CN105348607A - Antibacterial fishing net - Google Patents
Antibacterial fishing net Download PDFInfo
- Publication number
- CN105348607A CN105348607A CN201510731631.5A CN201510731631A CN105348607A CN 105348607 A CN105348607 A CN 105348607A CN 201510731631 A CN201510731631 A CN 201510731631A CN 105348607 A CN105348607 A CN 105348607A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- composite assistant
- minutes
- antibacterial
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial fishing net and relates to the technical field of fishing net making. The antibacterial fishing net comprises 120-135 parts by weight of polyethylene, 60-80 parts by weight of nylon, 8-9 parts by weight of fosetyl-aluminum, 3-5 parts by weight of polyisoprene, 4-5 parts by weight of quintozene and 11-12 parts by weight of a composite auxiliary agent. The antibacterial fishing net realizes fishing net antibiosis, has high strength and good wear resistance, is prepared from a special material, reduces bacterium viability on the net, prolongs a fishing net service life and saves a cost.
Description
Technical field
The present invention relates to fishing net manufacture technology field, particularly relate to a kind of antibacterial fishing net.
Background technology
Fishing net is used to fishing, and present fishing net mainly nylon material is made.When fishing, in river, ecotope is complicated, and fishing net is easily stained with bacterial micro-organism, uses for a long time, and fishing net easily rots to damage, and increases additional cost.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of fishing net that can be antibacterial.
For solving the problem, the antibacterial fishing net of one of the present invention, this fishing net is grouped into by the one-tenth of following weight part: polyethylene 120 ~ 135, nylon 60 ~ 80, phosethyl Al 8 ~ 9, poly-different diene 3 ~ 5, quintozene 4 ~ 5 and composite assistant 11 ~ 12.
Described composite assistant is grouped into by the one-tenth of following weight part: vinylbenzene 1.9 ~ 2.1, glycerine 1.6 ~ 1.9, Trisodium Citrate 1.4 ~ 1.5, dibutyl ester 1.7 ~ 1.9, methylethyl ketone peroxide 1.4 ~ 1.7 and potassium aluminium sulfate 2.4 ~ 2.7; The preparation method of described composite assistant is: join in the mixture of other compositions by potassium aluminium sulfate and glycerine, heat while stirring, stirs 40 ~ 55 minutes, and it is 135 DEG C ~ 155 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for antibacterial fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 120 ~ 135, nylon 60 ~ 80 are added in stirrer together with phosethyl Al 8 ~ 9 and stir, churning time is 23 ~ 29 minutes;
(2) mixture stirred is put into reactor, add poly-different diene 3 ~ 5 and quintozene 4 ~ 5, it is 92 DEG C ~ 113 DEG C that temperature controls, and the reaction times is 35 ~ 65 minutes;
(3) in reacted mixture, add composite assistant 11 ~ 12, stir, churning time is 15 ~ 25 minutes, is then heated to molten state, and heating and temperature control is 110 DEG C ~ 130 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described antibacterial fishing net.
Compared with prior art, the present invention has the following advantages: the invention solves the problem that fishing net is antibacterial, and provide the fishing net that intensity is high, wear resistance is good, fishing net utilizes exotic materials to make, and bacterium is stained with and not easily survives, and increases fishing net work-ing life, cost-saving.
Embodiment
Embodiment 1
A kind of fishing net that strengthens is grouped into by the one-tenth of following weight part: polyethylene 120, nylon 60, phosethyl Al 8, poly-different diene 3, quintozene 4 and composite assistant 11.
Composite assistant is grouped into by the one-tenth of following weight part: vinylbenzene 1.9, glycerine 1.6, Trisodium Citrate 1.4, dibutyl ester 1.7, methylethyl ketone peroxide 1.4 and potassium aluminium sulfate 2.4; The preparation method of composite assistant is: join in the mixture of other compositions by potassium aluminium sulfate and glycerine, heat while stirring, stirs 40 minutes, and it is 135 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for antibacterial fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 120, nylon 60 are added in stirrer together with phosethyl Al 8 and stir, churning time is 23 minutes;
(2) mixture stirred is put into reactor, add poly-different diene 3 and quintozene 4, it is 92 DEG C that temperature controls, and the reaction times is 35 minutes;
(3) in reacted mixture, add composite assistant 11, stir, churning time is 15 minutes, is then heated to molten state, and heating and temperature control is 110 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described antibacterial fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 36.5%
Anti-tensile degree (KG): 56.3
Knotting strength (KG): 46.2
Compared with common fishing net, on this fishing net, bacterial number reduces 70%.
Embodiment 2
A kind of fishing net that strengthens is grouped into by the one-tenth of following weight part: polyethylene 128, nylon 70, phosethyl Al 8, poly-different diene 4, quintozene 4 and composite assistant 12.
Composite assistant is grouped into by the one-tenth of following weight part: vinylbenzene 2.0, glycerine 1.7, Trisodium Citrate 1.4, dibutyl ester 1.8, methylethyl ketone peroxide 1.5 and potassium aluminium sulfate 2.6; The preparation method of composite assistant is: join in the mixture of other compositions by potassium aluminium sulfate and glycerine, heat while stirring, stirs 49 minutes, and it is 140 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for antibacterial fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 128, nylon 70 are added in stirrer together with phosethyl Al 8 and stir, churning time is 27 minutes;
(2) mixture stirred is put into reactor, add poly-different diene 4 and quintozene 4, it is 99 DEG C that temperature controls, and the reaction times is 50 minutes;
(3) in reacted mixture, add composite assistant 12, stir, churning time is 20 minutes, is then heated to molten state, and heating and temperature control is 120 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described antibacterial fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 41.3%
Anti-tensile degree (KG): 66.8
Knotting strength (KG): 57.6
Compared with common fishing net, on this fishing net, bacterial number reduces 87%.
Experimental data shows, and this fishing net germ resistance is best, meets actual user demand.
Embodiment 3
A kind of fishing net that strengthens is grouped into by the one-tenth of following weight part: polyethylene 135, nylon 80, phosethyl Al 9, poly-different diene 5, quintozene 5 and composite assistant 12.
Composite assistant is grouped into by the one-tenth of following weight part: vinylbenzene 2.1, glycerine 1.9, Trisodium Citrate 1.5, dibutyl ester 1.9, methylethyl ketone peroxide 1.7 and potassium aluminium sulfate 2.7; The preparation method of composite assistant is: join in the mixture of other compositions by potassium aluminium sulfate and glycerine, heat while stirring, stirs 55 minutes, and it is 155 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for antibacterial fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 135, nylon 80 are added in stirrer together with phosethyl Al 9 and stir, churning time is 29 minutes;
(2) mixture stirred is put into reactor, add poly-different diene 5 and quintozene 5, it is 113 DEG C that temperature controls, and the reaction times is 65 minutes;
(3) in reacted mixture, add composite assistant 12, stir, churning time is 25 minutes, is then heated to molten state, and heating and temperature control is 130 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described antibacterial fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 34.1%
Anti-tensile degree (KG): 60.3
Knotting strength (KG): 51.4
Compared with common fishing net, on this fishing net, bacterial number reduces 77%.
Claims (3)
1. an antibacterial fishing net, is characterized in that: this fishing net is grouped into by the one-tenth of following weight part: polyethylene 120 ~ 135, nylon 60 ~ 80, phosethyl Al 8 ~ 9, poly-different diene 3 ~ 5, quintozene 4 ~ 5 and composite assistant 11 ~ 12.
2. a kind of antibacterial fishing net according to claim 1, is characterized in that: described composite assistant is grouped into by the one-tenth of following weight part: vinylbenzene 1.9 ~ 2.1, glycerine 1.6 ~ 1.9, Trisodium Citrate 1.4 ~ 1.5, dibutyl ester 1.7 ~ 1.9, methylethyl ketone peroxide 1.4 ~ 1.7 and potassium aluminium sulfate 2.4 ~ 2.7; The preparation method of described composite assistant is: join in the mixture of other compositions by potassium aluminium sulfate and glycerine, heat while stirring, stirs 40 ~ 55 minutes, and it is 135 DEG C ~ 155 DEG C that temperature controls, and can obtain described composite assistant.
3. a preparation method for antibacterial fishing net as claimed in claim 1, is characterized in that: comprise following preparation process:
(1) above-mentioned polyethylene 120 ~ 135, nylon 60 ~ 80 are added in stirrer together with phosethyl Al 8 ~ 9 and stir, churning time is 23 ~ 29 minutes;
(2) mixture stirred is put into reactor, add poly-different diene 3 ~ 5 and quintozene 4 ~ 5, it is 92 DEG C ~ 113 DEG C that temperature controls, and the reaction times is 35 ~ 65 minutes;
(3) in reacted mixture, add composite assistant 11 ~ 12, stir, churning time is 15 ~ 25 minutes, is then heated to molten state, and heating and temperature control is 110 DEG C ~ 130 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described antibacterial fishing net.