CN105404109A - Fragrant printing powdered ink and preparation method thereof - Google Patents
Fragrant printing powdered ink and preparation method thereof Download PDFInfo
- Publication number
- CN105404109A CN105404109A CN201510826840.8A CN201510826840A CN105404109A CN 105404109 A CN105404109 A CN 105404109A CN 201510826840 A CN201510826840 A CN 201510826840A CN 105404109 A CN105404109 A CN 105404109A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- styrene
- acrylic resin
- polypropylene wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fragrant printing powdered ink and a preparation method thereof, belonging to the technical field of the preparation of a powdered ink. The constituents of the fragrant printing powered ink are as follows based on weight: 50-60 parts of magnetic iron oxide, 30-35 parts of styrene-acrylic resin, 20-25 parts of polypropylene wax, 10-15 parts of talcum powder, 1-5 parts of sodium silicate and 0.1-0.5 parts of essence powder. The preparation method of the fragrant printing powdered ink comprises the following steps of uniformly mixing the magnetic iron oxide, the polypropylene wax, the talcum powder and the essence powder, and carrying out ball grinding for 40 to 45 minutes; adding 80-90 parts of deionized water based on weight, then adding the styrene-acrylic resin, heating the mixture to 50-56 DEG C, and maintaining the temperature for 50 to 55 minutes; washing the mixture with 4 to 6 times of deionized water, filtering the mixture, and drying the mixture to form a granular material on a condition of 50-55 DEG C; and sieving the material, selecting particles with 3 to 8 micrometers, and drying the particles for 30 to 40 minutes at 50-55 DEG C to obtain the product. The powered ink has the advantages of shape regularity and uniformity, clearness in developing imaging, fragrance and durability, and is suitably used on various different machine types; and moreover, the preparation cost is relatively low, and industrial production is easily realized.
Description
Technical field
The present invention relates to a kind of printing ink powder, be specifically related to a kind of odor type printing ink powder and preparation method thereof, belong to ink powder preparing technical field.
Background technology
Printing (Printing, GraphicArts, also with using GraphicCommunications and figure propagation) be through operations such as plate-making, Shi Mo, pressurizations by original copys such as word, picture, photos, make printing ink transfer on the material surfaces such as paper, fabric, leather, the technology of batch duplicating original copy content.
Whole world printing market is divided into three bulks: the U.S., Europe and Asia respectively account for 1/3rd of global printing market.Chinese printing gross industrial output value rose to third place in the world in 2006.2012, Press and Publications Administration issued the first white paper of press " Chinese printing industry development (2012) "." white paper " shows, and by the end of the year 2011, the total all kinds of printing enterprise 102484 in the whole nation, will fall 1.8% on a year-on-year basis; Industry personnel 356.67 ten thousand people, reduces 2.7% on year-on-year basis; The printing gross output value 8677.13 hundred million yuan, increases by 12.59% on a year-on-year basis; Total assets 9256.66 hundred million yuan, increase by 9.96% on a year-on-year basis; Total profit 739.87 hundred million yuan, increases by 8.31% on a year-on-year basis; External processing trade volume 680.09 hundred million yuan, increases by 2.9% on a year-on-year basis.Wherein, publication printing enterprise 6821, the printing gross output value 1313.94 hundred million yuan, increases by 0.94% on a year-on-year basis; Packing and decorating printing enterprise 47377, the printing gross output value 6318.77 hundred million yuan, increases by 20.6% on a year-on-year basis; Other printed matter printing enterprises 44868, the printing gross output value 708.51 hundred million yuan, falls 15% on a year-on-year basis; Special typesetting, plate-making, binding enterprises 2676, the printing gross output value 77.32 hundred million yuan.On the whole, press is good in China's development.
Ink powder, also known as carbon dust, great majority are made up of resin and carbon black, electric charge agent, magnetic etc.Ink powder in paper fiber, reaches the object of printing through high temperature melt.For different demands, ink powder is produced to becoming more meticulous, colorize, high speed future development.Along with the requirement of consumer is more and more higher, ink powder product is also towards more diversified future development.With allowing people feel pleasure comfortable breath and the product of sense of taste, usually enjoy the favor of consumer.CN201210447391.2 discloses a kind of odor type ink powder and preparation method thereof, described odor type ink powder is made up of the component of following weight parts proportioning: styrene-acrylic resin composition 40 ~ 90 parts, colorant 3 ~ 50 parts, release agent 1 ~ 10 part, charge control agent 0.3 ~ 5 part, spices or 0 ~ 5 part, essence, external additive 1 ~ 5 part, this invention odor type ink powder makes printing or copying process giving out fragrance, has no irritating odor residual, can be used for many moneys printer, duplicating machine; The spices that this patent provides is self-control spices, method for making is by liquid daily chemical essence and aerosil mix and blend in a reservoir, obtain thus by liquid flavor through hydrophobic treatments receive micro belt electro-powder disperse embedding powder, this essence powder distributes although can effectively control fragrance last, but its preparation method is more complicated, and the use amount of essence is comparatively large, thus cause preparation cost higher, limit it and promote the use of.
Summary of the invention
The present invention is directed to prior art Problems existing, provide a kind of odor type printing ink powder, this toner particles shape is regular, even, development imaging clearly, fragrance delicate fragrance is lasting, is useful in multiple different type of machines and uses, and preparation cost is lower, easily realize suitability for industrialized production.
In order to solve the problem, the technical solution adopted in the present invention is:
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 50 ~ 60 parts, styrene-acrylic resin 30 ~ 35 parts, polypropylene wax 20 ~ 25 parts, talcum powder 10 ~ 15 parts, sodium silicate 1 ~ 5 part, essence powder 0.1 ~ 0.5 part;
Magnetic oxide 50 ~ 55 parts, styrene-acrylic resin 30 ~ 33 parts, polypropylene wax 23 ~ 25 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts, essence powder 0.25 ~ 0.5 part;
Magnetic oxide 55 ~ 60 parts, styrene-acrylic resin 33 ~ 35 parts, polypropylene wax 20 ~ 23 parts, talcum powder 10 ~ 13 parts, sodium silicate 3 ~ 5 parts, essence powder 0.25 ~ 0.5 part;
Magnetic oxide 53 ~ 57 parts, styrene-acrylic resin 33 ~ 35 parts, polypropylene wax 20 ~ 23 parts, talcum powder 10 ~ 13 parts, sodium silicate 1 ~ 3 part, essence powder 0.1 ~ 0.25 part;
Magnetic oxide 53 parts, styrene-acrylic resin 33 parts, polypropylene wax 20 parts, talcum powder 10 parts, sodium silicate 1 part, essence powder 0.1 part;
Magnetic oxide 57 parts, styrene-acrylic resin 35 parts, polypropylene wax 23 parts, talcum powder 13 parts, sodium silicate 3 parts, essence powder 0.25 part.
Described essence powder, be the powder that spraying dry is obtained, the essence content of powder is 40% ~ 45%.
Another object of the present invention is to provide a kind of preparation method of odor type printing ink powder, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 40 ~ 45 minutes; Adding weight portion is 80 ~ 90 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 ~ 56 DEG C, keeps 50 ~ 55 minutes; Use 4 ~ 6 times of washed with de-ionized water, filtration be dried to granular material under 50 ~ 55 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 50 ~ 55 DEG C of dryings, after 30 ~ 40 minutes, obtain product.
The present invention relative to the beneficial effect of prior art is:
A kind of odor type printing ink powder provided by the invention, water-fast, resistance to illumination, nontoxic, non-stimulated smell, climate adaptability is good, particle shape is regular, even, development imaging clearly, and fragrance delicate fragrance is lasting, be useful in multiple different type of machines and use, and preparation cost is lower, easily realizes suitability for industrialized production.
Embodiment
Be described in further details the present invention below by embodiment, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
embodiment 1
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 57 parts, styrene-acrylic resin 35 parts, polypropylene wax 23 parts, talcum powder 13 parts, sodium silicate 3 parts, essence powder 0.25 part.
Its preparation method, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 40 minutes; Adding weight portion is 80 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 DEG C, keeps 50 minutes; Use 4 times of washed with de-ionized water, filtration be dried to granular material under 50 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 50 DEG C of dryings, after 30 minutes, obtain product.
embodiment 2
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 53 parts, styrene-acrylic resin 33 parts, polypropylene wax 20 parts, talcum powder 10 parts, sodium silicate 1 part, essence powder 0.1 part.
Its preparation method, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 45 minutes; Adding weight portion is 90 parts of deionized waters, then adds styrene-acrylic resin, is heated to 56 DEG C, keeps 55 minutes; Use 6 times of washed with de-ionized water, filtration be dried to granular material under 55 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 55 DEG C of dryings, after 40 minutes, obtain product.
embodiment 3
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 55 parts, styrene-acrylic resin 33 parts, polypropylene wax 20 parts, talcum powder 10 parts, sodium silicate 3 parts, essence powder 0.25 part.
Its preparation method, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 43 minutes; Adding weight portion is 85 parts of deionized waters, then adds styrene-acrylic resin, is heated to 53 DEG C, keeps 53 minutes; Use 5 times of washed with de-ionized water, filtration be dried to granular material under 53 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 53 DEG C of dryings, after 35 minutes, obtain product.
embodiment 4
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 50 parts, styrene-acrylic resin 30 parts, polypropylene wax 23 parts, talcum powder 13 parts, sodium silicate 3 parts, essence powder 0.25 part.
Its preparation method, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 42 minutes; Adding weight portion is 84 parts of deionized waters, then adds styrene-acrylic resin, is heated to 52 DEG C, keeps 52 minutes; Use 5 times of washed with de-ionized water, filtration be dried to granular material under 53 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 53 DEG C of dryings, after 35 minutes, obtain product.
embodiment 5
A kind of odor type printing ink powder, the weight portion of each component is:
Magnetic oxide 60 parts, styrene-acrylic resin 35 parts, polypropylene wax 25 parts, talcum powder 15 parts, sodium silicate 5 parts, essence powder 0.5 part.
Its preparation method, comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 44 minutes; Adding weight portion is 85 parts of deionized waters, then adds styrene-acrylic resin, is heated to 53 DEG C, keeps 53 minutes; Use 5.5 times of washed with de-ionized water, filtration be dried to granular material under 54 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 55 DEG C of dryings, after 38 minutes, obtain product.
Claims (7)
1. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 50 ~ 60 parts, styrene-acrylic resin 30 ~ 35 parts, polypropylene wax 20 ~ 25 parts, talcum powder 10 ~ 15 parts, sodium silicate 1 ~ 5 part, essence powder 0.1 ~ 0.5 part.
2. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 50 ~ 55 parts, styrene-acrylic resin 30 ~ 33 parts, polypropylene wax 23 ~ 25 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts, essence powder 0.25 ~ 0.5 part.
3. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 55 ~ 60 parts, styrene-acrylic resin 33 ~ 35 parts, polypropylene wax 20 ~ 23 parts, talcum powder 10 ~ 13 parts, sodium silicate 3 ~ 5 parts, essence powder 0.25 ~ 0.5 part.
4. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 53 ~ 57 parts, styrene-acrylic resin 33 ~ 35 parts, polypropylene wax 20 ~ 23 parts, talcum powder 10 ~ 13 parts, sodium silicate 1 ~ 3 part, essence powder 0.1 ~ 0.25 part.
5. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 53 parts, styrene-acrylic resin 33 parts, polypropylene wax 20 parts, talcum powder 10 parts, sodium silicate 1 part, essence powder 0.1 part.
6. an odor type printing ink powder, is characterized in that: the weight portion of each component is:
Magnetic oxide 57 parts, styrene-acrylic resin 35 parts, polypropylene wax 23 parts, talcum powder 13 parts, sodium silicate 3 parts, essence powder 0.25 part.
7., according to a kind of odor type printing ink powder described in claim 1 ~ 6, it is characterized in that: preparation method comprises the following steps:
By described magnetic oxide, polypropylene wax, talcum powder, sodium silicate, essence powder, mixing, ball milling 40 ~ 45 minutes; Adding weight portion is 80 ~ 90 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 ~ 56 DEG C, keeps 50 ~ 55 minutes; Use 4 ~ 6 times of washed with de-ionized water, filtration be dried to granular material under 50 ~ 55 DEG C of conditions; Screen material, select the particle of 3 ~ 8 microns, 50 ~ 55 DEG C of dryings, after 30 ~ 40 minutes, obtain product.