CN105268246A - Drinking water energy-saving environment-friendly filter core and preparation method thereof - Google Patents
Drinking water energy-saving environment-friendly filter core and preparation method thereof Download PDFInfo
- Publication number
- CN105268246A CN105268246A CN201410319097.2A CN201410319097A CN105268246A CN 105268246 A CN105268246 A CN 105268246A CN 201410319097 A CN201410319097 A CN 201410319097A CN 105268246 A CN105268246 A CN 105268246A
- Authority
- CN
- China
- Prior art keywords
- filter core
- drinking water
- water energy
- preparation
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a drinking water energy-saving environment-friendly filter core and a preparation method thereof. According to the invention, raw materials of diatomaceous earth, kaolin, plant fiber, melamine polyester, wood powder, a binder, water, carbon powder, straw ash, seashell powder, natural zeolite, and chopped hair are mixed and stirred according to a certain weight ratio; the mixture is subjected to cast molding or compaction molding; and an obtained product is dried and then calcined under a temperature of 900-1300 DEG C, such that the drinking water energy-saving environment-friendly filter core is obtained. The preparation method provided by the invention is simple; the formula is reasonable; cost is low; and the prepared drinking water energy-saving environment-friendly filter core has good water resistance and wear resistance.
Description
Technical field
The invention belongs to drinking water environmental protection filtration art, particularly relate to a kind of drinking water energy-conserving and environment-protective filter core and preparation method thereof.
Background technology
As everyone knows, the filter opening of traditional heated type filtering drinking water energy-conserving and environment-protective filter core is all superfine micro-, and the distribution in high density, therefore for the area that water turbidity is higher, especially remote mountain areas, rural area, comparatively coarse granule impurity obstruction such as easy as rolling off a log round mud or iron rust etc., and affect its filtration water yield, therefore usually all the low-density filter core that more than together or one has larger filter opening is set again before this high density filter core, preposition filter core is utilized to remove thicker thick impurity in water in advance, mud, suspended material etc., so as to protecting rearmounted activated carbon cartridge, the high density filter cores such as ion exchange resin filter core or pellicle (R0) filter core, make it unlikely coating and affect the functions such as the clean or absorption of its filter by thicker thick impurity.Its major defect is: conventional preposition filter core, it is nothing more than being be made up of materials such as PP plastic cement, fiber, knitting wool, therefore namely must abandon after obstruction, cannot again rinse for reusing, not only expendable is large for it, causes manpower and materials to bear, and owing to not meeting environmental protection condition, decomposition cannot be completed at short notice, so that all becoming environment high pollution material in the future, not meet economic environmental requirement.
Summary of the invention
In order to solve shortcomings and deficiencies of the prior art, the object of the present invention is to provide a kind of drinking water energy-conserving and environment-protective filter core and preparation method thereof.Preparation method of the present invention is simple, and rationally, cost is low for formula, and obtained drinking water energy-conserving and environment-protective filter core is heat-resisting, excellent adsorption.
The present invention adopts following technical scheme to achieve these goals:
Drinking water energy-conserving and environment-protective filter core, is characterized in that the weight portion of its constitutive material is: 10-15 part sent out by diatomite 30-40 part, kaolin 10-15 part, string 15-25 part, melamine polyester 20-30 part, wood powder 6-9 part, plant adhesive 6-8 part, water 40-50 part, carbon dust 10-15 part, stalk ashes 3-5 part, seashell powder 10-15 part, natural zeolite 10-15 part, broken wool.
The preparation method of described drinking water energy-conserving and environment-protective filter core, it is characterized in that: take each constitutive material by the weight portion of constitutive material, after mix and blend through injection forming or pressed compact shaping, 900-1300 DEG C of calcining after drying, obtain this drinking water energy-conserving and environment-protective filter core.
Beneficial effect of the present invention:
Preparation method of the present invention is simple, and rationally, cost is low for formula, and obtained drinking water energy-conserving and environment-protective filter core is heat-resisting, wearability good.
Detailed description of the invention
Embodiment 1:
Drinking water energy-conserving and environment-protective filter core, the weight portion of its constitutive material is: have 30 parts, diatomite, kaolin 10 parts,
15 parts, string, melamine polyester 20 parts, wood powder 7 parts, plant adhesive CMC7 part, 45 parts, water, carbon dust 12 parts, 4 parts, stalk ashes, 12 parts, seashell powder, natural zeolite 12 parts, broken wool send out 12 parts.The preparation method of drinking water energy-conserving and environment-protective filter core: take each constitutive material by the weight portion of constitutive material, after mix and blend through injection forming or pressed compact shaping, 900-1300 DEG C of calcining after drying, obtain this drinking water energy-conserving and environment-protective filter core.
The Static Water adsorbance 18.2% of obtained drinking water energy-conserving and environment-protective filter core; Compression strength 4875N; Compatibility 0.0093%.
Embodiment 2:
Drinking water energy-conserving and environment-protective filter core, the weight portion of its constitutive material is: have 40 parts, diatomite, kaolin 15 parts, 25 parts, string, melamine polyester 30 parts, wood powder 6 parts, plant adhesive CMC6 part, 50 parts, water, carbon dust 10 parts, 3 parts, stalk ashes, 10 parts, seashell powder, natural zeolite 10 parts, broken wool to send out 10 parts.
The preparation method of drinking water energy-conserving and environment-protective filter core: take each constitutive material by the weight portion of constitutive material, after mix and blend through injection forming or pressed compact shaping, 900-1300 DEG C of calcining after drying, obtain this drinking water energy-conserving and environment-protective filter core.
The Static Water adsorbance 18.4% of obtained drinking water energy-conserving and environment-protective filter core; Compression strength 4945N; Compatibility 0.0089%.
Claims (2)
1. a drinking water energy-conserving and environment-protective filter core, is characterized in that the weight portion of its constitutive material is: 10-15 part sent out by diatomite 30-40 part, kaolin 10-15 part, string 15-25 part, melamine polyester 20-30 part, wood powder 6-9 part, plant adhesive 6-8 part, water 40-50 part, carbon dust 10-15 part, stalk ashes 3-5 part, seashell powder 10-15 part, natural zeolite 10-15 part, broken wool.
2. the preparation method of a drinking water energy-conserving and environment-protective filter core as claimed in claim 1, it is characterized in that: take each constitutive material by the weight portion of constitutive material, after mix and blend through injection forming or pressed compact shaping, 900-1300 DEG C of calcining after drying, obtain this drinking water energy-conserving and environment-protective filter core.