CN105176338A - Scratch-resistant water-based paint - Google Patents
Scratch-resistant water-based paint Download PDFInfo
- Publication number
- CN105176338A CN105176338A CN201510430070.5A CN201510430070A CN105176338A CN 105176338 A CN105176338 A CN 105176338A CN 201510430070 A CN201510430070 A CN 201510430070A CN 105176338 A CN105176338 A CN 105176338A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- defoamer
- trimethylolpropane
- magnesium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a scratch-resistant water-based paint. The paint is prepared from 36-40 parts of short oil alkyd resin, 10-12 parts of an acrylic emulsion, 4-6 parts of vermiculite powder, 2.5-4 parts of arachidic acid, 3.5-4 parts of magnesium chloride, 4.5-5.5 parts of calcined clay, 2.4-3 parts of trimethylolpropane, 3-5 parts of amide modified hydrogenated castor oil, 4-6 parts of methylisobutylketone, 2.5-3.5 parts of a flatting agent, 0.7-0.9 part of a defoamer, 35-40 parts of deionized water and 1.2-2.5 parts of pigments. The paint disclosed by the invention does not contain groups that can be easily oxidized or hydrolyzed, so that the paint is better in gloss retention, scratch resistance, water resistance and weather resistance.
Description
Technical field
The present invention relates to decorative paint field, specifically belong to a kind of damage resistant aqueous paint.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is thickness oil colour, inflammable in not dry situation, water insoluble, is slightly soluble in fat, dissolves in alcohol, aldehyde, ether, benzene, alkane, be soluble in gasoline, kerosene, diesel oil.
Kind is painted much in present market, but various paint is all made up of filmogen (various resin), solvent, pigment, siccative, additive.Common paint makes solvent with gasoline usually, and epoxy iron red shop primer is containing a small amount of dimethylbenzene, and dipping lacquer mainly containing toluene, also has a small amount of benzene, very large on human body impact.
Summary of the invention
The object of this invention is to provide a kind of damage resistant aqueous paint, not containing group that is oxidizable and hydrolysis, the gloss retention thus painted, scratch resistance, water tolerance and weathering resistance are better.
The technical solution used in the present invention is as follows:
A kind of damage resistant aqueous paint, by weight, is made up of following raw material:
Short-oil alkyd 36-40, ACRYLIC EMULSION 10-12, vermiculite power 4-6, eicosanoic acid 2.5-4, magnesium chloride 3.5-4, calcined clay 4.5-5.5, TriMethylolPropane(TMP) 2.4-3, amide modifications hydrogenated castor oil 3-5, mibk 4-6, flow agent 2.5-3.5, defoamer 0.7-0.9, deionized water 35-40, pigment 1.2-2.5;
After getting calcined clay, vermiculite power, magnesium chloride mixing, gained powder dodges in sudden strain of a muscle firing and burns 2-3 second at 1000-1060 DEG C, take out cooling again, after mixing with pigment, TriMethylolPropane(TMP), defoamer and appropriate amount of deionized water, three-roll grinder grinding 40-50 minute, taking out the sodium hydroxide solution adding 8-12% adjusts PH to be 7.8-8.2, add short-oil alkyd, amide modifications hydrogenated castor oil again, after ground slurry to 200-300 order, add carbonic acid soln again and be adjusted to neutrality, gained neutral blends mixes with other surplus stock, mixes and obtain this paint.
A kind of damage resistant aqueous paint, by weight, be made up of following raw material: short-oil alkyd 38, ACRYLIC EMULSION 11, vermiculite power 5, eicosanoic acid 3.2, magnesium chloride 3.75, calcined clay 5, TriMethylolPropane(TMP) 2.7, amide modifications hydrogenated castor oil 4, mibk 5, flow agent 3, defoamer 0.8, deionized water 37.5, pigment 1.8.
Containing short-oil alkyd, ACRYLIC EMULSION, mibk in starting material of the present invention, not containing group that is oxidizable and hydrolysis, the gloss retention thus painted, scratch resistance, water tolerance and weathering resistance are better.
Embodiment
A kind of damage resistant aqueous paint, by weight, be made up of following raw material: short-oil alkyd 38, ACRYLIC EMULSION 11, vermiculite power 5, eicosanoic acid 3.2, magnesium chloride 3.75, calcined clay 5, TriMethylolPropane(TMP) 2.7, amide modifications hydrogenated castor oil 4, mibk 5, flow agent 3, defoamer 0.8, deionized water 37.5, pigment 1.8;
After getting calcined clay, vermiculite power, magnesium chloride mixing, gained powder dodges burning 2.5 seconds in sudden strain of a muscle firing at 1030 DEG C, take out cooling again, after mixing with pigment, TriMethylolPropane(TMP), defoamer and appropriate amount of deionized water, three-roll grinder grinds 45 minutes, take out add 10% sodium hydroxide solution adjust PH be 8, add short-oil alkyd, amide modifications hydrogenated castor oil again, after ground slurry to 250 order, add carbonic acid soln again and be adjusted to neutrality, gained neutral blends mixes with other surplus stock, mixes and obtain this paint.
Performance test of the present invention:
Wet rubbing is washed, 25 days >11000 time
Film thickness, 0-2000 μ does not ftracture
Anti-aging test (100 hours Qq-uvb) nondiscoloration, hydrophobic nature is obvious
Resistance to stained (according to national standard) 12.0% is excellent.
Claims (2)
1. a damage resistant aqueous paint, by weight, is characterized in that, is made up of following raw material:
Short-oil alkyd 36-40, ACRYLIC EMULSION 10-12, vermiculite power 4-6, eicosanoic acid 2.5-4, magnesium chloride 3.5-4, calcined clay 4.5-5.5, TriMethylolPropane(TMP) 2.4-3, amide modifications hydrogenated castor oil 3-5, mibk 4-6, flow agent 2.5-3.5, defoamer 0.7-0.9, deionized water 35-40, pigment 1.2-2.5;
After getting calcined clay, vermiculite power, magnesium chloride mixing, gained powder dodges in sudden strain of a muscle firing and burns 2-3 second at 1000-1060 DEG C, take out cooling again, after mixing with pigment, TriMethylolPropane(TMP), defoamer and appropriate amount of deionized water, three-roll grinder grinding 40-50 minute, taking out the sodium hydroxide solution adding 8-12% adjusts PH to be 7.8-8.2, add short-oil alkyd, amide modifications hydrogenated castor oil again, after ground slurry to 200-300 order, add carbonic acid soln again and be adjusted to neutrality, gained neutral blends mixes with other surplus stock, mixes and obtain this paint.
2. damage resistant aqueous paint according to claim 1, it is characterized in that, by weight, be made up of following raw material: short-oil alkyd 38, ACRYLIC EMULSION 11, vermiculite power 5, eicosanoic acid 3.2, magnesium chloride 3.75, calcined clay 5, TriMethylolPropane(TMP) 2.7, amide modifications hydrogenated castor oil 4, mibk 5, flow agent 3, defoamer 0.8, deionized water 37.5, pigment 1.8.