CN105369616A - Base material used for waterproof coiled material and preparation method thereof - Google Patents
Base material used for waterproof coiled material and preparation method thereof Download PDFInfo
- Publication number
- CN105369616A CN105369616A CN201510822059.3A CN201510822059A CN105369616A CN 105369616 A CN105369616 A CN 105369616A CN 201510822059 A CN201510822059 A CN 201510822059A CN 105369616 A CN105369616 A CN 105369616A
- Authority
- CN
- China
- Prior art keywords
- fabrics
- parts
- base material
- fiber
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a base material used for a waterproof coiled material. The base material comprises the following components in parts by weight: 15 parts of absorbent cotton fiber, 2 parts of glass fiber, 10 parts of polyester fiber, and 0.2 parts of man-made spider fiber. A preparation method of the base material comprises the following steps: 1) taking absorbent cotton fiber and the man-made spider fiber as warp, taking glass fiber and polyester fiber as weft, performing weaving processing to obtain fabrics; 2) immersing the fabrics in warm water for 3-3.5 hours, taking the fabrics and draining, employing a spraying mode for sprinkling a strength enhancing agent on two surfaces of the fabrics, wherein each square meter of the fabrics is sprinkled with 15 ml, standing for 15-30 minutes and then sending the fabrics to drying equipment, pre-baking the fabrics for 4-6 minutes at temperature of 62-65 DEG C, then baking the fabrics for 3-5 minutes at temperature of 85-90 DEG C; and 3) sending the fabrics processed in the step 2) to refrigeration equipment, continuously refrigerating the fabrics for 3.5-4 hours at temperature of -20-23 DEG C, taking the fabrics out, sending the fabrics in the drying equipment, controlling the temperature at 55-58 DEG C for 10-20 minutes, taking the fabrics out, and cutting the fabrics to obtain the product as the base material.
Description
Technical field
The present invention relates to waterproof material processing technique field, be specifically related to a kind of waterproof roll base material and preparation method thereof.
Background technology
Be immersed on carcass by pitch class or high score subclass waterproof material, the waterproof material product be made into provides as coils, is called waterproof roll.Different according to main composition material, be divided into asphalt water-proof coiled material, polymer modified bituminous waterproof sheet material and synthetic polymeric waterproofing material; Be divided into without carcass coiled material, paper tire coiled material, glass fibre tire coiled material, glass cloth tire coiled material and polyethylene tire coiled material according to the difference of carcass.Be mainly used for the place such as construction wall, roofing and tunnel, highway, refuse landfill, play the flexible building material product of a kind of rollable one-tenth web-like resisting extraneous rainwater, underground water seepage, be connected as ne-leakage between engineering foundation with building, be the first barrier of whole engineering waterproofing, vital effect is played to whole engineering.Product mainly contains asphalt water-proof coiled material and polymer membranes.
Application number be 2007101208098 Chinese invention patent " a kind of low-temperature resistant self-adhesive rubber asphalt waterproofing coiled material " disclose a kind of by asphalt, subtract third fractional oil, waterproof roll that bitumen layer that thermoplastic styrene butadiene rubber, powder styrene butadiene rubber, coumarone indene resin, Petropols, terpene resin, small-molecular-weight polyisobutene, ultra-violet absorber, antioxidant, calcium carbonate are made makes.This waterproof roll also exists the shortcomings such as non-refractory.
Application number be 2009100663136 Chinese invention patent " a kind of preparation method of polymer membranes " disclose the polymer membranes be made up of pitch, rubber, carbon black and antiaging agent.The shortcomings such as this waterproof roll also also exists non-refractory, and antiseptic property is poor, and the scope of application is little.
Because present extreme weather is given prominence to, the performance of existing waterproof roll can not satisfy the demands, therefore the performance improving waterproof roll has become the technical problem needing solution badly.
Summary of the invention
Technical problem to be solved by this invention is to improve a kind of good toughness, corrosion resistant waterproof roll base material.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of waterproof roll base material, is made up of the component of following parts by weight: degreasing cotton fiber 15 parts, 2 parts, glass fibre, 10 parts, polyester fiber, imitative spider silk fiber 0.2 part;
Above-mentioned base material preparation method is as follows:
1) make warp with degreasing cotton fiber and imitative spider silk fiber, carry out weaving processing as parallel with glass fibre and polyester fiber, obtain fabric;
2) above-mentioned fabric is soaked 3-3.5 hour in warm water, taking-up drains the water, adopt the mode of spraying intensity reinforcing agent on the two sides of fabric is sprayed, every square metre is sprayed 15ml, leave standstill and send into drying plant after 15-30 minute, preliminary drying 4-6 minute at temperature 62-65 DEG C, then 3-5 minute is baked at temperature 85-90 DEG C;
3) will through step 2) fabric after process sends into freezing equipment, continuous freezing 3.5-4 hour under subzero 20-23 DEG C environment, takes out, send into drying plant, temperature controls at 55-58 DEG C, and the time is at 10-20 minute, take out cooling, cutting, is base material.
Above-mentioned intensity reinforcing agent is made up of the component of following weight: magnetized drinking water 1000kg, industry glycerol 1.5kg, electronic-grade silicon micro mist 2kg, water-soluble resin 10kg, softener 50kg, antistatic additive 5kg, antioxidant 3kg, fire retardant 2kg.
A waterproof roll containing above-mentioned base material, be melted by waterproof material, then dip-coating is on base material, described waterproof material is made up of the component of following parts by weight: pitch 80 parts, nano-ceramic powder 6 parts, nano oxidized boron 0.3 part, synthetic resin 2 parts, converted starch 0.8 part, fire retardant 1 part, 0.2 part, powder urea, linear polyethylene 2 parts, polyurethane 1.2 parts, dibutyl tin laurate 0.15 part, waste oil 1.2 parts, lithium acetate 0.05 part, stabilizing agent 0.5 part, oleamide 0.1 part, expanded graphite 0.8 part, potassium titanate crystal whisker 0.2 part, natural rubber powder 5 parts, fatty acid zinc 0.6 part, 0.5 part, zirconium English powder.
The invention has the beneficial effects as follows: the present invention adopts polyester fiber, imitative spider silk fiber coordinates with cotton fiber, solve the deficiency of simple cotton fibre material, improve the antiseptic power of base material, make base material have excellent low-temperature tenderness and heat resistance, under being applicable to various adverse circumstances.
Detailed description of the invention
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of waterproof roll base material, is made up of the component of following parts by weight: degreasing cotton fiber 15kg, glass fibre 2kg, polyester fiber 10kg, imitative spider silk fiber 0.2kg;
Above-mentioned base material preparation method is as follows:
1) make warp with degreasing cotton fiber and imitative spider silk fiber, carry out weaving processing as parallel with glass fibre and polyester fiber, obtain fabric;
2) above-mentioned fabric is soaked 3 hours in warm water, taking-up drains the water, and adopts the mode of spraying intensity reinforcing agent on the two sides of fabric is sprayed, every square metre is sprayed 15ml, leave standstill and send into drying plant after 20 minutes, preliminary drying 5 minutes at temperature 64 DEG C, then bake 3 minutes at temperature 90 DEG C;
3) will through step 2) fabric after process sends into freezing equipment, and under subzero 22 DEG C of environment freezing 3.5 hours continuously, take out, send into drying plant, temperature controlled at 56 DEG C, and the time, take out cooling, cutting, was base material at 15 minutes.
Above-mentioned intensity reinforcing agent is made up of the component of following weight: magnetized drinking water 1000kg, industry glycerol 1.5kg, electronic-grade silicon micro mist 2kg, water-soluble resin 10kg, softener 50kg, antistatic additive 5kg, antioxidant 3kg, fire retardant 2kg.
Embodiment 2
A kind of waterproof roll base material, is made up of the component of following parts by weight: degreasing cotton fiber 15 parts, 2 parts, glass fibre, 10 parts, polyester fiber, imitative spider silk fiber 0.2 part;
Above-mentioned base material preparation method is as follows:
1) make warp with degreasing cotton fiber and imitative spider silk fiber, carry out weaving processing as parallel with glass fibre and polyester fiber, obtain fabric;
2) above-mentioned fabric is soaked 3.5 hours in warm water, taking-up drains the water, and adopts the mode of spraying intensity reinforcing agent on the two sides of fabric is sprayed, every square metre is sprayed 15ml, leave standstill and send into drying plant after 30 minutes, preliminary drying 6 minutes at temperature 62 DEG C, then bake 5 minutes at temperature 85 DEG C;
3) will through step 2) fabric after process sends into freezing equipment, and under subzero 20 DEG C of environment freezing 3.5 hours continuously, take out, send into drying plant, temperature controlled at 55 DEG C, and the time, take out cooling, cutting, was base material at 20 minutes.
Above-mentioned intensity reinforcing agent is made up of the component of following weight: magnetized drinking water 1000kg, industry glycerol 1.5kg, electronic-grade silicon micro mist 2kg, water-soluble resin 10kg, softener 50kg, antistatic additive 5kg, antioxidant 3kg, fire retardant 2kg.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. a waterproof roll base material, is characterized in that, is made up of the component of following parts by weight: degreasing cotton fiber 15 parts, 2 parts, glass fibre, 10 parts, polyester fiber, imitative spider silk fiber 0.2 part;
Above-mentioned base material preparation method is as follows:
1) make warp with degreasing cotton fiber and imitative spider silk fiber, carry out weaving processing as parallel with glass fibre and polyester fiber, obtain fabric;
2) above-mentioned fabric is soaked 3-3.5 hour in warm water, taking-up drains the water, adopt the mode of spraying intensity enhancing finish on the two sides of fabric is sprayed, every square metre is sprayed 15ml, leave standstill and send into drying plant after 15-30 minute, preliminary drying 4-6 minute at temperature 62-65 DEG C, then 3-5 minute is baked at temperature 85-90 DEG C;
3) will through step 2) fabric after process sends into freezing equipment, continuous freezing 3.5-4 hour under subzero 20-23 DEG C environment, takes out, send into drying plant, temperature controls at 55-58 DEG C, and the time is at 10-20 minute, take out cooling, cutting, is base material.