CN103642306A - Calcium carbonate nano ink - Google Patents

Calcium carbonate nano ink Download PDF

Info

Publication number
CN103642306A
CN103642306A CN201310674491.3A CN201310674491A CN103642306A CN 103642306 A CN103642306 A CN 103642306A CN 201310674491 A CN201310674491 A CN 201310674491A CN 103642306 A CN103642306 A CN 103642306A
Authority
CN
China
Prior art keywords
parts
ink
calcium carbonate
nano ink
carbonate nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310674491.3A
Other languages
Chinese (zh)
Inventor
陈明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YIHENG PRINTING Co Ltd
Original Assignee
SUZHOU YIHENG PRINTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU YIHENG PRINTING Co Ltd filed Critical SUZHOU YIHENG PRINTING Co Ltd
Priority to CN201310674491.3A priority Critical patent/CN103642306A/en
Publication of CN103642306A publication Critical patent/CN103642306A/en
Pending legal-status Critical Current

Abstract

The invention relates to a calcium carbonate nano ink which is prepared from the following raw materials in parts by weight: 37-45 parts of pigment, 13-26 parts of CaCO3 with the average particle size of 100nm, 10-20 parts of maleic anhydride rosin, 21-29 parts of epoxy resin, 7-10 parts of acrylic resin, 3-7 parts of isopropanol and 1-2 parts of calcium stearate. The ink has the advantages of favorable stability, low pigment consumption, high covering power, full color, clear printed image and long service life, and is suitable for industrial production.

Description

A kind of calcium carbonate nano ink
Technical field
The present invention relates to technical field of ink, especially relate to a kind of nano ink.
Background technology
The uniform mixture that common ink is comprised of materials such as pigment (comprising colored pigment and stopping composition), low-melting ink vehicle, mineral oil, auxiliary agents, can print and be printed on object dryly, has the pulpous state glue disjunctor of color and certain degree of mobilization.Nano ink is basic identical with the composition of common ink, and the difference of their maximums is just the size of granules of pigments.The pigment particle size of common ink is micron order, and the pigment particle size of nano ink is nano level, and both sizes differ approximately 1000 times, and the ink fineness of making is like this greatly improved.The fineness of ink and purity are very large on the impact of print quality.Granules of pigments is less, and ink fineness is higher, and it is clear and full strong that the site on printed matter also more seems.And the fineness of ink is better, its concentration is also larger, and tinting strength is also just stronger, and product printing quality is just high.
Recently, although nano ink is just shown up prominently, it,, in the decoration of the processing of electronic unit and installation, expensive goods and decoration, degerming aspect medical and the fields such as anti-counterfeit printing of detection and Special Products, has tentatively shown excellent performance and huge magnetism.In printing industry, the application of nanotechnology is mainly manifested in printing-ink, printing equipment device and packages printing field etc., however the research many places of nano ink at theory stage, can practical application also rare.
Summary of the invention
The problems referred to above that exist for prior art, the applicant provides a kind of calcium carbonate nano ink.This ink stability is good, and amount of pigment is few, and opacifying power is high, and color and luster is full, and printed images is clear, and long service life is applicable to suitability for industrialized production.
Technical scheme of the present invention is as follows:
A calcium carbonate nano ink, is comprised of the raw material of following parts by weight: 37~45 parts of pigment, the CaCO that median size is 100nm 313~26 parts, 10~20 parts of MALEIC ANHYDRIDE rosin, 21~29 parts of epoxy resin, 7~10 parts of acrylic resins, 3~7 parts of Virahols, 1~2 part of calcium stearate.
The technique effect that the present invention is useful is:
1 median size is the nanometer CaCO of 100nm 3not only can play brighten, dilatation, the effect that reduces costs, also have for ink strengthening action, and in the use of ink, there is good dispersiveness.
2, MALEIC ANHYDRIDE rosin, epoxy resin, acrylic resin, as binder, have played the effect of character complementation.
3, Virahol is made thinner, calcium stearate defoamer.
Embodiment
Embodiment 1:
The present invention has prepared a kind of calcium carbonate nano ink, consists of: 37 parts of titanium whites, the CaCO that median size is 100nm the raw material of following parts by weight 313 parts, 10 parts of MALEIC ANHYDRIDE rosin, 21 parts of epoxy resin, 7 parts of acrylic resins, 3 parts of Virahols, 1 part of calcium stearate.
Embodiment 2:
The present invention has prepared a kind of calcium carbonate nano ink, consists of: 40 parts, ultramarine, the CaCO that median size is 100nm the raw material of following parts by weight 319 parts, 15 parts of MALEIC ANHYDRIDE rosin, 26 parts of epoxy resin, 8 parts of acrylic resins, 5 parts of Virahols, 2 parts of calcium stearates.
Embodiment 3:
The present invention has prepared a kind of calcium carbonate nano ink, the raw material of following parts by weight, consists of: husky yellow 45 parts of the Chinese, the CaCO that median size is 100nm 326 parts, 20 parts of MALEIC ANHYDRIDE rosin, 29 parts of epoxy resin, 10 parts of acrylic resins, 7 parts of Virahols, 2 parts of calcium stearates.

Claims (1)

1. a calcium carbonate nano ink, is characterized in that being comprised of the raw material of following parts by weight: 37~45 parts of pigment, the CaCO that median size is 100nm 313~26 parts, 10~20 parts of MALEIC ANHYDRIDE rosin, 21~29 parts of epoxy resin, 7~10 parts of acrylic resins, 3~7 parts of Virahols, 1~2 part of calcium stearate.
CN201310674491.3A 2013-12-11 2013-12-11 Calcium carbonate nano ink Pending CN103642306A (en)