CN105254262A - Environment-friendly building material - Google Patents
Environment-friendly building material Download PDFInfo
- Publication number
- CN105254262A CN105254262A CN201510505517.0A CN201510505517A CN105254262A CN 105254262 A CN105254262 A CN 105254262A CN 201510505517 A CN201510505517 A CN 201510505517A CN 105254262 A CN105254262 A CN 105254262A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum
- building material
- environment
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an environment-friendly building material. The building material comprises the following materials by weight: 10 to 15 parts of gypsum, 3 to 6 parts of kaolin, 1 to 3 parts of diatomite, 2 to 5 parts of an inorganic thickening agent, 8 to 15 parts of ethylene acrylate, 12 to 24 parts of polyvinyl chloride, 9 to 18 parts of hydroxyethyl cellulose, 6 to 15 parts of a high temperature-resistant binder, 3 to 8 parts of a fire retardant, 12 to 18 parts of talcum powder, 3 to 9 parts of hemihydrate gypsum, 4 to 12 parts of a filling material, 2 to 6 parts of perlite, 1 to 3 parts of vermiculite, 3 to 5 parts of small broken stone (80 to 150 meshes), 1 to 3 parts of an XK gypsum auxiliary agent, 10 to 25 parts of an antistatic agent, 2 to 8 parts of cellulose powder and 4 to 10 parts of titanium dioxide. The building material provided by the invention has the advantages of conservation of energy, environment friendliness, good fire resistance, high strength, long service life, ageing resistance, low cost, convenience in construction and good heat-preserving and thermal insulation performances.
Description
Technical field
The present invention relates to a kind of environmental protection and meet material of construction.
Background technology
Energy-conserving and environment-protective are the key subjects faced by people needed in 21 century, also the important topic that building trade must address is become, the clay class that current building trade uses and take cement as the wall body building material of jelling agent, there is high cost source and very easily to shortcomings such as environments, and improve the important measures that house heat-proof quality is building energy-saving consumption reduction, although some current environment-friendly materials have accomplished the ask for something of environmental protection substantially, but that does in intensity and heat-insulation and heat-preservation is also not so good as people's will, there is work-ing life short, easily aging, high in cost of production shortcoming, do not reach the requirement of people, and easily affect whole building quality.
Summary of the invention
The object of the present invention is to provide a kind of environmental protection to meet material of construction, energy-conserving and environment-protective, lightweight, resistivity against fire is good, and intensity is high, and long service life is anti-aging, and cost is low, easy construction, has good thermal and insulating performance.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of environmental protection meets material of construction, be made up of following weight part material: gypsum 10-15 part, kaolin 3-6 part, diatomite 1-3 part, inorganic thickening agent 2-5 part, salts of acrylic acid-ethylene 8-15 part, polyvinyl chloride 12-24 part, Natvosol 9-18 part, high temperature resistant binder 6-15 part, fire retardant 3-8 part, talcum powder 12-18 part, semi-hydrated gypsum 3-9 part, filler 4-12 part, perlite 2-6 part, vermiculite 1-3 part, broken gravelstone grain (80-150 order) 3-5 part, XK gypsum auxiliary agent 1-3 part, static inhibitor 10-25 part, cellulose powder 2-8 part, titanium dioxide 4-10 part.
The invention has the beneficial effects as follows: energy-conserving and environment-protective of the present invention, lightweight, resistivity against fire is good, and intensity is high, and long service life is anti-aging, and cost is low, easy construction, has good thermal and insulating performance.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
Embodiment one
A kind of environmental protection meets material of construction, be made up of following weight part material: gypsum 10-15 part, kaolin 3-6 part, diatomite 1-3 part, inorganic thickening agent 2-5 part, salts of acrylic acid-ethylene 8-15 part, polyvinyl chloride 12-24 part, Natvosol 9-18 part, high temperature resistant binder 6-15 part, fire retardant 3-8 part, talcum powder 12-18 part, semi-hydrated gypsum 3-9 part, filler 4-12 part, perlite 2-6 part, vermiculite 1-3 part, broken gravelstone grain (80-150 order) 3-5 part, XK gypsum auxiliary agent 1-3 part, static inhibitor 10-25 part, cellulose powder 2-8 part, titanium dioxide 4-10 part.
Embodiment two
A kind of environmental protection meets material of construction, is made up of: 11 parts, gypsum, kaolin 4 parts, 2 parts, diatomite following weight part material, inorganic thickening agent 3 parts, salts of acrylic acid-ethylene 12 parts, polyvinyl chloride 15 parts, Natvosol 12 parts, high temperature resistant binder 8 parts, fire retardant 4 parts, talcum powder 15 parts, semi-hydrated gypsum 7 parts, filler 6 parts, perlite 3 parts, vermiculite 2 parts, broken gravelstone grain (80-150 order) 3 parts, XK gypsum auxiliary agent 2 parts, 12 parts, static inhibitor, cellulose powder 4 parts, titanium dioxide 7 parts.
Embodiment two
A kind of environmental protection meets material of construction, is made up of: 13 parts, gypsum, kaolin 5 parts, 2 parts, diatomite following weight part material, inorganic thickening agent 4 parts, salts of acrylic acid-ethylene 9 parts, polyvinyl chloride 18 parts, Natvosol 15 parts, high temperature resistant binder 10 parts, fire retardant 6 parts, talcum powder 15 parts, semi-hydrated gypsum 8 parts, filler 10 parts, perlite 4 parts, vermiculite 2 parts, broken gravelstone grain (80-150 order) 4 parts, XK gypsum auxiliary agent 3 parts, 19 parts, static inhibitor, cellulose powder 6 parts, titanium dioxide 8 parts.
Embodiment three
A kind of environmental protection meets material of construction, is made up of: 14 parts, gypsum, kaolin 5 parts, 3 parts, diatomite following weight part material, inorganic thickening agent 4 parts, salts of acrylic acid-ethylene 10 parts, polyvinyl chloride 21 parts, Natvosol 16 parts, high temperature resistant binder 12 parts, fire retardant 7 parts, talcum powder 17 parts, semi-hydrated gypsum 8 parts, filler 9 parts, perlite 3 parts, vermiculite 2 parts, broken gravelstone grain (80-150 order) 4 parts, XK gypsum auxiliary agent 1 part, 24 parts, static inhibitor, cellulose powder 6 parts, titanium dioxide 8 parts.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. an environmental protection meets material of construction, be made up of following weight part material: gypsum 10-15 part, kaolin 3-6 part, diatomite 1-3 part, inorganic thickening agent 2-5 part, salts of acrylic acid-ethylene 8-15 part, polyvinyl chloride 12-24 part, Natvosol 9-18 part, high temperature resistant binder 6-15 part, fire retardant 3-8 part, talcum powder 12-18 part, semi-hydrated gypsum 3-9 part, filler 4-12 part, perlite 2-6 part, vermiculite 1-3 part, broken gravelstone grain (80-150 order) 3-5 part, XK gypsum auxiliary agent 1-3 part, static inhibitor 10-25 part, cellulose powder 2-8 part, titanium dioxide 4-10 part.