CN105218168A - A kind of curve glaze and manufacture craft - Google Patents
A kind of curve glaze and manufacture craft Download PDFInfo
- Publication number
- CN105218168A CN105218168A CN201510778050.7A CN201510778050A CN105218168A CN 105218168 A CN105218168 A CN 105218168A CN 201510778050 A CN201510778050 A CN 201510778050A CN 105218168 A CN105218168 A CN 105218168A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- curve
- mass ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of curve glaze and manufacture craft, be made up of in mass ratio component A and B component, component A is by potassium felspar sand, aluminium lime stone, coarse whiting stone, quartz, glue and zirconium white form by weight, B component is by albite, Longyan kaolin, quartz, zinc oxide, barium carbonate and frit form by weight, frit is by quartz, red lead, feldspar, rhombspar and barium carbonate form in mass ratio, respectively raw material is mixed in proportion obtained compound, add water more fully to stir, mesh screen is crossed after ball milling, glaze is applied in porcelain billet surface, send in heating-up furnace and fire, curved goods must be had after kiln discharge cooling.Curve glaze formula of the present invention is reasonable, and the glazing effect of the curve glaze produced is stablized, and curve shape is graceful, can demonstrate the glazing effect of different stereo effects under different illumination, more evenly attractive in appearance; Firing time in manufacture craft is short, and firing temperature is low, thus reduces energy consumption, energy-conserving and environment-protective, reduces production cost.
Description
Technical field
The present invention relates to the preparing technical field of glaze, specifically a kind of curve glaze and manufacture craft.
Background technology
The glaze of ceramic makes corresponding product obtain the favor of many human consumers with the effect of its uniqueness, there is various glaze in the market, thus make the pattern of fictile and kind varied.Also there is many shortcomings in existing glaze, as unstable in glazing effect, and glazing effect is single, kind is dull, cannot cater to the consumer demand of different individual character, and market does not almost have curve glaze, thus this type of ceramic does not appear in market yet; In addition, existing most glaze firing time is long, and firing temperature is high, and the fuel expended needed for production is more, and production efficiency is also relatively lower, and production cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of curve glaze and manufacture craft, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A kind of curve glaze, in mass ratio by component A and B component is mixed and forms in 1:1 ~ 3,
Described component A is made up of following raw material: potassium felspar sand 55 ~ 65 parts, aluminium lime stone 15 ~ 25 parts, 15 ~ 25 parts, coarse whiting stone, 8 ~ 12 parts, quartz, 0.6 ~ 1.0 part, glue, zirconium white 15 ~ 25 parts;
Described B component is made up of following raw material: albite 11.7 ~ 13.7 parts, Longyan kaolin 13.6 ~ 15.6 parts, 1.0 ~ 1.8 parts, quartz, 4.5 ~ 6.5 parts, zinc oxide, barium carbonate 12.6 ~ 14.6 parts, frit 50.2 ~ 54.2 parts; Frit is made up of in mass ratio following raw material: quartz: red lead: feldspar: rhombspar: barium carbonate is 2:8:3:2:5.
A manufacture craft for curve glaze, concrete making step is as follows:
(1) glaze is prepared: above-mentioned raw materials is mixed in proportion obtained compound, again component A and B component are mixed in mass ratio, by compound: water is that the mass ratio of 1:0.75 ~ 0.85 adds water, and stir 3 ~ 5h, after ball milling 4 ~ 6h, cross 150 ~ 200 object mesh screens, obtained curve glaze glaze;
(2) glazing: apply glaze in porcelain billet surface;
(3) fire: sent in heating-up furnace by the porcelain base substrate after glazing and fire, firing temperature is 1120 ~ 1170 DEG C, and the firing time is 12 ~ 16h, after kiln discharge cooling, curved goods must be had.
Compared with prior art, the invention has the beneficial effects as follows: curve glaze formula of the present invention is reasonable, the glazing effect of the curve glaze produced is stablized, and curve shape is graceful, can demonstrate the glazing effect of different stereo effects under different illumination, more evenly attractive in appearance; Firing time in manufacture craft is short, and firing temperature can be formed at 1100 DEG C, and firing temperature is low, thus reduces energy consumption, energy-conserving and environment-protective, reduces production cost.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
Curve glaze, by component A and B component in mass ratio 1:1 mix and form,
Described component A is made up of following raw material: potassium felspar sand 55 parts, aluminium lime stone 25 parts, 15 parts, coarse whiting stone, 12 parts, quartz, 0.6 part, glue, zirconium white 25 parts;
Described B component is made up of following raw material: albite 11.7 parts, Longyan kaolin 15.6 parts, 1.0 parts, quartz, 6.5 parts, zinc oxide, barium carbonate 12.6 parts, frit 54.2 parts; Frit is made up of in mass ratio following raw material: quartz: red lead: feldspar: rhombspar: barium carbonate is 2:8:3:2:5.
The manufacture craft of above-mentioned curve glaze, concrete making step is as follows:
(1) prepare glaze: above-mentioned raw materials is mixed in proportion obtained compound, then component A and B component are mixed, in mass ratio by compound: water is that the mass ratio of 1:0.75 adds water, and stir 4h, after ball milling 5h, cross 150 ~ 200 object mesh screens, obtained curve glaze glaze;
(2) glazing: apply glaze in porcelain billet surface;
(3) fire: sent in heating-up furnace by the porcelain base substrate after glazing and fire, firing temperature is 1120 ~ 1170 DEG C, and the firing time is 12h, after kiln discharge cooling, curved goods must be had.
Embodiment 2
Curve glaze, by component A and B component in mass ratio 1:2 mix and form,
Described component A is made up of following raw material: potassium felspar sand 60 parts, aluminium lime stone 20 parts, 20 parts, coarse whiting stone, 10 parts, quartz, 0.8 part, glue, zirconium white 20 parts;
Described B component is made up of following raw material: albite 12.7 parts, Longyan kaolin 14.6 parts, 1.4 parts, quartz, 5.5 parts, zinc oxide, barium carbonate 13.6 parts, frit 52.2 parts; Frit is made up of in mass ratio following raw material: quartz: red lead: feldspar: rhombspar: barium carbonate is 2:8:3:2:5.
The manufacture craft of above-mentioned curve glaze, concrete making step is as follows:
(1) prepare glaze: above-mentioned raw materials is mixed in proportion obtained compound, then component A and B component are mixed, in mass ratio by compound: water is that the mass ratio of 1:0.8 adds water, and stir 4h, after ball milling 5h, cross 150 ~ 200 object mesh screens, obtained curve glaze glaze;
(2) glazing: apply glaze in porcelain billet surface;
(3) fire: sent in heating-up furnace by the porcelain base substrate after glazing and fire, firing temperature is 1120 ~ 1170 DEG C, and the firing time is 14h, after kiln discharge cooling, curved goods must be had.
Embodiment 3
Curve glaze, by component A and B component in mass ratio 1:3 mix and form,
Described component A is made up of following raw material: potassium felspar sand 65 parts, aluminium lime stone 15 parts, 25 parts, coarse whiting stone, 8 parts, quartz, 1.0 parts, glue, zirconium white 15 parts;
Described B component is made up of following raw material: albite 13.7 parts, Longyan kaolin 13.6 parts, 1.8 parts, quartz, 4.5 parts, zinc oxide, barium carbonate 14.6 parts, frit 50.2 parts; Frit is made up of in mass ratio following raw material: quartz: red lead: feldspar: rhombspar: barium carbonate is 2:8:3:2:5.
The manufacture craft of above-mentioned curve glaze, concrete making step is as follows:
(1) prepare glaze: above-mentioned raw materials is mixed in proportion obtained compound, then component A and B component are mixed, in mass ratio by compound: water is that the mass ratio of 1:0.85 adds water, and stir 5h, after ball milling 5h, cross 150 ~ 200 object mesh screens, obtained curve glaze glaze;
(2) glazing: apply glaze in porcelain billet surface;
(3) fire: sent in heating-up furnace by the porcelain base substrate after glazing and fire, firing temperature is 1120 ~ 1170 DEG C, and the firing time is 16h, after kiln discharge cooling, curved goods must be had.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
Claims (2)
1. a curve glaze, is characterized in that, in mass ratio by component A and B component is mixed and forms in 1:1 ~ 3,
Described component A is made up of following raw material: potassium felspar sand 55 ~ 65 parts, aluminium lime stone 15 ~ 25 parts, 15 ~ 25 parts, coarse whiting stone, 8 ~ 12 parts, quartz, 0.6 ~ 1.0 part, glue, zirconium white 15 ~ 25 parts;
Described B component is made up of following raw material: albite 11.7 ~ 13.7 parts, Longyan kaolin 13.6 ~ 15.6 parts, 1.0 ~ 1.8 parts, quartz, 4.5 ~ 6.5 parts, zinc oxide, barium carbonate 12.6 ~ 14.6 parts, frit 50.2 ~ 54.2 parts; Frit is made up of in mass ratio following raw material: quartz: red lead: feldspar: rhombspar: barium carbonate is 2:8:3:2:5.
2. a manufacture craft for curve glaze as claimed in claim 1, is characterized in that, concrete making step is as follows:
(1) glaze is prepared: above-mentioned raw materials is mixed in proportion obtained compound, again component A and B component are mixed in mass ratio, again by compound: water is that the mass ratio of 1:0.75 ~ 0.85 adds water, and stir 3 ~ 5h, after ball milling 4 ~ 6h, cross 150 ~ 200 object mesh screens, obtained curve glaze glaze;
(2) glazing: apply glaze in porcelain billet surface;
(3) fire: sent in heating-up furnace by the porcelain base substrate after glazing and fire, firing temperature is 1120 ~ 1170 DEG C, and the firing time is 12 ~ 16h, after kiln discharge cooling, curved goods must be had.