CN105178562A - 无机晶磨石整体地坪系统及其施工工艺 - Google Patents
无机晶磨石整体地坪系统及其施工工艺 Download PDFInfo
- Publication number
- CN105178562A CN105178562A CN201510488455.7A CN201510488455A CN105178562A CN 105178562 A CN105178562 A CN 105178562A CN 201510488455 A CN201510488455 A CN 201510488455A CN 105178562 A CN105178562 A CN 105178562A
- Authority
- CN
- China
- Prior art keywords
- component
- terrace system
- grindstone
- integrated
- inorganic crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无机晶磨石整体地坪及其施工方法,无机晶磨石整体地坪由高强水泥;高分子乳液;抗裂聚炳烯纤维。及液态减水剂构成。地坪系统的施工方法,包含:基层处理,将砼表层以及含表层的各类涂层铣刨清除,铣刨深度4-6mm;伸缩缝等细部节点处理及地面基层冲洗清洁;基层涂刷界面剂,即B组份;铺筑无机晶磨石地坪系统的耐磨砂浆,即所述A组份+B组份+C组份;喷洒优质混凝土密封固化剂;硬化7-10天后,进行研磨找平,并补洒一次混凝土密封固化剂,抛光处理;养护1-2天。本发明环保、低耗能、无缝、抗冲击且造价较低,解决了环氧类地坪耐磨度低、易老化、起壳开裂,寿命短等缺陷;具有天然的抗漏、抗渗能力,地面不易被污染,节约大量的保洁人员。
Description
技术领域
本发明涉及建筑施工领域,具体地说是一种无机晶磨石整体地坪系统及其施工工艺。
背景技术
本发明针对原有老地坪存在的一些不易解决的问题。原有地坪为环氧类地坪或其他类地坪在使用过程中出现地面大量脱落,起砂,耐磨性明显降低的情况,以及原有地面存在各种大小的裂缝。整个工期要求非常紧迫的情况,本发明能够在非常短的时间内完工交付使用。以及业主对于地面要求燃烧性能达到A级的需求。
本发明针对上述情况,在以下范围内作出解决方案:
1)需在旧混凝土楼地面基层作高耐磨度无机晶磨石地面场所,如地下车库旧地坪改造;
2)需将环氧地坪改造为无机晶磨石地面的场所,如过去采用环氧树脂的涂层的工业厂房、地下车库;
3)学校、幼儿园、餐厅、图书馆、办公室等需要硬质、耐磨、环保地坪的场所;
4)计划采用无机晶磨石替代石材、瓷砖地坪的场所,如酒店大堂、会所、商场。
发明内容
本发明为解决现有的问题,旨在提供一种无机晶磨石整体地坪系统及其施工工艺。
为了达到上述目的,本发明提供一种无机晶磨石整体地坪,由三个组份构成:
A组份:高强水泥,莫氏硬度达到7以上的坚硬骨料,无机颜料及干粉减水剂;
B组份:高分子乳液;
C组份:抗裂聚丙烯纤维及液态减水剂。
其中,所述A组份中中配高硅含量石英砂和或含合金骨料和或无机颜料和干粉减水剂。
本发明提供一种地坪系统的施工工艺,包含下列步骤:
步骤一,基层处理,将砼表层以及含表层的各类涂层铣刨清除,铣刨深度4-6mm;
步骤二,伸缩缝等细部节点处理及地面基层冲洗清洁;
步骤三,基层完全水浸泡24小时;
步骤四,基层涂刷界面剂,即B组份;
步骤五,铺筑无机晶磨石地坪系统的高强聚合物快速摊铺型耐磨砂浆,即所述A组份+B组份+C组份+水;厚度为6-10mm;
步骤六,喷洒优质混凝土密封固化剂;
步骤七,硬化7-10天后,进行研磨,并补洒一次混凝土密封固化剂,抛光处理;
步骤八,养护1-2天,完成施工。
相比于现有技术,本发明产品的质感、硬度、寿命与传统的石材相近,独特的整体地面效果可以实现连续的图形构图,具有替代石材和瓷砖的天然优势,环保、低耗能、无缝、抗冲击且造价较低;在旧地面改造中解决了环氧类地坪耐磨度低、易老化、起壳开裂,寿命短等缺陷;材料中99.0%以上的材料为无机材料,从生产、运输、施工到废弃物各个环节均达到了最大限度的节能、环保、安全;超硬耐磨地面的抗压强度达到的90Mpa以上,莫氏硬度达到8,保证了无机晶磨石整体地坪系统地面的长期使用效果,节约大量的维修和翻新费用;具有天然的抗漏、抗渗能力,地面不易被污染,地面保洁只需很少的水和简单的工具,同时节约大量的保洁人员。
具体实施方式
下面结合实施例对本发明的具体实施方法作进一步描述。该实施例用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
具体实施方案:
在具体施工之前,要根据现场地面实际情况制定针对性、差异性设计方案。
本实施例的基础地表是:环氧类涂层的剥落,起砂;混凝土原浆收光使用后出现强度降低并伴有起灰、起砂等现象出现;耐磨地坪在使用后出现强度降低并伴有起灰、起砂等现象出现等等。根据铣刨出的效果,决定下一步的处理措施,如果地面在铣刨一次后就露出坚硬无松动颗粒和浮灰的基层,在标高要求下可为成本考量,降低摊铺砂浆的厚度,最薄为6mm。
如果铣刨一次,基层仍不符合施工要求,必须再一次铣刨,出现坚硬无松动颗粒和浮灰的基层,才能继续下一工序。否则,后期一定会出现空鼓,开裂,最后整体脱落。
如果该地面为重载地面,经常需要承受高负荷,高频次的车辆通行,那就需要增加摊铺的厚度,在预算成本许可的情况下,最好至10mm或更换金属骨料,或两者一起实施。。
首先采取步骤一,即对基层处理,将砼表层(含表层的各类涂层)铣刨清除,铣刨深度4-6mm。需要运用专业铣刨机,事前调节铣刨深度,按顺序依次铣刨作业,做到不留死角。
步骤二,对于伸缩缝等细部节点处理及地面基层冲洗;对于原有地面的伸缩缝,需要使用切割机在原来缝上往下切割3到4cm,在原有的缝上事先处理缝的问题,以免在后期使用过程中出现更多不可控的裂缝;同时,在对于以后可能出现新裂缝的地面,预留新缝。地面需要用水清洗浮灰和松动颗粒,用工业吸尘器处理干净。
步骤三,基层用水完全浸泡24小时;在已经处理好的基层需要洒水浸泡24小时,让地面充分湿润,这样才能让新摊铺的砂浆层与基层牢固地结合。
步骤四,基层涂刷界面剂(B组份);B组份为丁苯乳液,主要起到界面剂的作用,使得新老结合面牢固粘结。该组份可以滚涂或者喷洒,需要均匀涂覆。必须在界面剂未干之前,摊铺上已经搅拌好的砂浆层材料。
步骤五,铺筑KAFDTM无机晶磨石整体地坪系统耐磨砂浆,即运用A组份+B组份+C组份+水;小面积的可以使用手持式搅拌棒在25L或30L的塑料桶中先加入A、B、C组份后,再加入事前已经称量好的80%的水搅拌,最后再加入剩余20%的水,搅拌时间不少于3分钟,静置3分钟后,摊铺于已经涂覆未干的界面剂上,用刮尺刮平,用打磨机压实,收光处理。
步骤六、喷洒优质混凝土密封固化剂;主要成分为偏硅酸盐。喷洒液体固化剂可以起到保水,增加地面致密度的效果,使地面的强度和硬度都有相应提升。
步骤七,硬化7-10天后,进行研磨找平并补洒一次混凝土密封固化剂,抛光处理;
在养护1-2天后,即可交客户使用。
本发明可以在已硬化的新混凝土地面或使用多年的旧混凝土地面铺筑的超薄水泥基、快硬高强聚合物快速摊铺耐磨地坪系统。一举突破了水泥硬化地面,俗称金钢砂地面,只能与新浇筑混凝土找平层同步施工的技术瓶颈。为旧地面改造和室内整体装饰地坪提供了一个很有前景的解决方案。
上述仅为本发明的优选实施方式,应指出的是,对于本行业内的普通技术技术人员而言,在本发明的原理之下可以由一些改进和替换,该改进和替换也应视为本发明的保护范围。
Claims (3)
1.一种无机晶磨石整体地坪系统,其特征在于:由三个组份构成:
A组份:高强水泥,莫氏硬度达到7以上的坚硬骨料,无机颜料及干粉减水剂;
B组份:高分子乳液;
C组份:抗裂聚丙烯纤维及液态减水剂。
2.根据权利要求1所述的一种无机晶磨石整体地坪系统,其特征在于:所述A组份中配高硅含量石英砂和或含合金骨料和或无机颜料和或干粉减水剂。
3.一种地坪系统的施工方法,其特征在于:
包含下列步骤:
步骤一,基层处理,将砼表层以及含表层的各类涂层铣刨清除,铣刨深度4-6mm;
步骤二,伸缩缝等细部节点处理及地面基层冲洗清洁;
步骤三,基层完全水浸泡24小时;
步骤四,基层涂刷界面剂,即B组份;
步骤五,铺筑无机晶磨石地坪系统的高强聚合物快速摊铺型耐磨砂浆,即所述A组份+B组份+C组份+水;厚度为6-10mm;
步骤六,喷洒优质混凝土密封固化剂;
步骤七,硬化7-10天后,进行研磨,并补洒一次混凝土密封固化剂,抛光处理;
步骤八,养护1-2天,完成施工。