CN105220565A - 具有耐刮性能的离型材料 - Google Patents

具有耐刮性能的离型材料 Download PDF

Info

Publication number
CN105220565A
CN105220565A CN201510546136.7A CN201510546136A CN105220565A CN 105220565 A CN105220565 A CN 105220565A CN 201510546136 A CN201510546136 A CN 201510546136A CN 105220565 A CN105220565 A CN 105220565A
Authority
CN
China
Prior art keywords
scratch resistance
release
resistance performance
separated type
type material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510546136.7A
Other languages
English (en)
Inventor
金闯
张庆杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Sidike New Material Science and Technology Co Ltd
Original Assignee
Suzhou Sidike New Material Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Sidike New Material Science and Technology Co Ltd filed Critical Suzhou Sidike New Material Science and Technology Co Ltd
Publication of CN105220565A publication Critical patent/CN105220565A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种具有耐刮性能的离型材料，其特征在于：所述抗静电离型材料位于离型膜和离型剂层间，所述抗静电离型材料由下列质量百分含量的组分组成：硅石颗粒6%、平均分子量为500~2000的丙烯酸多元醇28%、平均分子量为200~2500的聚氧化烯系列多元醇的树脂42%、聚乙二醇17%、1-羟基环己基苯基甲酮-光引发剂184为7%。本发明雾面离型剂既提高了离型纸的淋膜层与离型剂的结合力且剥离力稳定，又提高了膜表面防静电性能，且具有特别优越的吸收结合水形式的水的能力。

Description

具有耐刮性能的离型材料
技术领域
本发明涉及一种离型材料，特别涉及一种具有耐刮性能的离型材料。
背景技术
现有的离型纸一般是在离型纸底纸层的表面淋膜一层淋膜层（采用的材料主要有聚乙烯），然后在淋膜层的表面涂布一层离型剂涂层（采用的材料主要为硅油）得到离型纸。但是由于淋膜层平整度高，离型剂涂层与淋膜层之间附着力差，当离型纸与涂覆有高粘度粘合剂的贴膜贴附时，容易导致离型纸上的离型剂涂层被粘附力更大的粘合剂带走，从而在贴膜的局部表面形成难以清理掉的离型剂涂层区域，破坏了贴膜整体的纯净、一致性。而且由于生产过程静电过大，导致离型涂布层局部不平整，不仅影响产品剥离力稳定性，而且容易产生静电火花导致火灾。
发明内容
本发明目的是提供一种具有耐刮性能的离型材料，该具有耐刮性能的离型材料既提高了离型纸的淋膜层与离型剂的结合力且剥离力稳定，又提高了膜表面防静电性能，且同时也提高了耐刮性能。
为达到上述目的，本发明采用的技术方案是：一种具有耐刮性能的离型材料，所述抗静电离型材料位于离型膜和离型剂层间，所述抗静电离型材料由下列质量百分含量的组分组成：
硅石颗粒2%，
平均分子量为500~2000的丙烯酸多元醇28%，
平均分子量为200~2500的聚氧化烯系列多元醇的树脂40%，
聚乙二醇20%，
1-羟基环己基苯基甲酮-光引发剂18410%；
所述硅石颗粒的粒径为由激光衍射·散射法测定的粒度分布中粒径在0.1~2um和1.5~5um的范围内分别具有峰值、且平均粒径为4um或以下。
上述技术方案中进一步改进的方案如下：
1、上述方案中，所述离型剂层为硅油。
2、上述方案中，所述离型膜厚度为0.3μm~0.35μm。
由于上述技术方案运用，本发明与现有技术相比具有下列优点和效果：
1、本发明具有耐刮性能的离型材料，其采用20~30%平均分子量为500~2000的丙烯酸多元醇和30~40%平均分子量为200~2500的聚氧化烯系列多元醇的树脂聚合而成的聚氨酯树脂，平均分子量为500~2000的丙烯酸多元醇和平均分子量为200~2500的聚氧化烯系列多元醇的树脂中的链提高了膜表面防静电性能，且同时也提高了耐刮性能；其多元醇丙烯酸酯单体具有500~2000的平均分子量，如果分子量小于500，膜的耐磨性趋于降低，如果平均分子量超过2000，固化成膜时适用性变差。如果多元醇丙烯酸酯单体特别为乙二醇，考虑到吸水能力，本发明选择平均分子量为200~1000的聚乙二醇，利用了其优越的吸收结合水的能力，进一步提高了防静电效果。由于这种多元醇丙烯酸单体具有特别优越的吸收结合水形式的水的能力，具有防静电效果，多元醇丙烯酸酯单体全部可以使用这种单体。
2、本发明具有耐刮性能的离型材料，首先对薄膜层的表面涂布雾面防静电涂层，经雾面防静电涂层通过配方和工艺处理后的表面具有若干均匀凹凸结构和防静电效果，然后在此表面涂布硅离型剂涂层涂层，硅离型剂涂层涂层的底面在液态下渗入所述雾面防静电涂层表面的凹缺处，硅离型剂涂层涂层在凝固后通过凹缺处与雾面防静电涂层固定相连，因此，结合力更加牢固、可靠。而且由于防静电处理，可以消除静电对硅油涂布不稳定带来的影响，离型剥离力会很稳定，也避免生产过程静电火花的发生。
3、本发明中采用光引发剂1-羟基环己基苯基甲酮引发，主要是考虑其在波段为320-400nm紫外光照射下，可瞬间固化成膜，可达到深层固化，具有很好的平整性和强度。所述光引发剂为1-羟基环己基苯基甲酮-光引发剂184，是一种高效不黄变的紫外光引发剂，用于引发不饱和预聚体系的UV聚合反应，其质量含量为5～10%。
4、本发明中紫外光的功率采用1200mW/cm2，主要是功率若低于1200mW/cm2，膜不完全固化，耐磨性降低；若功率若高于1200mW/cm2，影响膜平整度，适用性下降。采用紫外线波段为320~400nm，照度为1200mW/cm2，对所述雾面涂层剂进行照射，使所述组分在本发明特定作为光引发剂的1-羟基环己基苯基甲酮的作用下进行聚合反应得到雾面涂层，厚度为4~10um，具有防静电效果，再在所述雾面涂层的表面涂覆一层离型剂涂层得到雾面离型层。
具体实施方式
下面结合实施例对本发明作进一步描述：
实施例：一种具有耐刮性能的离型材料，所述抗静电离型材料位于离型膜和离型剂层间，所述抗静电离型材料由下列质量百分含量的组分组成：
硅石颗粒2%，
平均分子量为500~2000的丙烯酸多元醇28%，
平均分子量为200~2500的聚氧化烯系列多元醇的树脂40%，
聚乙二醇20%，
1-羟基环己基苯基甲酮-光引发剂18410%；
所述硅石颗粒的粒径为由激光衍射·散射法测定的粒度分布中粒径在0.1~2um和1.5~5um的范围内分别具有峰值、且平均粒径为4um或以下。
上述离型剂层为硅油；上述离型膜是聚丙烯薄膜。
上述离型膜厚度为0.3μm~0.35μm；上述硅石颗粒粒径为0.2μm~0.35μm。
性能指标如下表1所示：
表1
（1）、外观评价：通过目视观测对外观、透明度和裂纹的存在进行评价。没有问题的膜被评定为令人满意（O），有问题的膜被评定为不令人满意（X）；
（2）、手戳将离型层面手戳10次，无消光为合格，消光为不合格；
（3）、百格测试百格刀测试无脱落为合格产品，脱落为不合格产品；
（4）、剥离电压用滚轮将胶带压接（1公斤来回，速度0.3m/min）于离型膜面，其后，用手快速剥离（10m/min），用静电场测试仪（型号：SIMCOFMX-003）读取胶带粘离型膜面的剥离静电压的最大值，静电压小于0.3KV为合格产品，静电压大于0.3KV为不合格产品；
（5）、表面阻抗值用表面电阻测试仪G面两根平行铜电极置于样品表面任一处，按下黑色A键，等候30秒左右，LED显示测试处电阻，环境温湿度，作记录。显示表面电阻<1.0E+10Ω/sq，(65%RH，23℃)为合格；显示表面电阻>1.0E+10Ω/sq，(65%RH，23℃)不合格。
（6）耐磨性测试在钢丝面（#0000）的500g/cm2的加压下对硬涂层面摩擦30次后，对没有伤痕记作O，对有伤痕记作X。
（7）铅笔硬度测试按照GB/T6739-2006评价硬质涂层薄膜的铅笔硬度。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。

Claims (3)

1.一种具有耐刮性能的离型材料，其特征在于：所述抗静电离型材料位于作为离型膜的聚乙烯薄膜和离型剂层间，所述抗静电离型材料由下列质量百分含量的组分组成：
硅石颗粒2%、平均分子量为500~2000的丙烯酸多元醇28%、平均分子量为200~2500的聚氧化烯系列多元醇的树脂40%、聚乙二醇20%、1-羟基环己基苯基甲酮-光引发剂18410%；
所述硅石颗粒的粒径为由激光衍射·散射法测定的粒度分布中粒径在0.1~2um和1.5~5um的范围内分别具有峰值、且平均粒径为4um或以下。
2.根据权利要求1所述的具有耐刮性能的离型材料，其特征在于：所述离型剂层（2）为硅油。
3.根据权利要求1所述的具有耐刮性能的离型材料，其特征在于：所述离型膜厚度为0.3μm~0.35μm。
CN201510546136.7A 2012-12-20 2012-12-20 具有耐刮性能的离型材料 Pending CN105220565A (zh)