CN105255266A - Internal wall mercerizing latex paint based on HUER thickening agents, and production process thereof - Google Patents
Internal wall mercerizing latex paint based on HUER thickening agents, and production process thereof Download PDFInfo
- Publication number
- CN105255266A CN105255266A CN201410332393.6A CN201410332393A CN105255266A CN 105255266 A CN105255266 A CN 105255266A CN 201410332393 A CN201410332393 A CN 201410332393A CN 105255266 A CN105255266 A CN 105255266A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- huer
- interior wall
- thickening material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses an internal wall mercerizing latex paint based on HUER thickening agents, wherein the components comprise, by weight, 300 parts of water, 2 parts of a TritonCo-630 wetting agent, 3 parts of a KPA dispersing agent, 1 part of a FG-5 anti-foaming agent, 250 parts of a white light pigment filler, 20 parts of a Texanol film-forming auxiliary agent, 1.5 parts of a PU-40 polyurethane association type thickening agent, 380 parts of a styrene-acrylic emulsion, 2 parts of a PH value adjusting agent, 30 parts of an anti-freezing agent, and 5 parts of an acrylic acid thickening agent. According to the present invention, the KPA dispersing agent is matched, and experiment results prove that the HEUR products can produce dewatering precipitation in the presence of the polyacid homopolymer KPA dispersing agent, such that the flocculation phenomenon is avoided, and the latex paint with characteristics of excellent performance, good can opening effect and extreme good storage stability can be produced.
Description
Technical field
The present invention relates to a kind of paint, particularly a kind of medium-to-high grade interiro wall latex paint formula and production technique thereof.
Background technology
At present, along with the quality of life of people improves constantly, people are also more and more higher for the specification of quality of interiro wall latex paint, existing its polyoxyethylene backbone of HEUR class thickening material has wetting ability, hydrogen bond can be formed under normal circumstances with water. but under the environment that ionic concn is larger, water is easier and ionic bond then, therefore causes main chain to dewater and thickening material can not be dissolved, be separated on a microscopic scale, produce flocculation and cause mobility and gloss to decline or point water.
Summary of the invention
For solving the problem, the object of the present invention is to provide and can prevent its a kind of interior wall silk emulsion based on HUER class thickening material occurring flocculation and production technique thereof.
The present invention solves the technical scheme that its problem adopts:
Based on an interior wall silk emulsion for HUER class thickening material, the parts by weight of each component are: 300 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, FG-5 suds suppressor 1 part, white light color stuffing 250 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, benzene emulsion 380 parts, PH conditioning agent 2 parts, antifreezing agent 30 parts, acrylic thickener 5 parts.
Further, described acrylic thickener is made up of T-33 acrylic thickener 2 parts and MC35 acrylic thickener 3 parts.
Further, described white light color stuffing is made up of titanium dioxide 200 parts and water-ground limestone 50 parts.
Further, P-123 fungicidal preservative 2 parts is also comprised.
Further, described benzene emulsion is RS-998A benzene emulsion.
Further, AMP-19 defoamer 2 parts is also comprised.
A kind of manufacture craft of the interior wall silk emulsion based on HUER class thickening material, successively by 150 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, P-123 fungicidal preservative 2 parts, FG-5 suds suppressor 1 part, titanium dioxide 200 parts, water-ground limestone 50 parts mixing high speed dispersion after 20 minutes, slow down stirring velocity, and add successively: 150 parts, water, AMP-19 defoamer 2 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, RS-998A benzene emulsion 380 parts, PH conditioning agent 2 parts, T-33 acrylic thickener 2 parts, MC35 acrylic thickener 3 parts of mixing manufactures form.
The invention has the beneficial effects as follows: a kind of interior wall silk emulsion based on HUER class thickening material that the present invention adopts and production technique thereof, for making inner chamber silk emulsion, use T33 and PU-40 acrylic thickener, its peculiar internal crosslinking feature gives the workability of coating excellence, its yield value is high, can anti-settling, floating in anti-colored paint, be equipped with MC35 and PU-40 acrylic thickener, make it low, in, shear viscosity is more balanced, after 48 hours, viscosity tends towards stability fast, and the phenomenon in order to prevent it from occurring flocculation, the present invention is equipped with KPA dispersion agent, experiment proves, dehydration can be there is and separate out in HEUR series products when polyprotonic acid homopolymer KPA dispersion agent exists, thus avoid the phenomenon of flocculation, excellent performance can be made, good can opening effect, the emulsion paint that package stability is fabulous.
Embodiment
A kind of interior wall silk emulsion based on HUER class thickening material of the present invention, the parts by weight of each component are: 300 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, FG-5 suds suppressor 1 part, white light color stuffing 250 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, benzene emulsion 380 parts, PH conditioning agent 2 parts, antifreezing agent 30 parts, acrylic thickener 5 parts.
Further, described acrylic thickener is made up of T-33 acrylic thickener 2 parts and MC35 acrylic thickener 3 parts.T33 is acrylic thickener, and peculiar internal crosslinking feature gives the workability of coating excellence, and its yield value is high, can anti-settling, floating in anti-colored paint; PU40 is strong to emulsion associative ability, extremely outstanding can opening effect, and excellent workability, is specially adapted to the system that emulsion content is higher.
Further, described white light color stuffing is made up of titanium dioxide 200 parts and water-ground limestone 50 parts.Having in body of light system latex paint formulation, generally do not add filler (mainly most of filler all delustrings, but consider from cost angle, we select to add a small amount of stopping composition to reduce costs. and experiment proves, in the stopping composition of numerous cheapness, on the impact of glossiness, and its Baidu is high, rheological good for water-ground limestone.
Further, in order to strengthen the antiseptic property of emulsion paint, also comprise P-123 fungicidal preservative 2 parts.
Interior wall mercerising is filled a prescription, more coating factory likes selecting vac-veova emulsion, the gloss of film Du Lvegao that its paint film prepared is prepared compared with benzene emulsion, but vac-veova emulsion price comparatively benzene emulsion is high, and water-fast, alkali resistance is all not as benzene emulsion, so we think use vac-veova emulsion and non-best choice in interior wall mercerising formula, the present invention uses the benzene emulsion RS-998A of Ahmedabad richness (accounting for 38% of coating total amount) in interior wall mercerising formula, excellent combination property.
Further, AMP-19 defoamer 2 parts is also comprised.
A kind of manufacture craft of the interior wall silk emulsion based on HUER class thickening material, successively by 150 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, P-123 fungicidal preservative 2 parts, FG-5 suds suppressor 1 part, titanium dioxide 200 parts, water-ground limestone 50 parts mixing high speed dispersion after 20 minutes, slow down stirring velocity, and add successively: 150 parts, water, AMP-19 defoamer 2 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, RS-998A benzene emulsion 380 parts, PH conditioning agent 2 parts, T-33 acrylic thickener 2 parts, MC35 acrylic thickener 3 parts of mixing manufactures form.
Concrete system component of the present invention is as shown in the table:
Table 1
Its formula constant is:
Dry coating film thickness: 35uM;
Coating theoretical density: 1.19KG/L;
Area: 9.5M2/KG;
Amount solids content: 44.86%;
Volume solids content: 33.24%;
Resin-pigment ratio: 1.26:1;
PVC:23.38%；
PH value: 8.8;
Contrast ratio: 0.95;
Scrubbing resistance number of times: >20000 time;
Mobility: excellent;
Can opening effect: layering, stirs delayed sense well.
The above, just preferred embodiment of the present invention, the present invention is not limited to above-mentioned embodiment, as long as it reaches technique effect of the present invention with identical means, all should belong to protection scope of the present invention.
Claims (7)
1. the interior wall silk emulsion based on HUER class thickening material, it is characterized in that, the parts by weight of each component are: 300 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, FG-5 suds suppressor 1 part, white light color stuffing 250 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, benzene emulsion 380 parts, PH conditioning agent 2 parts, antifreezing agent 30 parts, acrylic thickener 5 parts.
2. a kind of interior wall silk emulsion based on HUER class thickening material according to claim 1, is characterized in that: described acrylic thickener is made up of T-33 acrylic thickener 2 parts and MC35 acrylic thickener 3 parts.
3. a kind of interior wall silk emulsion based on HUER class thickening material according to claim 1, is characterized in that: described white light color stuffing is made up of titanium dioxide 200 parts and water-ground limestone 50 parts.
4. a kind of interior wall silk emulsion based on HUER class thickening material according to claim 1, is characterized in that: also comprise P-123 fungicidal preservative 2 parts.
5. a kind of interior wall silk emulsion based on HUER class thickening material according to claim 1, is characterized in that: described benzene emulsion is RS-998A benzene emulsion.
6. a kind of interior wall silk emulsion based on HUER class thickening material according to claim 1, is characterized in that: also comprise AMP-19 defoamer 2 parts.
7. the manufacture craft based on the interior wall silk emulsion of HUER class thickening material, it is characterized in that: successively by 150 parts, water, TritonCo-630 wetting agent 2 parts, KPA dispersion agent 3 parts, P-123 fungicidal preservative 2 parts, FG-5 suds suppressor 1 part, titanium dioxide 200 parts, water-ground limestone 50 parts mixing high speed dispersion after 20 minutes, slow down stirring velocity, and add successively: 150 parts, water, AMP-19 defoamer 2 parts, Texanol film coalescence aid 20 parts, PU-40 polyurethane associative thickener 1.5 parts, RS-998A benzene emulsion 380 parts, PH conditioning agent 2 parts, T-33 acrylic thickener 2 parts, MC35 acrylic thickener 3 parts of mixing manufactures form.