CN105385138A - 一种高抗冲防炫目的pc材料 - Google Patents
一种高抗冲防炫目的pc材料 Download PDFInfo
- Publication number
- CN105385138A CN105385138A CN201510889738.2A CN201510889738A CN105385138A CN 105385138 A CN105385138 A CN 105385138A CN 201510889738 A CN201510889738 A CN 201510889738A CN 105385138 A CN105385138 A CN 105385138A
- Authority
- CN
- China
- Prior art keywords
- impact
- glare
- polycarbonate
- light diffusing
- diffusing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高抗冲防炫目的PC材料，其特征在于：包括聚碳酸酯、光扩散剂、抗冲改性剂、光稳定剂、抗氧剂及润滑剂，各成份的占比为：聚碳酸酯95％～99％，光扩散剂0.5％～2％，抗冲改性剂0.5％～2％，光稳定剂0.2％～1％，抗氧剂0.1％～1％，润滑剂0.2％～1％，其中，聚碳酸酯为双酚A型，重均分子量为25000-40000g/mol的树脂。本发明中公开了一种高抗冲防炫目的PC材料，光扩散率高，同时耐冲击，极端条件下户外的使用报废率低。
Description
技术领域
本发明涉及一种PC材料，尤其涉及一种高抗冲防炫目的PC材料。
背景技术
目前市场上的PC光扩散材料普遍耐低温冲击不好，而且在极端条件下户外使用报废率很高。针对这一缺陷，在满足光扩散效率的基础上，如何开发出耐冲击的PC光扩散材料，是本领域技术人员需要努力的方向。
发明内容
本发明目的是提供一种高抗冲防炫目的PC材料，通过使用该产品配比，保证了材料的光扩散效率，提高了材料的耐冲击力。
为达到上述目的，本发明采用的技术方案是：一种高抗冲防炫目的PC材料，包括聚碳酸酯、光扩散剂、抗冲改性剂、光稳定剂、抗氧剂及润滑剂，各成份的占比为：
其中，聚碳酸酯为双酚A型，重均分子量为25000-40000g/mol的树脂。
上述技术方案中，所述光扩散剂聚甲基丙烯酸甲酯。
上述技术方案中，所述光扩散剂的折射率为1.49。
上述技术方案中，所述抗冲改性剂为有机硅-丙烯酸复合胶。
上述技术方案中，所述光稳定剂为苯并三唑。
上述技术方案中，所述抗氧剂为汽巴Irganox1076及汽巴Irgafos168的复配物，所述汽巴Irganox1076及汽巴Irgafos168的复配比例为1：2。
上述技术方案中，所述润滑剂为聚乙烯蜡或乙撑双硬脂酰胺。
由于上述技术方案运用，本发明与现有技术相比具有下列优点：
1.本发明中PC材料包括聚碳酸酯、光扩散剂、抗冲改性剂、光稳定剂、抗氧剂及润滑剂，与以往的材料相比，及保证了PC材料的光扩散效率，也提高了PC材料的耐低温冲击力，使极端条件下户外使用的报废率大大降低。
具体实施方式
下面结合实施例对本发明作进一步描述：
实施例一：一种高抗冲防炫目的PC材料，包括聚碳酸酯、光扩散剂、抗冲改性剂、光稳定剂、抗氧剂及润滑剂，各成份的占比为：
其中，聚碳酸酯为双酚A型，重均分子量为25000-40000g/mol的树脂。所述光扩散剂聚甲基丙烯酸甲酯，所述光扩散剂的折射率为1.49。所述抗冲改性剂为有机硅-丙烯酸复合胶，所述光稳定剂为苯并三唑，所述抗氧剂为汽巴Irganox1076及汽巴Irgafos168的复配物，所述汽巴Irganox1076及汽巴Irgafos168的复配比例为1：2。所述润滑剂为聚乙烯蜡或乙撑双硬脂酰胺。
实施例二：一种高抗冲防炫目的PC材料，在本实施例中，取聚碳酸酯99份、光扩散剂1份、抗冲改性剂0份、抗氧剂0.3份、润滑剂0.5份及光稳定剂0.5份进行测试PC材料的物理性能，在ISO178的标准下，23℃的条件下悬臂缺口冲击强度为12KJ/m2；在ISO180的标准下，-30℃的条件下悬臂缺口冲击强度为6KJ/m2；在ASTMD1003的标准下，厚度为1mm的产品，透光度为94％；在ISO14782的标准下，厚度为1mm的产品，雾度为97％。
实施例三：一种高抗冲防炫目的PC材料，在本实施例中，取聚碳酸酯98份、光扩散剂1份、抗冲改性剂1份、抗氧剂0.3份、润滑剂0.5份及光稳定剂0.8份进行测试PC材料的物理性能，在ISO178的标准下，23℃的条件下悬臂缺口冲击强度为25KJ/m2；在ISO180的标准下，-30℃的条件下悬臂缺口冲击强度为15KJ/m2；在ASTMD1003的标准下，厚度为1mm的产品，透光度为66％；在ISO14782的标准下，厚度为1mm的产品，雾度为99％。
实施例四：一种高抗冲防炫目的PC材料，在本实施例中，取聚碳酸酯98份、光扩散剂1份、抗冲改性剂0.5份、抗氧剂0.3份、润滑剂0.5份及光稳定剂1份进行测试PC材料的物理性能，在ISO178的标准下，23℃的条件下悬臂缺口冲击强度为16KJ/m2；在ISO180的标准下，-30℃的条件下悬臂缺口冲击强度为12KJ/m2；在ASTMD1003的标准下，厚度为1mm的产品，透光度为76％；在ISO14782的标准下，厚度为1mm的产品，雾度为99％。
由此，用实施例二与实施例三及实施例四进行对比可知，实施例三及实施例四采用本发明的配比，在低温及极端条件下，抗冲击效果好，光扩散率高。
Claims (7)
1.一种高抗冲防炫目的PC材料，其特征在于：包括聚碳酸酯、光扩散剂、抗冲改性剂、光稳定剂、抗氧剂及润滑剂，各成份的占比为：
其中，聚碳酸酯为双酚A型，重均分子量为25000-40000g/mol的树脂。
2.根据权利要求1所述的高抗冲防炫目的PC材料，其特征在于：所述光扩散剂聚甲基丙烯酸甲酯。
3.根据权利要求2所述的高抗冲防炫目的PC材料，其特征在于：所述光扩散剂的折射率为1.49。
4.根据权利要求1所述的高抗冲防炫目的PC材料，其特征在于：所述抗冲改性剂为有机硅-丙烯酸复合胶。
5.根据权利要求1所述的高抗冲防炫目的PC材料，其特征在于：所述光稳定剂为苯并三唑。
6.根据权利要求1所述的高抗冲防炫目的PC材料，其特征在于：所述抗氧剂为汽巴Irganox1076及汽巴Irgafos168的复配物，所述汽巴Irganox1076及汽巴Irgafos168的复配比例为1：2。
7.根据权利要求1所述的高抗冲防炫目的PC材料，其特征在于：所述润滑剂为聚乙烯蜡或乙撑双硬脂酰胺。