CN105295673A - Bopet导电抗静电在线涂覆液、bopet膜及在线涂覆工艺 - Google Patents
Bopet导电抗静电在线涂覆液、bopet膜及在线涂覆工艺 Download PDFInfo
- Publication number
- CN105295673A CN105295673A CN201510652219.4A CN201510652219A CN105295673A CN 105295673 A CN105295673 A CN 105295673A CN 201510652219 A CN201510652219 A CN 201510652219A CN 105295673 A CN105295673 A CN 105295673A
- Authority
- CN
- China
- Prior art keywords
- bopet
- antistatic
- online coating
- coating liquid
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种BOPET导电抗静电在线涂覆液、BOPET膜及在线涂覆工艺，本BOPET导电抗静电在线涂覆液包括下列重量份数的物质：导电聚合物溶液10～75份，异丙醇5～42份，水性抗拉树脂6～15份；通过本发明的BOPET导电抗静电在线涂覆液的使用，实现了BOPET膜的在线涂覆，使Pet双向拉伸和涂覆在同一条生产线上一次完成，减少了生产工序，降低了生产成本。
Description
技术领域
本发明涉及一种BOPET薄膜，尤其涉及一种BOPET导电抗静电在线涂覆液BOPET膜及在线涂覆工艺。
背景技术
BOPET(双向拉伸PET)膜表面涂覆分在线涂和离线涂。在线涂是Pet流延膜经纵向拉伸后，在其表面涂覆，经过横向拉伸定型，BOPET基膜和表面涂覆在线一次完成；离线涂覆是Pet双向拉伸和涂覆不在同一条生产线上一次完成，需多一次生产工序。
由于BOPET膜的用途不同，有的需要抗静电，有的甚至要达到导电级别。抗静电剂主要有离子型、非离子型和聚合物型。离子型和非离子型一般是通过吸收空气中水分来达到抗静电的目的，这两种类型的抗静剂在BOPET上涂覆后，表面电阻率一般在109～1010级，最低不会低于108级，达不到导电的级别，正因为这两种抗静电剂都需要吸收空气中的水分，所以其抗静电效果跟温度和湿度有关，在不同的环境下会产生不一样的效果，放置时间长了会衰减到无抗静电效果。聚合物导电剂在BOPET表面涂覆后，表面电阻率可在104～108之间调节，这种材料不是通过吸收水分来抗静电，而是在BOPET表面形成不同密度的导电网，所以它性能稳定，可以长时间在不同环境下存放。但是这种导电液只能做离线涂，不能做拉伸，否则形成的导电网会被拉断，完全失去抗静电作用。本发明是通过在导电聚合物里加入抗拉树脂作为载体，使之能承受3.5倍的拉伸，使形成的导电网不断裂。
发明内容
本发明的目的是提供一种BOPET导电抗静电在线涂覆液，以一次性完成对BOPET膜进行涂覆、拉伸工序。
为了解决上述技术问题，本发明提供了一种BOPET导电抗静电在线涂覆液，包括下列重量份数的物质：
进一步，所述导电聚合物溶液采用PEDOT。
进一步，所述抗拉树脂包括丙烯酸树脂、聚氨酯树脂和聚酯树脂的一种或几种。
进一步，所述BOPET导电抗静电在线涂覆液还包括下列重量份数的物质：0.1～0.8份的流平剂。
进一步，所述流平剂为丙烯酸类流平剂、氟类流平剂的一种或几种。
又一方面，本发明还提供了一种BOPET膜，以解决BOPET膜在长时间存放，抗静电性能减弱的技术问题。
所述BOPET膜的表面涂覆有所述的BOPET导电抗静电在线涂覆液。
第三方面，本发明还提供了一种BOPET膜的在线涂覆工艺。
通过在线涂覆工艺，克服了传统的BOPET膜涂覆只能做离线涂覆，不能做拉伸的技术问题，避免了由于在拉伸过程中导电网拉断，造成抗静电效果失去。
所述BOPET膜的在线涂覆工艺，包括如下步骤：
步骤S1，在储液槽里注入BOPET导电抗静电在线涂覆液；
步骤S2，将Pet流延膜经纵向拉伸后，在其表面涂覆，并经过横向拉伸定型，以制成BOPET膜。
进一步，在Pet流延膜经纵向拉伸后，在其表面涂覆的方法包括：
步骤S21，调整喷头和刮液棒，以平行于BOPET膜表面；
步骤S22，打开涂覆液供给泵及喷涂阀，所述BOPET导电抗静电在线涂覆液从喷头口喷出，并调节其喷涂流量为1～1.2m3/h；
步骤S23，启动刮液棒，调整刮液棒的转速使之与薄膜线速度接近后，即开始涂覆。
进一步，所述横向拉伸为原宽度的3.5倍。
本发明的有益效果是，(1)通过本发明的BOPET导电抗静电在线涂覆液的使用，实现了BOPET膜的在线涂覆，使Pet双向拉伸和涂覆在同一条生产线上一次完成，减少了生产工序，降低了生产成本；(2)本BOPET膜适于长时间存放，具有表面电阻率低，稳定性越好的优点；(3)通过本发明的在线涂覆工艺，克服了传统的BOPET膜涂覆只能做离线涂覆，不能做拉伸的技术问题，避免了由于在拉伸过程中导电网拉断，造成抗静电效果失去，减少了生产工序和节约了生产成本。
附图说明
下面结合附图和实施例对本发明进一步说明。
图1是本发明的BOPET膜的在线涂覆工艺的步骤流程图；
图2是本发明的在BOPET膜表面涂覆的步骤流程图。
具体实施方式
现在结合附图对本发明作进一步详细的说明。这些附图均为简化的示意图，仅以示意方式说明本发明的基本结构，因此其仅显示与本发明有关的构成。
实施例1
本发明提供了一种BOPET导电抗静电在线涂覆液，其特征在于，包括下列重量份数的物质：
所述水性抗拉树脂包括丙烯酸树脂、聚氨酯树脂和聚酯树脂的一种或几种。
所述导电聚合物溶液采用聚噻吩(PEDOT)。
加入水性抗拉树脂一种或几种后，经涂覆和3.5倍拉伸后，表面电阻率在108级以下。
进一步，为了避免在BOPET的表面产生了均衡的纵向细条纹，提高涂覆液流平性。在实验中发现稀释涂覆液和加热涂覆液来增加流动性，虽然条纹可以浅一点，但都无法消除纵向条纹，这说明抗静电剂和抗拉树脂不能完全均匀分散，在BOPET薄膜表面存在一定的排斥性，通过添加流平剂增加底膜的润湿性，使表面张力趋向平衡，有效的避免在BOPET的表面产生了纵向细条纹。
具体的，所述BOPET导电抗静电在线涂覆液还包括下列重量份数的物质：0.1～0.8份的流平剂。
所述流平剂为丙烯酸类流平剂、氟类流平剂的一种或几种。
经过测试，在涂覆液中加入一种或两种流平剂搅拌后，在线涂覆经3.5倍拉伸，BOPET薄膜表面没有产生纵向条纹，并且检测表面电阻率在104～108之间可调。
下面用多个实施例，采用不同的组分及用量(其中用量为重量份数)，来说明本发明的BOPET导电抗静电在线涂覆液。
表1为实施例一至实施例八的具体组分含量份数表
实施例2
在实施例1基础上，本发明还提供了一种BOPET膜，即所述BOPET膜的表面涂覆有所述的BOPET导电抗静电在线涂覆液。
表2为本发明的BOPET膜的表面电阻率变化表
上述实施例二、实施例四、实施例五和实施例八的样品在常温常湿下保留六个月做跟踪检测，每半个月分别检测表面电阻率变化情况，前四个月基本在104～108之间和后两个月104～1010之间，说明原来表面电阻率越低，它的稳定性越好，保存时间更长，抗静电效果好；原来表面电阻率大的，它的稳定性会稍差，随着时间增加会有慢慢的衰减，但总体比离子和非离子型抗静电剂的稳定性要好、且性能稳定。
并且，本BOPET膜通过改变导电聚合物溶液(PEDOT)的含量，在满足在线涂覆的基础上，实现不同抗静电等级的调节。
实施例3
如图1所示，在实施例1和实施例2基础上，所述BOPET膜的生产工艺，包括如下步骤：
步骤S1，在储液槽里注入BOPET导电抗静电在线涂覆液；
步骤S2，将Pet流延膜经纵向拉伸后，在其表面涂覆，并经过横向拉伸定型，以制成BOPET膜。
进一步，如图2所示，在Pet流延膜经纵向拉伸后，在其表面涂覆的方法包括：
步骤S21，调整喷头和刮液棒，以平行于BOPET膜表面，并使所述喷头和刮液棒分别与BOPET膜的垂直距离相等；
步骤S22，打开涂覆液供给泵及喷涂阀，排除管道和喷头里的空气，使BOPET导电抗静电在线涂覆液从喷头口喷出，并调节其喷涂流量为1～1.2m3/h；
步骤S23，启动刮液棒，调整刮液棒的转速使之与薄膜线速度接近后，即开始涂覆。
所述BOPET导电抗静电在线涂覆液为实施例1所述的BOPET导电抗静电在线涂覆液。
进一步，所述横向拉伸为原宽度的3.5倍。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (10)
1.一种BOPET导电抗静电在线涂覆液，其特征在于，包括下列重量份数的物质：
2.根据权利要求1所述的BOPET导电抗静电在线涂覆液，其特征在于，所述导电聚合物溶液采用PEDOT。
3.根据权利要求2所述的BOPET导电抗静电在线涂覆液，其特征在于，所述水性抗拉树脂包括丙烯酸树脂、聚氨酯树脂和聚酯树脂的一种或几种。
4.根据权利要求3所述的BOPET导电抗静电在线涂覆液，其特征在于，所述BOPET导电抗静电在线涂覆液还包括下列重量份数的物质：0.1～0.8份的流平剂。
5.根据权利要求4所述的BOPET导电抗静电在线涂覆液，其特征在于，所述流平剂为丙烯酸类流平剂、氟类流平剂的一种或几种。
6.一种BOPET膜，其特征在于，所述BOPET膜的表面涂覆有如权利要求1至5任一所述的BOPET导电抗静电在线涂覆液。
7.一种BOPET膜的在线涂覆工艺，包括如下步骤：
步骤S1，在储液槽里注入BOPET导电抗静电在线涂覆液；
步骤S2，将Pet流延膜经纵向拉伸后，在其表面涂覆，并经过横向拉伸定型，以制成BOPET膜。
8.根据权利要求7所述的在线涂覆工艺，其特征在于，在Pet流延膜经纵向拉伸后，在其表面涂覆的方法包括：
步骤S21，调整喷头和刮液棒，以平行于膜表面；
步骤S22，打开涂覆液供给泵及喷涂阀，所述BOPET导电抗静电在线涂覆液从喷头口喷出，并调节其喷涂流量为1～1.2m3/h；
步骤S23，启动刮液棒，调整刮液棒的转速使之与薄膜线速度接近后，开始涂覆。
9.根据权利要求8所述的在线涂覆工艺，其特征在于，所述BOPET导电抗静电在线涂覆液为如权利要求1至5任一所述的BOPET导电抗静电在线涂覆液。
10.根据权利要求9所述的在线涂覆工艺，其特征在于，所述横向拉伸为原宽度的3.5倍。