CN105331305A - Fast-curing epoxy resin adhesive - Google Patents
Fast-curing epoxy resin adhesive Download PDFInfo
- Publication number
- CN105331305A CN105331305A CN201510941686.9A CN201510941686A CN105331305A CN 105331305 A CN105331305 A CN 105331305A CN 201510941686 A CN201510941686 A CN 201510941686A CN 105331305 A CN105331305 A CN 105331305A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- component
- parts
- weight
- components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fast-curing epoxy resin adhesive. The fast-curing epoxy resin adhesive comprises components A and components B. The components A are prepared from, by weight, 15-30 parts of epoxy resin, 60-80 parts of nitrile rubber and 5-15 parts of a fire-retardant agent. The components B are prepared from, by weight, 40-60 parts of polyamine, 35-50 parts of glycidyl ether and 5-10 parts of an accelerant. The matching ratio of the components A to the components B is 100:30-40. Due to the mode, the prepared adhesive is short in room temperature curing time and meanwhile has good heat resistance, high stripping strength and flame retardant performance.
Description
Technical field
The present invention relates to epoxy resin field, particularly relate to a kind of Rapid Curing Epoxy Adhesive.
Background technology
Epoxy resin adhesive is epoxy resin, solidifying agent, promotor, properties-correcting agent, thinner, the liquid state of the composition such as filler or solid-state sizing agent, it is to various metallic substance (steel, iron, copper, aluminium etc.), non-metallic material (timber, glass, concrete etc.), thermosetting material (phenoplast, aminoplastics, unsaturated polyester etc.) there is excellent adhesive property, at present, the epoxy resin adhesive used in a large number in China is all longer for set time, room temperature generally needs more than 1-36h, also often dozens of minutes is needed under hot conditions, improve the curing speed of epoxy resin adhesive, to adapt to the service requirements of different occasion, it is the problem that sizing agent industry is concerned about always.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of Rapid Curing Epoxy Adhesive, and the self-vulcanizing time is short, has good resistance toheat, higher stripping strength simultaneously, and has flame retardant properties.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of Rapid Curing Epoxy Adhesive, comprise component A and B component, the composition of described component A and weight are: epoxy resin 15-30 part, paracril 60-80 part, fire retardant chemical 5-15 part; The composition of described B component and weight proportion are: polyamine 40-60 part, glycidyl ether 35-50 part, promotor 5-10 part; The mixing match of described component A and described B component is 100:30-40;
The preparation method of described Rapid Curing Epoxy Adhesive comprises the steps:
A, preparation component A: get the described epoxy resin of formula ratio, paracril and fire retardant chemical, under nitrogen protection, under the temperature of reaction of 150-160 DEG C, react 1-2h, obtained epoxy resin toughened;
B, preparation B component: get the described polyamine of formula ratio, glycidyl ether and promotor, under the temperature of reaction of 70-80 DEG C, react 1-2h, obtained modified amine curing agent;
The ratio of c, the described epoxy resin toughened and modified amine curing agent that obtained by step a and b 100:30-40 by weight mixes obtained described Rapid Curing Epoxy Adhesive.
In a preferred embodiment of the present invention, described polyamine is aromatic amine.
In a preferred embodiment of the present invention, in described step c, described mixed weight ratio that is epoxy resin toughened and modified amine curing agent is 100:35.
The invention has the beneficial effects as follows: Rapid Curing Epoxy Adhesive of the present invention is mixed by optimum proportioning by homemade epoxy resin toughened and modified amine curing agent, its preparation technology is simple, cost is low, and this sizing agent has the self-vulcanizing time is short, resistance toheat good, stripping strength is high feature and also has flame retardant properties simultaneously.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention comprises:
A kind of Rapid Curing Epoxy Adhesive, comprise component A and B component, the composition of described component A and weight are: epoxy resin 15-30 part, paracril 60-80 part, fire retardant chemical 5-15 part; The composition of described B component and weight proportion are: polyamine 40-60 part, glycidyl ether 35-50 part, promotor 5-10 part; The mixing match of described component A and described B component is 100:30-40;
The preparation method of described Rapid Curing Epoxy Adhesive comprises the steps:
A, preparation component A: get the described epoxy resin of formula ratio, paracril and fire retardant chemical, under nitrogen protection, under the temperature of reaction of 150-160 DEG C, react 1-2h, obtained epoxy resin toughened;
B, preparation B component: get the described polyamine of formula ratio, glycidyl ether and promotor, under the temperature of reaction of 70-80 DEG C, react 1-2h, obtained modified amine curing agent;
The ratio of c, the described epoxy resin toughened and modified amine curing agent that obtained by step a and b 100:30-40 by weight mixes obtained described Rapid Curing Epoxy Adhesive.
Wherein, described polyamine is aromatic amine.There is the performances such as excellent thermotolerance, low-temperature curing and wet surface solidification.
In described step c, described mixed weight ratio that is epoxy resin toughened and modified amine curing agent is 100:35.Reasonable ratio, makes the Rapid Curing Epoxy Adhesive obtained have excellent over-all properties.
Embodiment one:
Preparation component A: extracting epoxy resin 30kg, paracril 65kg, fire retardant chemical 3kg, under nitrogen protection, reacts 2h under the temperature of reaction of 150 DEG C, obtained epoxy resin toughened;
Preparation B component: get aromatic amine 40kg, glycidyl ether 50kg, promotor 10kg, react 2h under the temperature of reaction of 70 DEG C, obtained modified amine curing agent;
Again the ratio of above-mentioned obtained described epoxy resin toughened and modified amine curing agent 100:35 is by weight mixed obtained described Rapid Curing Epoxy Adhesive.
Embodiment two:
Preparation component A: extracting epoxy resin 15kg, paracril 70kg, fire retardant chemical 15kg, under nitrogen protection, reacts 1h under the temperature of reaction of 160 DEG C, obtained epoxy resin toughened;
Preparation B component: get aromatic amine 60kg, glycidyl ether 35kg, promotor 5kg, react 1h under the temperature of reaction of 80 DEG C, obtained modified amine curing agent;
Again the ratio of above-mentioned obtained described epoxy resin toughened and modified amine curing agent 100:35 is by weight mixed obtained described Rapid Curing Epoxy Adhesive.
Present invention is disclosed a kind of Rapid Curing Epoxy Adhesive, mixed by optimum proportioning by homemade epoxy resin toughened and modified amine curing agent, its preparation technology is simple, cost is low, sizing agent after solidification has good thermotolerance, keep the stripping strength of 4Kn/m under normal temperature, there is excellent wet and heat ageing resistant performance and heat-resistant aging simultaneously.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a Rapid Curing Epoxy Adhesive, is characterized in that, comprises component A and B component, and the composition of described component A and weight are: epoxy resin 15-30 part, paracril 60-80 part, fire retardant chemical 5-15 part; The composition of described B component and weight proportion are: polyamine 40-60 part, glycidyl ether 35-50 part, promotor 5-10 part; The mixing match of described component A and described B component is 100:30-40;
The preparation method of described Rapid Curing Epoxy Adhesive comprises the steps:
A, preparation component A: get the described epoxy resin of formula ratio, paracril and fire retardant chemical, under nitrogen protection, under the temperature of reaction of 150-160 DEG C, react 1-2h, obtained epoxy resin toughened;
B, preparation B component: get the described polyamine of formula ratio, glycidyl ether and promotor, under the temperature of reaction of 70-80 DEG C, react 1-2h, obtained modified amine curing agent;
The ratio of c, the described epoxy resin toughened and modified amine curing agent that obtained by step a and b 100:30-40 by weight mixes obtained described Rapid Curing Epoxy Adhesive.
2. Rapid Curing Epoxy Adhesive according to claim 1, is characterized in that, described polyamine is aromatic amine.
3. Rapid Curing Epoxy Adhesive according to claim 1, is characterized in that, in described step c, described mixed weight ratio that is epoxy resin toughened and modified amine curing agent is 100:35.