CN105256573A - Production technology of sandwich mesh fabric - Google Patents
Production technology of sandwich mesh fabric Download PDFInfo
- Publication number
- CN105256573A CN105256573A CN201510804309.0A CN201510804309A CN105256573A CN 105256573 A CN105256573 A CN 105256573A CN 201510804309 A CN201510804309 A CN 201510804309A CN 105256573 A CN105256573 A CN 105256573A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- production technology
- stir
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology of sandwich mesh fabric. The production technology comprises the following steps: (1) adding 2.3 parts by mass of ethylenediamine polyoxyethylene polypropylene oxide block polyether, 2-3 parts by mass of calcium bicarbonate and 2.6 parts by mass of sodium polyacrylate to 10.3 parts by mass of deionized water and stirring the raw materials evenly; (2) sequentially adding 2.5 parts by mass of magnesium chloride and 1.3 parts by mass of butyl ricinoleate sodium sulfate, and further stirring until the raw materials are fully mixed evenly to prepare a finishing liquid; and (3) carrying out padding treatment on the fabric in the finishing liquid and carrying out constant-temperature drying. According to the production technology of the sandwich mesh fabric, disclosed by the invention, the finished fabric has washing durability and excellent antibacterial property and antifouling property.
Description
Technical field
The present invention relates to the production technology of sandwich eyelet fabric.
Background technology
The wash durability of existing fabric, antibacterial and antifouling property all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of production technology of sandwich eyelet fabric, the fabric after its arrangement is water-fastness, and has excellent antibacterial and antifouling property.
For achieving the above object, technical scheme of the present invention designs a kind of production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 ~ 3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2.3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Advantage of the present invention and beneficial effect are: the production technology providing a kind of sandwich eyelet fabric, and the fabric after its arrangement is water-fastness, and has excellent antibacterial and antifouling property.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
The production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Embodiment 2
The production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
Embodiment 3
The production technology of sandwich eyelet fabric, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2.3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. the production technology of sandwich eyelet fabric, is characterized in that, comprises the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 ~ 3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
2. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
3. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.
4. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) 2.3 parts by mass ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2.3 parts by mass calcium bicarbonates, 2.6 parts by mass Sodium Polyacrylates are dropped in 10.3 parts by mass deionized waters, stir;
2) add 2.5 parts by mass magnesium chlorides, 1.3 parts by mass castor oil acid butyl ester sodium sulphate more successively, continue to stir, to fully mixing, obtained dressing liquid;
3) fabric is padded process in dressing liquid, constant temperature drying.