CN105176267A - Waterborne wood-grained color developing agent and preparation method thereof - Google Patents
Waterborne wood-grained color developing agent and preparation method thereof Download PDFInfo
- Publication number
- CN105176267A CN105176267A CN201510677108.9A CN201510677108A CN105176267A CN 105176267 A CN105176267 A CN 105176267A CN 201510677108 A CN201510677108 A CN 201510677108A CN 105176267 A CN105176267 A CN 105176267A
- Authority
- CN
- China
- Prior art keywords
- water
- wood grain
- based wood
- agent
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterborne wood-grained color developing agent and a preparation method thereof. The waterborne wood-grained color developing agent consists of the following components in percentage by mass: 1 to 10 percent of inorganic gel, 0.5 to 1.0 percent of PH agent, 30 to 50 percent of water, 20 to 40 percent of propylene glycol, 20 to 40 percent of acrylic resin, 0.1 to 0.5 percent of wetting agent, 0.1 to 1 percent of defoaming agent, 0.1 to 0.2 percent of preservative and 0.1 to 0.2 percent of mold inhibitor. The waterborne wood-grained color developing agent disclosed by the invention can effectively replace Glaze, finishing varnish does not need to be applied, thus the problem of yellowing does not exist, the waterborne color developing agent disclosed by the invention has excellent adhesive force, water resistance and chemical resistance, and thereby the durability of the coated surface effect is guaranteed.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of water-based wood grain developer and preparation method thereof.
Background technology
The painted general employing Ge Lisi of obliterating of the various wood furniture products such as current solid wood, subsides wood skin, it is also called antiquing paint, and be a kind of translucent to transparent pigment colorant, its translucency can reduce wood furniture brightness, make face soft, formed when hatching effect.When using, be generally use solvent type Ge Lisi to carry out painted to open finish paint, to be dried completely after, then spray solvent-borne type Lacquer finish finish paint.But Ge Lisi and Lacquer finish finish paint sticking power are also bad, easily peel off after the time is long, and the easy xanthochromia of Lacquer finish finish paint thus to affect plate face attractive in appearance.
Therefore, prior art has yet to be improved and developed.
Summary of the invention
In view of above-mentioned the deficiencies in the prior art, the object of the present invention is to provide a kind of water-based wood grain developer and preparation method thereof, be intended to solve the finish paint run into when using Ge Lisi painted at present and easily come off, the problem of easy xanthochromia.
Technical scheme of the present invention is as follows:
A kind of water-based wood grain developer, wherein, consists of the following composition by mass percentage:
Inorganic gel 1-10%;
PH agent 0.5-1.0%;
Water 30-50%;
Propylene glycol 20-40%;
Acrylic resin 20-40%;
Wetting agent 0.1-0.5%;
Defoamer 0.1-1%;
Sanitas 0.1-0.2%;
Mould inhibitor 0.1-0.2%.
Described water-based wood grain developer, wherein, the pH value of described inorganic gel is 7-9.5.
Described water-based wood grain developer, wherein, described PH agent is AMP-95, and acrylic resin is J-95, and wetting agent is TEGO245, and defoamer is 5202, and sanitas is Kathon CG, and mould inhibitor is OBPA.
Described water-based wood grain developer, wherein, described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 2.7%;
PH agent 0.5%;
Water 45%;
Propylene glycol 15%;
Acrylic resin 35%;
Wetting agent 0.5%;
Defoamer 1.0%;
Sanitas 0.1%;
Mould inhibitor 0.2%.。
A preparation method for water-based wood grain developer as above, wherein, said method comprising the steps of:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and disperse 5-10 minute to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 10-15 minute to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, mixture is disperseed under dispersion machine 400r/min rotating speed, through 200 mesh screen packagings after being up to the standards.
The preparation method of described water-based wood grain developer, wherein, in described step B high speed dispersion, dispersing speed is 800r/min.
Beneficial effect: the invention provides a kind of water-based wood grain developer and preparation method thereof, this water-based wood grain developer effectively can substitute Ge Lisi, and it is without the need to using finishing paint, thus there is not xanthochromia problem, water-based developer of the present invention has excellent sticking power, water tolerance and chemical-resistant simultaneously, thus ensure that the persistence spreading surface effect.
Embodiment
The invention provides a kind of water-based wood grain developer and preparation method thereof, for making object of the present invention, technical scheme and effect clearly, clearly, the present invention is described in more detail below.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
The invention provides a kind of water-based wood grain developer, wherein, consist of the following composition by mass percentage:
Inorganic gel 1-10%;
PH agent 0.5-1.0%;
Water 30-50%;
Propylene glycol 20-40%;
Acrylic resin 20-40%;
Wetting agent 0.1-0.5%;
Defoamer 0.1-1%;
Sanitas 0.1-0.2%;
Mould inhibitor 0.1-0.2%.
It is preferred that the parameter of described inorganic gel is as shown in the table:
| Performance | Parameter |
| PH value (5% aqueous solution) | 7-9.5 |
| The water solubles | <1% |
| Acid-soluble material | <1% |
| Dispersion viscosity (5% solid content) | 2000~4500cps |
| Wet screening surplus (+325 order) | <0.01% |
| Moisture content (105 DEG C) | <15% |
| Loss on ignition (600 DEG C) | <18% |
| Heavy metal content (in pb) | <10ppm |
Further, described PH agent is AMP-95, and acrylic resin is J-95, and wetting agent is TEGO245, and defoamer is 5202, and sanitas is Kathon CG, and mould inhibitor is OBPA.
In preferred embodiment, described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 2.7%;
PH agent 0.5%;
Water 45%;
Propylene glycol 15%;
Acrylic resin 35%;
Wetting agent 0.5%;
Defoamer 1.0%;
Sanitas 0.1%;
Mould inhibitor 0.2%.
Use water-based wood grain developer of the present invention directly can carry out painted to open finish paint, and can be completed by seasoning or 60 degree of low-temperature bake 10min.Performance Detection is carried out to dried finish paint surface and proves, between water-based wood grain developer of the present invention and finish paint, there is excellent sticking power, and, avoid the use of finishing paint, thus there is not xanthochromia problem, water-based wood grain developer of the present invention also has excellent water tolerance and chemical resistant properties simultaneously, ensure that the attractive in appearance for a long time of lacquer painting.
The present invention also provides a kind of preparation method of water-based wood grain developer as above, wherein, said method comprising the steps of:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and under 800r/min rotating speed, disperse 5-10 minute to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 10-15 minute to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, disperse 5-10 minute under dispersion machine 400r/min rotating speed after, through 200 mesh screen packagings after being up to the standards.
Set forth further below by embodiment and the scheme of the present invention about water-based wood grain developer is described.
Embodiment 1
Described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 2.7%;
PH agent 0.5%;
Water 45%;
Propylene glycol 15%;
Acrylic resin 35%;
Wetting agent 0.5%;
Defoamer 1.0%;
Sanitas 0.1%;
Mould inhibitor 0.2%.
Prepare water-based wood grain developer as follows:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and under 800r/min rotating speed, disperse 10 minutes to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 15 minutes to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, disperse after 10 minutes under dispersion machine 400r/min rotating speed, through 200 mesh screen packagings after being up to the standards.
Carry out water resistance test to water-based wood grain developer of the present invention: concrete operations add mill base or pearlescence in hydrotropisms's wood grain developer, being adjusted to institute must color.With cotton strap be stained with paint in the mode of turn-taking, paint liquid is rubbed into wood grain, then with on clean cotton along the grain direction Shi Jingmu footpath remaining.After drying, with Crystal drops were dripping down on water-based wood grain developer, the sticking power of test different time sections.With judgement water resistance that clean calico bar fades.Test result is as following table:
| Soak time | 1h | 4h | 12h | 24h |
| Whether fade | No | No | No | No |
As can be seen from the above table, the water-based wood grain developer of embodiment 1 has good water resistance.
Embodiment 2
Described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 7.5%;
PH agent 0.6%;
Water 40%;
Propylene glycol 30%;
Acrylic resin 20%;
Wetting agent 0.5%;
Defoamer 1%;
Sanitas 0.2%;
Mould inhibitor 0.2%.
Prepare water-based wood grain developer as follows:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and under 800r/min rotating speed, disperse 10 minutes to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 10 minutes to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, disperse after 10 minutes under dispersion machine 400r/min rotating speed, through 200 mesh screen packagings after being up to the standards.
The water-based wood grain developer of the method for embodiment 1 to embodiment 2 is utilized to carry out water resistance test.Concrete test result is as following table:
| Soak time | 1h | 4h | 12h | 24h |
| Whether fade | No | No | No | No |
As can be seen from the above table, the water-based wood grain developer of embodiment 2 has good water resistance.
Embodiment 3
Described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 10%;
PH agent 1%;
Water 32%;
Propylene glycol 26.5%;
Acrylic resin 28.8%;
Wetting agent 0.5%;
Defoamer 1%;
Sanitas 0.1%;
Mould inhibitor 0.1%.
Prepare water-based wood grain developer as follows:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and under 800r/min rotating speed, disperse 5 minutes to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 10 minutes to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, disperse after 10 minutes under dispersion machine 400r/min rotating speed, through 200 mesh screen packagings after being up to the standards.
The water-based wood grain developer of the method for embodiment 1 to embodiment 3 is utilized to carry out water resistance test.Concrete test result is as following table:
| Soak time | 1h | 4h | 12h | 24h |
| Whether fade | No | No | No | No |
As can be seen from the above table, the water-based wood grain developer of embodiment 3 has good water resistance.
The invention provides a kind of water-based wood grain developer and preparation method thereof, this water-based wood grain developer effectively can substitute Ge Lisi, and it is without the need to using finishing paint, thus there is not xanthochromia problem, water-based developer of the present invention has excellent sticking power, water tolerance and chemical-resistant simultaneously, thus ensure that the persistence spreading surface effect.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (6)
1. a water-based wood grain developer, is characterized in that, consists of the following composition by mass percentage:
Inorganic gel 1-10%;
PH agent 0.5-1.0%;
Water 30-50%;
Propylene glycol 20-40%;
Acrylic resin 20-40%;
Wetting agent 0.1-0.5%;
Defoamer 0.1-1%;
Sanitas 0.1-0.2%;
Mould inhibitor 0.1-0.2%.
2. water-based wood grain developer according to claim 1, is characterized in that, the pH value of described inorganic gel is 7-9.5.
3. water-based wood grain developer according to claim 2, is characterized in that, described PH agent is AMP-95, and acrylic resin is J-95, and wetting agent is TEGO245, and defoamer is 5202, and sanitas is Kathon CG, and mould inhibitor is OBPA.
4. water-based wood grain developer according to claim 3, is characterized in that, described water-based wood grain developer consists of the following composition by mass percentage:
Inorganic gel 2.7%;
PH agent 0.5%;
Water 45%;
Propylene glycol 15%;
Acrylic resin 35%;
Wetting agent 0.5%;
Defoamer 1.0%;
Sanitas 0.1%;
Mould inhibitor 0.2%.
5. a preparation method for the water-based wood grain developer as described in any one of claim 1-4, is characterized in that, said method comprising the steps of:
A, the inorganic gel of respective quality ratio, PH agent joined in dispersion machine stir to washing and do not glue;
B, the water adding respective quality ratio in mixture and propylene glycol and acrylic resin, and disperse 5-10 minute to even;
C, mixture is disperseed under dispersion machine 600r/min rotating speed, in mixture, add wetting agent and defoamer simultaneously, disperse 10-15 minute to scraper plate without shrinkage cavity;
D, in mixture, add sanitas and mould inhibitor, disperse 5-10 minute under dispersion machine 400r/min rotating speed after, through 200 mesh screen packagings after being up to the standards.
6. the preparation method of water-based wood grain developer according to claim 5, is characterized in that, in described step B high speed dispersion, dispersing speed is 800r/min.