CN105388717A - Color printing ink powder and preparation method therefor - Google Patents
Color printing ink powder and preparation method therefor Download PDFInfo
- Publication number
- CN105388717A CN105388717A CN201510828550.7A CN201510828550A CN105388717A CN 105388717 A CN105388717 A CN 105388717A CN 201510828550 A CN201510828550 A CN 201510828550A CN 105388717 A CN105388717 A CN 105388717A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- printing ink
- ink powder
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to color printing ink powder and a preparation method therefor, and belongs to the technical field of ink powder preparation. The color printing ink powder is prepared from the following components by weight: 60-70 parts of pigment powder, 10-15 parts of modified starch, 10-20 parts of styrene-acrylic resin, 10-15 parts of talcum powder, and 1-5 parts of sodium silicate. The preparation method comprises: uniformly mixing the pigment powder, the modified starch, the talcum powder and sodium silicate, and ball-milling for 30-35 minutes; adding 100-110 parts by weight of de-ionized water, then adding the styrene-acrylic resin, heating to 50-56 DEG C, and keeping the temperature for 50-55 minutes; washing a mixture with de-ionized water 8-10 times heavier than the mixture, filtering the washed mixture, and drying the filtered mixture into granular materials; and screening the materials, selecting granules of 2-10 microns, and drying the granules at 50-55 DEG C for 30-40 minutes to obtain the color printing ink powder. The ink powder is regular and uniform in granule shape, clear in development imaging, distinct in color layer, suitable for use in various different machines, relatively low in preparation cost, and easy for industrialized production.
Description
Technical field
The present invention relates to a kind of printing ink powder, be specifically related to a kind of colored printing ink powder and preparation method thereof, belong to ink powder preparing technical field.
Background technology
Printing (Printing, GraphicArts, also with using GraphicCommunications and figure propagation) be through operations such as plate-making, Shi Mo, pressurizations by original copys such as word, picture, photos, make printing ink transfer on the material surfaces such as paper, fabric, leather, the technology of batch duplicating original copy content.
Whole world printing market is divided into three bulks: the U.S., Europe and Asia respectively account for 1/3rd of global printing market.Chinese printing gross industrial output value rose to third place in the world in 2006.2012, Press and Publications Administration issued the first white paper of press " Chinese printing industry development (2012) "." white paper " shows, and by the end of the year 2011, the total all kinds of printing enterprise 102484 in the whole nation, will fall 1.8% on a year-on-year basis; Industry personnel 356.67 ten thousand people, reduces 2.7% on year-on-year basis; The printing gross output value 8677.13 hundred million yuan, increases by 12.59% on a year-on-year basis; Total assets 9256.66 hundred million yuan, increase by 9.96% on a year-on-year basis; Total profit 739.87 hundred million yuan, increases by 8.31% on a year-on-year basis; External processing trade volume 680.09 hundred million yuan, increases by 2.9% on a year-on-year basis.Wherein, publication printing enterprise 6821, the printing gross output value 1313.94 hundred million yuan, increases by 0.94% on a year-on-year basis; Packing and decorating printing enterprise 47377, the printing gross output value 6318.77 hundred million yuan, increases by 20.6% on a year-on-year basis; Other printed matter printing enterprises 44868, the printing gross output value 708.51 hundred million yuan, falls 15% on a year-on-year basis; Special typesetting, plate-making, binding enterprises 2676, the printing gross output value 77.32 hundred million yuan.On the whole, press is good in China's development.
Ink powder, also known as carbon dust, great majority are made up of resin and carbon black, electric charge agent, magnetic etc.Ink powder in paper fiber, reaches the object of printing through high temperature melt.For different demands, ink powder is produced to becoming more meticulous, colorize, high speed future development.CN201210524730.2 discloses a kind of printer color toner, belongs to pigment art, and described color toner is Yellow ink powder, and described Yellow ink powder contains yellow uitramarine, and described yellow uitramarine, by mass parts, is made up of following component: La
2o
3: 20 ~ 40, MoO
3: 10 ~ 40, Pr
6o
11: 5 ~ 10, Nd1.8Sm0.2O
3: 5 ~ 10.This color toner adopts inorganic oxide to be pigment, the gorgeous and stable in properties of this Yellow ink powder color, and long-term storage still can stablize performance effect, is particularly useful for a large amount of printing speed; CN201010610201.5 discloses a kind of process for preparing color toner for color laser printer, and this technique, for first to prepare pigment dispersion A, can prepare green grass or young crops, Huang, pigment dispersion A that magenta is different with black four kinds according to pigment used difference; Then four kinds of toner material are obtained after being prepared burden respectively by four kinds of different pigment dispersion A; Then four kinds of toner material are carried out mixing with pulverizing; In the toner material obtained, finally carry out outer interpolation mixing, namely obtain the ink powder of four kinds of different colours, ink powder of this invention has dispersive property, the color rendering performance of pigment, the even performance advantage all preferably of ink powder.But the ink powder that above patent provides, preparation technology is more numerous and diverse, and preparation cost is higher, limits it to a certain extent and promotes.
Summary of the invention
The present invention is directed to prior art Problems existing, provide a kind of colored printing ink powder, this toner particles shape is regular, even, development imaging clearly, gradation is clearly demarcated, is useful in multiple different type of machines and uses, and preparation cost is lower, easily realize suitability for industrialized production.
In order to solve the problem, the technical solution adopted in the present invention is:
A kind of colored printing ink powder, the weight portion of each component is:
60 ~ 70 parts, pigment powder, converted starch 10 ~ 15 parts, styrene-acrylic resin 10 ~ 20 parts, talcum powder 10 ~ 15 parts, sodium silicate 1 ~ 5 part;
60 ~ 65 parts, pigment powder, converted starch 10 ~ 13 parts, styrene-acrylic resin 15 ~ 20 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts;
65 ~ 70 parts, pigment powder, converted starch 13 ~ 15 parts, styrene-acrylic resin 10 ~ 15 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts;
63 ~ 68 parts, pigment powder, converted starch 13 ~ 15 parts, styrene-acrylic resin 10 ~ 15 parts, talcum powder 10 ~ 13 parts, sodium silicate 1 ~ 3 part;
63 parts, pigment powder, converted starch 13 parts, styrene-acrylic resin 10 parts, talcum powder 10 parts, sodium silicate 1 part;
68 parts, pigment powder, converted starch 15 parts, styrene-acrylic resin 15 parts, talcum powder 13 parts, sodium silicate 3 parts.
Described pigment is zirconia, cadmium yellow, manganese red, cobalt ultramarine.
Another object of the present invention is to provide a kind of preparation method of colored printing ink powder, comprises the following steps:
By described pigment powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 30 ~ 35 minutes; Adding weight portion is 100 ~ 110 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 ~ 56 DEG C, keeps 50 ~ 55 minutes; Use 8 ~ 10 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 50 ~ 55 DEG C of dryings, after 30 ~ 40 minutes, obtain product.
The present invention relative to the beneficial effect of prior art is:
Colored printing ink powder provided by the invention, water-fast, resistance to illumination, nontoxic, non-stimulated smell, climate adaptability is good, particle shape is regular, even, development imaging clearly, and gradation is clearly demarcated, be useful in multiple different type of machines and use, and preparation cost is lower, easily realizes suitability for industrialized production.
Embodiment
Be described in further details the present invention below by embodiment, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
embodiment 1
A kind of colored printing ink powder, the weight portion of each component is:
Zirconia powder 68 parts, converted starch 15 parts, styrene-acrylic resin 15 parts, talcum powder 13 parts, sodium silicate 3 parts.
Its preparation method, comprises the following steps:
By described zirconia powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 30 minutes; Adding weight portion is 100 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 DEG C, keeps 50 minutes; Use 8 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 50 DEG C of dryings, after 30 minutes, obtain product.
embodiment 2
A kind of colored printing ink powder, the weight portion of each component is:
63 parts, cadmium yellow powder, converted starch 13 parts, styrene-acrylic resin 10 parts, talcum powder 10 parts, sodium silicate 1 part.
Its preparation method, comprises the following steps:
By described cadmium yellow powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 35 minutes; Adding weight portion is 110 parts of deionized waters, then adds styrene-acrylic resin, is heated to 56 DEG C, keeps 55 minutes; Use 10 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 10 microns, 55 DEG C of dryings, after 40 minutes, obtain product.
embodiment 3
A kind of colored printing ink powder, the weight portion of each component is:
65 parts, manganese red powder, converted starch 13 parts, styrene-acrylic resin 10 parts, talcum powder 13 parts, sodium silicate 3 parts.
Its preparation method, comprises the following steps:
By described manganese red powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 33 minutes; Adding weight portion is 105 parts of deionized waters, then adds styrene-acrylic resin, is heated to 53 DEG C, keeps 53 minutes; Use 9 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 53 DEG C of dryings, after 35 minutes, obtain product.
embodiment 4
A kind of colored printing ink powder, the weight portion of each component is:
60 parts, manganese red powder, converted starch 10 parts, styrene-acrylic resin 15 parts, talcum powder 13 parts, sodium silicate 3 parts.
Its preparation method, comprises the following steps:
By described manganese red powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 32 minutes; Adding weight portion is 104 parts of deionized waters, then adds styrene-acrylic resin, is heated to 52 DEG C, keeps 52 minutes; Use 8.5 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 52 DEG C of dryings, after 31 minutes, obtain product.
embodiment 5
A kind of colored printing ink powder, the weight portion of each component is:
70 parts, cobalt ultramarine powder, converted starch 15 parts, styrene-acrylic resin 20 parts, talcum powder 15 parts, sodium silicate 5 parts.
Its preparation method, comprises the following steps:
By described cobalt ultramarine powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 34 minutes; Adding weight portion is 107 parts of deionized waters, then adds styrene-acrylic resin, is heated to 54 DEG C, keeps 54 minutes; Use 9.5 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 54 DEG C of dryings, after 36 minutes, obtain product.
Claims (8)
1. a colored printing ink powder, is characterized in that: the weight portion of each component is:
60 ~ 70 parts, pigment powder, converted starch 10 ~ 15 parts, styrene-acrylic resin 10 ~ 20 parts, talcum powder 10 ~ 15 parts, sodium silicate 1 ~ 5 part.
2. a colored printing ink powder, is characterized in that: the weight portion of each component is:
60 ~ 65 parts, pigment powder, converted starch 10 ~ 13 parts, styrene-acrylic resin 15 ~ 20 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts.
3. a colored printing ink powder, is characterized in that: the weight portion of each component is:
65 ~ 70 parts, pigment powder, converted starch 13 ~ 15 parts, styrene-acrylic resin 10 ~ 15 parts, talcum powder 13 ~ 15 parts, sodium silicate 3 ~ 5 parts.
4. a colored printing ink powder, is characterized in that: the weight portion of each component is:
63 ~ 68 parts, pigment powder, converted starch 13 ~ 15 parts, styrene-acrylic resin 10 ~ 15 parts, talcum powder 10 ~ 13 parts, sodium silicate 1 ~ 3 part.
5. a colored printing ink powder, is characterized in that: the weight portion of each component is:
63 parts, pigment powder, converted starch 13 parts, styrene-acrylic resin 10 parts, talcum powder 10 parts, sodium silicate 1 part.
6. a colored printing ink powder, is characterized in that: the weight portion of each component is:
68 parts, pigment powder, converted starch 15 parts, styrene-acrylic resin 15 parts, talcum powder 13 parts, sodium silicate 3 parts.
7., according to a kind of colored printing ink powder described in claim 1 ~ 6, it is characterized in that: its preparation method, comprise the following steps:
Described pigment powder, converted starch, talcum powder, sodium silicate, mixing, ball milling 30 ~ 35 minutes; Adding weight portion is 100 ~ 110 parts of deionized waters, then adds styrene-acrylic resin, is heated to 50 ~ 56 DEG C, keeps 50 ~ 55 minutes; Use 8 ~ 10 times of washed with de-ionized water, filtration be dried to granular material; Screen material, select the particle of 2 ~ 10 microns, 50 ~ 55 DEG C of dryings, after 30 ~ 40 minutes, obtain product.
8. according to a kind of colored printing ink powder described in claim 1 ~ 7, it is characterized in that: described pigment is zirconia, cadmium yellow, manganese red, cobalt ultramarine.