CN105219047A - A kind of high-temperature-resistant flame-retardant resin - Google Patents
A kind of high-temperature-resistant flame-retardant resin Download PDFInfo
- Publication number
- CN105219047A CN105219047A CN201510598774.3A CN201510598774A CN105219047A CN 105219047 A CN105219047 A CN 105219047A CN 201510598774 A CN201510598774 A CN 201510598774A CN 105219047 A CN105219047 A CN 105219047A
- Authority
- CN
- China
- Prior art keywords
- temperature
- retardant resin
- resistant flame
- thinner
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-temperature-resistant flame-retardant resin, each component and weight percent content thereof respectively: unsaturated polyester resin 27-45%, glass fibre 10-20%, thinner 5-8%, vinylformic acid isooctyl 1-5%, calcium carbonate 20-30%, fluorinated ethylene propylene 1-5%, silicon-dioxide 8-12%.The present invention is high temperature resistant and flame retardant properties good.
Description
Technical field
The present invention relates to technical field of polymer materials, particularly relate to a kind of high-temperature-resistant flame-retardant resin.
Background technology
Along with the development of corrosion and protection and the raising of industrialization degree, the Application Areas of matrix material is also more and more wider, and applying working condition, medium becomes increasingly complex, and use temperature is also more and more higher, and the requirement of market to its performance is also more and more higher.
At present, domestic and international field adopts high-property resin composite material material more single, and cause product use temperature low, at high temperature ability to bear is poor.Therefore, traditional matrix material far can not meet the market requirement more and more higher to its performance.
Summary of the invention
Technical problem to be solved by this invention is, provides a kind of high-temperature-resistant flame-retardant resin, high temperature resistant and flame retardant properties is better.
In order to solve the problems of the technologies described above, the invention provides a kind of high-temperature-resistant flame-retardant resin, it is characterized in that, each component and weight percent content thereof respectively:
Unsaturated polyester resin 27-45%,
Glass fibre 10-20%,
Thinner 5-8%,
Vinylformic acid isooctyl 1-5%,
Calcium carbonate 20-30%,
Fluorinated ethylene propylene 1-5%,
Silicon-dioxide 8-12%.
Optionally, described thinner is N-BUTYL ACETATE.
Optionally, described thinner is No. 200 solvent oils
Further, described content of glass fiber is 15%.
Further, described calcium carbonate content is 25%.
Further, described dioxide-containing silica is 10%.
Implement the present invention, there is following beneficial effect: the present invention is high temperature resistant and flame retardant properties is better.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Test according to composition shown in table 1.
Table 1
| Composition | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Unsaturated polyester resin | 45 | 45 | 27 |
| Glass fibre | 10 | 15 | 20 |
| Thinner | 5 | 8 | 5 |
| Vinylformic acid isooctyl | 5 | 1 | 1 |
| Calcium carbonate | 25 | 20 | 30 |
| Fluorinated ethylene propylene | 2 | 1 | 5 |
| Silicon-dioxide | 8 | 10 | 12 |
Wherein, described thinner is N-BUTYL ACETATE or No. 200 solvent oils
The effect of each embodiment is for shown in table 2.
Table 2
| Usefulness | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Glowing filament (850 DEG C of GWIT) | PASS | PASS | PASS |
| Glowing filament (950 DEG C of GWIT) | PASS | PASS | PASS |
implement the present invention, there is following beneficial effect: the present invention is high temperature resistant and flame retardant properties is better.
It should be noted that, in this article, term " comprises ", " comprising " or its any other variant are intended to contain comprising of nonexcludability, thus make to comprise the process of a series of key element, method, article or device and not only comprise those key elements, but also comprise other key elements clearly do not listed, or also comprise by the intrinsic key element of this process, method, article or device.When not more restrictions, the key element limited by statement " comprising ... ", and be not precluded within process, method, article or the device comprising this key element and also there is other identical element.
To the above-mentioned explanation of the disclosed embodiments, professional and technical personnel in the field are realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (6)
1. a high-temperature-resistant flame-retardant resin, is characterized in that, each component and weight percent content thereof respectively:
Unsaturated polyester resin 27-45%,
Glass fibre 10-20%,
Thinner 5-8%,
Vinylformic acid isooctyl 1-5%,
Calcium carbonate 20-30%,
Fluorinated ethylene propylene 1-5%,
Silicon-dioxide 8-12%.
2. high-temperature-resistant flame-retardant resin as claimed in claim 1, it is characterized in that, described thinner is N-BUTYL ACETATE.
3. high-temperature-resistant flame-retardant resin as claimed in claim 1, it is characterized in that, described thinner is No. 200 solvent oils.
4. high-temperature-resistant flame-retardant resin as claimed in claim 1, it is characterized in that, described content of glass fiber is 15%.
5. high-temperature-resistant flame-retardant resin as claimed in claim 1, it is characterized in that, described calcium carbonate content is 25%.
6. high-temperature-resistant flame-retardant resin as claimed in claim 1, it is characterized in that, described dioxide-containing silica is 10%.