CN108219227A - A kind of high load type transmission belt primer and its preparation method and application - Google Patents
A kind of high load type transmission belt primer and its preparation method and application Download PDFInfo
- Publication number
- CN108219227A CN108219227A CN201810101514.4A CN201810101514A CN108219227A CN 108219227 A CN108219227 A CN 108219227A CN 201810101514 A CN201810101514 A CN 201810101514A CN 108219227 A CN108219227 A CN 108219227A
- Authority
- CN
- China
- Prior art keywords
- primer
- parts
- agent
- mixing
- high load
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high load type transmission belt primers,In parts by weight,The primer includes 90~110 parts of neoprene,1~2 part of vinal,8~15 parts of reinforcing fiber,6~8 parts of coupling agent,50~90 parts of filler,20~30 parts of metal oxide,Primer of the present invention deflected under the use condition of low load and high load number >=10000 times,Every mechanical property change rate is between 0~5%,Amplitude of variation is little,Ageing-resistant performance is excellent,High load type transmission belt is suitable as to be used with primer,The present invention in primer by introducing the materials such as vinal,Make it have synergistic effect,So that the primer has high tensile,Suitable elongation at break and tearing strength,Stronger impact force can be also carried under the use condition of high load,The invention also provides a kind of new conveyer belt primer processing technologys,This is simple for process,Environmental protection,Controllability is stronger,Stablized by primer product quality prepared by the technique.
Description
Technical field
Field of rubber materials of the present invention more particularly to a kind of high load type transmission belt primer and preparation method thereof and use
On the way.
Background technology
Rubber is a kind of important industrial materials, is had in production and living important and irreplaceable role, rubber are pressed
Natural rubber and synthetic rubber can be divided into according to source, the toughness and fatigue durability of natural rubber are preferable, but other performances are such as
Intensity, heat resistance, oil resistance etc. are poor compared with synthetic rubber, therefore the functional rubber components used now is mostly using conjunction
Into rubber material, such as nitrile rubber, neoprene, butyl rubber, EP rubbers.
Neoprene has good caking property, is a kind of important rubber material for Transmission belt base rubber, in addition, chlorine
Buna has good mechanical property and the performances such as excellent oil resistant, heat-resisting, resistant to chemical etching, however, neoprene
High load performance especially deflects poor-performing, as Transmission belt base rubber in use, being difficult under high stress and strain
Maintain its mechanical property constant under the use environment of high load, so, the prior art mainly adopts add auxiliary agent thereto, fill out
The additives such as material or reinforcing fiber are to enhance its performance under high load use environment, for example, leading in CN107057145A
It crosses and Fypro and viscose fiber is added into the mixed rubber based on neoprene to enhance the high load of rubber material
Performance, fiber therein bear main stress load so that and the high load performance of rubber material increases,
Phenolic resin and the carbon fiber line of rubber constituent are attached with by adding in surface into rubber in CN104956000A, is utilized
The high intensity of carbon fiber line, obtained up to ten thousand stretching experiments for carrying load of rubber material experience, mechanical property conservation rate
More than 80% can be reached, however, using above-mentioned material as Transmission belt base rubber, the resistance to ag(e)ing in the use environment of high load
Can and it deflect that number is still relatively low, and hydraulic performance decline is still more serious after long-time use.
Those skilled in the art is needed on the basis of existing technology by improving the formula of rubber and additive, into one
Step improves the high load performance of rubber material, especially chloroprene rubber material, makes that it is suitable for as high load conveyer belt
Primer uses, moreover, additive therefor, into should be relatively low, processing technology should be as easy as possible.
Invention content
One of the objects of the present invention is to provide a kind of high load type transmission belt primers, in parts by weight, the primer
Including following components:
Wherein, the parts by weight of neoprene can be 91 parts, 95 parts, 97 parts, 101 parts, 105 parts, 109 parts etc., poly- second
The parts by weight of enol fiber can be 1.1 parts, 1.5 parts, 1.7 parts, 1.9 parts etc., and the parts by weight of reinforcing fiber can be 9
Part, 11 parts, 13 parts, 14 parts etc., the parts by weight of coupling agent can be 6.3 parts, 6.8 parts, 7.5 parts, 7.9 parts etc., the weight of filler
It can be 52 parts, 58 parts, 67 parts, 76 parts, 88 parts etc. to measure number, the parts by weight of metal oxide can be 21 parts, 23 parts, 25
Part, 27 parts, 29 parts etc..
The high load type transmission belt refers to according to standard GB/T/T 12735-91《Agricultural machinery V band fatigue tests
Method》, in load testing load type for more than HL types, driven wheel loads more than 23kW, the test condition with total tension >=2000N
Under, carry out such as standard GB/T/T 15328-2009《Classical V-belt fatigue test method》Described in fatigue life test, obtain
To the transmission belt for deflecting number >=10000 time, it is corresponding, low-load type transmission belt be load type be HK types and hereinafter, from
Driving wheel is supported on 18kW hereinafter, deflecting the transmission belt of number >=10000 time.
Transmission belt used in heavy mechanical equipment needs to meet the requirement that can be run under high load, this hair
It is bright by introducing vinal, reinforcing fiber etc. in the component of traditional neoprene Transmission belt base rubber, disclosure satisfy that height
The requirement of support type transmission belt, service life are greatly increased relative to traditional transmission band primer.
There is synergistic effect, polyvinyl alcohol between the components such as vinal, the reinforcing fiber added in the present invention
Fiber and reinforcing fiber play the role of enhancing rubber toughness, and especially under the use condition of high load, reinforcing fiber exists
It is crystallized under high stress, mechanical strength can be improved, but also weaken the binding force with noncrystalline phase rubber, poly- second accordingly simultaneously
The introducing of enol fiber is not only able to the mechanical strength of enhancing rubber, additionally it is possible to improve the effect between crystal region and non-crystalline areas
Power achievees the purpose that toughening, increase elongation at break, the generation for reducing the defects of crackle, reduces ageing of rubber speed, coupling agent
Introducing with filler so that the generation of more perfect rubber network structure, crackle or stress concentration point is less, metal oxide
Introducing being capable of effectively heat radiation level, the heat speed of reduction rubber material under high load, while also serve as a kind of filler
For enhancing the mechanical property of rubber.
Preferably, the length of the vinal be 2.5~3.5mm, such as 2.6mm, 2.8mm, 3.0mm,
3.2mm, 3.4mm etc., preferably 2.8~3.2mm, the fiber being of convenient length can preferably with rubber matrix and reinforcing fiber knot
It closing, is conducive to the promotion of mechanical property, long fiber is easily distributed in a jumble inside rubber, and too short fiber is not easy to crystallize,
It is unfavorable for the promotion of rubber material performance under high load.
Preferably, elasticity modulus >=35GPa of the vinal, for example, 36GPa, 38GPa, 40GPa,
44GPa, 48GPa, 52GPa, 56GPa etc., further preferably 38~45GPa.
Preferably, MM-1 type polyethylene of the vinal for the good Chemical Industry Science Co., Ltd's production of Shanghai fond dream
Alcohol fiber.
Preferably, the elasticity modulus of the reinforcing fiber be 100~200GPa, for example, 105GPa, 110GPa,
130GPa, 150GPa, 170GPa, 190GPa, 195GPa etc..
Preferably, the length of the reinforcing fiber is 1~6mm, for example, 2mm, 3mm, 4mm, mm, 5.5mm etc..
Preferably, the reinforcing fiber is any one in nylon fiber, aramid fiber, Kafra fiber, carbon fiber
Or at least two mixture.
Preferably, the coupling agent is any one in silane coupling agent, the further preferably limited public affairs of Huangyan, Zhejiang
Take charge of the SI69 type coupling agents of production.
Preferably, the grain size of the filler be 1~60mm, for example, 2mm, 10mm, 20mm, 30mm, 40mm, 50mm,
55mm etc..
Preferably, mixing of the filler including any one in white carbon, carbon black, modified calcium carbonate or at least two
Object.
Preferably, it is (3~4) that the filler, which includes weight ratio,:5:6 white carbon, carbon black and modified calcium carbonate, above-mentioned ratio
The filler of example is for neoprene performance boost maximum.
Preferably, the EDS type easily disperse silica that the white carbon is really produced for Wuxi into chemistry of silicones company.
Preferably, the carbon black is the N330 type carbon blacks of Cabot Co., Ltd of U.S. production.
Preferably, the modified calcium carbonate is the superthin light activated Calcium carbonate of Huzhou Jin Yuan chemical companies production.
Preferably, the grain size of the metal oxide be 1~60mm, for example, 2mm, 10mm, 20mm, 30mm, 40mm,
50mm, 55mm etc..
Preferably, the metal oxide is any one in the metal oxide that metallic element therein is positive divalent
Or at least two mixture, further preferably magnesia and/or zinc oxide.
Preferably, it is 1 that the metal oxide, which is weight ratio,:The magnesia and zinc oxide of (3~5).
Preferably, further included in the component of the primer 10~30 parts by weight (such as 11 parts, 12 parts, 14 parts, 18 parts, 24
Part, 26 parts, 28 parts etc.) addition auxiliary agent.
Those skilled in the art can select any one or more addition for being suitable for neoprene to help according to demand
Agent, it is preferable that the addition auxiliary agent include antioxidant, accelerating agent, anti-aging agent, in softening agent any one or at least two
Mixture.
Preferably, it is 1 that the addition auxiliary agent, which includes weight ratio,:(1~2):(2~3):3 antioxidant, is prevented always accelerating agent
Agent and softening agent.
Preferably, the antioxidant is 264 type antioxidant of Huangyan, Zhejiang Co., Ltd production.
Preferably, the accelerating agent is the DM type accelerating agents of Suqian Hua Xing chemical companies production.
Preferably, the anti-aging agent is the ODA type anti-aging agents of the Huangyan East Sea, Taizhou chemical company production.
Preferably, the softening agent is the DOP type softening agents of Ningbo Han Sheng companies production.
Preferably, further included in the component of the primer 3~5 parts by weight (such as 3.2 parts, 3.6 parts, 4 parts, 4.4 parts, 4.8
Part etc.) anti-tear crack resin.
Preferably, the anti-tear crack resin is the E5051 types of Qingdao Zi Guan trading companies supply, Shanghai Mao Tong industrial corporations
Any one in the TYC0500 types of supply, the anti-tear crack resin of 260 types of Jinan Tai Wang Chemical Co., Ltd.s supply or at least two
The mixture of kind.
The second object of the present invention is to provide a kind of preparation method of the primer, and the preparation method includes following step
Suddenly:
Step (1), by the neoprene of formula ratio 1/3rd, the vinal of formula ratio whole, reinforcing fiber
Mixer is added in optional tear-proof resin Composition, mixing, bottom sheet obtain mixing rubber master batch;
The metal oxide of formula ratio with other components is uniformly mixed, mixture A is obtained, by formula ratio by step (2)
Coupling agent is uniformly mixed with other components, obtains mixture B;
Step (3), by filling out for the neoprene of remaining formula ratio, whole mixing rubber master batch and mixture B and formula ratio
Material adds in mixer, carries out a mixing, treats all components after mixing, adds in whole mixture A thereto and carries out two
Secondary mixing, after secondary mixing, product dumping enters open mill, in open mill by slightly refining, bottom sheet, obtain institute after cooling
State primer;
Other components include optional any one or at least two addition auxiliary agents.
Preferably, the mixing time described in step (1) is 40~60s, for example, 42s, 45s, 48s, 52s, 55s, 58s
It it is 100~300 DEG C, for example, 120 DEG C, 150 DEG C, 180 DEG C, 220 DEG C, 240 DEG C, 270 DEG C, 290 DEG C etc. Deng, temperature.
Preferably, the time of a mixing described in step (3) be 30~50s, for example, 32s, 35s, 38s, 42s,
45s, 48s etc., temperature are 100~300 DEG C, for example, 120 DEG C, 150 DEG C, 180 DEG C, 220 DEG C, 240 DEG C, 270 DEG C, 290 DEG C etc..
Preferably, the time of the secondary mixing described in step (3) be 40~60s, for example, 42s, 45s, 48s, 52s,
55s, 58s etc., temperature are 100~300 DEG C, for example, 120 DEG C, 150 DEG C, 180 DEG C, 220 DEG C, 240 DEG C, 270 DEG C, 290 DEG C etc..
Preferably, the time slightly refined described in step (3) be 40~80s, temperature be 100~200 DEG C, for example, 120
DEG C, 140 DEG C, 160 DEG C, 180 DEG C, 190 DEG C etc..
Preferably, linear cooling down is cooled to described in step (3), cooldown rate is 1~10 DEG C/min, for example,
2℃/min、4℃/min、6℃/min、8℃/min、9℃/min。
The third object of the present invention is to provide a kind of purposes of the high load type transmission belt primer, the primer
It is non-aging under the use condition of high load, it deflects number not but not declines, increased instead, mechanical property change rate
It is equally smaller, only 0~5% or so, it is suitable as the use of trimming tooth type Transmission belt base rubber.
Compared with prior art, the invention has the advantages that:
(1) heretofore described primer deflected under the use condition of low load and high load number >=10000 times,
Do not decline not only, increased instead, for every mechanical property change rate between 0~5%, amplitude of variation is little, illustrates this
It is excellent with primer ageing-resistant performance to invent the conveyer belt being prepared, is suitable as high load type transmission belt and is used with primer.
(2) reinforcing fiber and rubber are enhanced by introducing vinal innovative in being formulated in primer in the present invention
Binding force so that the reinforcing fiber in rubber is fully dispersed, and the introducing of coupling agent and filler causes rubber network structure more
The generation for adding kind, crackle or stress concentration point is less, the introducing of metal oxide can effectively heat radiation it is horizontal, reduce rubber
The heat speed of glue material under high load, the synergistic effect of said components cause primer prepared by the present invention to have high stretch by force
Degree, suitable elongation at break and tearing strength so that the primer of preparation can also be carried under the use condition of high load compared with
Strong impact force.
(3) the invention also provides a kind of new conveyer belt primer processing technology, this is simple for process, environmentally friendly, controllability
It is relatively strong, stablized by primer product quality prepared by the technique.
Specific embodiment
The technical solution further illustrated the present invention below by specific embodiment.
Those skilled in the art it will be clearly understood that the embodiment be only to aid in understand the present invention, be not construed as to this hair
Bright concrete restriction.
Embodiment 1
Primer 1 is made by the steps:
Step (1), the length by the neoprene of 30kg, the good Chemical Industry Science Co., Ltd's production of 2kg Shanghai fond dream is 3mm
Elasticity modulus be 38GPa MM-1 types vinal, length be 6mm elasticity modulus be 105GPa 10kg nylon66 fibers
Fiber and the anti-tear crack resin addition mixer of 5kg aramid fibers, the E5051 types of 5kg Qingdao Zi Guan trading companies supply, 100 DEG C
Lower mixing 60s, bottom sheet, obtain mixing rubber master batch;
Step (2) produces 5kg magnesia and 25kg zinc oxide that grain size is 40mm with 3kg Huangyan, Zhejiangs Co., Ltd
264 type antioxidant and 9kg Ningbo Han Sheng companies production DOP type softening agents be uniformly mixed, mixture A is obtained, by 8kg Zhejiang
The DM types accelerating agent and 6kg Taizhou that the SI69 types coupling agent of Huangyan Co., Ltd production is produced with 6kg Suqians Hua Xing chemical companies
The ODA type anti-aging agents of Huangyan East Sea chemical company production are uniformly mixed, and obtain mixture B;
The neoprene of remaining 60kg, whole mixing rubber master batch and mixture B and 90kg weight ratio be by step (3)
3:5:The 6 Wuxi N330 that really the EDS type easily disperses silica into the production of chemistry of silicones company, Cabot Co., Ltd of the U.S. produce
Type carbon black and the superthin light activated Calcium carbonate of Jin Yuan chemical companies production add in mixer as filler, are carried out at 120 DEG C
Mixing, mixing time 30s treat all components after mixing, whole mixture A are added in thereto, at 100 DEG C
Carry out secondary mixing, after secondary mixing 40s, product dumping enters open mill, carried out at 120 DEG C in open mill thick refining 40s,
Bottom sheet after being cooled down with the cooling velocity of 10 DEG C/min, obtains the primer 1.
Embodiment 2
Primer 2 is made by the steps:
With differing only in for embodiment 1, the addition of polyvinyl alcohol is 1kg in step (1).
Embodiment 2 obtains primer 2.
Embodiment 3
Primer 3 is made by the steps:
With differing only in for embodiment 1, the addition of nylon fiber is 8kg in step (1), the addition of aramid fiber
For 1kg.
Embodiment 3 obtains primer 3.
Embodiment 4
Primer 4 is made by the steps:
With differing only in for embodiment 1, the addition of coupling agent is 6kg in step (2), in step (3) filler plus
Enter amount for 50kg.
Embodiment 4 obtains primer 4.
Embodiment 5
Primer 5 is made by the steps:
With differing only in for embodiment 1, the addition of zinc oxide is 15kg in step (2), magnesia and zinc oxide
Grain size is 1mm.
Embodiment 5 obtains primer 5.
Embodiment 6
Primer 6 is made by the steps:
With differing only in for embodiment 1, it is 1 that the middle filler added in of step (3), which is only mass ratio,:1 carbon black and ultra-fine
Light active calcium carbonate.
Embodiment 6 obtains primer 6.
Embodiment 7
Primer 7 is made by the steps:
With differing only in for embodiment 1, the addition of tear-proof resin is 3kg in step (1).
Embodiment 7 obtains primer 7.
Embodiment 8
Primer 8 is made by the steps:
With differing only in for embodiment 1, the middle filler added in of step (3) is only superthin light activated Calcium carbonate, accordingly
A mixing, secondary mixing and time for slightly refining be respectively 50s, 60s and 80s, cooldown rate is 1 DEG C/min.
Embodiment 8 obtains primer 8.
Reference examples 1
Primer 9 is made by the steps:
With differing only in for embodiment 1, step is added without vinal in (1).
Reference examples 9 obtain primer 9.
Reference examples 2
Primer 10 is made by the steps:
With differing only in for embodiment 1, step is added without coupling agent in (2).
Reference examples 10 obtain primer 10.
Reference examples 3
Primer 11 is made by the steps:
With differing only in for embodiment 1, step is added without polyoxygenated magnesium and zinc oxide in (2).
Reference examples 11 obtain primer 11.
Reference examples 4
Primer 12 is made by the steps:
With differing only in for embodiment 1, step is added without filler in (1).
Reference examples 4 obtain primer 12.
Reference examples 5
Primer 13 is made by the steps:
With differing only in for embodiment 1, step is added without nylon fiber and aramid fiber in (1).
Reference examples 5 obtain primer 13.
Reference examples 6
Primer 14 is made by the steps:
With differing only in for embodiment 1, the vinal in step (1) is replaced with into granule of polyvinyl alcohol material.
Reference examples 6 obtain primer 14.
The primer 1~14 and industrial cloth that are obtained in above-described embodiment and reference examples are passed through respectively by following test method
The low-load performance and high-load performance for pressing obtained transmission belt are tested, and test result is listed in table 1.
The test condition of the high load is according to standard GB/T/T 12735-91《Agricultural machinery V band fatigue tests
Method》Described in, in load testing load type for more than HL types, driven wheel loads more than 23kW, the test with total tension >=2000N
Under the conditions of tested.
It is corresponding, the test condition of the low-load be low-load type transmission belt be load type be HK types and hereinafter, from
Driving wheel is supported on 18kW hereinafter, being tested under the test condition with total tension < 2000N.
(1) tensile strength, tearing strength and elongation at break test
According to standard GB/T/T 3686-1998《V band tensile strength and elongation rate test method》Described in test side
Method tests the tensile strength of transmission belt, tearing strength and the elongation at break being prepared with primer 1~14 for primer respectively.
(2) number test is deflected
According to standard GB/T/T 15328-2009《Classical V-belt fatigue test method》Described in test method, test
The transmission belt being prepared with primer 1~14 for primer deflects number.
The performance comparison table in low load and high load of transmission belt prepared by 1 primer 1~14 of table
As it can be seen from table 1 the primer 1~8 prepared by the present invention deflects under the use condition of low load and high load
Number >=10000 times, do not decline not only, increased instead, and mechanical property change rate is between 0~5%, variation
Amplitude is little, illustrates that, with reference to corresponding technique, the primer ageing-resistant performance being prepared is excellent by heretofore described formula
It is different, it is suitable as high load type transmission belt and is used with primer, and the primer 9~14 obtained in reference examples 1~6 lacks accordingly
Necessary component so that do not have the effect that mutually cooperates between each component, the primer product mechanical property finally obtained and resistance to old
Change performance and be below the present invention, decline acutely moreover, deflecting number under the use condition of high load, be not suitable for negative as height
Load type transmission belt is used with primer.
Applicant states that the present invention illustrates the process of the present invention, but not office of the invention by above-described embodiment
It is limited to above-mentioned processing step, that is, does not mean that the present invention has to rely on above-mentioned processing step and could implement.Technical field
Technical staff it will be clearly understood that any improvement in the present invention, equivalence replacement and auxiliary element to raw material selected by the present invention
Addition, selection of concrete mode etc., all fall within protection scope of the present invention and the open scope.
Claims (10)
1. a kind of high load type transmission belt primer, which is characterized in that in parts by weight, the primer includes following components:
2. primer according to claim 1, which is characterized in that the length of the vinal is 2.5~3.5mm,
Preferably 2.8~3.2mm;
Preferably, elasticity modulus >=35GPa of the vinal, preferably 38~45GPa;
Preferably, the vinal is MM-1 type vinals.
3. primer according to claim 1 or 2, which is characterized in that the elasticity modulus of the reinforcing fiber for 100~
200GPa;
Preferably, the length of the reinforcing fiber is 1~6mm;
Preferably, the reinforcing fiber be nylon fiber, aramid fiber, Kafra fiber, in carbon fiber any one or extremely
Mixture two kinds few.
4. the primer according to one of claims 1 to 3, which is characterized in that the coupling agent is appointing in silane coupling agent
Meaning is a kind of, preferably SI69 types coupling agent;
Preferably, the grain size of the filler is 1~60mm;
Preferably, mixture of the filler including any one in white carbon, carbon black, modified calcium carbonate or at least two;
Preferably, it is (3~4) that the filler, which includes weight ratio,:5:6 white carbon, carbon black and modified calcium carbonate;
Preferably, the white carbon is EDS type easily disperse silica;
Preferably, the carbon black is N330 type carbon blacks:
Preferably, the modified calcium carbonate is superthin light activated Calcium carbonate.
5. the primer according to one of Claims 1 to 4, which is characterized in that the grain size of the metal oxide for 1~
60mm;
Preferably, the metal oxide be in the metal oxide that metallic element therein is positive divalent any one or extremely
Mixture two kinds few, further preferably magnesia and/or zinc oxide;
Preferably, it is 1 that the metal oxide, which is weight ratio,:The magnesia and zinc oxide of (3~5).
6. the primer according to one of Claims 1 to 5, which is characterized in that further include 10~30 in the component of the primer
The addition auxiliary agent of parts by weight;
Preferably, the addition auxiliary agent includes any one in antioxidant, accelerating agent, anti-aging agent, softening agent or at least two
Mixture;
Preferably, it is 1 that the addition auxiliary agent, which includes weight ratio,:(1~2):(2~3):3 antioxidant, accelerating agent, anti-aging agent and
Softening agent;
Preferably, the antioxidant is 264 type antioxidant;
Preferably, the accelerating agent is DM type accelerating agents;
Preferably, the anti-aging agent is ODA type anti-aging agents;
Preferably, the softening agent is DOP type softening agents.
7. the primer according to one of claim 1~6, which is characterized in that 3~5 weights are further included in the component of the primer
Measure the anti-tear crack resin of part:
Preferably, the anti-tear crack resin be E5051 types, TYC0500 types, in the anti-tear crack resin of 260 types any one or extremely
Mixture two kinds few.
8. the preparation method of a kind of primer as described in one of claim 1~7, which is characterized in that wrapped in the preparation method
Include following steps:
Step (1), by the neoprene of formula ratio 1/3rd, the vinal of formula ratio whole, reinforcing fiber and can
The tear-proof resin Composition of choosing adds in mixer, and mixing, bottom sheet obtain mixing rubber master batch;
The metal oxide of formula ratio with other components is uniformly mixed, obtains mixture A, by the coupling of formula ratio by step (2)
Agent is uniformly mixed with other components, obtains mixture B;
Step (3) adds the neoprene of remaining formula ratio, whole mixing rubber master batch and the filler of mixture B and formula ratio
Enter mixer, carry out a mixing, treat all components after mixing, it is secondary close to add in whole mixture A progress thereto
Refining, after secondary mixing, product dumping enters open mill, in open mill by slightly refining, bottom sheet, obtain the bottom after cooling
Glue;
Other components include optional any one or at least two addition auxiliary agents.
9. preparation method according to claim 8, which is characterized in that mixing time described in step (1) for 40~
60s, temperature are 100~300 DEG C;
Preferably, the time of a mixing described in step (3) is 30~50s, and temperature is 100~300 DEG C;
Preferably, the time of the secondary mixing described in step (3) is 40~60s, and temperature is 100~300 DEG C;
Preferably, the time slightly refined described in step (3) is 40~80s, and temperature is 100~200 DEG C;
Preferably, linear cooling down is cooled to described in step (3), cooldown rate is 1~10 DEG C/min.
10. the purposes of a kind of primer as described in one of claim 1~7, which is characterized in that the primer is as trimming tooth type
Transmission belt is used with primer.