CN104213409A - Production method of towels - Google Patents

Abstract

The invention discloses a production method of towels. The production method comprises the following steps: (1) weaving cloth; (2) mixing 2-3 parts of block ethanediamine-polyoxyethylene-polyoxypropylene polyether, 1-2 parts of benzyl alcohol, 2-3 parts of triethanolamine and 2-3 parts of fluoro-silicon resin, then, slowly adding 1-2 parts of sucrose fatty acid ester, 1-2 parts of ethyl acetate, 2-3 parts of arabic gum powder, 2-3 parts of sodium polyacrylate and 150 parts of butanol simultaneously, feeding all the materials within 35-40 minutes, and continuously mixing for 1-2 hours to obtain an impregnation solution; and (3) performing padding treatment on the towels in the impregnation solution under the pressure of 1-2MPa until the take-up rate is in the range of 60-65%, and then drying at 145-150 DEG C for 1-2 hours. The towels produced by use of the production method of the towels have excellent water resistance.

Description

The production method of towel

Technical field

The present invention relates to the production method of towel.

Background technology

Towel conventional at present, resistance to water is poor.

Summary of the invention

The object of the present invention is to provide a kind of production method of towel, its towel produced has good resistance to water.

For achieving the above object, technical scheme of the present invention designs a kind of production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 2 ~ 3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 ~ 2 part of phenmethylol, 2 ~ 3 parts of triethanolamines, 2 ~ 3 parts of fluorine silicon resin mixing, then slowly add 1 ~ 2 part of sucrose fatty ester, 1 ~ 2 part of ethyl acetate, 2 ~ 3 parts of gum arabic powder, 2 ~ 3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 35 ~ 40 minutes complete, continue mixing 1 ~ 2 hour, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1 ~ 2MPa, liquid carrying rate 60 ~ 65%, dry 1 ~ 2 hour at 145 ~ 150 DEG C.

Preferably, the production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 2.3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.5 parts of phenmethylols, 2.3 parts of triethanolamines, 2.3 parts of fluorine silicon resin mixing, then slowly add 1.5 parts of sucrose fatty esters, 1.5 parts of ethyl acetate, 2.3 parts of gum arabic powder, 2.3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 37 minutes complete, continue mixing 1.5 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1.5MPa, liquid carrying rate 62%, dry 1.5 hours at 148 DEG C.

Preferably, the production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts of phenmethylols, 3 parts of triethanolamines, 3 parts of fluorine silicon resin mixing, then slowly add 2 parts of sucrose fatty esters, 2 parts of ethyl acetate, 3 parts of gum arabic powder, 3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 2MPa, liquid carrying rate 65%, dry 2 hours at 150 DEG C.

Preferably, the production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 2 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 part of phenmethylol, 2 parts of triethanolamines, 2 parts of fluorine silicon resin mixing, then slowly add 1 part of sucrose fatty ester, 1 part of ethyl acetate, 2 parts of gum arabic powder, 2 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 35 minutes complete, continue mixing 1 hour, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1MPa, liquid carrying rate 60%, dry 1 hour at 145 DEG C.

Advantage of the present invention and beneficial effect are: the production method providing a kind of towel, and its towel produced has good resistance to water.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

Embodiment 1

The production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 2.3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.5 parts of phenmethylols, 2.3 parts of triethanolamines, 2.3 parts of fluorine silicon resin mixing, then slowly add 1.5 parts of sucrose fatty esters, 1.5 parts of ethyl acetate, 2.3 parts of gum arabic powder, 2.3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 37 minutes complete, continue mixing 1.5 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1.5MPa, liquid carrying rate 62%, dry 1.5 hours at 148 DEG C.

Embodiment 2

The production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts of phenmethylols, 3 parts of triethanolamines, 3 parts of fluorine silicon resin mixing, then slowly add 2 parts of sucrose fatty esters, 2 parts of ethyl acetate, 3 parts of gum arabic powder, 3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 2MPa, liquid carrying rate 65%, dry 2 hours at 150 DEG C.

Embodiment 3

The production method of towel, comprises the steps:

1) weave cotton cloth;

2) by 2 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 part of phenmethylol, 2 parts of triethanolamines, 2 parts of fluorine silicon resin mixing, then slowly add 1 part of sucrose fatty ester, 1 part of ethyl acetate, 2 parts of gum arabic powder, 2 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 35 minutes complete, continue mixing 1 hour, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1MPa, liquid carrying rate 60%, dry 1 hour at 145 DEG C.

 

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (4)

1. the production method of towel, is characterized in that, comprises the steps:

1) weave cotton cloth;

2) by 2 ~ 3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 ~ 2 part of phenmethylol, 2 ~ 3 parts of triethanolamines, 2 ~ 3 parts of fluorine silicon resin mixing, then slowly add 1 ~ 2 part of sucrose fatty ester, 1 ~ 2 part of ethyl acetate, 2 ~ 3 parts of gum arabic powder, 2 ~ 3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 35 ~ 40 minutes complete, continue mixing 1 ~ 2 hour, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1 ~ 2MPa, liquid carrying rate 60 ~ 65%, dry 1 ~ 2 hour at 145 ~ 150 DEG C.

2. the production method of towel according to claim 1, is characterized in that, comprises the steps:

1) weave cotton cloth;

2) by 2.3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.5 parts of phenmethylols, 2.3 parts of triethanolamines, 2.3 parts of fluorine silicon resin mixing, then slowly add 1.5 parts of sucrose fatty esters, 1.5 parts of ethyl acetate, 2.3 parts of gum arabic powder, 2.3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 37 minutes complete, continue mixing 1.5 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1.5MPa, liquid carrying rate 62%, dry 1.5 hours at 148 DEG C.

3. the production method of towel according to claim 1, is characterized in that, comprises the steps:

1) weave cotton cloth;

2) by 3 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 2 parts of phenmethylols, 3 parts of triethanolamines, 3 parts of fluorine silicon resin mixing, then slowly add 2 parts of sucrose fatty esters, 2 parts of ethyl acetate, 3 parts of gum arabic powder, 3 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 2MPa, liquid carrying rate 65%, dry 2 hours at 150 DEG C.

4. the production method of towel according to claim 1, is characterized in that, comprises the steps:

1) weave cotton cloth;

2) by 2 parts of ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1 part of phenmethylol, 2 parts of triethanolamines, 2 parts of fluorine silicon resin mixing, then slowly add 1 part of sucrose fatty ester, 1 part of ethyl acetate, 2 parts of gum arabic powder, 2 parts of Sodium Polyacrylates, 150 parts of butanols simultaneously, feed intake in 35 minutes complete, continue mixing 1 hour, obtained maceration extract;

3) towel is padded process in maceration extract, pressure 1MPa, liquid carrying rate 60%, dry 1 hour at 145 DEG C.