CN104261754B - Wall heat insulation material that a kind of building materials waste residue is produced and preparation method thereof - Google Patents
Wall heat insulation material that a kind of building materials waste residue is produced and preparation method thereof Download PDFInfo
- Publication number
- CN104261754B CN104261754B CN201410436226.6A CN201410436226A CN104261754B CN 104261754 B CN104261754 B CN 104261754B CN 201410436226 A CN201410436226 A CN 201410436226A CN 104261754 B CN104261754 B CN 104261754B
- Authority
- CN
- China
- Prior art keywords
- waste residue
- building materials
- heat insulation
- add
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses the wall heat insulation material that a kind of building materials waste residue is produced, it is to be made by the raw material of following weight parts: modification building materials waste residue 5-15, white cement 80-100, float stone 70-90, attapulgite powder 10-15, bamboo charcoal powder 2-4, monoalky lether phosphate 1-2, Silicone acrylic emulsion 10-15, sodium oxalate 1-2, sweet mellow wine 1-3, maltitol 0.5-1, hydroxypropyl methyl cellulose ether 2-4; Wall heat insulation material of the present invention is rationally recycled building materials waste residue and is produced wall heat insulation material, is ensureing, under the prerequisite of heat insulating effect, to reach the object of energy-conserving and environment-protective.
Description
Technical field
The present invention relates to building material field, be specifically related to wall heat insulation material of a kind of building materials waste residue production and preparation method thereof.
Background technology
Wall heat insulation material is as affecting key factor of building energy conservation, and its exploitation and application have more and more been subject to the generally attention of countries in the world. Reasonable development wall heat insulation material, the waste residue waste material that the building industry that is effectively recycled produces, can save materials for wall in a large number, can reach and economize on resources again, reduces the object of environmental pollution, meets the policy of national energy-saving environmental protection.
Summary of the invention
The object of this invention is to provide the wall heat insulation material that a kind of building materials waste residue is produced.
The present invention is achieved by the following technical solutions:
The wall heat insulation material that building materials waste residue is produced, it is to be made by the raw material of following weight parts:
Modification building materials waste residue 5-15, white cement 80-100, float stone 70-90, attapulgite powder 10-15, bamboo charcoal powder 2-4, monoalky lether phosphate 1-2, Silicone acrylic emulsion 10-15, sodium oxalate 1-2, sweet mellow wine 1-3, maltitol 0.5-1, hydroxypropyl methyl cellulose ether 2-4;
Modification building materials waste residue is made up of the raw material of following weight portion:
Ceramic waste residue 5-10, marble waste residue 10-15, boron gypsum 1-2, atoleine 0.5-1.5, oleic acid 0.2-0.5, triisopropanolamine 1-2, sodium tartrate 1-3, aluminate coupling agent 0.2-0.5;
The preparation method of modification building materials waste residue is:
800-1000 DEG C of calcining 2-4h after ceramic waste residue, marble waste residue and boron gypsum are mixed, after cooling, add appropriate 4-6% acetum, add triisopropanolamine and sodium tartrate, 200-400r/min stirs 1-2h, after dry, grind evenly, cross 50-100 mesh sieve, then add aluminate coupling agent, 100-150 DEG C, 400-600r/min stirs 20-40min, add atoleine and oleic acid, under similarity condition, stir 20-40min, to obtain final product;
A preparation method for the wall heat insulation material that building materials waste residue is produced, comprises the following steps:
(1) Silicone acrylic emulsion, monoalky lether phosphate and hydroxypropyl methyl cellulose ether are mixed to rear 800-1000r/min and stir 15-30min, after spraying is dry, obtain active powder;
(2) attapulgite powder and bamboo charcoal powder are mixed after 400-600 DEG C of calcining 1-2h, add sweet mellow wine, maltitol and sodium oxalate after cooling, after mixing, grind evenly, cross 100-200 mesh sieve, add active powder and all the other raw materials, packing after stirring, to obtain final product.
Advantage of the present invention is:
1. rationally recycle building materials waste residue and produce wall heat insulation material, economize on resources, reduce the hidden danger of environmental pollution and ecological disruption;
2. water-fast, good corrosion resistance, long service life, good weatherability;
3. constant product quality, is applicable to multiple environment for use.
Detailed description of the invention
Non-limiting examples of the present invention is as follows:
Embodiment 1
The wall heat insulation material that building materials waste residue is produced, is prepared from by the component raw material of following weight (kg):
Modification building materials waste residue 10, white cement 90, float stone 80, attapulgite powder 12, bamboo charcoal powder 3, monoalky lether phosphate 1.5, Silicone acrylic emulsion 12, sodium oxalate 1.5, sweet mellow wine 2, maltitol 0.8, hydroxypropyl methyl cellulose ether 3;
Wherein, modification building materials waste residue is made up of the raw material of following weight (kg):
Ceramic waste residue 7, marble waste residue 12, boron gypsum 1.5, atoleine 1, oleic acid 0.3, triisopropanolamine 1.5, sodium tartrate 2, aluminate coupling agent 0.4;
The preparation method of modification building materials waste residue:
Ceramic waste residue, marble waste residue and boron gypsum are mixed to rear 800 DEG C of calcining 3h, after cooling, add appropriate 4% acetum, add triisopropanolamine and sodium tartrate, 200r/min stirs 2h, after dry, grind evenly, cross 100 mesh sieves, then add aluminate coupling agent, 100 DEG C, 600r/min stirs 30min, add atoleine and oleic acid, under similarity condition, stir 30min, to obtain final product.
The preparation method of the wall heat insulation material that building materials waste residue is produced comprises the following steps:
(1) Silicone acrylic emulsion, monoalky lether phosphate and hydroxypropyl methyl cellulose ether are mixed to rear 1000r/min and stir 15min, after spraying is dry, obtain active powder;
(2) attapulgite powder and bamboo charcoal powder are mixed to rear 400 DEG C of calcining 2h, add sweet mellow wine, maltitol and sodium oxalate after cooling, after mixing, grind evenly, cross 100 mesh sieves, add active powder and all the other raw materials, packing after stirring, to obtain final product.
Embodiment is dry powder material, when use, need add water at the construction field (site) and be modulated into slip, can construct.
Carry out properties of product test according to DB34/T1279-2010, the test result of above-mentioned enforcement is as follows:
Dry apparent density (kg/m3):283;
Linear shrinkage (%): 0.15;
Compression strength (MPa): 0.97;
Adhesion strength (KPa): 85;
Thermal conductivity factor (w/m ﹒ k): 0.062;
Coefficient of softing: 0.63.
Claims (1)
1. the wall heat insulation material that building materials waste residue is produced, is characterized in that, it is to be made by the raw material of following weight parts: modification building materials waste residue 5-15, white cement 80-100, float stone 70-90, attapulgite powder 10-15, bamboo charcoal powder 2-4, monoalky lether phosphate 1-2, Silicone acrylic emulsion 10-15, sodium oxalate 1-2, sweet mellow wine 1-3, maltitol 0.5-1, hydroxypropyl methyl cellulose ether 2-4; Described modification building materials waste residue is made up of the raw material of following weight portion: ceramic waste residue 5-10, marble waste residue 10-15, boron gypsum 1-2, atoleine 0.5-1.5, oleic acid 0.2-0.5, triisopropanolamine 1-2, sodium tartrate 1-3, aluminate coupling agent 0.2-0.5;
The preparation method of described modification building materials waste residue is: 800-1000 DEG C of calcining 2-4h after ceramic waste residue, marble waste residue and boron gypsum are mixed, after cooling, add appropriate 4-6% acetum, add triisopropanolamine and sodium tartrate, 200-400r/min stirs 1-2h, after dry, grind evenly, cross 50-100 mesh sieve, then add aluminate coupling agent, 100-150 DEG C, 400-600r/min stirs 20-40min, add atoleine and oleic acid, under similarity condition, stir 20-40min, to obtain final product;
The preparation method of the wall heat insulation material that described a kind of building materials waste residue is produced, comprises the following steps:
(1) Silicone acrylic emulsion, monoalky lether phosphate and hydroxypropyl methyl cellulose ether are mixed to rear 800-1000r/min and stir 15-30min, after spraying is dry, obtain active powder;
(2) attapulgite powder and bamboo charcoal powder are mixed after 400-600 DEG C of calcining 1-2h, add sweet mellow wine, maltitol and sodium oxalate after cooling, after mixing, grind evenly, cross 100-200 mesh sieve, add active powder and all the other raw materials, packing after stirring, to obtain final product.