CN105297440A - 一种对蚕丝接枝改性的方法 - Google Patents

一种对蚕丝接枝改性的方法 Download PDF

Info

Publication number
CN105297440A
CN105297440A CN201510762649.1A CN201510762649A CN105297440A CN 105297440 A CN105297440 A CN 105297440A CN 201510762649 A CN201510762649 A CN 201510762649A CN 105297440 A CN105297440 A CN 105297440A
Authority
CN
China
Prior art keywords
silk
graft modification
polymer
steps
carbodiimide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510762649.1A
Other languages
English (en)
Other versions
CN105297440B (zh
Inventor
王际平
方奇生
陈涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Lvyu Textile Technology Co ltd
Original Assignee
Zhejiang University of Technology ZJUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University of Technology ZJUT filed Critical Zhejiang University of Technology ZJUT
Priority to CN201510762649.1A priority Critical patent/CN105297440B/zh
Publication of CN105297440A publication Critical patent/CN105297440A/zh
Application granted granted Critical
Publication of CN105297440B publication Critical patent/CN105297440B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及纺织领域，公开了一种对蚕丝接枝改性的方法，以4-二甲氨基吡啶为催化剂，以碳二亚胺为缩合剂，活化含有羧基的聚合物，然后与蚕丝的氨基反应，将聚合物结合到蚕丝上。采用碳二亚胺为缩合试剂，活化羧基后与蚕丝的氨基反应，形成酰胺键，反应条件温和，且不同于传统的物理吸附改性，制得的改性蚕丝具有蓬松度高，耐久性好，耐磨度强，牢度高，不容易在使用中损失等优点。

Description

一种对蚕丝接枝改性的方法
技术领域
本发明涉及纺织领域，尤其涉及一种对蚕丝接枝改性的方法。
背景技术
蚕丝是一种高档的纺织原料，它的性能优良，被誉为“纤维皇后”。由于天然蚕丝原料紧缺，致使蚕丝织物价格昂贵。蚕丝用作家纺中被芯的填充具有冬暖夏凉，护肤保健等功效，但是蚕丝被胎存在长期使用易板结和耐磨性耐久性不足的缺点。因此寻找有效改善蚕丝易板结特性的方法，提高蚕丝的耐磨性耐久度，成为人们关注的焦点。
发明内容
本发明针对现有技术中蚕丝易板结，耐磨性持久度差的缺点，提供了一种对蚕丝接枝改性的方法。
为了解决上述技术问题，本发明通过下述技术方案得以解决：
一种对蚕丝接枝改性的方法，以4-二甲氨基吡啶为催化剂，以碳二亚胺为缩合剂，活化含有羧基的聚合物，然后与蚕丝的氨基反应，将聚合物结合到蚕丝上。碳二亚胺类缩合试剂，主要用于活化羧基，促进酰胺或酯的生成，整个反应条件温和，高效，副产物少。
作为优选，一种对蚕丝接枝改性的方法，包括如下步骤：
步骤A：将含有羧基的聚合物溶解于溶剂中，配成浓度为25～100g/L的溶液，加入相当于聚合物干重2～5％的4-二甲氨基吡啶，室温下搅拌反应1～2小时；
步骤B：将相当于聚合物羧基摩尔量0.8～1.2倍摩尔量的碳二亚胺溶解于溶剂中，配置成50～100g/L的溶液，将蚕丝浸没入液面下，浴比1:10～1:22，室温下搅拌反应1～2小时；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应20～30小时，得改性蚕丝。
将含有催化剂的溶液和反应底物的溶液分开配制，之后向底物中加入催化剂，催化剂催化碳二亚胺活化羧基，被活化的羧基在与氨基反应，形成酰胺键，蚕丝与聚合物通过酰胺键结合到一起。反应温和高效，不同于传统蚕丝改性中采用吸附等物理结合的方法，聚合物与蚕丝通过酰胺键结合，化学结合牢固。由于聚合物具有较长较大的侧链基团，极大的提高了蚕丝的蓬松度和保暖性；同时，通过化学结合聚合物，减少蚕丝蛋白的摩擦，提高了蚕丝的耐磨性和持久度。
作为优选，碳二亚胺为N,Nˊ-二环己基碳二亚胺或N,N'-二异丙基碳二亚胺或1-(3-二甲氨基丙基)-3-乙基碳二亚胺盐酸盐。
作为优选，步骤A和步骤B的溶剂为四氢呋喃或甲苯或二甲基亚砜中的任一种或混合物。
作为优选，步骤C之后还包括后处理步骤，将步骤C中的蚕丝分别用乙醇和水冲洗，之后35～65℃真空干燥8～24小时。采用乙醇和水分别冲洗改性蚕丝，彻底冲走残留的化学试剂，避免化学试剂对皮肤造成刺激。
作为优选，步骤A之前还包括前处理步骤，待改性蚕丝先进行脱胶处理，然后分别用乙醇和水冲洗，之后35～65℃干燥8～24小时。丝胶是一种包络在蚕丝外层的蛋白，占蚕丝四分之一以上，丝胶蛋白不同于丝素蛋白，为球状蛋白，氨基酸组成复杂，对湿热易变性，因此，需要除去丝胶蛋白提高蚕丝的耐久性。
作为优选，前处理步骤中，脱胶处理采用皂碱法脱胶处理，碱液pH值为9-10.5。温和碱性条件下，有助于丝胶蛋白肽键断裂，丝胶蛋白水解效率高。
本发明由于采用了以上技术方案，具有显著的技术效果：采用本发明制得的改性蚕丝，由于聚合物与蚕丝通过化学酰胺键结合，结合牢固度高，蚕丝的蓬松度、耐磨性、耐久性、牢度等指标均高于普通蚕丝，可以广泛应用服装，家纺或特种服饰领域。
附图说明
图1是未经过改性接枝处理的蚕丝的显微照片；
图2是经过改性接枝处理后的蚕丝的显微照片。
具体实施方式
下面结合实施例对本发明作进一步详细描述。
实施例1
一种对蚕丝接枝改性的方法，包括如下步骤：
前处理步骤：将待改性蚕丝先进行脱胶处理，然后分别用乙醇和水冲洗2次，之后55℃恒温干燥12小时。其中，脱胶方法采用皂碱法，碱液pH值为10；
步骤A：以四氢呋喃为溶剂，以1g聚N-异丙基丙烯酰胺-co-丙烯酸聚合物为溶质，配成50g/L的溶液0.02L，加入0.02g催化剂4-二甲氨基吡啶，室温下搅拌反应1h；
步骤B：以四氢呋喃为溶剂，以0.1g的N,Nˊ-二环己基碳二亚胺为溶质，配成50g/L的溶液，将2g经过前处理步骤的蚕丝浸没入液面，溶浴比为1:10，室温下搅拌反应1h；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应24h，得改性蚕丝；
后处理步骤：将步骤C中的蚕丝分别用乙醇和水冲洗2次，之后置于50℃真空干燥12h。
实施例2
一种对蚕丝接枝改性的方法，包括如下步骤：
前处理步骤：将待改性蚕丝先进行脱胶处理，然后分别用乙醇和水冲洗3次，之后35℃恒温干燥24小时。其中，脱胶方法采用皂碱法，碱液pH值为9.5；
步骤A：以甲苯为溶剂，以0.5gPMEO2MA-b-PAA聚合物为溶质，配成50g/L的溶液0.01L，加入0.02g催化剂4-二甲氨基吡啶，室温下搅拌反应1.5h；
步骤B：以甲苯为溶剂，以0.2g的N,Nˊ-二环己基碳二亚胺为溶质，配成50g/L的溶液，将1g经过前处理步骤的蚕丝浸没入液面，溶浴比为1:14，室温下搅拌反应1.5h；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应20h，得改性蚕丝；
后处理步骤：将步骤C中的蚕丝分别用乙醇和水冲洗3次，之后置于35℃真空干燥24h。
实施例3
一种对蚕丝接枝改性的方法，包括如下步骤：
前处理步骤：将待改性蚕丝先进行脱胶处理，然后依次用乙醇、水、乙醇和水分4次冲洗，之后45℃恒温干燥18小时。其中，脱胶方法采用皂碱法，碱液pH值为10.5；
步骤A：以四氢呋喃为溶剂，以0.5gPMEO2MA-b-PAA聚合物为溶质，配成25g/L的溶液0.02L，加入0.01g催化剂4-二甲氨基吡啶，室温下搅拌反应2h；
步骤B：以四氢呋喃为溶剂，以0.2g的N,N'-二异丙基碳二亚胺为溶质，配成100g/L的溶液0.002L，将1g经过前处理步骤的蚕丝浸没入液面，溶浴比为1:22，室温下搅拌反应2h；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应27h，得改性蚕丝；
后处理步骤：将步骤C中的蚕丝分别用乙醇和水冲洗2次，之后置于65℃真空干燥8h。
实施例4
一种对蚕丝接枝改性的方法，包括如下步骤：
前处理步骤：将待改性蚕丝先进行脱胶处理，然后分别用乙醇和水冲洗3次，之后65℃恒温干燥8小时。其中，脱胶方法采用皂碱法，碱液pH值为9；
步骤A：以二甲基亚砜为溶剂，以0.4gPMEO2MA-b-PAA聚合物为溶质，配成100g/L的溶液0.005L，加入0.01g催化剂4-二甲氨基吡啶，室温下搅拌反应1.5h；
步骤B：以二甲基亚砜为溶剂，以0.1g的1-(3-二甲氨基丙基)-3-乙基碳二亚胺盐酸盐为溶质，配成50g/L的溶液0.002L，将0.5g经过前处理步骤的蚕丝浸没入液面，溶浴比为1:14，室温下搅拌反应1.5h；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应30h，得改性蚕丝；
后处理步骤：将步骤C中的蚕丝依次用乙醇、水、乙醇和水分为4次冲洗，之后置于45℃真空干燥18h。
实施例5
对实施例1-4制得的蚕丝和未改性蚕丝进行检测，检测结果如下表。
25℃接触角(pH＝6) 40℃接触角(pH＝6) 40℃接触角(pH＝12)
实施例1制得的蚕丝 88° 131° 90°
实施例2制得的蚕丝 96° 128° 95°
实施例3制得的蚕丝 99° 129° 100°
实施例4制得的蚕丝 102° 130° 101°
未改性处理的蚕丝 118° 119° 118°
接触角小表示蚕丝亲水，接触角大表示蚕丝疏水。通过上述检测结果可知，未经改性处理的蚕丝接触角随温度变化较小，改性后的蚕丝接触角随温度、pH值变化而变化，即改性的蚕丝可以通过调节温度调节蚕丝的亲疏水性。
总之，以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所作的均等变化与修饰，皆应属本发明专利的涵盖范围。

Claims (7)

1.一种对蚕丝接枝改性的方法，其特征在于，以4-二甲氨基吡啶为催化剂，以碳二亚胺为缩合剂，活化含有羧基的聚合物，然后与蚕丝的氨基反应，将聚合物结合到蚕丝上。
2.根据权利要求1所述的一种对蚕丝接枝改性的方法，其特征在于：包括如下步骤：
步骤A：将含有羧基的聚合物溶解于溶剂中，配成浓度为25～100g/L的溶液，加入相当于聚合物干重2～5％的4-二甲氨基吡啶，室温下搅拌反应1～2小时；
步骤B：将相当于聚合物羧基摩尔量0.8～1.2倍摩尔量的碳二亚胺溶解于溶剂中，配置成50～100g/L的溶液，将蚕丝浸没入液面下，浴比1:10～1:22，室温下搅拌反应1～2小时；
步骤C：将步骤A中制得的溶液倒入步骤B的容器中，室温下搅拌反应20～30小时，得改性蚕丝。
3.根据权利要求1或2所述的一种对蚕丝接枝改性的方法，其特征在于：碳二亚胺为N,Nˊ-二环己基碳二亚胺或N,N'-二异丙基碳二亚胺或1-(3-二甲氨基丙基)-3-乙基碳二亚胺盐酸盐。
4.根据权利要求3所述的一种对蚕丝接枝改性的方法，其特征在于：步骤A和步骤B的溶剂为四氢呋喃或甲苯或二甲基亚砜中的任一种或混合物。
5.根据权利要求2所述的一种对蚕丝接枝改性的方法，其特征在于：步骤C之后还包括后处理步骤，将步骤C中的蚕丝分别用乙醇和水冲洗，之后35～65℃真空干燥8～24小时。
6.根据权利要求2所述的一种对蚕丝接枝改性的方法，其特征在于：步骤A之前还包括前处理步骤，待改性蚕丝先进行脱胶处理，然后分别用乙醇和水冲洗，之后35～65℃干燥8～24小时。
7.根据权利要求6所述的一种对蚕丝接枝改性的方法，其特征在于：前处理步骤中，脱胶处理采用皂碱法脱胶处理，碱液pH值为9-10.5。
CN201510762649.1A 2015-11-11 2015-11-11 一种对蚕丝接枝改性的方法 Active CN105297440B (zh)