CN105196738A - Manufacturing method of fluorescent wooden pencils - Google Patents
Manufacturing method of fluorescent wooden pencils Download PDFInfo
- Publication number
- CN105196738A CN105196738A CN201510577790.4A CN201510577790A CN105196738A CN 105196738 A CN105196738 A CN 105196738A CN 201510577790 A CN201510577790 A CN 201510577790A CN 105196738 A CN105196738 A CN 105196738A
- Authority
- CN
- China
- Prior art keywords
- pencil
- pencils
- fluorescence
- mixture
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of production and processing of pencils, in particular to a manufacturing method of fluorescent wooden pencils. The manufacturing method is characterized by comprising steps as follows: (1), pencil boards are soaked in a fluorescent solvent for 4 hours, then taken out and dried at the temperature of 90 DEG C-110 DEG C; (2), the pencil boards are planed by a router to form groove plates which are 4.1-4.2mm thick and have core grooves matched with the diameter of pencil leads, and then the pencil leads and the pencil boards are bonded together with a binder, heated and dried for 1-8 hours at the temperature ranging from 50 DEG C-120 DEG C in a clamping state and processed into pencils with white bodies in the length of 178-180 mm by a planing machine; (3), the pencils with the white bodies are polished, and the wooden pencils are formed. The manufactured pencils can emit fluorescent light in dark, the fluorescent effect is stable and lasts long, the decorative performance and the interestingness of the pencils are improved, and the pencils can perform a certain illumination function on a desk at night to a certain degree.
Description
Technical field:
The present invention relates to the production and processing field of pencil, more specifically to a kind of manufacture method of fluorescence Wood pencil.
Background technology:
Along with global economy fast development, the raising of people's living standard, concept also constantly changes, and the requirement on stationery is also at constantly seeking change and innovation, and original old tradition continued to use by present pencil always, centuries, never too large change, the developing country particularly resemble China, continues to use the outmoded old tradition of black lead bag wood skin bar especially, outward appearance and moulding do not have too large change, the multifarious demand of people can not be met.
Summary of the invention:
Technical problem to be solved by this invention is to overcome the manufacture method that existing technological deficiency provides a kind of fluorescence Wood pencil.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A manufacture method for fluorescence Wood pencil, is characterized in that comprising the following steps:
(1) pencil board to be immersed in fluorescence solvent 4 hours, then take out oven dry, bake out temperature is 90-110 DEG C;
(2) thickness is become to be 4.1 ~ 4.2mm pencil board planer with keyway planer, and have the frid of the core groove adapted with lead core diameter, then adhesive is used lead for retractable pencil and pencil board gummed to be got up, heat (50 ~ 120 DEG C) in the clamp state after dry 1 ~ 8 hour, make through the machined of plane bar the white shaft pencil that length is 178 ~ 180mm;
(3) white shaft pencil sanding and polishing is become Wood pencil.
Further, described fluorescence solvent comprises the component of following weight portion: 50-60 part trichloro-ethylene, 40-50 part benzinum, 6-10 part olive oil, 1-3 part defoamer, 2-4 part stabilizing agent, 4-7 part alundum (Al2O3) pulvis, 1-2 part diffusant, 6-9 part rosin, 40-50 part photo-induced energy storage luminescent powder.
Further, the preparation method of described fluorescence solvent is:
(1) trichloro-ethylene, alundum (Al2O3) pulvis are uniformly mixed at the temperature of 50 DEG C, obtain mixture A;
(2) in mixture A, add rosin, olive oil to be uniformly mixed at the temperature of 70 DEG C, be then cooled to normal temperature, obtain mixture B
(3) benzinum, photo-induced energy storage luminescent powder are uniformly mixed at normal temperatures, obtain mixture C;
(4) mixture B is poured in mixture C, add and slowly stir, add defoamer, stabilizing agent, diffusant simultaneously, obtain fluorescence solvent.
The pencil that the present invention obtains can send fluorescence at dark place, and fluorescent effect is stable lasting, adds the ornamental and interesting of pencil, also can play illuminating effect to a certain extent at night on the table.
Detailed description of the invention:
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1: a kind of manufacture method of fluorescence Wood pencil, is characterized in that comprising the following steps:
(1) pencil board to be immersed in fluorescence solvent 4 hours, then take out oven dry, bake out temperature is 90 DEG C;
(2) thickness is become to be 4.1mm pencil board planer with keyway planer, and have the frid of the core groove adapted with lead core diameter, then adhesive is used lead for retractable pencil and pencil board gummed to be got up, heat (50 DEG C) in the clamp state after dry 8 hours, make through the machined of plane bar the white shaft pencil that length is 178mm;
(3) white shaft pencil sanding and polishing is become Wood pencil.
Fluorescence solvent comprises the component of following weight portion: 50 parts of trichloro-ethylenes, 40 parts of benzinums, 6 parts of olive oil, 1 part of defoamer, 2 parts of stabilizing agents, 4 parts of alundum (Al2O3) pulvis, 1 part of diffusant, 6 parts of rosin, 40 parts of photo-induced energy storage luminescent powders.
The preparation method of fluorescence solvent is:
(1) trichloro-ethylene, alundum (Al2O3) pulvis are uniformly mixed at the temperature of 50 DEG C, obtain mixture A;
(2) in mixture A, add rosin, olive oil to be uniformly mixed at the temperature of 70 DEG C, be then cooled to normal temperature, obtain mixture B
(3) benzinum, photo-induced energy storage luminescent powder are uniformly mixed at normal temperatures, obtain mixture C;
(4) mixture B is poured in mixture C, add and slowly stir, add defoamer, stabilizing agent, diffusant simultaneously, obtain fluorescence solvent.
Embodiment 2: a kind of manufacture method of fluorescence Wood pencil, is characterized in that comprising the following steps:
(1) pencil board to be immersed in fluorescence solvent 4 hours, then take out oven dry, bake out temperature is 110 DEG C;
(2) thickness is become to be 4.2mm pencil board planer with keyway planer, and have the frid of the core groove adapted with lead core diameter, then adhesive is used lead for retractable pencil and pencil board gummed to be got up, heat (120 DEG C) in the clamp state after dry 1 hour, make through the machined of plane bar the white shaft pencil that length is 180mm;
(3) white shaft pencil sanding and polishing is become Wood pencil.
Fluorescence solvent comprises component 60 parts of trichloro-ethylenes of following weight portion, 50 parts of benzinums, 10 parts of olive oil, 3 parts of defoamers, 4 parts of stabilizing agents, 7 parts of alundum (Al2O3) pulvis, 2 parts of diffusants, 9 parts of rosin, 50 parts of photo-induced energy storage luminescent powders.
The preparation method of fluorescence solvent is:
(1) trichloro-ethylene, alundum (Al2O3) pulvis are uniformly mixed at the temperature of 50 DEG C, obtain mixture A;
(2) in mixture A, add rosin, olive oil to be uniformly mixed at the temperature of 70 DEG C, be then cooled to normal temperature, obtain mixture B
(3) benzinum, photo-induced energy storage luminescent powder are uniformly mixed at normal temperatures, obtain mixture C;
(4) mixture B is poured in mixture C, add and slowly stir, add defoamer, stabilizing agent, diffusant simultaneously, obtain fluorescence solvent.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. a manufacture method for fluorescence Wood pencil, is characterized in that comprising the following steps:
(1) pencil board to be immersed in fluorescence solvent 4 hours, then take out oven dry, bake out temperature is 90-110 DEG C;
(2) thickness is become to be 4.1 ~ 4.2mm pencil board planer with keyway planer, and have the frid of the core groove adapted with lead core diameter, then adhesive is used lead for retractable pencil and pencil board gummed to be got up, heat (50 ~ 120 DEG C) in the clamp state after dry 1 ~ 8 hour, make through the machined of plane bar the white shaft pencil that length is 178 ~ 180mm;
(3) white shaft pencil sanding and polishing is become Wood pencil.
2. the manufacture method of a kind of fluorescence Wood pencil according to claim 1, is characterized in that described fluorescence solvent comprises the component of following weight portion: 50-60 part trichloro-ethylene, 40-50 part benzinum, 6-10 part olive oil, 1-3 part defoamer, 2-4 part stabilizing agent, 4-7 part alundum (Al2O3) pulvis, 1-2 part diffusant, 6-9 part rosin, 40-50 part photo-induced energy storage luminescent powder.
3. the manufacture method of a kind of fluorescence Wood pencil according to claim 2, is characterized in that the preparation method of described fluorescence solvent is:
(1) trichloro-ethylene, alundum (Al2O3) pulvis are uniformly mixed at the temperature of 50 DEG C, obtain mixture A;
(2) in mixture A, add rosin, olive oil to be uniformly mixed at the temperature of 70 DEG C, be then cooled to normal temperature, obtain mixture B
(3) benzinum, photo-induced energy storage luminescent powder are uniformly mixed at normal temperatures, obtain mixture C;
(4) mixture B is poured in mixture C, add and slowly stir, add defoamer, stabilizing agent, diffusant simultaneously, obtain fluorescence solvent.