CN105368134A - Letterpress printing ink - Google Patents
Letterpress printing ink Download PDFInfo
- Publication number
- CN105368134A CN105368134A CN201510993956.0A CN201510993956A CN105368134A CN 105368134 A CN105368134 A CN 105368134A CN 201510993956 A CN201510993956 A CN 201510993956A CN 105368134 A CN105368134 A CN 105368134A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- maleic anhydride
- letterpress printing
- anhydride rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A letterpress printing ink is prepared from the following raw materials in parts by weight: 6-11 parts of a pigment, 15-24 parts of a bonding material, 6-14 parts of dibutyltin dilaurate, 7-9 parts of maleic anhydride rosin, 12-17 parts of maleic anhydride rosin, 3-8 parts of calcium stearate, 6-12 parts of azodiisobutyronitrile, 1.5-3 parts of diethyleneglycoldiethylether, 0.6-2.4 parts of an aminating agent, 6-11 parts of cobalt naphtenate, 4-9 parts of ethanol, 5-7 parts of methyl cellulose, 11-17 parts of pentaerythritol, 6-10 parts of titanium dioxide and 8-9 parts of acrylic resin. The letterpress printing ink has the following benefits of being environmentally friendly, good in wear resistance, high in glossiness, definite in printed image and long in service life.
Description
Technical field
The present invention relates to a kind of letterpress printing ink.
Background technology
One of a kind of technology that letterpress people grasp the earliest, it is characterized in that the part of relief printing is picture and text to be printed, ink contacts with the convex surface of forme, and direct being transferred to by picture and text is held on primer.Forme is the earliest made by timber or stone material, adopted font afterwards, and made letter press become the synonym of letterpress within a very long time.Letterpress ink refers to the general name of the various letterpress inks that various letterpress mode adopts.Be suitable for a class ink of letterpress, in order to a class ink of Printing books and periodicals, newspaper, picture album, document, account book etc.But containing a large amount of toxic and harmful substance in existing printing ink solvent, harmful, along with the development of society, people are more and more higher for the requirement of environmental protection.Therefore, existing letterpress printing ink awaits further improvement, meets the user demand of people.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of letterpress printing ink, environmental protection, and wear resistance is good simultaneously, and glossiness is high, and printed images is clear, and the life-span is long.
For solving prior art problem, technical scheme provided by the invention is, a kind of letterpress printing ink, and it is made up of the raw material of following parts by weight:
Pigment 6-11 part, binder 15-24 part, di-n-butyltin dilaurate 6-14 part, MALEIC ANHYDRIDE rosin 7-9 part, MALEIC ANHYDRIDE rosin 12-17 part, calcium stearate 3-8 part, Diisopropyl azodicarboxylate 6-12 part, diethylene glycol diethyl ether 1.5-3 part, aminating agent 0.6-2.4 part, naphthoic acid cobalt 6-11 part, ethanol 4-9 part, methylcellulose gum 5-7 part, tetramethylolmethane 11-17 part, titanium dioxide 6-10 part, acrylic resin 8-9 part.
Further, a kind of letterpress printing ink, it is made up of the raw material of following parts by weight:
Pigment 9 parts, binder 19 parts, di-n-butyltin dilaurate 10 parts, MALEIC ANHYDRIDE rosin 8 parts, MALEIC ANHYDRIDE rosin 14 parts, calcium stearate 5.5 parts, Diisopropyl azodicarboxylate 9 parts, diethylene glycol diethyl ether 2.1 parts, aminating agent 1.6 parts, naphthoic acid cobalt 9 parts, ethanol 6.5 parts, methylcellulose gum 6 parts, tetramethylolmethane 14 parts, titanium dioxide 8 parts, acrylic resin 8.5 parts.
The invention has the beneficial effects as follows: letterpress printing ink of the present invention, environmental protection, wear resistance is good simultaneously, and glossiness is high, and printed images is clear, and the life-span is long.
Embodiment
embodiment 1
A kind of letterpress printing ink, it is made up of the raw material of following parts by weight:
Pigment 6 parts, binder 15 parts, di-n-butyltin dilaurate 6 parts, MALEIC ANHYDRIDE rosin 7 parts, MALEIC ANHYDRIDE rosin 12 parts, calcium stearate 3 parts, Diisopropyl azodicarboxylate 6 parts, diethylene glycol diethyl ether 1.5 parts, aminating agent 0.6 part, naphthoic acid cobalt 6 parts, ethanol 4 parts, methylcellulose gum 5 parts, tetramethylolmethane 11 parts, titanium dioxide 6 parts, acrylic resin 8 parts.
embodiment 2
A kind of letterpress printing ink, it is made up of the raw material of following parts by weight:
Pigment 11 parts, binder 24 parts, di-n-butyltin dilaurate 14 parts, MALEIC ANHYDRIDE rosin 9 parts, MALEIC ANHYDRIDE rosin 17 parts, calcium stearate 8 parts, Diisopropyl azodicarboxylate 12 parts, diethylene glycol diethyl ether 3 parts, aminating agent 2.4 parts, naphthoic acid cobalt 11 parts, ethanol 9 parts, methylcellulose gum 7 parts, tetramethylolmethane 17 parts, titanium dioxide 10 parts, acrylic resin 9 parts.
embodiment 3
A kind of letterpress printing ink, it is made up of the raw material of following parts by weight:
Pigment 9 parts, binder 19 parts, di-n-butyltin dilaurate 10 parts, MALEIC ANHYDRIDE rosin 8 parts, MALEIC ANHYDRIDE rosin 14 parts, calcium stearate 5.5 parts, Diisopropyl azodicarboxylate 9 parts, diethylene glycol diethyl ether 2.1 parts, aminating agent 1.6 parts, naphthoic acid cobalt 9 parts, ethanol 6.5 parts, methylcellulose gum 6 parts, tetramethylolmethane 14 parts, titanium dioxide 8 parts, acrylic resin 8.5 parts.
Claims (2)
1. a letterpress printing ink, is characterized in that: it is made up of the raw material of following parts by weight:
Pigment 6-11 part, binder 15-24 part, di-n-butyltin dilaurate 6-14 part, MALEIC ANHYDRIDE rosin 7-9 part, MALEIC ANHYDRIDE rosin 12-17 part, calcium stearate 3-8 part, Diisopropyl azodicarboxylate 6-12 part, diethylene glycol diethyl ether 1.5-3 part, aminating agent 0.6-2.4 part, naphthoic acid cobalt 6-11 part, ethanol 4-9 part, methylcellulose gum 5-7 part, tetramethylolmethane 11-17 part, titanium dioxide 6-10 part, acrylic resin 8-9 part.
2. letterpress printing ink according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
Pigment 9 parts, binder 19 parts, di-n-butyltin dilaurate 10 parts, MALEIC ANHYDRIDE rosin 8 parts, MALEIC ANHYDRIDE rosin 14 parts, calcium stearate 5.5 parts, Diisopropyl azodicarboxylate 9 parts, diethylene glycol diethyl ether 2.1 parts, aminating agent 1.6 parts, naphthoic acid cobalt 9 parts, ethanol 6.5 parts, methylcellulose gum 6 parts, tetramethylolmethane 14 parts, titanium dioxide 8 parts, acrylic resin 8.5 parts.