CN104294589A - Water-repellent finishing method of clothes - Google Patents
Water-repellent finishing method of clothes Download PDFInfo
- Publication number
- CN104294589A CN104294589A CN201410552581.XA CN201410552581A CN104294589A CN 104294589 A CN104294589 A CN 104294589A CN 201410552581 A CN201410552581 A CN 201410552581A CN 104294589 A CN104294589 A CN 104294589A
- Authority
- CN
- China
- Prior art keywords
- parts
- clothes
- water
- hours
- maceration extract
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-repellent finishing method of clothes. The water-repellent finishing method comprises the following steps: (1) mixing 23 parts of water, 1-2 parts of polyethylene glycol distearate, 2-3 parts of acrylic resin, 3-4 parts of polyvinylpyrrolidone and 4-5 parts of triethanolamine, simultaneously slowly adding 7-8 parts of anionic polyacrylamide, 1-2 parts of polyoxyethylene ether, 6-7 parts of an HPC-1 finishing agent, 8-9 parts of dimethylol ethylene urea and 1-2 parts of glycerin monostearate within 40 minutes, and continuously mixing for 2 hours to obtain a steeping liquid; and (2) steeping the clothes into the steeping liquid, and carrying out constant temperature treatment on the clothes at 145 DEG C for 2.5 hours after the clothes are dried, wherein the steeping pressure is 2.5MPa, and the pick-up rate is 73%. The clothes finished by virtue of the water-repellent finishing method have water repellency and good durability.
Description
Technical field
The present invention relates to clothes water-repellent finishing method.
Background technology
Existing clothes water-repellent finishing method, it is bad that water durability refused by its clothes arranged.
Summary of the invention
The object of the present invention is to provide a kind of clothes water-repellent finishing method, its clothes arranged has water repellency, and good endurance.
For achieving the above object, technical scheme of the present invention is a kind of clothes water-repellent finishing method of design, comprises the steps:
1) by 23 parts of water, 1 ~ 2 part of polyethylene glycol stearate diester, 2 ~ 3 parts of acrylic resins, 3 ~ 4 parts of polyvinylpyrrolidones, 4 ~ 5 parts of triethanolamine mixing, then slowly add 7 ~ 8 parts of anionic polyacrylamide, 1 ~ 2 part of polyoxyethylene ether, 6 ~ 7 parts of HPC-1 finishing agents, 8 ~ 9 parts of dihydroxymethyl ethylene ureas, 1 ~ 2 part of glycerin monostearate simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Preferably, clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 1.2 parts of polyethylene glycol stearate diesters, 2.3 parts of acrylic resins, 3.4 parts of polyvinylpyrrolidones, 4.5 parts of triethanolamine mixing, then slowly add 7.8 parts of anionic polyacrylamide, 1.2 parts of polyoxyethylene ether, 6.7 parts of HPC-1 finishing agents, 8.9 parts of dihydroxymethyl ethylene ureas, 1.2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Preferably, clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 2 parts of polyethylene glycol stearate diesters, 3 parts of acrylic resins, 4 parts of polyvinylpyrrolidones, 5 parts of triethanolamine mixing, then slowly add 8 parts of anionic polyacrylamide, 2 parts of polyoxyethylene ether, 7 parts of HPC-1 finishing agents, 9 parts of dihydroxymethyl ethylene ureas, 2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Preferably, clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 1 part of polyethylene glycol stearate diester, 2 parts of acrylic resins, 3 parts of polyvinylpyrrolidones, 4 parts of triethanolamine mixing, then slowly add 7 parts of anionic polyacrylamide, 1 part of polyoxyethylene ether, 6 parts of HPC-1 finishing agents, 8 parts of dihydroxymethyl ethylene ureas, 1 part of glycerin monostearate simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Advantage of the present invention and beneficial effect are: provide a kind of clothes water-repellent finishing method, and its clothes arranged has water repellency, and good endurance.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 1.2 parts of polyethylene glycol stearate diesters, 2.3 parts of acrylic resins, 3.4 parts of polyvinylpyrrolidones, 4.5 parts of triethanolamine mixing, then slowly add 7.8 parts of anionic polyacrylamide, 1.2 parts of polyoxyethylene ether, 6.7 parts of HPC-1 finishing agents, 8.9 parts of dihydroxymethyl ethylene ureas, 1.2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Embodiment 2
Clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 2 parts of polyethylene glycol stearate diesters, 3 parts of acrylic resins, 4 parts of polyvinylpyrrolidones, 5 parts of triethanolamine mixing, then slowly add 8 parts of anionic polyacrylamide, 2 parts of polyoxyethylene ether, 7 parts of HPC-1 finishing agents, 9 parts of dihydroxymethyl ethylene ureas, 2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
Embodiment 3
Clothes water-repellent finishing method, comprises the steps:
1) by 23 parts of water, 1 part of polyethylene glycol stearate diester, 2 parts of acrylic resins, 3 parts of polyvinylpyrrolidones, 4 parts of triethanolamine mixing, then slowly add 7 parts of anionic polyacrylamide, 1 part of polyoxyethylene ether, 6 parts of HPC-1 finishing agents, 8 parts of dihydroxymethyl ethylene ureas, 1 part of glycerin monostearate simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. clothes water-repellent finishing method, is characterized in that, comprises the steps:
1) by 23 parts of water, 1 ~ 2 part of polyethylene glycol stearate diester, 2 ~ 3 parts of acrylic resins, 3 ~ 4 parts of polyvinylpyrrolidones, 4 ~ 5 parts of triethanolamine mixing, then slowly add 7 ~ 8 parts of anionic polyacrylamide, 1 ~ 2 part of polyoxyethylene ether, 6 ~ 7 parts of HPC-1 finishing agents, 8 ~ 9 parts of dihydroxymethyl ethylene ureas, 1 ~ 2 part of glycerin monostearate simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
2. clothes water-repellent finishing method according to claim 1, is characterized in that, comprise the steps:
1) by 23 parts of water, 1.2 parts of polyethylene glycol stearate diesters, 2.3 parts of acrylic resins, 3.4 parts of polyvinylpyrrolidones, 4.5 parts of triethanolamine mixing, then slowly add 7.8 parts of anionic polyacrylamide, 1.2 parts of polyoxyethylene ether, 6.7 parts of HPC-1 finishing agents, 8.9 parts of dihydroxymethyl ethylene ureas, 1.2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
3. clothes water-repellent finishing method according to claim 1, is characterized in that, comprise the steps:
1) by 23 parts of water, 2 parts of polyethylene glycol stearate diesters, 3 parts of acrylic resins, 4 parts of polyvinylpyrrolidones, 5 parts of triethanolamine mixing, then slowly add 8 parts of anionic polyacrylamide, 2 parts of polyoxyethylene ether, 7 parts of HPC-1 finishing agents, 9 parts of dihydroxymethyl ethylene ureas, 2 parts of glycerin monostearates simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.
4. clothes water-repellent finishing method according to claim 1, is characterized in that, comprise the steps:
1) by 23 parts of water, 1 part of polyethylene glycol stearate diester, 2 parts of acrylic resins, 3 parts of polyvinylpyrrolidones, 4 parts of triethanolamine mixing, then slowly add 7 parts of anionic polyacrylamide, 1 part of polyoxyethylene ether, 6 parts of HPC-1 finishing agents, 8 parts of dihydroxymethyl ethylene ureas, 1 part of glycerin monostearate simultaneously, feed intake in 40 minutes complete, continue mixing 2 hours, obtained maceration extract;
2) clothes is padded process in maceration extract, pressure 2.5MPa, liquid carrying rate 73%, after oven dry by clothes 145 DEG C of constant temperature 2.5 hours.