CN1052150A - 一种低合金耐硫酸露点腐蚀钢 - Google Patents
一种低合金耐硫酸露点腐蚀钢 Download PDFInfo
- Publication number
- CN1052150A CN1052150A CN 89109017 CN89109017A CN1052150A CN 1052150 A CN1052150 A CN 1052150A CN 89109017 CN89109017 CN 89109017 CN 89109017 A CN89109017 A CN 89109017A CN 1052150 A CN1052150 A CN 1052150A
- Authority
- CN
- China
- Prior art keywords
- steel
- sulfuric acid
- low
- corrosion
- point corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种Cu-Cr-RE系列低合金耐硫酸露点腐蚀
钢,适于制造锅炉空气预热器和其它接触二氧化硫、
三氧化硫气氛,易发生硫酸露点腐蚀的设备部件。具
有优异的耐硫酸露点腐蚀性能及含金元素用量少、冶
炼工艺简单、成本低廉、机械性能良好等优点。用这
种钢制造锅炉空气预热器可比A3钢的寿命提高2.5
倍以上。
Description
本发明涉及一种Cu-Cr-RE系列低合金耐硫酸露点腐蚀钢(以下简称Cu-Cr-RE钢),特别适用于制造锅炉空气预热器及其它接触二氧化硫、三氧化硫气氛,受硫酸露点腐蚀的设备部件。
锅炉通常所用的燃料如重油、煤中都含有一定量的硫(S),硫燃烧生成二氧化硫(SO2),其中一部分还会再氧化生成三氧化硫(SO2),三氧化硫与烟气中的水蒸汽结合成为硫酸蒸汽(H2SO4),在锅炉的低温部位如空气预热器,当其金属表面温度低于烟气露点时,硫酸就会凝结在金属表面上,引起硫酸露点腐蚀。
目前,世界上多数锅炉所设置的空气预热器采用普碳钢制造,耐低温硫酸露点腐蚀性能差,使用寿命短,更换频繁。空气预热气腐蚀漏泄不仅降低锅炉的热效率,而且增加大量的检修费用,甚至造成停产损失。不仅是锅炉,其它接触二氧化硫、三氧化硫气氛,受硫酸露点腐蚀的设备部件也同样存在类似的问题。为了解决上述问题,各国专家都进行了不懈的努力,相继地研制出一些钢种,其中有代表性的是美国专利US3443934号的“含Cu、Cr、Sn(或Sb)的耐硫酸腐蚀钢”,这种钢含有一定量的Sn或Sb,成本较高。基于这种情况,本发明人研制出一种Cu-Cr-RE钢,它不使用价格昂贵的Sn或Sb以及Ni等,Cr的加入量较少,最具特点的是它加入了一定量的RE元素,具有优异的耐硫酸露点腐蚀性能及合金元素用量少、冶炼工艺简单,成本低廉、机械性能良好等特点。
在低合金钢中,Cu的加入不仅能使钢产生固溶强化,提高钢的屈强比及疲劳强度,而且提高钢的耐硫酸露点腐蚀性能。少量Cu的加入,在钢中以弥散状态存在,起微阴极作用,Fe基则为微阳极。在腐蚀过程中,随着Fe的腐蚀在Fe氧化层和基体之间形成富Cu层,这个富Cu层能阻滞或延缓腐蚀的进行;Cr的加入是利用其所特有的优异的纯化性能,可使Fe基合金产生一钝化层,阻滞阳极过程,从而抑制腐蚀的发展;RE的加入,可以细化晶粒,提高钢的均匀性,改善夹杂物形状。经试验研究表明:RE的加入对提高钢耐硫酸腐蚀性能有着及其显著的作用。通过Cu、Cr和RE元素在钢中的加入及其适当的配比,以及对S、Si、P的适当控制,可使Cu-Cr-RE系列低合金钢具有良好的机械、工艺性能和极其优异的耐硫酸露点腐蚀性能。
本发明所提出的Cu-Cr-RE钢的化学成分如下:C≤0.13%,S=0.2%~0.8%,Mn=0.2%~1.0%,P≤0.035%,S=0.01%~0.035%,Cu=0.2%~0.4%,Cr=0.4%~1.0%,RE≤0.2%,其余为Fe和不可避免的杂质。
本发明所提出的Cu-Cr-RE钢,可在平炉或转炉上按常规优质镇静钢生产工艺冶炼,如采用炉外精炼则可进一步提高其综合性能。在冶炼过程中,Cu、Cr在炉内加入,RE可在出钢过程中或出钢后的钢包中加入,采用下注法浇注,钢锭脱膜后热送初轧,控制均热炉呈中性或还原性气氛,尽量减少待轧时间,最后按优质镇静钢工艺轧制成材。
本发明的Cu-Cr-RE钢的特点结合实施例说明如下:
国内某电厂燃油锅炉,使用含硫0.5%的重油,由于这种油酸值高,煤油厂在炼制过程中加入了大量的碱(NaOH),结果造成该电厂锅炉受热面严重结渣,被迫在运行中采用低温水冲洗,致使锅炉尾部受热面严重腐蚀,其中的空气预热器3~4年更换一次。在这种情况下,本发明人推荐使用Cu-Cr-RE钢代替原碳素钢制造空气预热器,所推荐钢种的化学成分为:C=0.1%,Si=0.38%,Mn=0.56%,P=0.012%,S=0.0265%,Cu=0.295%,Cr=0.638%,RE=0.106%,其余为Fe和不可避免的杂质。其机械性能与A3钢的比较情况如下表:
Cu-Cr-RE钢与A3钢机械性能对比 表1
在进行Cu-Cr-RE钢试验中,也与Cu-Cr钢进行了比较,表2给出了Cu-Cr-RE钢与Cu-Cr钢及A3钢的耐硫酸和硫酸露点腐蚀的试验结果:
从表2可以看到,在浓度为20%与40%的硫酸条件下,Cu-Cr-RE钢的耐腐蚀率分别为A3钢的19倍和14倍;在浓度为85%的流酸加活性炭条件下,Cu-Cr-RE钢的耐腐蚀率为A3钢的3.8倍。从表2还可以看到,加RE元素的Cu-Cr-RE钢比不加RE元素的Cu-Cr钢耐腐蚀率有显著提高。
本推荐钢种在该电厂锅炉空气预热部位进行了5688小时挂片试验,试验结果列如表3。
Cu-Cr-RE钢与A3钢、Cu-Cr钢挂片试验结果 表3
从表3中可以看出,Cu-Cr-RE钢耐腐蚀率为A3钢的3.5倍;加RE元素的Cu-Cr-RE钢与不加RE元素的Cu-Cr钢比较,其耐腐蚀率提高15%。以上结果表明,使用Cu-Cr-RE钢代替A3钢制造锅炉空气预热器可延长使用寿命2.5倍。
Claims (1)
1、一种Cu-Cr-RE系列低合金耐硫酸露点腐蚀钢,其特征在于其化学成分组成为:C≤0.13%,S=0.2%~0.8%,Mn=0.2%~1.0%,P≤0.035%,S=0.01%~0.035%,Cu=0.2%~0.4%,Cr=0.4%~1.0%,RE≤0.2%,其余为Fe和不可避免的杂质。