105419160A
CN105419160A CN201510947641.2A CN201510947641A CN105419160A CN 105419160 A CN105419160 A CN 105419160A CN 201510947641 A CN201510947641 A CN 201510947641A CN 105419160 A CN105419160 A CN 105419160A
Authority
CN
China
Prior art keywords
parts
formula
wood
agent
plastic composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510947641.2A
Other languages
Chinese (zh)
Inventor
杨磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd filed Critical ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Priority to CN201510947641.2A priority Critical patent/CN105419160A/en
Publication of CN105419160A publication Critical patent/CN105419160A/en
Pending legal-status Critical Current

Abstract

The invention discloses a formula of a novel wood plastic composite. The formula is prepared from 100 parts of PVC (Poly Vinyl Chloride) (k=57 to 60), 40 parts of wood powder (fillers), 1.5 parts of AC (azodicarbonamide, a foaming agent), 2 parts of amino silane (a coupling agent), 2 parts of calcium stearate and zinc stearate (an auxiliary foaming agent and a lubricating agent), 10 parts of acrylic acid (a plasticizer), 1 part of nano calcium carbonate (a nucleating agent), 2 parts of paraffins (a lubricant), 0.2 part of ZB (Zinc Borate) (a preservative), 0.2 part of 1010 (an antioxidant) and 3 parts of S-07(an anti-ant agent). According to the formula of the novel wood plastic composite, disclosed by the invention, the wood plastic composite which is prepared by the formula has the dual characteristics of wood and plastic, a product resists damage from moth; fungus is not generated, strong acid resistance and strong alkali resistance are obtained, water is not absorbed, deformation is avoided, the mechanical performance is good, the durability is higher than that of a simple wood product by several times, and the wood plastic composite has the advantages of stiffness, toughness, durability, abrasion resistance, stable size and the like.

Description

A kind of formula of Wood-plastic material
Technical field
The present invention relates to Wood-plastic material field, specifically a kind of formula of Wood-plastic material.
Background technology
Wood plastic composite has the dual nature of timber and plastics concurrently, goods be not afraid of damage by worms, not raw fungi, anti-strong acid and strong base, do not absorb moisture, not yielding, mechanical property good, wearing quality than simple timber product's high several times, there is the advantages such as hard, tough, durable, wear-resisting, dimensional stabilizing.
Summary of the invention
The object of the present invention is to provide a kind of formula of Wood-plastic material.
The present invention is achieved through the following technical solutions:
A kind of formula of Wood-plastic material, it is characterized in that: comprise PVC(k=57 ~ 60) 100 parts, wood powder (filler) 40 parts, AC (Cellmic C 121, whipping agent) 1.5 parts, aminosilane (coupling agent) 2 parts, calcium stearate, Zinc Stearate (blowing promotor, lubrication) 2 parts, 10 parts, vinylformic acid (softening agent), nano-calcium carbonate (nucleator) 1 part, 2 parts, paraffin (lubricant), zinc borate (sanitas) 0.2 part, 1010(oxidation inhibitor) 0.2 part, S-07(anti-termite agent) 3 parts.
The invention has the beneficial effects as follows:
This formula, using PVC as matrix resin, as foam wood/plastic composite material, selects the PVC that molecular mass is suitable extremely important, molecular mass is too low, melt strength is poor, the obstruction ability that melt is escaped to foamed gas, is difficult to obtain the fine and closely woven porous plastics of uniform foam cell; If molecular weight is too high, the tensile strength of melt is very large, suppresses the growth of abscess, causes foaming insufficient, is also difficult to the porous plastics obtaining high foaming rate.Therefore select K value be 57 ~ 60 PVC comparatively suitable.
The Wood-plastic material that this formula is made has the dual nature of timber and plastics concurrently, goods be not afraid of damage by worms, not raw fungi, anti-strong acid and strong base, do not absorb moisture, not yielding, mechanical property good, wearing quality than simple timber product's high several times, there is the advantages such as hard, tough, durable, wear-resisting, dimensional stabilizing.
Embodiment
The present invention is set forth further below in conjunction with specific embodiment.Following examples are only for further specific descriptions of the present invention, instead of for the restriction to application claims protection domain.
This formula comprises PVC(k=57 ~ 60) 100 parts, wood powder (filler) 40 parts, AC (Cellmic C 121, whipping agent) 1.5 parts, aminosilane (coupling agent) 2 parts, calcium stearate, Zinc Stearate (blowing promotor, lubrication) 2 parts, 10 parts, vinylformic acid (softening agent), nano-calcium carbonate (nucleator) 1 part, 2 parts, paraffin (lubricant), zinc borate (sanitas) 0.2 part, 1010(oxidation inhibitor) 0.2 part, S-07(anti-termite agent) 3 parts.

Claims (1)

1. the formula of a Wood-plastic material, it is characterized in that: comprise PVC(k=57 ~ 60) 100 parts, wood powder (filler) 40 parts, AC (Cellmic C 121, whipping agent) 1.5 parts, aminosilane (coupling agent) 2 parts, calcium stearate, Zinc Stearate (blowing promotor, lubrication) 2 parts, 10 parts, vinylformic acid (softening agent), nano-calcium carbonate (nucleator) 1 part, 2 parts, paraffin (lubricant), zinc borate (sanitas) 0.2 part, 1010(oxidation inhibitor) 0.2 part, S-07(anti-termite agent) 3 parts.
CN201510947641.2A 2015-12-17 2015-12-17 Formula of novel wood plastic composite Pending CN105419160A (en)