CN105176295A - Fireproof paint for wooden furniture - Google Patents
Fireproof paint for wooden furniture Download PDFInfo
- Publication number
- CN105176295A CN105176295A CN201510430071.XA CN201510430071A CN105176295A CN 105176295 A CN105176295 A CN 105176295A CN 201510430071 A CN201510430071 A CN 201510430071A CN 105176295 A CN105176295 A CN 105176295A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- water
- slurry
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof paint for wooden furniture. The fireproof paint for wooden furniture is prepared from the following raw materials in parts by weight: 25-27 parts of SEBS resin, 3-5 parts of toner slurry, 5-7 parts of polyvinyl butyral, 4.5-7 parts of bentonite, 1.5-2.5 parts of ferric oxide, 3.5-5.5 parts of calcined kaolin, 5.5-8.5 parts of non-floating type aluminum powder slurry, 4-6 parts of turpentine, 1.4-2.5 parts of a water reducer, 1.5-1.9 parts of a flame retardant 400A and 32-36 parts of water. According to the invention, the raw materials are low in price, the use amount of harmful chemicals is low, and the paint has good viscosity and can be quickly set while being capable of maintaining long-term attachment.
Description
Technical field
The present invention relates to paint field, specifically belong to a kind of wood furniture retardant paint.
Background technology
Modern paint is of a great variety, purposes also gets more and more, painting general use-pattern is cover body surface by the mode such as whitewashing, play fire prevention, protection against the tide, the works effect such as antirust, can the stickiness of wherein painting paint the important performance indexes that effectively cover, it is poor to there is stickiness in present paint, to whitewash in process not easily rapid solidification, containing problems such as irritant chemical compositions.
Summary of the invention
The object of this invention is to provide a kind of wood furniture retardant paint, the prices of raw and semifnished materials are low, and Harmful chemicals consumption is few, stickiness is good, can rapid solidification, the retardant paint of long-term attachment can be kept.
The technical solution used in the present invention is as follows:
A kind of wood furniture retardant paint, by weight, is made up of following raw material:
SEBS resin 25-27 part, toner slurry 3-5 part, polyvinyl butyral acetal 5-7 part, wilkinite 4.5-7 part, ferric oxide 1.5-2.5 part, calcined kaolin 3.5-5.5 part, not floating type aluminium powder slurries 5.5-8.5, turps 4-6 part, water reducer 1.4-2.5 part, fire retardant 400A1.5-1.9 part, water 32-36 part;
Its concrete preparation method is as follows:
1) ferric oxide after fine grinding, calcined kaolin, wilkinite are put in whipping device, granularity is 100-200 order, and add suitable quantity of water and fully stir, stirring cannot not add floatingly type aluminium powder slurries, water reducer, stirring velocity 880-1000r/min, churning time is 1.5-2h, and the slurry after stirring carries out steam curing, curing temperature controls at 90-105 DEG C, curing time 14-16h;
2) slurry after vapor cure fully mixes with surplus stock, enters in carbonizing chamber after mixing, carbonizing chamber C0
2the concentration of gas remains 15 soil 3%, and the temperature of carbonizing chamber controls at 25 ~ 30 DEG C, and relative air humidity remains on 90-93%, and carbonization time is 12 ~ 15h;
3) paint work in-process after carbonization, after static 3-5 days, carry out barrelling, warehouse-in.
Ferric oxide after fine grinding, calcined kaolin, wilkinite are put in whipping device, granularity is 150 orders, and add suitable quantity of water and fully stir, stirring cannot not add floatingly type aluminium powder slurries, water reducer, stirring velocity 940r/min, churning time is 1.8h, and the slurry after stirring carries out steam curing, curing temperature controls at 97 DEG C, curing time 15h.
There is no toxic raw materials in raw material of the present invention, and in technique, adopt wilkinite as dispersion agent, improve dispersion efficiency, shorten jitter time.The prices of raw and semifnished materials are low, and flame retardant properties is good, and Harmful chemicals consumption is few, and paint adhesion is strong, and strength of coating is high, good permeability, and acid and alkali-resistance is ageing-resistant, excellent property.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of wood furniture retardant paint, by weight, is made up of following raw material:
SEBS resin 26 parts, toner starch 4 parts, polyvinyl butyral acetal 6 parts, wilkinite 5.7 parts, ferric oxide 2 parts, calcined kaolin 4 parts, floating type aluminium powder slurries 7,5 parts, turps, water reducer 1.9 parts, fire retardant 400A1.7 part, 34 parts, water;
Its concrete preparation method is as follows:
1) ferric oxide after fine grinding, calcined kaolin, wilkinite are put in whipping device, granularity is 150 orders, and add suitable quantity of water and fully stir, stirring cannot not add floatingly type aluminium powder slurries, water reducer, stirring velocity 940r/min, churning time is 1.8h, and the slurry after stirring carries out steam curing, curing temperature controls at 97 DEG C, curing time 15h;
2) slurry after vapor cure fully mixes with surplus stock, enters in carbonizing chamber after mixing, carbonizing chamber C0
2the concentration of gas remains 15%, and the temperature of carbonizing chamber controls at 28 DEG C, and relative air humidity remains on 91.5%, and carbonization time is 13.5h;
3) paint work in-process after carbonization, after static 3-5 days, carry out barrelling, warehouse-in.
The test performance of the present invention's paint.
Air permeance resistance, Sd-value 0.025m is excellent
Sticking power 4.12N/mm
2excellent
Package stability, 27 days/48 DEG C excellent
Wet rubbing is washed, 4 days >2200 time.
Claims (2)
1. a wood furniture retardant paint, by weight, is characterized in that, is made up of following raw material:
SEBS resin 25-27 part, toner slurry 3-5 part, polyvinyl butyral acetal 5-7 part, wilkinite 4.5-7 part, ferric oxide 1.5-2.5 part, calcined kaolin 3.5-5.5 part, not floating type aluminium powder slurries 5.5-8.5, turps 4-6 part, water reducer 1.4-2.5 part, fire retardant 400A1.5-1.9 part, water 32-36 part;
Its concrete preparation method is as follows:
1) ferric oxide after fine grinding, calcined kaolin, wilkinite are put in whipping device, granularity is 100-200 order, and add suitable quantity of water and fully stir, stirring cannot not add floatingly type aluminium powder slurries, water reducer, stirring velocity 880-1000r/min, churning time is 1.5-2h, and the slurry after stirring carries out steam curing, curing temperature controls at 90-105 DEG C, curing time 14-16h;
2) slurry after vapor cure fully mixes with surplus stock, enters in carbonizing chamber after mixing, carbonizing chamber C0
2the concentration of gas remains 15 soil 3%, and the temperature of carbonizing chamber controls at 25 ~ 30 DEG C, and relative air humidity remains on 90-93%, and carbonization time is 12 ~ 15h;
3) paint work in-process after carbonization, after static 3-5 days, carry out barrelling, warehouse-in.
2. wood furniture retardant paint according to claim 1, it is characterized in that, ferric oxide after fine grinding, calcined kaolin, wilkinite are put in whipping device, and granularity is 150 orders, and add suitable quantity of water and fully stir, stirring cannot not add floatingly type aluminium powder slurries, water reducer, stirring velocity 940r/min, churning time is 1.8h, and the slurry after stirring carries out steam curing, curing temperature controls at 97 DEG C, curing time 15h.