CN105274873A - High temperature levelling agent for textile dyeing and finishing - Google Patents
High temperature levelling agent for textile dyeing and finishing Download PDFInfo
- Publication number
- CN105274873A CN105274873A CN201510805718.2A CN201510805718A CN105274873A CN 105274873 A CN105274873 A CN 105274873A CN 201510805718 A CN201510805718 A CN 201510805718A CN 105274873 A CN105274873 A CN 105274873A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- high temperature
- levelling agent
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high temperature levelling agent for textile dyeing and finishing. The high temperature levelling agent is prepared from 5% of polyester and polyether silicone oil block copolymer with the number-average molecular weight being 30000, 35% of polyethylene glycol monostearate and the balance water. The polyester and polyether silicone oil block copolymer is prepared from, by mass, 3-4 parts of 3-piperazine propyl methyl dimethoxy silane, 1-2 parts of ethylenediamine polyoxyethylene polyoxypropylene block polyether, 7-8 parts of dimethyl terephthalate, 2-3 parts of fatty alcohol ether sodium sulfate, 1-2 parts of dodecyl trimethyl ammonium sulfate, 4-5 parts of polyethylene glycol, 1-2 parts of gamma-glycidyl ether group trimethoxy silane and 6-7 parts of sodium hexametaphosphate. The high temperature levelling agent for textile dyeing and finishing has the finishing effects of fluffing and softening.
Description
Technical field
The present invention relates to textile printing and dyeing high temperature levelling agent.
Background technology
In the dyeing course of silvalin, line or fabric, for impelling even dyeing, not producing the fault such as vitta, color spot often needs to add levelling agent.But existing levelling agent only has even dyeing effect, and does not have other finishing effect.For polyester fiber or its fabric, this just needs after dyeing completes, then carries out the anti-arrangements such as such as antistatic, fluffy softness, and so, make production technology more complicated, cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of textile printing and dyeing high temperature levelling agent, there is fluffy soft-touch finish.
For achieving the above object, technical scheme of the present invention is a kind of textile printing and dyeing high temperature levelling agent of design, by number-average molecular weight be the polyester polyether silicone oil block copolymer 5% of 30000, the water of polyethylene glycol mono stearate 35% and surplus forms;
The composition of raw materials of described polyester polyether silicone oil block copolymer is: 3 ~ 4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1 ~ 2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7 ~ 8 parts by mass dimethyl terephthalate (DMT)s, 2 ~ 3 parts by mass fatty alcohol-ether sodium sulfates, 1 ~ 2 parts by mass trimethyl ammonium sulfate, 4 ~ 5 parts by mass polyethylene glycol, 1 ~ 2 parts by mass γ-glycidyl ether trimethoxy silane, 6 ~ 7 parts by mass calgons.
Preferably, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 8 parts by mass dimethyl terephthalate (DMT)s, 3 parts by mass fatty alcohol-ether sodium sulfates, 2 parts by mass trimethyl ammonium sulfate, 5 parts by mass polyethylene glycol, 2 parts by mass γ-glycidyl ether trimethoxy silane, 7 parts by mass calgons.
Preferably, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 3 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7 parts by mass dimethyl terephthalate (DMT)s, 2 parts by mass fatty alcohol-ether sodium sulfates, 1 parts by mass trimethyl ammonium sulfate, 4 parts by mass polyethylene glycol, 1 parts by mass γ-glycidyl ether trimethoxy silane, 6 parts by mass calgons.
Preferably, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 3.4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1.2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7.8 parts by mass dimethyl terephthalate (DMT)s, 2.3 parts by mass fatty alcohol-ether sodium sulfates, 1.2 parts by mass trimethyl ammonium sulfate, 4.5 parts by mass polyethylene glycol, 1.2 parts by mass γ-glycidyl ether trimethoxy silane, 6.7 parts by mass calgons.
Advantage of the present invention and beneficial effect are: provide a kind of textile printing and dyeing high temperature levelling agent, have fluffy soft-touch finish.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of textile printing and dyeing high temperature levelling agent, by number-average molecular weight be the polyester polyether silicone oil block copolymer 5% of 30000, the water of polyethylene glycol mono stearate 35% and surplus forms;
The composition of raw materials of described polyester polyether silicone oil block copolymer is: 4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 8 parts by mass dimethyl terephthalate (DMT)s, 3 parts by mass fatty alcohol-ether sodium sulfates, 2 parts by mass trimethyl ammonium sulfate, 5 parts by mass polyethylene glycol, 2 parts by mass γ-glycidyl ether trimethoxy silane, 7 parts by mass calgons.
Embodiment 2
A kind of textile printing and dyeing high temperature levelling agent, by number-average molecular weight be the polyester polyether silicone oil block copolymer 5% of 30000, the water of polyethylene glycol mono stearate 35% and surplus forms;
The composition of raw materials of described polyester polyether silicone oil block copolymer is: 3 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7 parts by mass dimethyl terephthalate (DMT)s, 2 parts by mass fatty alcohol-ether sodium sulfates, 1 parts by mass trimethyl ammonium sulfate, 4 parts by mass polyethylene glycol, 1 parts by mass γ-glycidyl ether trimethoxy silane, 6 parts by mass calgons.
Embodiment 3
A kind of textile printing and dyeing high temperature levelling agent, by number-average molecular weight be the polyester polyether silicone oil block copolymer 5% of 30000, the water of polyethylene glycol mono stearate 35% and surplus forms;
The composition of raw materials of described polyester polyether silicone oil block copolymer is: 3.4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1.2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7.8 parts by mass dimethyl terephthalate (DMT)s, 2.3 parts by mass fatty alcohol-ether sodium sulfates, 1.2 parts by mass trimethyl ammonium sulfate, 4.5 parts by mass polyethylene glycol, 1.2 parts by mass γ-glycidyl ether trimethoxy silane, 6.7 parts by mass calgons.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. textile printing and dyeing high temperature levelling agent, is characterized in that, by number-average molecular weight be the polyester polyether silicone oil block copolymer 5% of 30000, the water of polyethylene glycol mono stearate 35% and surplus forms;
The composition of raw materials of described polyester polyether silicone oil block copolymer is: 3 ~ 4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1 ~ 2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7 ~ 8 parts by mass dimethyl terephthalate (DMT)s, 2 ~ 3 parts by mass fatty alcohol-ether sodium sulfates, 1 ~ 2 parts by mass trimethyl ammonium sulfate, 4 ~ 5 parts by mass polyethylene glycol, 1 ~ 2 parts by mass γ-glycidyl ether trimethoxy silane, 6 ~ 7 parts by mass calgons.
2. textile printing and dyeing high temperature levelling agent according to claim 1, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 8 parts by mass dimethyl terephthalate (DMT)s, 3 parts by mass fatty alcohol-ether sodium sulfates, 2 parts by mass trimethyl ammonium sulfate, 5 parts by mass polyethylene glycol, 2 parts by mass γ-glycidyl ether trimethoxy silane, 7 parts by mass calgons.
3. textile printing and dyeing high temperature levelling agent according to claim 1, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 3 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7 parts by mass dimethyl terephthalate (DMT)s, 2 parts by mass fatty alcohol-ether sodium sulfates, 1 parts by mass trimethyl ammonium sulfate, 4 parts by mass polyethylene glycol, 1 parts by mass γ-glycidyl ether trimethoxy silane, 6 parts by mass calgons.
4. textile printing and dyeing high temperature levelling agent according to claim 1, the composition of raw materials of described polyester polyether silicone oil block copolymer is: 3.4 parts by mass 3-gamma-piperazinepropyl methyldimethoxysilanes, 1.2 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 7.8 parts by mass dimethyl terephthalate (DMT)s, 2.3 parts by mass fatty alcohol-ether sodium sulfates, 1.2 parts by mass trimethyl ammonium sulfate, 4.5 parts by mass polyethylene glycol, 1.2 parts by mass γ-glycidyl ether trimethoxy silane, 6.7 parts by mass calgons.