CN105385224A - High-performance UV printing ink - Google Patents
High-performance UV printing ink Download PDFInfo
- Publication number
- CN105385224A CN105385224A CN201510994873.3A CN201510994873A CN105385224A CN 105385224 A CN105385224 A CN 105385224A CN 201510994873 A CN201510994873 A CN 201510994873A CN 105385224 A CN105385224 A CN 105385224A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- good
- reactive thinner
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
High-performance UV printing ink is prepared from, by weight, 11-17 parts of ultraviolet light curing resin, 3-8 parts of reactive diluent, 6-15 parts of 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1-acetone, 15-26 parts of UV curable varnish, 8-12 parts of fumed silica, 8-13 parts of pearl powder, 3-8 parts of aluminum-based silver paste, 0.6-2.5 parts of ethyl alcohol, 3-6 parts of plasticizer, 8-12 parts of 804 organic silicon resin, 4-6 parts of ethyl acetate, 3-6 parts of acetic acid, 1.2-4 parts of reactive diluent, 0.5-2.4 parts of lubricating agent, 10-16 parts of ternary chloroparaffin resin and 3-6 parts of stabilizer. The high-performance UV printing ink has the advantages of being high in drying speed, good in lustre, good in abrasion resistance and durability, capable of saving energy, environmentally friendly and good in use value.
Description
Technical field
The present invention relates to a kind of high performance UV ink.
Background technology
UV ink refers under uviolizing, utilizes different wave length and the UV-light of energy to make the monomer polymerization in ink adhesive become polymkeric substance, makes ink film forming and dry ink.UV ink also belongs to ink, and as ink, they must possess gorgeous color (except Special Circumstances), good printability, suitable solidification drying rate.There is good sticking power simultaneously, and possess the characteristics such as wear-resisting, anti-corrosion, weather-proof.UV ink is a kind of economic, efficient ink, contained all print fields at present, but comparatively solvent type ink is high due to price, so general comparatively multiplex on high-grade printed document.At the print surface of metallic mirror surface gloss, adopt silk-screen printing technique means by the drying plant of UV ink printing after the processing of UV light, produce a kind of visual effect of uniqueness, seem graceful, serious, luxurious, be mainly used in the packages printing of the cigarette of medium-to-high grade gracefulness uniqueness, wine, makeup, healthcare products, food, medicine.Due to the better performances of UV ink, range of application is more and more wider.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of UV ink, and rate of drying is fast, and good luster, has good wear resistance and weather resistance, energy-conserving and environment-protective simultaneously, has good use value.
For solving prior art problem, technical scheme provided by the invention is, a kind of high performance UV ink, and it is made up of the raw material of following parts by weight:
UV-cured resin 11-17 part, reactive thinner 3-8 part, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl]-1-acetone 6-15 part, UV gloss oil 15-26 part, aerosil 8-12 part, pearlescence 8-13 part, aluminium base silver slurry 3-8 part, ethanol 0.6-2.5 part, softening agent 3-6 part, 804 silicone resin 8-12 parts, ethyl acetate 4-6 part, acetic acid 3-6 part, reactive thinner 1.2-4 part, lubricant 0.5-2.4 part, ternary chlorine wax tree fat 10-16 part, stablizer 3-6 part.
Further, a kind of high performance UV ink, it is made up of the raw material of following parts by weight:
UV-cured resin 14 parts, reactive thinner 5.5 parts, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl] 10 parts ,-1-acetone, UV gloss oil 21 parts, aerosil 10 parts, pearlescence 10 parts, aluminium base 5.5 parts, silver slurry, ethanol 1.5 parts, 4.5 parts, softening agent, 804 silicone resins 10 parts, ethyl acetate 5 parts, acetic acid 4.5 parts, reactive thinner 2.6 parts, lubricant 1.9 parts, 13 parts, ternary chlorine wax tree fat, stablizer 4.5 parts.
The invention has the beneficial effects as follows: UV ink of the present invention, rate of drying is fast, and good luster, has good wear resistance and weather resistance, energy-conserving and environment-protective simultaneously, has good use value.
Embodiment
embodiment 1
A kind of high performance UV ink, it is made up of the raw material of following parts by weight:
UV-cured resin 11 parts, reactive thinner 3 parts, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl] 6 parts ,-1-acetone, UV gloss oil 15 parts, aerosil 8 parts, pearlescence 8 parts, aluminium base 3 parts, silver slurry, ethanol 0.6 part, 3 parts, softening agent, 804 silicone resins 8 parts, ethyl acetate 4 parts, acetic acid 3 parts, reactive thinner 1.2 parts, lubricant 0.5 part, 10 parts, ternary chlorine wax tree fat, stablizer 3 parts.
embodiment 2
A kind of high performance UV ink, it is made up of the raw material of following parts by weight:
UV-cured resin 17 parts, reactive thinner 8 parts, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl] 15 parts ,-1-acetone, UV gloss oil 26 parts, aerosil 12 parts, pearlescence 13 parts, aluminium base 8 parts, silver slurry, ethanol 2.5 parts, 6 parts, softening agent, 804 silicone resins 12 parts, ethyl acetate 6 parts, acetic acid 6 parts, reactive thinner 4 parts, lubricant 2.4 parts, 16 parts, ternary chlorine wax tree fat, stablizer 6 parts.
embodiment 3
A kind of high performance UV ink, it is made up of the raw material of following parts by weight:
UV-cured resin 14 parts, reactive thinner 5.5 parts, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl] 10 parts ,-1-acetone, UV gloss oil 21 parts, aerosil 10 parts, pearlescence 10 parts, aluminium base 5.5 parts, silver slurry, ethanol 1.5 parts, 4.5 parts, softening agent, 804 silicone resins 10 parts, ethyl acetate 5 parts, acetic acid 4.5 parts, reactive thinner 2.6 parts, lubricant 1.9 parts, 13 parts, ternary chlorine wax tree fat, stablizer 4.5 parts.
Claims (2)
1. a high performance UV ink, is characterized in that: it is made up of the raw material of following parts by weight:
UV-cured resin 11-17 part, reactive thinner 3-8 part, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl]-1-acetone 6-15 part, UV gloss oil 15-26 part, aerosil 8-12 part, pearlescence 8-13 part, aluminium base silver slurry 3-8 part, ethanol 0.6-2.5 part, softening agent 3-6 part, 804 silicone resin 8-12 parts, ethyl acetate 4-6 part, acetic acid 3-6 part, reactive thinner 1.2-4 part, lubricant 0.5-2.4 part, ternary chlorine wax tree fat 10-16 part, stablizer 3-6 part.
2. high performance UV ink according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
UV-cured resin 14 parts, reactive thinner 5.5 parts, 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio group) phenyl] 10 parts ,-1-acetone, UV gloss oil 21 parts, aerosil 10 parts, pearlescence 10 parts, aluminium base 5.5 parts, silver slurry, ethanol 1.5 parts, 4.5 parts, softening agent, 804 silicone resins 10 parts, ethyl acetate 5 parts, acetic acid 4.5 parts, reactive thinner 2.6 parts, lubricant 1.9 parts, 13 parts, ternary chlorine wax tree fat, stablizer 4.5 parts.