CN105400447A - 楞纸板用粘合剂及制备方法 - Google Patents
楞纸板用粘合剂及制备方法 Download PDFInfo
- Publication number
- CN105400447A CN105400447A CN201410416379.4A CN201410416379A CN105400447A CN 105400447 A CN105400447 A CN 105400447A CN 201410416379 A CN201410416379 A CN 201410416379A CN 105400447 A CN105400447 A CN 105400447A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- bond
- sodium hydroxide
- hydroxide solution
- corrugated board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种楞纸板用粘合剂及制备方法,属于纸板制造技术领域。本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:植物淀粉30-40%、环氧树脂1-2%、增韧剂0.1-0.5%、氢氧化钠溶液0.4-0.8%、羧甲基纤维素0.5~0.8%、防腐剂0.5~1%、硫酸亚铁铵0.01~0.02%、余量为水。本发明的瓦楞纸板用粘合剂具有粘合速度快,粘结牢、干燥快、易凝胶,易涂抹均匀等优点;其制备过程简单,使用方便,制作效率高、成本低;其不沉淀、不霉变、质量稳定,使用期长,制成的瓦楞板粘合牢固度达到5-6kg/cm。本发明还公开了上述瓦楞纸板用粘合剂的制备方法。
Description
技术领域
本发明涉及一种纸板粘合剂及制备方法,具体讲是一种楞纸板用粘合剂及制备方法,属于纸板制造技术领域。
背景技术
瓦楞纸板在生产过程中需要用粘合剂将每一层粘合在一起,其粘合强度是对瓦楞纸板进行物理性能检验的一个重要指标。在现有的技术中瓦所用的粘合剂一般为淀粉胶,淀粉胶以其价格低廉、制胶工艺简便、干燥速度较快、能适应该苏生产要求等优点广泛应用于国内外的瓦楞纸工业。现有的瓦楞纸粘合剂存在粘力弱、容易霉变、保存周期短且制胶工艺复杂等缺点,不能满足当前瓦楞纸板生产需求。
发明内容
本发明所要解决的技术问题在于克服现有技术缺陷,提供一种粘力强、保存时间长且制备工艺简单的楞纸板用粘合剂及制备方法。
为了解决上述技术问题,本发明提供的瓦楞纸板用粘合剂,由以下重量百分比成份组成:植物淀粉30-40%、环氧树脂1-2%、增韧剂0.1-0.5%、氢氧化钠溶液0.4-0.8%、羧甲基纤维素0.5~0.8%、防腐剂0.5~1%、硫酸亚铁铵0.01~0.02%、余量为水。
本发明中,所述的瓦楞纸板用粘合剂,由以下重量百分比成份组成:植物淀粉35%、环氧树脂2%、增韧剂0.3%、氢氧化钠溶液0.6%、羧甲基纤维素0.6%、防腐剂0.8%、硫酸亚铁铵0.02%,余量为水。
本发明中,所述植物淀粉为红薯淀粉、木薯淀粉、魔竽淀粉、玉米淀粉、大米淀粉、糯米淀粉中的一种或任意几种组合。
本发明中,所述氢氧化钠溶液的浓度为33%。
本发明还提供了一种瓦楞纸板用粘合剂的制备方法,包括以下步骤:
1)、向反应釜中加入植物淀粉、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到75-80℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
本发明的有益效果在于:(1)、本发明的瓦楞纸板用粘合剂具有粘合速度快,粘结牢、干燥快、易凝胶,易涂抹均匀等优点;其制备过程简单,使用方便,制作效率高、成本低;(2)、本发明的瓦楞纸板用粘合剂不沉淀、不霉变、质量稳定,使用期长,制成的瓦楞板粘合牢固度达到5-6kg/cm。
具体实施方式
下面结合具体实施例对本发明作进一步详细说明。
实施例1
本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:
红薯淀粉35%、环氧树脂2%、增韧剂0.3%、氢氧化钠溶液0.6%、羧甲基纤维素0.6%、防腐剂0.8%、硫酸亚铁铵0.02%,余量为水。
制备过程:
1)、向反应釜中加入红薯淀粉、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到75℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
实施例2
本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:
木薯淀粉40%、环氧树脂1%、增韧剂0.1%、氢氧化钠溶液0.4%、羧甲基纤维素0.8%、防腐剂0.5%、硫酸亚铁铵0.01%,余量为水。
制备过程:
1)、向反应釜中加入木薯淀粉、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到80℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
实施例3
本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:
魔竽淀粉和玉米淀粉混合物30%、环氧树脂1.5%、增韧剂0.5%、氢氧化钠溶液0.5%、羧甲基纤维素0.5%、防腐剂0.7%、硫酸亚铁铵0.01%,余量为水。
制备过程:
1)、向反应釜中加入魔竽淀粉和玉米淀粉混合物、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到76℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
实施例4
本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:
红薯淀粉、玉米淀粉和大米淀粉混合物33%、环氧树脂2%、增韧剂0.4%、氢氧化钠溶液0.7%、羧甲基纤维素0.7%、防腐剂1%、硫酸亚铁铵0.02%,余量为水。
制备过程:
1)、向反应釜中加入红薯淀粉、玉米淀粉和大米淀粉混合物、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到79℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
实施例5
本发明瓦楞纸板用粘合剂由以下重量百分比成份组成:
木薯淀粉、魔竽淀粉、玉米淀粉和糯米淀粉混合物38%、环氧树脂1.8%、增韧剂0.5%、氢氧化钠溶液0.8%、羧甲基纤维素0.7%、防腐剂0.9%、硫酸亚铁铵0.02%,余量为水。
制备过程:
1)、向反应釜中加入木薯淀粉、魔竽淀粉、玉米淀粉和糯米淀粉混合物、玉米淀粉和大米淀粉混合物、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到71℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下还可以做出若干改进,这些改进也应视为本发明的保护范围。
Claims (5)
1.一种瓦楞纸板用粘合剂,其特征在于由以下重量百分比成份组成:植物淀粉30-40%、环氧树脂1-2%、增韧剂0.1-0.5%、氢氧化钠溶液0.4-0.8%、羧甲基纤维素0.5~0.8%、防腐剂0.5~1%、硫酸亚铁铵0.01~0.02%、余量为水。
2.根据权利要求1所述的瓦楞纸板用粘合剂,其特征在于由以下重量百分比成份组成:植物淀粉35%、环氧树脂2%、增韧剂0.3%、氢氧化钠溶液0.6%、羧甲基纤维素0.6%、防腐剂0.8%、硫酸亚铁铵0.02%,余量为水。
3.根据权利要求2所述的瓦楞纸板用粘合剂,其特征在于:所述植物淀粉为红薯淀粉、木薯淀粉、魔竽淀粉、玉米淀粉、大米淀粉、糯米淀粉中的一种或任意几种组合。
4.根据权利要求3所述的瓦楞纸板用粘合剂,其特征在于:所述氢氧化钠溶液的浓度为33%。
5.根据权利要求1至4任一项所述瓦楞纸板用粘合剂的制备方法,其特征在于包括以下步骤:
1)、向反应釜中加入植物淀粉、环氧树脂氢、氧化钠溶液、羧甲基纤维素、硫酸亚铁铵和水进行充分混合搅拌均匀;
2)、逐渐升温到75-80℃,进行糊化后依次加入增韧剂和防腐剂,混合搅拌10-15min;
3)、自然冷却后得到粘合剂。