CN103483795A - 一种改善了硬度和耐寒性能的pc/asa组合物 - Google Patents

一种改善了硬度和耐寒性能的pc/asa组合物 Download PDF

Info

Publication number
CN103483795A
CN103483795A CN201310398689.3A CN201310398689A CN103483795A CN 103483795 A CN103483795 A CN 103483795A CN 201310398689 A CN201310398689 A CN 201310398689A CN 103483795 A CN103483795 A CN 103483795A
Authority
CN
China
Prior art keywords
parts
ethylene
copolymer
asa
styrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310398689.3A
Other languages
English (en)
Inventor
许第修
段海斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHENZHEN XINGSHENGDI NEW MATERIALS CO Ltd
Original Assignee
SHENZHEN XINGSHENGDI NEW MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN XINGSHENGDI NEW MATERIALS CO Ltd filed Critical SHENZHEN XINGSHENGDI NEW MATERIALS CO Ltd
Priority to CN201310398689.3A priority Critical patent/CN103483795A/zh
Publication of CN103483795A publication Critical patent/CN103483795A/zh
Pending legal-status Critical Current

Abstract

一种改善了硬度和耐寒性能的PC/ASA组合物，其特征在于按重量份数计其组成如下：80份的聚碳酸酯,10份的丙烯腈-苯乙烯-丙烯酸酯，1~20份的增韧剂，1~10份的耐寒剂，1~10份的阻燃剂，1~10份的流动剂，所述增韧剂选自乙烯辛烯共聚物、乙烯丁烯共聚物、乙烯丙烯共聚物及苯乙烯丁二烯共聚物中的至少一种，所述耐寒剂选自乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯无规三元共聚物、乙烯-丙烯酸甲酯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、马来酸酐接枝高密度聚乙烯中的至少一种，相对现有技术本发明提升了PC/ASA组合物的硬度和耐寒性能。

Description

一种改善了硬度和耐寒性能的PC/ASA组合物
技术领域
本发明涉及一种改善了硬度和耐寒性能的PC/ASA组合物，属于高分子复合材料领域。
背景技术
聚碳酸酯(PC)塑料具有耐热性高，透明度好，光泽高，韧性好等优点，但是它流动性差，成型困难；制品对缺口敏感，容易产生应力开裂；不耐溶剂，而且价格昂贵。
有许多己知的通过制备PC塑料合金的方法来改善这些缺点，其中PC/ABS共混改性是最常见的方法，PC/ABS合金具有熔体粘度低，加工性能好，冲击强度高等良好的综合性能。
丙烯腈一苯乙烯一丙烯酸酯(ASA)是一种物理机械性能与ABS相类似的工程塑料。ASA塑料具有良好的尺寸稳定性能，缺口冲击性能高的特点。同时，与ABS相比，ASA在材料的耐候性、耐紫外光性等方面有很大的提高（约提高10倍），因此ASA工程塑料在汽车、通信、电子等行业有很大的市场应用空间，可用于制作高性能的汽车外饰件、家电室外部件、通信产品，如汽车后视镜、空调室外机、室外卫星天线线路壳体等。
将PC和ASA树脂制成共混材料，能获得这样一种具有优异的耐侯性能，良好的抗冲击性能，同时兼具耐热温度高和加工性能优良的材料，是业界的共识，发明专利ZL200810207591.4就公开了一种这样的PC/ASA组合物，ZL200810207591.4所公开的PC/ASA组合物，由聚碳酸酯、丙烯腈一苯乙烯一丙烯酸酯接枝共聚物、丙烯腈一苯乙烯共聚物、凝胶化苯乙烯一丙烯腈共聚物、乙烯一丙烯酸酯共聚物弹
性体、光稳定剂和抗氧剂组成。所述的聚碳酸酯为30～90重量份，丙烯腈一苯乙烯一丙烯酸酯接枝共聚物为5～30重量份，丙烯腈一苯乙烯共聚物为0～30重量份，凝胶化苯乙烯一丙烯腈共聚物为l～5重量份，乙烯一丙烯酸酯共聚物弹性体为2～10重量份，光稳定剂为0.2～2重量份，抗氧剂为0.2～l重量份。
所述的聚碳酸酯为双酚A型芳香族聚碳酸酯；所述聚碳酸酯树脂的重均分子量为20000-40000g；所述丙烯腈一苯乙烯一丙烯酸酯接枝共聚物以重量百分比计丙烯酸酯橡胶含量为40-80%；所述乙烯一丙烯酸酯共聚物弹性体选自乙烯一甲基丙烯酸酯共聚物EMA，乙烯一丙烯酸丁酯共聚物EBA，乙烯一丙烯酸酯一丙烯酸缩水甘油酯共聚物EMA-GMA，以及它们的混和物；所述乙烯一丙烯酸酯共聚物弹性体选自丙烯酸酯含量为16～30%乙烯一丙烯酸酯共聚物中的一种或几种；所述光稳定剂为苯并三唑类光吸收剂；所述抗氧稳定剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂的混合物；所述组合物还可包括其它着色剂，填料，热稳定剂，润滑剂等。
ZL200810207591.4所公开的PC/ASA组合物尽管有相当不错的常规性能指标，但硬度和耐寒性能较差，不太适合对材料硬度以及耐寒性能有特殊要求的应用场合，同时，ZL200810207591.4所公开的PC/ASA组合物对聚碳酸酯树脂的选择有较为严格的要求，使得成本较高，综上所述，显然现有技术有进一步改进的必要。
发明内容
本发明的目的在于提供一种改善了硬度和耐寒性能的PC/ASA组合物，以克服现有技术存在的问题。
本发明的一种改善了硬度和耐寒性能的PC/ASA组合物，其特征在于按重量份数计其组成如下：
80份的聚碳酸酯（PC）,10份的丙烯腈-苯乙烯-丙烯酸酯，1～20份的增韧剂，1～10份的耐寒剂，1～10份的阻燃剂，1～10份的流动剂；
所述增韧剂选自乙烯辛烯共聚物、乙烯丁烯共聚物、乙烯丙烯共聚物及苯乙烯丁二烯共聚物中的至少一种；
所述耐寒剂选自乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯无规三元共聚物、乙烯-丙烯酸甲酯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、马来酸酐接枝高密度聚乙烯中的至少一种；所述阻燃剂选自磷酸三苯酯、磷酸三甲苯酯、双酚A双磷酸二苯酯中的至少一种；
所述流动剂选自乙撑双硬脂酰胺（EBS）、季戊四醇硬脂酸（PETS）、PE蜡及PP蜡中的至少一种。
本发明的这种改善了硬度和耐寒性能的PC/ASA组合物，可以采用常规的混合挤出造粒工艺生产，推荐的制成方法为：混合时使用高速搅拌机搅拌，挤出时采用75#双螺杆挤出机，转速为400r/min，挤出机头一区温度为240℃，二区温度为245℃，三区温度为245℃，四区温度为245℃，五区温度为240℃。
本发明的这种改善了硬度和耐寒性能的PC/ASA组合物，与现有技术的以及市面上普通的PC/ASA组合物材料相比，在保有较好的机械性能指标的同时，硬度以及耐寒性得到了较大的提升，硬度的提高使得采用这种PC/ASA组合物制成的部件的耐磨性得到了提升，耐寒性能的改善使得采用本发明的这种PC/ASA组合物制成的部件或结构件能够满足长期低温环境中使用的需要，显然本发明的目的得以实现。
具体实施方式
下面将结合具体实施例，对本发明做进一步说明，但所述实施例仅用于说明本发明而不是限制本发明。
本发明各实施例的一种改善了硬度和耐寒性能的PC/ASA组合物按重量份数计其组成如表一所示：
表一：
组份 实施例1 实施例2 实施例3 实施例4
聚碳酸酯（PC） 80份 80份 80份 80份
丙烯腈-苯乙烯-丙烯酸酯共聚物（ASA） 10份 10份 10份 10份
增韧剂:
乙烯辛烯共聚物（POE） 2份 6份
乙烯丁烯共聚物
乙烯丙烯共聚物 4份
苯乙烯丁二烯共聚物 8份
耐寒剂:
甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物（MBS） 1份
乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯无规三元共聚物 7份
乙烯-丙烯酸甲酯共聚物
马来酸酐接枝高密度聚乙烯 4份 9份
阻燃剂:
双酚A双磷酸二苯酯 2.5份 9份
磷酸三苯酯 4份
磷酸三甲苯酯 7份
流动剂:
季戊四醇硬脂酸 0.5份
乙撑双硬脂酰胺（EBS）
PE蜡 4份 9份
PP蜡 7份
本发明各实施例的一种改善了硬度和耐寒性能的PC/ASA组合物，其制成方法均为混合时使用高速搅拌机搅拌，挤出时采用75#双螺杆挤出机，转速为400r/min，挤出机头一区温度为240℃，二区温度为245℃，三区温度为245℃，四区温度为245℃，五区温度为240℃。
本发明各实施例的一种改善了硬度和耐寒性能的PC/ASA组合物的性能测试条件如表二所示：
表二：
Figure BDA0000377002540000031
Figure BDA0000377002540000041
本发明各实施例的一种改善了硬度和耐寒性能的PC/ASA组合物的测试所得的性能参数如表三和表四所示，其中表三为常温环境下的测试数据，表四为低温-40℃环境下静置40小时后的测试数据：
表三：
表四：
Figure BDA0000377002540000043

Claims (1)

1.一种改善了硬度和耐寒性能的PC/ASA组合物，其特征在于按重量份数计其组成如下：
80份的聚碳酸酯, 10份的丙烯腈-苯乙烯-丙烯酸酯，1~20份的增韧剂，1~10份的耐寒剂， 1~10份的阻燃剂， 1~10份的流动剂；
所述增韧剂选自乙烯辛烯共聚物、乙烯丁烯共聚物、乙烯丙烯共聚物及苯乙烯丁二烯共聚物中的至少一种；
所述耐寒剂选自乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯无规三元共聚物、乙烯-丙烯酸甲酯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、马来酸酐接枝高密度聚乙烯中的至少一种；
所述阻燃剂选自磷酸三苯酯、磷酸三甲苯酯、双酚A双磷酸二苯酯中的至少一种；
所述流动剂选自乙撑双硬脂酰胺（EBS）、季戊四醇硬脂酸（PETS）、PE蜡及PP蜡中的至少一种。
CN201310398689.3A 2013-09-04 2013-09-04 一种改善了硬度和耐寒性能的pc/asa组合物 Pending CN103483795A (zh)