CN105349052A - Preparation method of high-strength carton adhesive - Google Patents
Preparation method of high-strength carton adhesive Download PDFInfo
- Publication number
- CN105349052A CN105349052A CN201510726341.1A CN201510726341A CN105349052A CN 105349052 A CN105349052 A CN 105349052A CN 201510726341 A CN201510726341 A CN 201510726341A CN 105349052 A CN105349052 A CN 105349052A
- Authority
- CN
- China
- Prior art keywords
- parts
- carton
- adhesive
- water
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a high-strength carton adhesive. The high-strength carton adhesive is formed by the following components, by weight, 20-35 parts of dry starch, 0.01-0.03 parts of potassium permanganate, 0.03-0.05 parts of borax, 10-15 parts of sodium hydroxide, 1-3 parts of dicyandiamide, 1-3 parts of a stabilizer, 2-3 parts of calcium carbonate, 0.02-0.05 parts of a catalyst, 0.001-0.002 parts of a tackifier, 2-4 parts of bentonite, 6-8 parts of sodium silicate and 60-80 parts of water. The carton adhesive disclosed in the invention has more stable performances than carton adhesives in the prior art and has lower cost than traditional water glass, and the dosage reduces by 50-60%; and the high-strength carton adhesive has the advantages of good adhesion firmness, good moisture resistance, difficult fragile folding of finished products, no corrugated deflection, wire drawing or skinning, fast drying speed, extremely convenient packaging, storage and use, long storage life, low cost, simple production process, and suitableness for bonding various carton products.
Description
Technical field
The present invention relates to technical field of adhesive, specifically a kind of preparation method of high-intensity carton tackiness agent.
Background technology
Current domestic making carton, paper bag, the bonding of mulberry paper goods still generally uses sodium silicate or general amylan, the former used till today from the thirties, its alkalescence is large, after sticky paper because of the accumulation of salt in the surface soil moisture absorption, easy yellowing is come unstuck and stupefied, ultimate compression strength is little, the easy moldy metamorphism of in-built commodity or get rusty, include again alkali poison, food and daily life product adopt sodium silicate to seal sticky packaging, be detrimental to health, because of life-time service sodium silicate, hand is rotten poisoning aborning for workman, in use cost, sodium silicate is than great, easy precipitation, glue consumption is many, production cost is high, bonding intensity is poor, easily there is the deficiencies such as crisp folding in the carton of bonding, cause the carton of bonding of low quality.
Summary of the invention
The present invention aims to provide a kind of preparation method of high-intensity carton tackiness agent.
For realizing described object, the invention provides following technical scheme:
A kind of high-intensity carton adhesive preparation method, it is made up of the composition of following weight part: dry starch 20 ~ 35 parts, 0.01 ~ 0.03 part, potassium permanganate, borax 0.03 ~ 0.05 part, 10 ~ 15 parts, sodium hydroxide, Dyhard RU 100 1 ~ 3 part, stablizer 1 ~ 3 part, 2 ~ 3 parts, calcium carbonate, catalyzer 0.02 ~ 0.05 part, tackifier 0.001 ~ 0.002 part, wilkinite 2 ~ 4 parts, water glass 6 ~ 8 parts, 60 ~ 80 parts, water.
A preparation method for high-intensity carton tackiness agent, comprises the following steps:
(1) water of above-mentioned weight part is heated to 50 ~ 60 DEG C, adds weight part dry starch 10 ~ 20 parts, stir for subsequent use;
(2) above-mentioned weight part potassium permanganate and borax being dropped into temperature is stirring and dissolving in the boiling water of 80 ~ 100 DEG C;
(3) solution in described step (2) is mixed with the starch mixture in described step (1), be stirred to evenly, and be heated to 80 ~ 100 DEG C, slowly add sodium hydroxide, Dyhard RU 100, stablizer, calcium carbonate, catalyzer, the tackifier of above-mentioned weight part more successively, continuous uniform stirs 6 ~ 8min, cools, leaves standstill;
(4) mixture in described step (3) is heated to 90 ~ 110 DEG C, adds water glass, stir, then Temperature fall, get product.
The fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and is sieved.
After adding water glass in step (4), mixture is placed in water-bath and heats, control temperature, at 80 DEG C, reacts 10min, then at constant temperature underwater curing 1-3h, obtains adhesive for paper box.
Compared with prior art, the invention has the beneficial effects as follows: the product performance of adhesive for paper box of the present invention are stablized, and cost is lower than traditional sodium silicate, and consumption reduces 50-60%; Bonding firmness is good, and humidity resistance is good, and finished product are crisp folding not easily, this tackiness agent does not run stupefied, not wire drawing, not skinning, rate of drying is fast, packaging, storage, uses all extremely convenient, and storage period is long, and with low cost, production technique is simple, is suitable for the bonding of various box paper product.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Specific embodiment 1 one kinds of high-intensity carton adhesive preparation methods, it is made up of the composition of following weight part: dry starch 20 parts, 0.01 part, potassium permanganate, borax 0.03 part, 10 parts, sodium hydroxide, Dyhard RU 100 1 part, stablizer 1 part, 2 parts, calcium carbonate, catalyzer 0.02 part, tackifier 0.001 part, wilkinite 2 parts, water glass 6 parts, 60 parts, water.
A preparation method for high-intensity carton tackiness agent, comprises the following steps:
(1) water of above-mentioned weight part is heated to 50 ~ 60 DEG C, adds weight part dry starch 10 ~ 20 parts, stir for subsequent use;
(2) above-mentioned weight part potassium permanganate and borax being dropped into temperature is stirring and dissolving in the boiling water of 80 ~ 100 DEG C;
(3) solution in described step (2) is mixed with the starch mixture in described step (1), be stirred to evenly, and be heated to 80 ~ 100 DEG C, slowly add sodium hydroxide, Dyhard RU 100, stablizer, calcium carbonate, catalyzer, the tackifier of above-mentioned weight part more successively, continuous uniform stirs 6 ~ 8min, cools, leaves standstill;
(4) mixture in described step (3) is heated to 90 ~ 110 DEG C, adds water glass, stir, then Temperature fall, get product.
The fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and is sieved.
After adding water glass in step (4), mixture is placed in water-bath and heats, control temperature, at 80 DEG C, reacts 10min, then at constant temperature underwater curing 1-3h, obtains adhesive for paper box.
Specific embodiment 2 one kinds of high-intensity carton adhesive preparation methods, it is made up of the composition of following weight part: dry starch 35 parts, 0.03 part, potassium permanganate, borax 0.05 part, 15 parts, sodium hydroxide, Dyhard RU 100 3 parts, stablizer 3 parts, 3 parts, calcium carbonate, catalyzer 0.05 part, tackifier 0.002 part, wilkinite 4 parts, water glass 8 parts, 80 parts, water.
A preparation method for high-intensity carton tackiness agent, comprises the following steps:
(1) water of above-mentioned weight part is heated to 50 ~ 60 DEG C, adds weight part dry starch 10 ~ 20 parts, stir for subsequent use;
(2) above-mentioned weight part potassium permanganate and borax being dropped into temperature is stirring and dissolving in the boiling water of 80 ~ 100 DEG C;
(3) solution in described step (2) is mixed with the starch mixture in described step (1), be stirred to evenly, and be heated to 80 ~ 100 DEG C, slowly add sodium hydroxide, Dyhard RU 100, stablizer, calcium carbonate, catalyzer, the tackifier of above-mentioned weight part more successively, continuous uniform stirs 6 ~ 8min, cools, leaves standstill;
(4) mixture in described step (3) is heated to 90 ~ 110 DEG C, adds water glass, stir, then Temperature fall, get product.
The fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and is sieved.
After adding water glass in step (4), mixture is placed in water-bath and heats, control temperature, at 80 DEG C, reacts 10min, then at constant temperature underwater curing 1-3h, obtains adhesive for paper box.
Specific embodiment 3 one kinds of high-intensity carton adhesive preparation methods, it is made up of the composition of following weight part: dry starch 30 parts, 0.02 part, potassium permanganate, borax 0.04 part, 15 parts, sodium hydroxide, Dyhard RU 100 2 parts, stablizer 2 parts, 23 parts, calcium carbonate, catalyzer 0.04 part, tackifier 0.001 part, wilkinite 3 parts, water glass 7 parts, 80 parts, water.
A preparation method for high-intensity carton tackiness agent, comprises the following steps:
(1) water of above-mentioned weight part is heated to 50 ~ 60 DEG C, adds weight part dry starch 10 ~ 20 parts, stir for subsequent use;
(2) above-mentioned weight part potassium permanganate and borax being dropped into temperature is stirring and dissolving in the boiling water of 80 ~ 100 DEG C;
(3) solution in described step (2) is mixed with the starch mixture in described step (1), be stirred to evenly, and be heated to 80 ~ 100 DEG C, slowly add sodium hydroxide, Dyhard RU 100, stablizer, calcium carbonate, catalyzer, the tackifier of above-mentioned weight part more successively, continuous uniform stirs 6 ~ 8min, cools, leaves standstill;
(4) mixture in described step (3) is heated to 90 ~ 110 DEG C, adds water glass, stir, then Temperature fall, get product.
The fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and is sieved.
After adding water glass in step (4), mixture is placed in water-bath and heats, control temperature, at 80 DEG C, reacts 10min, then at constant temperature underwater curing 1-3h, obtains adhesive for paper box.
Claims (4)
1. a high-intensity carton adhesive preparation method, it is made up of the composition of following weight part: dry starch 20 ~ 35 parts, 0.01 ~ 0.03 part, potassium permanganate, borax 0.03 ~ 0.05 part, 10 ~ 15 parts, sodium hydroxide, Dyhard RU 100 1 ~ 3 part, stablizer 1 ~ 3 part, 2 ~ 3 parts, calcium carbonate, catalyzer 0.02 ~ 0.05 part, tackifier 0.001 ~ 0.002 part, wilkinite 2 ~ 4 parts, water glass 6 ~ 8 parts, 60 ~ 80 parts, water.
2. a preparation method for high-intensity carton tackiness agent, is characterized in that, comprises the following steps:
(1) water of above-mentioned weight part is heated to 50 ~ 60 DEG C, adds weight part dry starch 10 ~ 20 parts, stir for subsequent use;
(2) above-mentioned weight part potassium permanganate and borax being dropped into temperature is stirring and dissolving in the boiling water of 80 ~ 100 DEG C;
(3) solution in described step (2) is mixed with the starch mixture in described step (1), be stirred to evenly, and be heated to 80 ~ 100 DEG C, slowly add sodium hydroxide, Dyhard RU 100, stablizer, calcium carbonate, catalyzer, the tackifier of above-mentioned weight part more successively, continuous uniform stirs 6 ~ 8min, cools, leaves standstill;
(4) mixture in described step (3) is heated to 90 ~ 110 DEG C, adds water glass, stir, then Temperature fall, get product.
3. a kind of high-intensity carton tackiness agent according to claim 1, is characterized in that: the fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and sieved.
4. the preparation method of a kind of high-intensity carton tackiness agent according to claim 2, it is characterized in that: after adding water glass in step (4), mixture is placed in water-bath heat, control temperature is at 80 DEG C, reaction 10min, again at constant temperature underwater curing 1-3h, obtain adhesive for paper box.