CN105400024A - 一种高耐磨氯丁橡胶 - Google Patents

一种高耐磨氯丁橡胶 Download PDF

Info

Publication number
CN105400024A
CN105400024A CN201510907487.6A CN201510907487A CN105400024A CN 105400024 A CN105400024 A CN 105400024A CN 201510907487 A CN201510907487 A CN 201510907487A CN 105400024 A CN105400024 A CN 105400024A
Authority
CN
China
Prior art keywords
chloroprene rubber
carbon black
graphene
formula
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510907487.6A
Other languages
English (en)
Inventor
刘力
许宗超
温世鹏
张立群
卢咏来
冯予星
廖坤
张继阳
杨云河
董志鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING BEIHUAXINXIANG SPECIAL MATERIAL TECHNOLOGY Co Ltd
Beijing University of Chemical Technology
Original Assignee
BEIJING BEIHUAXINXIANG SPECIAL MATERIAL TECHNOLOGY Co Ltd
Beijing University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING BEIHUAXINXIANG SPECIAL MATERIAL TECHNOLOGY Co Ltd, Beijing University of Chemical Technology filed Critical BEIJING BEIHUAXINXIANG SPECIAL MATERIAL TECHNOLOGY Co Ltd
Priority to CN201510907487.6A priority Critical patent/CN105400024A/zh
Publication of CN105400024A publication Critical patent/CN105400024A/zh
Pending legal-status Critical Current

Abstract

一种高耐磨氯丁橡胶涉及橡胶复合材料制备技术领域，具体涉及一种硫调型氯丁橡胶配方，采用该配方制备氯丁橡胶复合材料具有良好的加工安全性和优异的耐磨性。本发明在配方中引入大片层结构石墨烯与炭黑、白炭黑并用补强氯丁橡胶，石墨烯加入不仅对赋予氯丁橡胶优异的力学性能，同时石墨烯大片层结构吸附硫化剂，延长焦烧期，改善加工安全性，从而制备高性能氯丁橡胶复合材料，采用该配方制备的氯丁橡胶制品不仅可以满足产品性能要求，同时有效延长氯丁橡胶制品实际使用寿命，实现较大的工业价值和效益。

Description

一种高耐磨氯丁橡胶
技术领域：
本发明涉及橡胶复合材料领域领域，具体涉及一种硫调型氯丁橡胶配方，采用该配方制备的氯丁橡胶复合材料具有良好的加工安全性和优异的耐磨性。
背景技术：
氯丁橡胶以氯丁二烯为单体通过自由基乳液聚合而成。氯丁橡胶大分子链上有97.5％的Cl原子直接连接在双键碳原子上，Cl原子的吸电性使双键变得活泼，所以氯丁橡胶分子链结构上虽然有双键但是不能采用硫磺硫化。通用型氯丁橡胶分为硫调型和非硫调型两种，硫调型氯丁橡胶硫化时可以不需要促进剂，非硫调型氯丁橡胶需配合促进剂。氯丁橡胶因其结构特点，使得氯丁橡胶具有优异的力学性能、耐光照及耐老化性能。自从2004年石墨烯被发现以来，石墨烯/橡胶复合材料的制备成为橡胶领域研究工作者的研究热点。石墨烯作为一种新型的非石油依赖性填料较炭黑、白炭黑表现出明显的优势，石墨烯大尺寸结构不仅可以赋予氯丁橡胶优异的力学强度及良好的耐磨性和阻隔性能，同时石墨烯还可以吸附橡胶硫化剂，改善氯丁橡胶硫化过程中易焦烧的技术难题。
发明内容：
本发明的目的是为了提供一种高耐磨氯丁橡胶配方，不仅解决氯丁橡胶复合材料耐磨性差的问题，而且利用石墨烯大尺寸片层结构可以吸附硫化剂，延长焦烧时间，改善氯丁橡胶的加工安全性，采用本配方制备的氯丁橡胶复合材料具有优异的力学性能，同时还具备较低的压缩永久变形性能和良好的耐磨性能等特点。
为实现发明目的，本发明采用如下技术方案：一种高耐磨氯丁橡胶配方，其特征包括以下以质量的原料组分
首先采用乳液复合将石墨烯预分散在硫调型氯丁橡胶中，随后将氯丁橡胶中放入橡胶炼胶机中混炼2min，随后加入防老剂、硬脂酸、炭黑、白炭黑、硅烷偶联剂、增塑剂混炼10min；最后加入氧化锌、氧化镁混炼3min，最后得到石墨烯-炭黑-白炭黑/氯丁橡胶混炼胶，硫化并测试性能。
最后加入氧化锌、氧化镁混炼3min，最后得到石墨烯-炭黑-白炭黑/氯丁橡胶混炼胶，硫化并测试性能。
本发明所述原料组分中氯丁橡胶为硫调型氯丁橡胶。
本发明所述原料组分中炭黑可以为超耐炭黑，中超耐磨炭黑，高耐磨炭黑，快压出炭黑，通用炭黑，半补强炭黑。
本发明所述原料组分中白炭黑可以为沉淀法白炭黑、气相法白炭黑。
本发明所述原料组分中硅烷偶联剂可以为Si69、Si747、KH550、KH560、KH570。
本发明所述原料组分中防老剂可以为胺类防老剂，酚类防老剂。
本发明所述原料组分中增塑剂可以为石油系增塑剂，煤焦油系增塑剂，合成增塑剂。
具体实施方式：
为体现配方中石墨烯对硫调型氯丁橡胶力学性能的提高及对加工安全性的改善，故采用对比例1(不添加石墨烯)与实施例1对比，下面结合对比例和实施例对发明作进一步说明
对比例1：
实施例1：
实施例2：
实施例3：
实施例4：
实施例5：
实施例6：
对比例与实施例中石墨烯/氯丁橡胶复合材料的制备工艺将石墨烯采用乳液复合方法预分散在硫调型氯丁橡胶中，随后将石墨烯/氯丁橡胶中放入橡胶炼胶机中混炼2min，随后加入防老剂、硬脂酸、炭黑、白炭黑、硅烷偶联剂、增塑剂混炼10min，最后加入氧化锌、氧化镁混炼3min，最后得到石墨烯-炭黑-白炭黑/氯丁橡胶混炼胶，硫化并测试性能。
实施例与对比例中硫调型氯丁橡胶复合材料性能对比如下：
以上已对本发明中性能较佳实施例进行了详细说明，但本发明并不局限于所述实施例，熟悉本领域的技术人员在不违背本发明精神的前提下还可以做出种种的等同的变型或替换，本方法中的炭黑仍可采用其它填料如白炭黑、蒙脱土、陶土等，硅烷偶联仍可采用钛酸酯偶联剂或铝酸酯偶联剂替代，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。

Claims (6)

1.一种高耐磨氯丁橡胶，其特征在于：以氯丁橡胶质量份数为100为基准，氯丁橡胶复合材料中各组分的质量份数如下：
2.根据权利要求1所述橡胶，其特征在于：所述炭黑为超耐炭黑，中超耐磨炭黑，高耐磨炭黑，快压出炭黑，通用炭黑或者半补强炭黑。
3.根据权利要求1所述橡胶，其特征在于：白炭黑为沉淀法白炭黑或者气相法白炭黑。
4.根据权利要求1所述橡胶，其特征在于：硅烷偶联剂为Si69、Si747、KH550、KH560或KH570。
5.根据权利要求1所述橡胶，其特征在于：防老剂为胺类防老剂或酚类防老剂。
6.根据权利要求1所述橡胶，其特征在于：增塑剂为石油系增塑剂，煤焦油系增塑剂或合成增塑剂。
CN201510907487.6A 2015-12-10 2015-12-10 一种高耐磨氯丁橡胶 Pending CN105400024A (zh)