CN105255228A - Bird driving coating for outdoor box body of electricity grid and preparation method of coating - Google Patents
Bird driving coating for outdoor box body of electricity grid and preparation method of coating Download PDFInfo
- Publication number
- CN105255228A CN105255228A CN201510698521.3A CN201510698521A CN105255228A CN 105255228 A CN105255228 A CN 105255228A CN 201510698521 A CN201510698521 A CN 201510698521A CN 105255228 A CN105255228 A CN 105255228A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- electric power
- power network
- driving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bird driving coating for an outdoor box body of the electricity grid and a preparation method of the coating. Aqueous acrylic resin, epoxy modified silicon resin, silicon carbide, a carbon nano tube, carbon black, eucalyptus oil, acrylic acid, zirconium silicate, dibutyltin dilaurate, styrene-acrylic emulsion, sodium tripolyphosphate, gas phase aluminium sesquioxide, aluminium silicate fiber, isopropyl phenyl diphenyl phosphate, PVP, titanium dioxide, folium artemisiae argyi, rushes, musk, iron powder and a silica solution are taken as raw materials, and the bird driving coating, which is corrosion-resistant and abrasion-resistant and capable of absorbing heat, for the outdoor box body of the electricity grid is prepared with a substep mixing method.
Description
Technical field
The invention belongs to and drive bird paint field, particularly a kind of electric power network outdoor case is with driving bird coating and preparation method thereof.
Background technology
Power equipment (powersystem) mainly comprises with generating set and the large class of power-supply unit two, generating set is station boiler, steam turbine, internal combustion turbine, water turbine, generator, transformer etc. mainly, the transmitting line, mutual inductor, contactor etc. of power-supply unit mainly various voltage range.
Along with industrial expansion, in electric power network outdoor case, drive bird coating for main coating can play anticorrosion, wear-resisting, acid and alkali-resistance effect is more and more important, at present, the common bird coating that drives easily is corroded with aging, can not play automatically cleaning, acid and alkali-resistance effect.
Summary of the invention
The object of the invention is for the problems referred to above, develop a kind of corrosion-resistant, wear-resisting, the electric power network outdoor case that can absorb heat is with driving bird coating and preparation method thereof.
A kind of electric power network outdoor case is with driving bird coating, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 20-50 part;
Epoxide modified silicone resin 20-50 part;
Silicon carbide 20-50 part;
Carbon nanotube 20-50 part;
Carbon black 20-50 part;
Eucalyptus oil 20-50 part;
Vinylformic acid 1-11 part;
Zirconium silicate 1-11 part;
Dibutyl tin laurate 1-11 part;
Benzene emulsion 1-11 part;
Tripoly phosphate sodium STPP 1-11 part;
Gas phase aluminium sesquioxide 1-11 part;
Aluminum silicate fiber 1-11 part;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 1-11 part;
PVP1-11 part;
Titanium dioxide 1-11 part;
Tarragon 1-11 part;
Stem or leaf of cattail 1-11 part;
Moschus 1-11 part;
Iron powder 1-11 part;
Silicon sol 1-11 part.
As preferably, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed in casing, well heater and power supply: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 35 parts;
Epoxide modified silicone resin 35 parts;
35 parts, silicon carbide;
Carbon nanotube 35 parts;
Carbon black 35 parts;
Eucalyptus oil 35 parts;
5 parts, vinylformic acid;
Zirconium silicate 5 parts;
Dibutyl tin laurate 5 parts;
Benzene emulsion 5 parts;
Tripoly phosphate sodium STPP 5 parts;
Gas phase aluminium sesquioxide 5 parts;
Aluminum silicate fiber 5 parts;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 5 parts;
PVP5 part;
Titanium dioxide 5 parts;
Tarragon 5 parts;
The stem or leaf of cattail 5 parts;
5 parts, Moschus;
Iron powder 5 parts;
Silicon sol 5 parts.
As preferably, the particle diameter of described water-borne acrylic resin is 20-60nm.
Prepare an electric power network outdoor case method of driving bird coating described above, comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.
Beneficial effect of the present invention:
(1) adopt water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube, carbon black and eucalyptus oil as the main component of driving bird coating, the wherein compound use of resin and carbon black, will strengthen the performance of driving the wear-resisting, corrosion-resistant of bird coating and acid and alkali-resistance greatly; And inorganic materials silicon carbide and novel nano-material carbon nanotube, because self is for the reinforced effects of coating, as main component, the wear resistance of coating is strengthened greatly; The compound use of eucalyptus oil and other several raw materials, can not only play the effect of driving bird, also by the compatible crossing effect with resin, carbon nanotube and carbon black, promotes the synergy of each raw material.
(2) in order to optimize the performance of driving bird coating further, have selected vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol are ancillary component, this is not only made to drive the wear-resisting of bird coating, corrosion-resistant, acid-proof alkaline is improved, or this must drive bird coating there is good hydrophobic performance, and owing to the addition of solar selectively absorptive function iron powder and silicon sol combination, make this drive bird coating and can be used in the relevant electric power network outdoor case of sun power.
(3) the present invention is selecting tarragon, the stem or leaf of cattail, Moschus and eucalyptus oil as driving bird coating, said composition is common material, nontoxic, and it is cheap, efficient effect on driving birds can be played simultaneously, simultaneously eucalyptus oil or the main component of said composition, has important promoter action for wear-resisting, the lubrication of said composition and cleaning effect.
(4) this drives bird Paint preparation technology simply, is easy to industrialization, and raw material sources are extensive, are applicable to very much being applied to production.
Embodiment
Below in conjunction with specific embodiment, and comparable data describes in further detail the present invention.Should be understood that these embodiments just in order to demonstrate the invention, but not limit the scope of the invention by any way.
Embodiment 1:
A kind of electric power network outdoor case is with driving bird coating, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 35 parts;
Epoxide modified silicone resin 35 parts;
35 parts, silicon carbide;
Carbon nanotube 35 parts;
Carbon black 35 parts;
Eucalyptus oil 35 parts;
5 parts, vinylformic acid;
Zirconium silicate 5 parts;
Dibutyl tin laurate 5 parts;
Benzene emulsion 5 parts;
Tripoly phosphate sodium STPP 5 parts;
Gas phase aluminium sesquioxide 5 parts;
Aluminum silicate fiber 5 parts;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 5 parts;
PVP5 part;
Titanium dioxide 5 parts;
Tarragon 5 parts;
The stem or leaf of cattail 5 parts;
5 parts, Moschus;
Iron powder 5 parts;
Silicon sol 5 parts;
The particle diameter of described water-borne acrylic resin is 30nm.
Prepare an electric power network outdoor case method of driving bird coating described above, comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.
Embodiment 2:
A kind of electric power network outdoor case is with driving bird coating, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 46 parts;
Epoxide modified silicone resin 46 parts;
46 parts, silicon carbide;
Carbon nanotube 46 parts;
Carbon black 46 parts;
Eucalyptus oil 46 parts;
6 parts, vinylformic acid;
Zirconium silicate 6 parts;
Dibutyl tin laurate 6 parts;
Benzene emulsion 6 parts;
Tripoly phosphate sodium STPP 6 parts;
Gas phase aluminium sesquioxide 6 parts;
Aluminum silicate fiber 6 parts;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 6 parts;
PVP6 part;
Titanium dioxide 6 parts;
Tarragon 6 parts;
The stem or leaf of cattail 6 parts;
6 parts, Moschus;
Iron powder 6 parts;
Silicon sol 6 parts;
The particle diameter of described water-borne acrylic resin is 30nm.
Prepare an electric power network outdoor case method of driving bird coating described above, comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.
Embodiment 3:
A kind of electric power network outdoor case is with driving bird coating, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 30 parts;
Epoxide modified silicone resin 30 parts;
30 parts, silicon carbide;
Carbon nanotube 30 parts;
Carbon black 30 parts;
Eucalyptus oil 30 parts;
1 part, vinylformic acid;
Zirconium silicate 1 part;
Dibutyl tin laurate 1 part;
Benzene emulsion 1 part;
Tripoly phosphate sodium STPP 1 part;
Gas phase aluminium sesquioxide 1 part;
Aluminum silicate fiber 1 part;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 1 part;
PVP1 part;
Titanium dioxide 1 part;
Tarragon 1 part;
The stem or leaf of cattail 1 part;
1 part, Moschus;
Iron powder 1 part;
Silicon sol 1 part;
The particle diameter of described water-borne acrylic resin is 40nm.
Prepare an electric power network outdoor case method of driving bird coating described above, comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.
Embodiment 4:
A kind of electric power network outdoor case is with driving bird coating, described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 20 parts;
Epoxide modified silicone resin 20 parts;
20 parts, silicon carbide;
Carbon nanotube 20 parts;
Carbon black 20 parts;
Eucalyptus oil 20 parts;
10 parts, vinylformic acid;
Zirconium silicate 10 parts;
Dibutyl tin laurate 10 parts;
Benzene emulsion 10 parts;
Tripoly phosphate sodium STPP 10 parts;
Gas phase aluminium sesquioxide 10 parts;
Aluminum silicate fiber 10 parts;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 10 parts;
PVP10 part;
Titanium dioxide 10 parts;
Tarragon 10 parts;
The stem or leaf of cattail 10 parts;
10 parts, Moschus;
Iron powder 10 parts;
Silicon sol 10 parts;
The particle diameter of described water-borne acrylic resin is 40nm.
Prepare an electric power network outdoor case method of driving bird coating described above, comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.
Carry out salt-fog test to the electric power network outdoor case of driving bird paint prepared by embodiment 1-4 and scratch results of property, result is as follows:
| Erosion resistance (salt-fog test) | Scratch resistant | |
| Embodiment 1 | 633 hours | 0 |
| Embodiment 2 | 637 hours | 0 |
| Embodiment 3 | 634 hours | 0 |
| Embodiment 4 | 629 hours | 0 |
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (4)
1. an electric power network outdoor case is with driving bird coating, it is characterized in that: described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 20-50 part;
Epoxide modified silicone resin 20-50 part;
Silicon carbide 20-50 part;
Carbon nanotube 20-50 part;
Carbon black 20-50 part;
Eucalyptus oil 20-50 part;
Vinylformic acid 1-11 part;
Zirconium silicate 1-11 part;
Dibutyl tin laurate 1-11 part;
Benzene emulsion 1-11 part;
Tripoly phosphate sodium STPP 1-11 part;
Gas phase aluminium sesquioxide 1-11 part;
Aluminum silicate fiber 1-11 part;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 1-11 part;
PVP1-11 part;
Titanium dioxide 1-11 part;
Tarragon 1-11 part;
Stem or leaf of cattail 1-11 part;
Moschus 1-11 part;
Iron powder 1-11 part;
Silicon sol 1-11 part.
2. electric power network outdoor case as claimed in claim 2 is with driving a bird coating, it is characterized in that:
Described casing is environment real-time monitoring system casing, for outdoor mechanism case, humidity sensor, humidity regulator, temperature sensor, temperature regulator are installed, well heater and power supply in casing: this electric power network outdoor case is made up of following weight part material with driving bird coating:
Water-borne acrylic resin 35 parts;
Epoxide modified silicone resin 35 parts;
35 parts, silicon carbide;
Carbon nanotube 35 parts;
Carbon black 35 parts;
Eucalyptus oil 35 parts;
5 parts, vinylformic acid;
Zirconium silicate 5 parts;
Dibutyl tin laurate 5 parts;
Benzene emulsion 5 parts;
Tripoly phosphate sodium STPP 5 parts;
Gas phase aluminium sesquioxide 5 parts;
Aluminum silicate fiber 5 parts;
ISOPROPYL PHENYL DIPHENYL PHOSPHATE 5 parts;
PVP5 part;
Titanium dioxide 5 parts;
Tarragon 5 parts;
The stem or leaf of cattail 5 parts;
5 parts, Moschus;
Iron powder 5 parts;
Silicon sol 5 parts.
3. electric power network outdoor case as claimed in claim 1 or 2 is with driving a bird coating, it is characterized in that: the particle diameter of described water-borne acrylic resin is 20-60nm.
4. prepare an electric power network outdoor case method of driving bird coating as claimed in claim 1, it is characterized in that: comprise the steps:
(1) prepare burden according to driving bird system component;
(2) first add water-borne acrylic resin, epoxide modified silicone resin, silicon carbide, carbon nanotube and carbon black according to formula ratio, shredder ground and mixed 3min, adds eucalyptus oil subsequently again, stirs 20min with homogenizer;
(3) at 45 DEG C, vinylformic acid, zirconium silicate, dibutyl tin laurate, benzene emulsion, tripoly phosphate sodium STPP, gas phase aluminium sesquioxide, aluminum silicate fiber, ISOPROPYL PHENYL DIPHENYL PHOSPHATE, PVP, titanium dioxide, tarragon, the stem or leaf of cattail, Moschus, iron powder and silicon sol is added again, and stir 40min, obtain electric power network outdoor case with driving bird coating.