CN105177733A - 聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法 - Google Patents
聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法 Download PDFInfo
- Publication number
- CN105177733A CN105177733A CN201510512844.9A CN201510512844A CN105177733A CN 105177733 A CN105177733 A CN 105177733A CN 201510512844 A CN201510512844 A CN 201510512844A CN 105177733 A CN105177733 A CN 105177733A
- Authority
- CN
- China
- Prior art keywords
- spinning
- spinning nozzle
- spinning head
- draw
- liquid level
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法,属于高分子材料的制备领域,其特征在于包括如下步骤:(1)把预处理好的喷丝头与物料管线连接好,开启计量泵,向喷丝头内打料。(2)观察喷丝板面,直至喷丝板面出物料。(3)快速并匀速把喷丝板没入凝固液液面以下至1mm-5mm。(4)待喷丝板处喷出的丝束达到所要求的长度时,用棉绳系好,引出凝固浴槽。(5)把丝束引出凝固浴槽,上引丝辊稳定后,缓慢提高喷丝头高度,直至离开液面至指定高度后固定好喷丝头。
Description
技术领域
本发明涉及一种高分子材料的制备领域,具体地说是一种聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法。
背景技术
众所周知,碳纤维由于其轻量化,得到了广泛的应用。近年来,随着国内市场的扩大,对碳纤维的低成本化的呼声越来越高,这就使得高效低成本的干喷湿纺得到了快速发展。干喷湿纺关键点之一是凝固过程,如何得到好的凝固丝条是各个碳纤维企业研究的重点,而引丝方法是大家一致认为的难点。
发明内容
为了克服现有技术的不足,本发明提供一种聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法,使用此方法引丝,喷丝头板面不糊板,且板面无水滴,为后续的纺丝提供了保障。
本发明解决其技术问题所采用的技术方案是:一种聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法,其特征在于包括如下步骤:
(1)把预处理好的喷丝头与物料管线连接好,开启计量泵,向喷丝头内打料。
(2)观察喷丝板面,直至喷丝板面出物料。
(3)快速并匀速把喷丝板没入凝固液液面以下至1mm-5mm。
(4)待喷丝板处喷出的丝束达到一定长度时,用棉绳系好,引出凝固浴槽。
(5)把丝束引出凝固浴槽,上引丝辊稳定后,缓慢提高喷丝头高度,直至离开液面至指定高度后固定好喷丝头。
本发明的有益效果是,使用此方法引丝,喷丝头板面不糊板,且板面无水滴,为后续的纺丝提供了保障。
具体实施方式
下面通过实施例对本发明进一步说明。
本发明干喷湿纺喷丝头的引丝方法,其步骤包括:
(1)把预处理好的喷丝头与物料管线连接好,开启计量泵,向喷丝头内打料。
(2)观察喷丝板面,直至喷丝板面出物料。
(3)快速并匀速把喷丝板没入凝固液液面以下至一定深度。
(4)待喷丝板处喷出的丝束达到所要求的长度时,用棉绳系好,引出凝固浴槽。
(5)把丝束引出凝固浴槽,上引丝辊稳定后,缓慢提高喷丝头高度,直至离开液面至指定高度后固定好喷丝头。
本发明的工作原理:把喷丝头的板面没入凝固液指定深度后引丝,这样可以保证未出丝的孔直接堵塞,不会形成糊板点;正常喷丝的孔在单丝喷出喷丝孔的瞬间凝固,不对相邻的单丝形成影响;喷丝板面不会滞留凝固液滴,不会对喷丝板的预处理形成破坏。
实施例1:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面没入凝固液液面1mm,喷丝板面出现糊板点数量为0个,板面无凝固液滴滞留。
实施例2:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面没入凝固液液面3mm,喷丝板面出现糊板点数量为0个,板面无凝固液滴滞留。
实施例3:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面没入凝固液液面5mm,喷丝板面出现糊板点数量为0个,板面无凝固液滴滞留。
实施例4:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面没入凝固液液面6mm,喷丝板面出现糊板点数量为0个,板面有凝固液滴滞留。
实施例5:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面没入凝固液液面10mm,喷丝板面出现糊板点数量为0个,板面有凝固液滴滞留。
比较例1:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面在凝固液液面上方1mm,喷丝板面出现糊板点数量为3个,板面无凝固液滴滞留。
比较例2:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面在凝固液液面上方2mm,喷丝板面出现糊板点数量为3个,板面无凝固液滴滞留。
比较例3:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面在凝固液液面上方5mm,喷丝板面出现糊板点数量为4个,板面无凝固液滴滞留。
比较例4:按上述喷丝头引丝步骤进行操作,其中步骤(3)中喷丝板面在凝固液液面上方10mm,喷丝板面出现糊板点数量为5个,板面无凝固液滴滞留。
实施例1、实施例2、实施例3、实施例4、实施例5、比较例1、比较例2、比较例3、比较例4与喷丝头板面出现糊板点的关系如表1所示:
表1
根据表1的具体实施例和比较例可以看出:
从实施例1、实施例2、实施例3、实施例4、实施例5和比较例1、比较例2、比较例3、比较例4中可以看出,把喷丝头板面没入凝固液液面下引丝,喷丝板出现糊板点数量为0;在凝固液液面以上引丝,出现糊板点的数量明显多于把喷丝头没入凝固液中引丝的糊板点数量。
从实施例1、实施例2、实施例3、实施例4、实施例5中可以看出,把喷丝头喷丝板没入凝固液液面以下1mm-5mm喷丝板板面无水珠,效果较好;把喷丝头喷丝板没入凝固液液面以下6mm-10mm,喷丝板板面有水珠。
Claims (1)
1.一种聚丙烯腈碳纤维原丝干喷湿纺喷丝头的引丝方法,其特征在于包括如下步骤:
(1)把预处理好的喷丝头与物料管线连接好,开启计量泵,向喷丝头内打料;
(2)观察喷丝板面,直至喷丝板面出物料;
(3)快速并匀速把喷丝板没入凝固液液面以下至1mm-5mm;
(4)待喷丝板处喷出的丝束达到所要求的长度时,用棉绳系好,引出凝固浴槽;
(5)把丝束引出凝固浴槽,上引丝辊稳定后,缓慢提高喷丝头高度,直至离开液面至指定高度后固定好喷丝头。