CN105369085A - 一种流动性好的铸造合金 - Google Patents

一种流动性好的铸造合金 Download PDF

Info

Publication number
CN105369085A
CN105369085A CN201510928390.3A CN201510928390A CN105369085A CN 105369085 A CN105369085 A CN 105369085A CN 201510928390 A CN201510928390 A CN 201510928390A CN 105369085 A CN105369085 A CN 105369085A
Authority
CN
China
Prior art keywords
alloy
casting
magnesium
casting alloy
cast
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510928390.3A
Other languages
English (en)
Inventor
陈学忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CITY HONGQIAO STEEL Co Ltd
Original Assignee
CHANGSHU CITY HONGQIAO STEEL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CITY HONGQIAO STEEL Co Ltd filed Critical CHANGSHU CITY HONGQIAO STEEL Co Ltd
Priority to CN201510928390.3A priority Critical patent/CN105369085A/zh
Publication of CN105369085A publication Critical patent/CN105369085A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种流动性好的铸造合金，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝55%-60%、镁20%-25%、硅10%-15%、锰0.5%-2.5%、锌3%-5%、钛1%-4%、铍0.48%-1.98%、不可避免的杂质≤0.02%。通过上述方式，本发明具有良好的流动性，充填性能好，能提高铸件的表面及内在质量，提高铸件成品合格率。

Description

一种流动性好的铸造合金
技术领域
本发明涉及铸造合金领域，特别是涉及一种流动性好的铸造合金。
背景技术
铸造合金是适于熔融状态下充填铸型获得一定形状和尺寸铸件毛坯的合金，在有色金属合金中，铜合金、铝合金、镁合金、锌合金等都可用于铸造。有色金属铸件广泛使用于机器制造、航空、汽车、建筑等工业中。
在有色金属复杂零部件的铸造过程中，由于复杂零件壁厚差异大，在薄壁部分由于过快的冷却速度会降低熔融金属的流动性，导致不完全填充和气孔的产生，造成铸件表面出现裂纹，使得铸件成品率低。
发明内容
本发明主要解决的技术问题是：针对现有技术的不足，提供一种流动性好的铸造合金，具有良好的流动性，充填性能好，能提高铸件的表面及内在质量，提高铸件成品合格率。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种流动性好的铸造合金，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝55%-60%、镁20%-25%、硅10%-15%、锰0.5%-2.5%、锌3%-5%、钛1%-4%、铍0.48%-1.98%、不可避免的杂质≤0.02%。
在本发明一个较佳实施例中，所述铝镁铸造合金的熔炼温度为650-700℃。
在本发明一个较佳实施例中，所述铝镁铸造合金熔炼成铝镁合金溶液后还需进行超声波精炼除气处理。
本发明的有益效果是：本发明通过调整铝镁铸造合金各合金元素的配比，使其经高温熔炼后的铝镁合金溶液具有良好的流动性，充填性能好，能提高铸件的表面及内在质量，提高铸件成品合格率。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：
实施例一：
一种流动性好的铸造合金，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝55%、镁20%、硅15%、锰2.5%、锌4%、钛3%、铍0.48%、不可避免的杂质0.02%。
其中，所述铝镁铸造合金的熔炼温度为650℃。
所述铝镁铸造合金熔炼成铝镁合金溶液后还需进行超声波精炼除气处理，对铝镁合金溶液进行除气，可以细化其浇注而成的铸件组织晶粒，提高组件的内在质量。
实施例二：
一种流动性好的铸造合金，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝55%、镁22%、硅10%、锰2%、锌5%、钛4%、铍1.98%、不可避免的杂质0.02%。
其中，所述铝镁铸造合金的熔炼温度为680℃。
所述铝镁铸造合金熔炼成铝镁合金溶液后还需进行超声波精炼除气处理，对铝镁合金溶液进行除气，可以细化其浇注而成的铸件组织晶粒，提高组件的内在质量。
实施例三：
一种流动性好的铸造合金，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝60%、镁25%、硅10%、锰0.5%、锌3%、钛1%、铍0.48%、不可避免的杂质0.02%。
其中，所述铝镁铸造合金的熔炼温度为700℃。
所述铝镁铸造合金熔炼成铝镁合金溶液后还需进行超声波精炼除气处理，对铝镁合金溶液进行除气，可以细化其浇注而成的铸件组织晶粒，提高组件的内在质量。
本发明揭示了一种流动性好的铸造合金，通过调整铝镁铸造合金各合金元素的配比，使其经高温熔炼后的铝镁合金溶液具有良好的流动性，充填性能好，能提高铸件的表面及内在质量，提高铸件成品合格率。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种流动性好的铸造合金，其特征在于，所述铸造合金为铝镁铸造合金，所述铝镁铸造合金的合金元素包括：铝、镁、硅、锰、锌、钛、铍及其他不可避免的杂质，所述各合金元素所占的质量百分比为：铝55%-60%、镁20%-25%、硅10%-15%、锰0.5%-2.5%、锌3%-5%、钛1%-4%、铍0.48%-1.98%、不可避免的杂质≤0.02%。
2.根据权利要求1所述的流动性好的铸造合金，其特征在于，所述铝镁铸造合金的熔炼温度为650-700℃。
3.根据权利要求1所述的流动性好的铸造合金，其特征在于，所述铝镁铸造合金熔炼成铝镁合金溶液后还需进行超声波精炼除气处理。
CN201510928390.3A 2015-12-15 2015-12-15 一种流动性好的铸造合金 Pending CN105369085A (zh)