CN105330207A - 一种抗冲耐磨的混凝土 - Google Patents

一种抗冲耐磨的混凝土 Download PDF

Info

Publication number
CN105330207A
CN105330207A CN201510695827.3A CN201510695827A CN105330207A CN 105330207 A CN105330207 A CN 105330207A CN 201510695827 A CN201510695827 A CN 201510695827A CN 105330207 A CN105330207 A CN 105330207A
Authority
CN
China
Prior art keywords
concrete
resisting
impact
cement
wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510695827.3A
Other languages
English (en)
Inventor
唐先奇
葛培清
伍绍华
刘存福
魏功林
朱自先
章国红
谢黎进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangnan Water Resources And Hydropower Engineering Co Ltd
Original Assignee
Jiangnan Water Resources And Hydropower Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangnan Water Resources And Hydropower Engineering Co Ltd filed Critical Jiangnan Water Resources And Hydropower Engineering Co Ltd
Priority to CN201510695827.3A priority Critical patent/CN105330207A/zh
Publication of CN105330207A publication Critical patent/CN105330207A/zh
Pending legal-status Critical Current

Abstract

一种抗冲耐磨的混凝土涉及一种建筑材料，特别涉及一种用于水电工程中抗水流冲击的混凝土，本发明主要由水、水泥、骨料、粉煤灰和外加剂混合而成，每立方米混凝土中材料用量为：水130-140kg，水泥300-350kg，骨料1650-1890kg，粉煤灰50-60kg，外加剂为4-4.9kg。本发明所述的抗冲耐磨的混凝土，其抗冲耐磨性能好，且质量稳定，生产成本低。

Description

一种抗冲耐磨的混凝土
技术领域
本发明涉及一种建筑材料，特别涉及一种用于水电工程中抗水流冲击的混凝土。
背景技术
抗冲耐磨性能是混凝土在一种特殊环境下的耐久性能，主要发生在水利水电工程中高水头泄水建筑物表面、交通工程中路面、桥面等与车辆直接接触部位。近年来在很多连岛工程、跨海大桥、跨江大桥的开工建设与运行中，也发现了携沙水流对桥墩、桥梁承台等关键部位的冲刷作用，这些造成了混凝土的严重冲磨破坏，可以认为混凝土的抗冲耐磨性能决定了这些建筑物的安全使用寿命及运行维护成本。在抗冲耐磨混凝土性能的提高途径上，研究者主要从骨料、胶凝材料、化学外加剂、纤维等方面对其进行改性，考虑到耐磨骨料，如铁钢砂，但其价格比较高，往往运输距离远，提高了混凝土单位生产成本；胶凝材料，如硅粉的早期高收缩性及纤维的高成本和不易在混凝土中均匀分散影响混凝土的性能及和易性等缺陷，因而研制高效的抗冲耐磨化学外加剂成为了提高混凝土耐磨性能的一种有效途径。以往的耐磨剂大多掺入了大量有机耐磨成分，如橡胶粉、纤维及尼龙等，基于对混凝土抗冲耐磨混凝土的破坏机理研究，导致混凝土抗冲耐磨性能的最直接原因是其基体本身的抗冲耐磨性低，而有机成分并不能与水泥基材料产生良好的胶合力，从本质上说其并不能提高水泥基体自身的耐磨性，由“短板效应”可知，有机耐磨成分改善混凝土耐磨性的能力有限。
发明内容
本发明的目的，就是为了解决上述问题而提供了一种抗冲耐磨，且质量稳定，生产成本低的抗冲耐磨的混凝土。
本发明所述的抗冲耐磨的混凝土，主要由水、水泥、骨料、粉煤灰和外加剂混合而成，每立方米混凝土中材料用量为：水130-140kg，水泥300-350kg，骨料1650-1890kg，粉煤灰50-60kg，外加剂为4-4.9kg。
所述的骨料为：砂、碎石块和公分石混合物。其中，砂的用量为每立方米620-720kg，碎石块的用量为每立方米480-580kg，公分石550-590kg。
所述的外加剂为：减水剂和引气剂，所述的减水剂的用量为每立方米3.99-4.88kg，引气剂的用量为每立方米0.01-0.02kg。
本发明所述的抗冲耐磨的混凝土，将上述物料按量配比后，坍落度14-16cm泵入仓内搅拌即得。
本发明中，水泥采用满足《能用硅酸水泥》要求的3d强度为26.5MPa，28d强度为55MPa的水泥，强度偏高不利于抗冲耐磨的温控。粉煤灰氧化钙含量较低，其自身所能产生的水化作用是微不足道的，但若受到水泥水化生成氢氧化钙的激发，粉煤灰会逐渐发生水化作用和水泥一起成为胶凝材料，使混凝土胶结并产生力学强度，采用粉煤灰替代部分水泥，可获得良好的技术经济效益，使混凝土性能得到很大改善，提高混凝土的抗裂性和耐久性。而采用砂、碎石和公分石作为骨料，混凝土的和易性好且容重较大，级配好，空隙少，在相同水泥浆量的条件下，流动性要更好，而外加剂选用聚羧酸盐减水剂，掺量为1.2％，减水率为21.3％，初凝时间为202分钟，终凝时间为223分钟，而引气剂的掺量为0.005％，收缩率小于125。采用上述的物料混合而成的混凝土，经抗冲耐磨比的试验，混凝土28d强度最大值可达61.8MPa，其抗冲耐磨的性能明显得到了提升。
本发明所述的抗冲耐磨的混凝土，其抗冲耐磨性能好，且质量稳定，生产成本低。
具体实施方式
下面将结合实施例，对本发明作进一步说明。
实施例1
本发明所述的抗冲耐磨的混凝土，主要由水、水泥、骨料、粉煤灰和外加剂混合而成，每立方米混凝土中材料用量为：水138kg，水泥317kg，砂697kg，碎石块573kg，公分石573kg，粉煤灰56kg，减水剂4.476kg，引气剂0.0186kg，将上述物料按量配比后，坍落度14cm泵入仓内搅拌即得。
实施例2
本发明所述的抗冲耐磨的混凝土，主要由水、水泥、骨料、粉煤灰和外加剂混合而成，每立方米混凝土中材料用量为：水130-140kg，水泥300-350kg，骨料1650-1890kg，粉煤灰50-60kg，外加剂为4-4.9kg。
所述的骨料为：砂、碎石块和公分石混合物。其中，砂的用量为每立方米620-720kg，碎石块的用量为每立方米480-580kg，公分石550-590kg。
所述的外加剂为：减水剂和引气剂，所述的减水剂的用量为每立方米3.99-4.88kg，引气剂的用量为每立方米0.01-0.02kg。
本发明所述的抗冲耐磨的混凝土，将上述物料按量配比后，坍落度16cm泵入仓内搅拌即得。
实施例3
本发明所述的抗冲耐磨的混凝土，主要由水、水泥、骨料、粉煤灰和外加剂混合而成，每立方米混凝土中材料用量为：水140kg，水泥350kg，粉煤灰60kg，砂620kg，碎石块480kg，公分石550kg，减水剂3.99kg，引气剂0.01kg。
本发明所述的抗冲耐磨的混凝土，将上述物料按量配比后，坍落度15cm泵入仓内搅拌即得。

Claims (4)

1.一种抗冲耐磨的混凝土，主要由水、水泥、骨料、粉煤灰和外加剂混合而成，其特征在于，每立方米混凝土中材料用量为：水130-140kg，水泥300-350kg，骨料1650-1890kg，粉煤灰50-60kg，外加剂为4-4.9kg。
2.根据权利要求1所述的抗冲耐磨的混凝土，其特征在于，所述的骨料为：砂、碎石块和公分石混合物。其中，砂的用量为每立方米620-720kg，碎石块的用量为每立方米480-580kg，公分石550-590kg。
3.根据权利要求1所述的抗冲耐磨的混凝土，其特征在于，所述的外加剂为：减水剂和引气剂，所述的减水剂的用量为每立方米3.99-4.88kg，引气剂的用量为每立方米0.01-0.02kg。
4.根据权利要求1所述的抗冲耐磨的混凝土，其特征在于，本发明所述的抗冲耐磨的混凝土，将上述物料按量配比后，坍落度14-16cm泵入仓内搅拌即得。
CN201510695827.3A 2015-10-24 2015-10-24 一种抗冲耐磨的混凝土 Pending CN105330207A (zh)