CN105252215A - 一种锤子耐磨手柄及其制备方法 - Google Patents
一种锤子耐磨手柄及其制备方法 Download PDFInfo
- Publication number
- CN105252215A CN105252215A CN201510651965.1A CN201510651965A CN105252215A CN 105252215 A CN105252215 A CN 105252215A CN 201510651965 A CN201510651965 A CN 201510651965A CN 105252215 A CN105252215 A CN 105252215A
- Authority
- CN
- China
- Prior art keywords
- slag
- hammer
- abrasion
- handle
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及五金生产加工领域,更具体地说涉及一种锤子耐磨手柄,其特征在于由下列重量份的原料制成:90-100份改性矿渣、0.1-0.5份铜、1-2份铁、0.01-0.08份铬、0.5-1份铝、0.02-0.1份镁、0.3-0.8份磷、0.08-0.2份碳、0.06-0.3份钨,本发明采用矿渣为原料,对废物进行回收再利用,节约了大量资源,并且经过改性处理去了大部分不能用于锻造的杂质,后面的精炼步骤更是将矿渣进一步提炼,加入的其他金属成份,使得制得的手柄坚固耐磨,且成本低廉。
Description
技术领域:
本发明涉及五金生产加工领域,更具体地说涉及一种锤子耐磨手柄。
背景技术:
五金:传统的五金制品,也称“小五金”。指金、银、铜、铁、铝五种金属。经人工加工可以制成刀、剑等艺术品或金属器件。现代社会的五金更为广泛,例如五金工具、五金零部件、日用五金、建筑五金以及安防用品等。小五金产品大都不是最终消费品,五金工具中含有锤子。
锤子是敲打物体使其移动或变形的工具。最常用来敲钉子,矫正或是将物件敲开。锤子有着各式各样的形式,常见的形式是一柄把手以及顶部。顶部的一面是平坦的以便敲击,另一面则是锤头。锤头的形状可以像羊角,也可以是楔形,其功能为拔出钉子。另外也有着圆头形的锤头。常见的锤子手柄有木质、金属、橡胶、塑料等,木质和橡胶塑料耐磨性差,而金属制的手柄造价成本有点高。
发明内容:
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种成本低的锤子耐磨手柄。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种锤子耐磨手柄,其特征在于由下列重量份的原料制成:90-100份改性矿渣、0.1-0.5份铜、1-2份铁、0.01-0.08份铬、0.5-1份铝、0.02-0.1份镁、0.3-0.8份磷、0.08-0.2份碳、0.06-0.3份钨。
进一步的,所述的改性矿渣由下列重量份的原料组成:80-90份矿渣、7-9份盐酸、2-3份六偏磷酸钠、9-14份聚丙烯酰胺、6-8份碳醋氢钙、3-5份橄榄油、6-8份硼砂、0.5-2份陶粒、2-3份树木灰烬、1-2份交联剂。
进一步的,所述的改性矿渣的制备方法为:先将矿渣磨成粉末状,在干燥氮气保护下,向装有温度计、搅拌装置和回流冷凝器的密闭反应釜中投入矿渣粉、盐酸、六偏磷酸钠,加入一定量的乙醇溶液,升温至70-80℃反应半个小时,降温至50-60℃,加入聚丙烯酰胺反应10分钟,再加入碳醋氢钙和橄榄油,反应约1.5小时,进一步降低温度至45℃,加入硼砂、陶粒和树木灰烬,继续保温反应一个小时,降温至常温,最后加入交联剂然后过滤干燥即得改性矿渣。
一种锤子耐磨手柄的制备方法,其特征在于包括下列步骤:
(1)配料,然后进行铸造,为了消除气体和非金属杂质,进行精炼,精炼后将合金注入铸模,进行连续铸造法,浇铸速度为每小时2-3米,然后铸轧,盘卷;
(2)对铸轧坯料进行挤压,挤压工艺参数:挤压筒温度450-500℃,铸锭加热温度500-600℃,模具加热温度460-520℃,挤压速度10-15m/min。
本发明采用矿渣为原料,对废物进行回收再利用,节约了大量资源,并且经过改性处理去了大部分不能用于锻造的杂质,后面的精炼步骤更是将矿渣进一步提炼,加入的其他金属成份,使得制得的手柄坚固耐磨,且成本低廉。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1:一种锤子耐磨手柄,其特征在于由下列重量份的原料制成:90份改性矿渣、0.1份铜、1份铁、0.01份铬、0.5份铝、0.02份镁、0.3份磷、0.08份碳、0.06份钨。
改性矿渣由下列重量份的原料组成:80份矿渣、7份盐酸、2份六偏磷酸钠、9份聚丙烯酰胺、6份碳醋氢钙、3份橄榄油、6份硼砂、0.5份陶粒、2份树木灰烬、1份交联剂。
实施例2:一种锤子耐磨手柄,其特征在于由下列重量份的原料制成:100份改性矿渣、0.5份铜、2份铁、0.08份铬、1份铝、0.1份镁、0.8份磷、0.2份碳、0.3份钨。
改性矿渣由下列重量份的原料组成:90份矿渣、9份盐酸、3份六偏磷酸钠、14份聚丙烯酰胺、8份碳醋氢钙、5份橄榄油、8份硼砂、2份陶粒、3份树木灰烬、2份交联剂。
改性矿渣的制备方法为:先将矿渣磨成粉末状,在干燥氮气保护下,向装有温度计、搅拌装置和回流冷凝器的密闭反应釜中投入矿渣粉、盐酸、六偏磷酸钠,加入一定量的乙醇溶液,升温至70-80℃反应半个小时,降温至50-60℃,加入聚丙烯酰胺反应10分钟,再加入碳醋氢钙和橄榄油,反应约1.5小时,进一步降低温度至45℃,加入硼砂、陶粒和树木灰烬,继续保温反应一个小时,降温至常温,最后加入交联剂然后过滤干燥即得改性矿渣。
一种锤子耐磨手柄的制备方法,其特征在于包括下列步骤:
(1)配料,然后进行铸造,为了消除气体和非金属杂质,进行精炼,精炼后将合金注入铸模,进行连续铸造法,浇铸速度为每小时2-3米,然后铸轧,盘卷;
(2)对铸轧坯料进行挤压,挤压工艺参数:挤压筒温度450-500℃,铸锭加热温度500-600℃,模具加热温度460-520℃,挤压速度10-15m/min。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种锤子耐磨手柄,其特征在于由下列重量份的原料制成:90-100份改性矿渣、0.1-0.5份铜、1-2份铁、0.01-0.08份铬、0.5-1份铝、0.02-0.1份镁、0.3-0.8份磷、0.08-0.2份碳、0.06-0.3份钨。
2.根据权利要求1所述的一种锤子耐磨手柄,其特征在于所述的改性矿渣由下列重量份的原料组成:80-90份矿渣、7-9份盐酸、2-3份六偏磷酸钠、9-14份聚丙烯酰胺、6-8份碳醋氢钙、3-5份橄榄油、6-8份硼砂、0.5-2份陶粒、2-3份树木灰烬、1-2份交联剂。
3.根据权利要求2所述的一种锤子耐磨手柄,其特征在于所述的改性矿渣的制备方法为:先将矿渣磨成粉末状,在干燥氮气保护下,向装有温度计、搅拌装置和回流冷凝器的密闭反应釜中投入矿渣粉、盐酸、六偏磷酸钠,加入一定量的乙醇溶液,升温至70-80℃反应半个小时,降温至50-60℃,加入聚丙烯酰胺反应10分钟,再加入碳醋氢钙和橄榄油,反应约1.5小时,进一步降低温度至45℃,加入硼砂、陶粒和树木灰烬,继续保温反应一个小时,降温至常温,最后加入交联剂然后过滤干燥即得改性矿渣。
4.一种锤子耐磨手柄的制备方法,其特征在于包括下列步骤:
(1)配料,然后进行铸造,为了消除气体和非金属杂质,进行精炼,精炼后将合金注入铸模,进行连续铸造法,浇铸速度为每小时2-3米,然后铸轧,盘卷;
(2)对铸轧坯料进行挤压,挤压工艺参数:挤压筒温度450-500℃,铸锭加热温度500-600℃,模具加热温度460-520℃,挤压速度10-15m/min。