CN103666019A - Alcohol-soluble letterpress ink - Google Patents
Alcohol-soluble letterpress ink Download PDFInfo
- Publication number
- CN103666019A CN103666019A CN201310669905.3A CN201310669905A CN103666019A CN 103666019 A CN103666019 A CN 103666019A CN 201310669905 A CN201310669905 A CN 201310669905A CN 103666019 A CN103666019 A CN 103666019A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- weight
- alcohol
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an alcohol-soluble letterpress ink which is prepared from the following raw materials in parts by weight: 15-25 parts of pigment, 35-40 parts of binder, 15-18 parts of barium sulfate, 20-30 parts of anhydrous ethanol, 1-2 parts of TX-9, 1-3 parts of tridecanol, 1-2 parts of di-n-butyltin dilaurate and 0.5-1 part of vaseline. The binder is prepared from the following raw materials in parts by weight: 25-28 parts of polyvinyl butyral resin, 7-13 parts of acrylic acid monomer, 3-7 parts of phenol aldehyde resin, 4-7 parts of tung oil, 40-45 parts of anhydrous ethanol, 5-7 parts of nitrocellulose solution and 0.5-1.5 parts of paraffin. The ink can be degrade in an alcohol solvent, has the advantages of environmental protection, no pollution, high adhesive force, favorable wear resistance and high glossiness, and is suitable for large-scale industrial production.
Description
Technical field
The present invention relates to printing-ink technical field, especially relate to a kind of ink formulations of environmental protection.
Background technology
Along with improving constantly that people require quality of life and living environment, people are more and more higher to the requirement of the product of energy-conservation, low consumption, nontoxic, pollution-free, easy degraded, and printing-ink is to pollute one of comparatively serious material.In solvent-borne type printing-ink, contain a large amount of toxic and harmful substances, comprise heavy metal, residual solvent, organic volatile, and polycyclic aromatic hydrocarbons etc.These hazardous and noxious substances can send chemistry and shift, and make people be infected with the objectionable impuritiess such as toluene, dimethylbenzene, lead, mercury, arsenic, chromium in life, work, study.The environment-friendly type ink that water color ink, alcohol-soluble printing ink, UV ink be representative of take is at present subject to printing the favor of manufacturers just day by day.Wherein alcohol-soluble printing ink has larger usage ratio in actual applications.Although but current environment-friendly type ink compare with traditional ink, environmental-protecting performance improves greatly, aspect the stability of base material sticking power and frictional coefficient, still can not reach promising result.
Summary of the invention
The problems referred to above that exist for prior art, the applicant provides a kind of ethanol-soluble type letterpress ink.This ink not only can be degraded in alcoholic solvent, environment friendly and pollution-free, and strong adhesion, and wear resistance is good, and glossiness is high, is applicable to large-scale industrial production.
Technical scheme of the present invention is as follows:
An ethanol-soluble type letterpress ink, is comprised of the raw material of following parts by weight: 15～25 parts of pigment, 35～40 parts of binders, 15～18 parts, barium sulfate, 20～30 parts of dehydrated alcohols, TX-91～2 part, 1～3 part of tridecanol, 1～2 part of di-n-butyltin dilaurate, 0.5～1 part, Vaseline; Described binder is comprised of the raw material of following parts by weight: 25～28 parts of polyvinyl butyral resins, 7～13 parts of Acrylic Acid Monomers, 3～7 parts, resol, 4～7 parts of tung oil, 40～45 parts of dehydrated alcohols, 5～7 parts of nitro-cotton liquid, 0.5～1.5 part, paraffin.
The technique effect that the present invention is useful is:
The present invention utilizes dehydrated alcohol as solvent, the alcohol-soluble printing ink safety and environmental protection of preparing, nontoxic, tinting strength and stable friction factor, good dispersity, mobility is good, it had both overcome the large shortcoming of toxicity of solvent type polyurethane resin, and the water volatilization that has overcome again waterborne polyurethane resin is slow, affects the shortcoming that production efficiency and energy consumption are large.
Embodiment
Embodiment 1:
The present invention has prepared a kind of ethanol-soluble type letterpress ink, consists of: 15 parts of red iron oxides, 35 parts of binders, 15 parts, barium sulfate, 20 parts of dehydrated alcohols, TX-91 part, 1 part of tridecanol, 1 part of di-n-butyltin dilaurate, 0.5 part, Vaseline the raw material of following parts by weight; Described binder is comprised of the raw material of following parts by weight: 25 parts of polyvinyl butyral resins, 7 parts of Acrylic Acid Monomers, 3 parts, resol, 4 parts of tung oil, 40 parts of dehydrated alcohols, 5 parts of nitro-cotton liquid, 0.5 part, paraffin.
Embodiment 2:
The present invention has prepared a kind of ethanol-soluble type letterpress ink, consists of: 20 parts of titanium whites, 38 parts of binders, 17 parts, barium sulfate, 25 parts of dehydrated alcohols, TX-92 part, 2 parts of tridecanols, 2 parts of di-n-butyltin dilaurates, 1 part, Vaseline the raw material of following parts by weight; Described binder is comprised of the raw material of following parts by weight: 27 parts of polyvinyl butyral resins, 10 parts of Acrylic Acid Monomers, 5 parts, resol, 6 parts of tung oil, 43 parts of dehydrated alcohols, 6 parts of nitro-cotton liquid, 1 part, paraffin.
Embodiment 3:
The present invention has prepared a kind of ethanol-soluble type letterpress ink, consists of: 25 parts of lead-chrome yellows, 40 parts of binders, 18 parts, barium sulfate, 30 parts of dehydrated alcohols, TX-92 part, 3 parts of tridecanols, 2 parts of di-n-butyltin dilaurates, 1 part, Vaseline the raw material of following parts by weight; Described binder is comprised of the raw material of following parts by weight: 28 parts of polyvinyl butyral resins, 13 parts of Acrylic Acid Monomers, 7 parts, resol, 7 parts of tung oil, 45 parts of dehydrated alcohols, 7 parts of nitro-cotton liquid, 1.5 parts, paraffin.
Claims (1)
1. an ethanol-soluble type letterpress ink, it is characterized in that being formed by the raw material of following parts by weight: 15～25 parts of pigment, 35～40 parts of binders, 15～18 parts, barium sulfate, 20～30 parts of dehydrated alcohols, TX-91～2 part, 1～3 part of tridecanol, 1～2 part of di-n-butyltin dilaurate, 0.5～1 part, Vaseline;
Described binder is comprised of the raw material of following parts by weight: 25～28 parts of polyvinyl butyral resins, 7～13 parts of Acrylic Acid Monomers, 3～7 parts, resol, 4～7 parts of tung oil, 40～45 parts of dehydrated alcohols, 5～7 parts of nitro-cotton liquid, 0.5～1.5 part, paraffin.