CN105174873A - Inorganic dry powder texture coating and preparation method - Google Patents
Inorganic dry powder texture coating and preparation method Download PDFInfo
- Publication number
- CN105174873A CN105174873A CN201510604603.7A CN201510604603A CN105174873A CN 105174873 A CN105174873 A CN 105174873A CN 201510604603 A CN201510604603 A CN 201510604603A CN 105174873 A CN105174873 A CN 105174873A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic
- dry powder
- iron oxide
- texture coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an inorganic dry powder texture coating and a preparation method. The inorganic dry powder texture coating is prepared from, by weight, 42 parts of white cement No. 425, 7 parts of redispersible emulsion powder, 0.4 part of hydroxyethyl methyl cellulose, 0.4 part of moisture repellent, 0.4 part of wood fibers, 0.1 part of inorganic pigment iron oxide red, 0.2 part of inorganic pigment iron oxide yellow, 62 parts of 80-120-mesh coloured sand and 18 parts of 325-mesh quartz powder. The inorganic dry powder texture coating can be used for damp underground spaces or civil air-defense construction, has the advantages of being completely inorganic, free of releasing of any organic substance, free of any pollution to the environment, free of influences on human bodies, easy to construct, simple, free of mildew and peeling, resisting to ultraviolet rays, being not prone to color changing, unique in texture, high in decorativeness, resisting to water, being breathable, rich and natural in color, good in durability and the like.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of building coating, can be used for the moist underground space or the inorganic dry powder texture coating of civil air defense constructions and installations, have completely inorganic, without any organic substance release, to environment without any pollution, on human body without any impact, the advantage such as to construct easy, simple, and have do not go mouldy and non-scale, uvioresistant, be not easy variable color, texture is unique, ornamental strong, water-fast, ventilative, the characteristics such as rich color nature, good endurance.
Background technology
Inorganic dry powder painting is inorganic silicic acid salt, inorganic phosphate salt, silicon sol class and the material such as polysiloxane-based composition mainly, and the base material of most of inorganic paint is all the natural crystal that very enriches of very common, reserves or metal oxide etc. is raw material.Production technique is also uncomplicated, and energy consumption is relatively low.Its advantage is: completely inorganic, without any organic substance release, to environment without any pollution, to human body also just without any have impact on.More popularly saying, all disengaging without any taste exactly when constructing and after construction, the concentration of narmful substance that enviromental protection instrument is measured is " zero ".Can construct on limit completely, while come into operation, than limewash all environmental protection, limewash also has when color dullness and brush hears the defect drawing carbonic anhydride.Do not go mouldy and non-scale, can use in the underground space of humidity or civil air defense constructions and installations; Because inorganic, the anti-ultraviolet property of color is also relatively quite a lot of, relatively stable, and similar stone material does not allow allochroic reason than paint; And state in dry powdered form during not enabled, decrement can transport and deposit, meeting the feature of low-carbon economy.
Summary of the invention
The object of the present invention is to provide a kind of building coating, can be used for the moist underground space or the inorganic dry powder texture coating of civil air defense constructions and installations, have completely inorganic, discharge without any organic substance, to environment without any pollution, on human body without any impact, the advantage such as to construct easy, simple, and have do not go mouldy and non-scale, uvioresistant, be not easy variable color, texture is unique, ornamental strong, water-fast, ventilative, the characteristics such as rich color nature, good endurance.
Present invention employs such technical scheme: described inorganic dry powder texture coating material and weight proportion respectively: No. 425 white cements 42 parts, redispersable latex powder 7 parts, hydroxyethylmethyl-cellulose 0.4 part, hydrophober 0.4 part, wood fibre 0.4 part, mineral dye red iron oxide 0.1 part, mineral dye iron oxide yellow 0.2 part, 80-120 order color 62 parts, sand, 325 order silica powder 18 parts.
The present invention is specifically related to a kind of building coating, can be used for the moist underground space or the inorganic dry powder texture coating of civil air defense constructions and installations.
This product has completely inorganic, discharge without any organic substance, to environment without any pollution, on human body without any impact, the advantage such as to construct easy, simple, and have do not go mouldy and non-scale, uvioresistant, be not easy variable color, texture is unique, ornamental strong, water-fast, ventilative, the characteristics such as rich color nature, good endurance.
Embodiment
Inorganic dry powder texture coating material of the present invention and weight proportion be respectively: No. 425 white cements 42 parts, redispersable latex powder 7 parts, hydroxyethylmethyl-cellulose 0.4 part, hydrophober 0.4 part, wood fibre 0.4 part, mineral dye red iron oxide 0.1 part, mineral dye iron oxide yellow 0.2 part, 80-120 order color 62 parts, sand, 325 order silica powder 18 parts.
Its preparation method is following steps:
Step one), in mixing machine, add No. 425 white cements 42 parts, redispersable latex powder 7 parts, hydroxyethylmethyl-cellulose 0.4 part, hydrophober 0.4 part, wood fibre 0.4 part, mineral dye red iron oxide 0.1 part, mineral dye iron oxide yellow 0.2 part, 80-120 order color 62 parts, sand, 325 order silica powder 18 parts, carry out abundant mixing and stirring;
Step 2), by step one) material-filling that obtains, finished product.
Claims (2)
1. an inorganic dry powder texture coating, it is characterized in that, material and weight proportion respectively: No. 425 white cements 42 parts, redispersable latex powder 7 parts, hydroxyethylmethyl-cellulose 0.4 part, hydrophober 0.4 part, wood fibre 0.4 part, mineral dye red iron oxide 0.1 part, mineral dye iron oxide yellow 0.2 part, 80-120 order color 62 parts, sand, 325 order silica powder 18 parts.
2. according to inorganic dry powder texture coating according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), in mixing machine, add No. 425 white cements 42 parts, redispersable latex powder 7 parts, hydroxyethylmethyl-cellulose 0.4 part, hydrophober 0.4 part, wood fibre 0.4 part, mineral dye red iron oxide 0.1 part, mineral dye iron oxide yellow 0.2 part, 80-120 order color 62 parts, sand, 325 order silica powder 18 parts, carry out abundant mixing and stirring;
Step 2), by step one) material-filling that obtains, finished product.