CN105350350A - Method for dyeing and painting silk on glass table plate - Google Patents
Method for dyeing and painting silk on glass table plate Download PDFInfo
- Publication number
- CN105350350A CN105350350A CN201510704526.2A CN201510704526A CN105350350A CN 105350350 A CN105350350 A CN 105350350A CN 201510704526 A CN201510704526 A CN 201510704526A CN 105350350 A CN105350350 A CN 105350350A
- Authority
- CN
- China
- Prior art keywords
- silk
- dye
- table plate
- glass table
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for dyeing and painting silk on a glass table plate. The method comprises the following steps: preparing silk fabrics, an acidic dye or a reactive dye; employing the acidic dye or the reactive dye for dyeing and painting on the silk fabrics, performing complex formulation by using a mixed preparation before usage of the reactive dye, wherein the dyeing and painting method is carried out by alternatively dyeing and painting; drying the dyed and painted silk with a liner plate at temperature being 50-60 DEG C for 20-25 minutes; steaming the dried silk at temperature of 90-100 DEG C for 15-30 minutes; washing the silk by hot water at temperature of 60-70 DEG C for 35-40 minutes; then washing the silk for 20-25 minutes by normal temperature water; curing the rinsed silk by clear water at temperature being 90-100 DEG C for 5-7 minutes; wherein running speed for curing is 3-4 m/min, and drying to obtain a finished product. In the dyeing and dye fixation technology, the prepared product has the advantages that a color fastness detection standard and an environmental protection index completely accord with a national standard.
Description
Technical field
The present invention relates to textiles printing technology field, more particularly, relate to a kind of silk glass table plate dye and paint technique.
Background technology
The silk printing dyeing method of prior art has craft or machine stamp, tie dyeing, batik, the Freehandhand-drawing of insulation rubber ACID DYES, active digit printing etc.Silk printrng and dyeing more stable, usually adopt ACID DYES and REACTIVE DYES, these two kinds of dyestuffs operationally require difference, and specific procedure regulation is also had any different.The color of existing silk printrng pattern, dyeing, due to the restriction by Processes and apparatus, is difficult to provide diversified, art up color, pattern meets individual requirements.
Summary of the invention
The technical problem to be solved in the present invention is, for the above-mentioned defect of prior art, provides a kind of silk glass table plate to contaminate and paints technique.
The technical solution adopted for the present invention to solve the technical problems is:
Construct a kind of silk glass table plate dye and paint technique, wherein, comprise the following steps:
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt ACID DYES or REACTIVE DYES to carry out dye to silk fabrics to paint, REACTIVE DYES needs before using to use built agent to carry out composite: the dye method of painting is that glass table plate dye is painted, namely first with water, dyestuff dissolved dilution is become liquid look water, or re-use thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate;
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 50-60 DEG C, time 20-25min;
(4) step is evaporated: evaporated by the silk after drying, temperature 90-100 DEG C; Time 15-30min;
(5) water-washing step: first use 60-70 DEG C of hot water, washing time 35-40min; Then 20-25min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 90-100 DEG C, time 5-7min; Bake speed of a motor vehicle 3-4m/min, finally fall machine finished product.
Silk glass table plate of the present invention dye paints technique, wherein, described built agent component and weight content ratio as follows: thickener Na-alginate 3%, unit is bright is powder 1%, urea 6%, sodium bicarbonate 2%, water 88%.
Silk glass table plate dye of the present invention paints technique, wherein, when ACID DYES or REACTIVE DYES use and allocate in described step (2), adds thickener and allocates.
Silk glass table plate dye of the present invention paints technique, and wherein, reactive thickening agent is selected from hydroxyethylcellulose, one or both combination in thickener Na-alginate.
Silk glass table plate dye of the present invention paints technique, and wherein, ACID DYES thickener is selected from thickener PS-14, W-8, one or more combinations in hydroxyethylcellulose.
Silk glass table plate dye of the present invention paints technique, and wherein, described step adds auxiliary agent in (2) in ACID DYES or REACTIVE DYES.
Silk glass table plate dye of the present invention paints technique, and wherein, ACID DYES auxiliary agent is selected from atoleine, waterproofing agent, bleeding agent, sodium formaldehyde sulfoxylate, edible salt, ethylene glycol, one or more combinations in adhesive.
Silk glass table plate dye of the present invention paints technique, and wherein, REACTIVE DYES auxiliary agent is selected from thickener Na-alginate, urea, sodium bicarbonate, glauber salt, dietary alkali, running water, one or more combinations in deionized water.
Beneficial effect of the present invention is: paint technique conventional acidity, REACTIVE DYES by silk glass table plate dye, various auxiliary agent and the new material being suitable for silk fabrics, in conjunction with the conventional painting skill in silk jacquard product, Printing design, and for the characteristic of silk fiber, dyes paints the particular color effect that dyestuff and silk produce.Silk glass table plate dye of the present invention paints product prepared by technique, color fixing process is painted in dye, COLOR FASTNESS examination criteria, environmental protection index meets national standard completely, and dye is wherein painted step and belonged to freely to contaminate completely and paint, contaminate material, the collocation of color, the form of pattern, silk fabric face ink, the control of watercolor charm, the program of front and back of painting and made by oneself by operator.
Detailed description of the invention
In order to make the object of the embodiment of the present invention, technical scheme and advantage clearly, clear, complete description is carried out below in conjunction with the technical scheme in the embodiment of the present invention, obviously, described embodiment is section Example of the present invention, instead of whole embodiment.Based on embodiments of the invention, the every other embodiment that those of ordinary skill in the art obtain under the prerequisite not paying creative work, all belongs to protection scope of the present invention.
The silk glass table plate dye of present pre-ferred embodiments is painted technique and is comprised the following steps:
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt ACID DYES or REACTIVE DYES to carry out dye to silk fabrics to paint, REACTIVE DYES needs before using to use built agent to carry out composite: the dye method of painting is that glass table plate dye is painted, namely first with water, dyestuff dissolved dilution is become liquid look water, or re-use thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate;
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 50-60 DEG C, time 20-25min;
(4) step is evaporated: evaporated by the silk after drying, temperature 90-100 DEG C; Time 15-30min;
(5) water-washing step: first use 60-70 DEG C of hot water, washing time 35-40min; Then 20-25min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 90-100 DEG C, time 5-7min; Bake speed of a motor vehicle 3-4m/min, finally fall machine finished product.
Above-mentioned ACID DYES, REACTIVE DYES are purchased from Fino, Wuxi Chemical Co., Ltd., and hydroxyethylcellulose, thickener Na-alginate, thickener PS-14, W-8 are common commercially available prod.ACID DYES can be selected; One or two or more kinds combination in red GRS, yellow GN, product blue 6B, black AMR, bright red F-3GL, pake purpke 4BL, gorgeous blue G, light green 3GM, orange GSN; REACTIVE DYES can to select in black C-NN, red C-2B, yellow C-4G, blue C-M, dark blue C-MR one or two or more kinds combination, silk fabrics be selected from plain crepe-back satin 14654,14101, a kind of in crepe de Chine 12102 or crepe de Chine 12033.
Above-mentioned silk glass table plate dye is painted in technique, preferably, described built agent component and weight content ratio as follows: thickener Na-alginate 3%, unit is bright is powder 1%, urea 6%, sodium bicarbonate 2%, water 88%.
Above-mentioned silk glass table plate dye is painted in technique, preferably, when ACID DYES or REACTIVE DYES use and allocate in described step (2), adds thickener and allocates.
Above-mentioned silk glass table plate dye is painted in technique, and preferably, reactive thickening agent is selected from hydroxyethylcellulose, one or both combination in thickener Na-alginate.
Above-mentioned silk glass table plate dye is painted in technique, and preferably, ACID DYES thickener is selected from thickener PS-14, W-8, one or more combinations in hydroxyethylcellulose.
Above-mentioned silk glass table plate dye is painted in technique, and preferably, step adds auxiliary agent in (2) in ACID DYES or REACTIVE DYES.
Above-mentioned silk glass table plate dye is painted in technique, and preferably, ACID DYES auxiliary agent is selected from atoleine, waterproofing agent, bleeding agent, sodium formaldehyde sulfoxylate, edible salt, ethylene glycol, one or more combinations in adhesive.
Above-mentioned silk glass table plate dye is painted in technique, and preferably, REACTIVE DYES auxiliary agent is selected from thickener Na-alginate, urea, sodium bicarbonate, glauber salt, dietary alkali, running water, one or more combinations in deionized water.
embodiment 1
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt ACID DYES to carry out dye to silk fabrics to paint: the dye method of painting is that glass table plate dye is painted, and namely first with water, dyestuff dissolved dilution is become liquid look water, or re-uses thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate; When ACID DYES uses and allocates, add thickener and allocate, ACID DYES thickener is hydroxyethylcellulose; Aid liquid paraffin is added in ACID DYES.
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 50 C, time 20min;
(4) step is evaporated: evaporated by the silk after drying, temperature 90 DEG C; Time 25min;
(5) water-washing step: first use 70 DEG C of hot water, washing time 35min; Then 20min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 90 DEG C, time 5min; Bake speed of a motor vehicle 3m/min, finally fall machine finished product.
embodiment 2
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt REACTIVE DYES to carry out dye to silk fabrics to paint, REACTIVE DYES needs before using to use built agent to carry out composite, built agent component and weight content ratio as follows: thickener Na-alginate 3%, unit is bright is powder 1%, urea 6%, sodium bicarbonate 2%, water 88%: the dye method of painting is that glass table plate dye is painted, namely first with water, dyestuff dissolved dilution is become liquid look water, or re-use thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate.
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 60 C, time 25min;
(4) step is evaporated: evaporated by the silk after drying, temperature 100 DEG C; Time 25min;
(5) water-washing step: first use 70 DEG C of hot water, washing time 35min; Then 25min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 100 DEG C, time 5min; Bake speed of a motor vehicle 4m/min, finally fall machine finished product.
embodiment 3
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt REACTIVE DYES to carry out dye to silk fabrics to paint, REACTIVE DYES needs before using to use built agent to carry out composite, built agent component and weight content ratio as follows: thickener Na-alginate 3%, unit is bright is powder 1%, urea 6%, sodium bicarbonate 2%, water 88%: the dye method of painting is that glass table plate dye is painted, namely first with water, dyestuff dissolved dilution is become liquid look water, or re-use thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate.
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 55 DEG C, time 20-25min;
(4) step is evaporated: evaporated by the silk after drying, temperature 95 DEG C; Time 25min;
(5) water-washing step: first use 65 DEG C of hot water, washing time 35min; Then 24min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 95 DEG C, time 5min; Bake speed of a motor vehicle 3.5m/min, finally fall machine finished product.
Should be understood that, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (8)
1. silk glass table plate dye paints a technique, it is characterized in that, comprises the following steps:
(1) silk fabrics is prepared, ACID DYES or REACTIVE DYES;
(2) adopt ACID DYES or REACTIVE DYES to carry out dye to silk fabrics to paint, REACTIVE DYES needs before using to use built agent to carry out composite: the dye method of painting is that glass table plate dye is painted, namely first with water, dyestuff dissolved dilution is become liquid look water, or re-use thickener thickening; Or directly use solid toner, need to contaminate on plate glass platen to paint according to picture, when dye is painted and met designing requirement, silk is laid in above the dyestuff contaminating the glass table plate painted, after silk fabric face is filled look, packs up and be placed on the strong paper of moisture absorption, then be placed on preparation oven dry on wooden liner plate;
(3) baking step: dry contaminating the silk painted together with liner plate, temperature 50-60 DEG C, time 20-25min;
(4) step is evaporated: evaporated by the silk after drying, temperature 90-100 DEG C; Time 15-30min;
(5) water-washing step: first use 60-70 DEG C of hot water, washing time 35-40min; Then 20-25min is washed by normal-temperature water;
(6) baking step: the silk that clear water rinsing is good bakes; Temperature 90-100 DEG C, time 5-7min; Bake speed of a motor vehicle 3-4m/min, finally fall machine finished product.
2. silk glass table plate according to claim 1 dye paints technique, it is characterized in that, described built agent component and weight content ratio as follows: thickener Na-alginate 3%, unit is bright is powder 1%, urea 6%, sodium bicarbonate 2%, water 88%.
3. silk glass table plate dye according to claim 1 paints technique, it is characterized in that, when ACID DYES or REACTIVE DYES use and allocate in described step (2), adds thickener and allocates.
4. silk glass table plate dye according to claim 3 paints technique, and it is characterized in that, reactive thickening agent is selected from hydroxyethylcellulose, one or both combination in thickener Na-alginate.
5. silk glass table plate dye according to claim 3 paints technique, and it is characterized in that, ACID DYES thickener is selected from thickener PS-14, W-8, one or more combinations in hydroxyethylcellulose.
6. silk glass table plate dye according to claim 1 paints technique, and it is characterized in that, described step adds auxiliary agent in (2) in ACID DYES or REACTIVE DYES.
7. silk glass table plate dye according to claim 6 paints technique, and it is characterized in that, ACID DYES auxiliary agent is selected from atoleine, waterproofing agent, bleeding agent, sodium formaldehyde sulfoxylate, edible salt, ethylene glycol, one or more combinations in adhesive.
8. silk glass table plate dye according to claim 6 paints technique, and it is characterized in that, REACTIVE DYES auxiliary agent is selected from thickener Na-alginate, urea, sodium bicarbonate, glauber salt, dietary alkali, running water, one or more combinations in deionized water.