CN105295169A - Sunshine resistant fishing net - Google Patents
Sunshine resistant fishing net Download PDFInfo
- Publication number
- CN105295169A CN105295169A CN201510727754.1A CN201510727754A CN105295169A CN 105295169 A CN105295169 A CN 105295169A CN 201510727754 A CN201510727754 A CN 201510727754A CN 105295169 A CN105295169 A CN 105295169A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- parts
- composite assistant
- minutes
- sun
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sunshine resistant fishing net, and relates to the technical field of fishing net manufacturing. The sunshine resistant fishing net consists of the following components in parts by weight: 70-85 parts of polyethylene, 60-70 parts of nylon, 20-30 parts of polyethylene, 3-6 parts of dimethyl silicon oil, 2-3 parts of fish bone powder, 5-7 parts of polyisodiene, 1-2 parts of spice and 11-14 parts of a composite additive. By adopting the sunshine resistant fishing net, the problem that a fishing net can be aged after being exposed in sunshine is solved, a fishing net which is high in strength and good in abrasion resistance is provided, due to special materials and processes, the fishing net can be prevented from aging after being exposed in intense sunshine, the service life of the fishing net can be prolonged, and the cost can be lowered.
Description
Technical field
The present invention relates to fishing net manufacture technology field, particularly relate to a kind of sun-resistant fishing net.
Background technology
Fishing net is used to fishing, and modern fishing net mainly polyethylene and nylon material is made.Fishing net needs airing after fishing terminates, and the sun can promote the aging of fishing net according to solarization, shortens the work-ing life of fishing net, increases extra cost.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of fishing net that can be sun-resistant.
For solving the problem, the sun-resistant fishing net of one of the present invention, this fishing net is grouped into by the one-tenth of following weight part: high-molecular polythene 90 ~ 110, polystyrene 50 ~ 65, boron phosphide BP 3 ~ 5, tetramethylolmethane 4 ~ 6, isopropylimdazole 3 ~ 6, sodium stearate 4 ~ 7 and composite assistant 9 ~ 13.
Described composite assistant is grouped into by the one-tenth of following weight part: Mono-n-butyltin 1.1 ~ 1.4, resol 1.3 ~ 1.7, Trisodium Citrate 1.8 ~ 2.3, epoxidized linseed oil 1.1 ~ 1.3, Oil of Eucalyptus 0.9 ~ 1.2 and vinylbenzene 1.6 ~ 1.9; The preparation method of described composite assistant is: join in the mixture of other compositions by Oil of Eucalyptus and resol, heat while stirring, stirs 25 ~ 35 minutes, and it is 120 DEG C ~ 140 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for sun-resistant fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 90 ~ 110, polystyrene 50 ~ 65 are added in stirrer together with boron phosphide BP 3 ~ 5 and stir, churning time is 10 ~ 18 minutes;
(2) mixture stirred is put into reactor, add tetramethylolmethane 4 ~ 6 and isopropylimdazole 3 ~ 6, it is 85 DEG C ~ 100 DEG C that temperature controls, and the reaction times is 11 ~ 17 minutes;
(3) in reacted mixture, add sodium stearate 4 ~ 7 and composite assistant 9 ~ 13, stir, churning time is 19 ~ 28 minutes, is then heated to molten state, and heating and temperature control is 120 DEG C ~ 150 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described sun-resistant fishing net.
Compared with prior art, the present invention has the following advantages: problem aging after the invention solves fishing net Exposure to Sunlight, the fishing net that intensity is high, wear resistance is good is provided, fishing net utilizes exotic materials and technique to make, can bear strong solar radiation does not occur aging, add the work-ing life of fishing net, reduce cost.
Embodiment
Embodiment 1
A kind of sun-resistant fishing net is grouped into by the one-tenth of following weight part: high-molecular polythene 90, polystyrene 50, boron phosphide BP 3, tetramethylolmethane 4, isopropylimdazole 3, sodium stearate 4 and composite assistant 9.
Composite assistant is grouped into by the one-tenth of following weight part: Mono-n-butyltin 1.1, resol 1.3, Trisodium Citrate 1.8, epoxidized linseed oil 1.1, Oil of Eucalyptus 0.9 and vinylbenzene 1.6; The preparation method of composite assistant is: join in the mixture of other compositions by Oil of Eucalyptus and resol, heat while stirring, stirs 25 minutes, and it is 120 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for sun-resistant fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 90, polystyrene 50 are added in stirrer together with boron phosphide BP 3 and stir, churning time is 10 minutes;
(2) mixture stirred is put into reactor, add tetramethylolmethane 4 and isopropylimdazole 3, it is 85 DEG C that temperature controls, and the reaction times is 11 minutes;
(3) in reacted mixture, add sodium stearate 4 and composite assistant 9, stir, churning time is 19 minutes, is then heated to molten state, and heating and temperature control is 120 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described sun-resistant fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 31.8%
Anti-tensile degree (KG): 54.7
Knotting strength (KG): 45.6
Compared with common fishing net, this fishing net increases by 28% work-ing life.
Embodiment 2
A kind of sun-resistant fishing net is grouped into by the one-tenth of following weight part: high-molecular polythene 100, polystyrene 57, boron phosphide BP 4, tetramethylolmethane 5, isopropylimdazole 4, sodium stearate 5 and composite assistant 11.
Composite assistant is grouped into by the one-tenth of following weight part: Mono-n-butyltin 1.3, resol 1.5, Trisodium Citrate 2.1, epoxidized linseed oil 1.2, Oil of Eucalyptus 1.1 and vinylbenzene 1.8; The preparation method of composite assistant is: join in the mixture of other compositions by Oil of Eucalyptus and resol, heat while stirring, stirs 30 minutes, and it is 130 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for sun-resistant fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 100, polystyrene 57 are added in stirrer together with boron phosphide BP 4 and stir, churning time is 14 minutes;
(2) mixture stirred is put into reactor, add tetramethylolmethane 5 and isopropylimdazole 4, it is 93 DEG C that temperature controls, and the reaction times is 14 minutes;
(3) in reacted mixture, add sodium stearate 5 and composite assistant 11, stir, churning time is 24 minutes, is then heated to molten state, and heating and temperature control is 135 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described sun-resistant fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 36.7%
Anti-tensile degree (KG): 63.4
Knotting strength (KG): 57.3
Compared with common fishing net, this fishing net increases by 51% work-ing life.
Experimental data shows, and this fishing net is the longest for work-ing life, meets actual user demand.
Embodiment 3
A kind of sun-resistant fishing net is grouped into by the one-tenth of following weight part: high-molecular polythene 110, polystyrene 65, boron phosphide BP 5, tetramethylolmethane 6, isopropylimdazole 6, sodium stearate 7 and composite assistant 13.
Composite assistant is grouped into by the one-tenth of following weight part: Mono-n-butyltin 1.4, resol 1.7, Trisodium Citrate 2.3, epoxidized linseed oil 1.3, Oil of Eucalyptus 1.2 and vinylbenzene 1.9; The preparation method of composite assistant is: join in the mixture of other compositions by Oil of Eucalyptus and resol, heat while stirring, stirs 35 minutes, and it is 140 DEG C that temperature controls, and can obtain described composite assistant.
A preparation method for sun-resistant fishing net, comprises following preparation process:
(1) above-mentioned polyethylene 110, polystyrene 65 are added in stirrer together with boron phosphide BP 5 and stir, churning time is 18 minutes;
(2) mixture stirred is put into reactor, add tetramethylolmethane 6 and isopropylimdazole 6, it is 100 DEG C that temperature controls, and the reaction times is 17 minutes;
(3) in reacted mixture, add sodium stearate 7 and composite assistant 13, stir, churning time is 28 minutes, is then heated to molten state, and heating and temperature control is 150 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described sun-resistant fishing net.
It is as follows that experiment obtains filament properties data:
Elongation at break: 32.7%
Anti-tensile degree (KG): 54.5
Knotting strength (KG): 51.6
Compared with common fishing net, this fishing net increases by 39% work-ing life.
Claims (3)
1. a sun-resistant fishing net, is characterized in that: this fishing net is grouped into by the one-tenth of following weight part: high-molecular polythene 90 ~ 110, polystyrene 50 ~ 65, boron phosphide BP 3 ~ 5, tetramethylolmethane 4 ~ 6, isopropylimdazole 3 ~ 6, sodium stearate 4 ~ 7 and composite assistant 9 ~ 13.
2. a kind of sun-resistant fishing net according to claim 1, is characterized in that: described composite assistant is grouped into by the one-tenth of following weight part: Mono-n-butyltin 1.1 ~ 1.4, resol 1.3 ~ 1.7, Trisodium Citrate 1.8 ~ 2.3, epoxidized linseed oil 1.1 ~ 1.3, Oil of Eucalyptus 0.9 ~ 1.2 and vinylbenzene 1.6 ~ 1.9; The preparation method of described composite assistant is: join in the mixture of other compositions by Oil of Eucalyptus and resol, heat while stirring, stirs 25 ~ 35 minutes, and it is 120 DEG C ~ 140 DEG C that temperature controls, and can obtain described composite assistant.
3. a preparation method for sun-resistant fishing net as claimed in claim 1, is characterized in that: comprise following preparation process:
(1) above-mentioned polyethylene 90 ~ 110, polystyrene 50 ~ 65 are added in stirrer together with boron phosphide BP 3 ~ 5 and stir, churning time is 10 ~ 18 minutes;
(2) mixture stirred is put into reactor, add tetramethylolmethane 4 ~ 6 and isopropylimdazole 3 ~ 6, it is 85 DEG C ~ 100 DEG C that temperature controls, and the reaction times is 11 ~ 17 minutes;
(3) in reacted mixture, add sodium stearate 4 ~ 7 and composite assistant 9 ~ 13, stir, churning time is 19 ~ 28 minutes, is then heated to molten state, and heating and temperature control is 120 DEG C ~ 150 DEG C;
(4) molten state mixture is added forcing machine, extrusion moulding, obtain described sun-resistant fishing net.