CN105174812A - 一种墙面环保填缝剂、制备方法和使用方法 - Google Patents
一种墙面环保填缝剂、制备方法和使用方法 Download PDFInfo
- Publication number
- CN105174812A CN105174812A CN201510597292.6A CN201510597292A CN105174812A CN 105174812 A CN105174812 A CN 105174812A CN 201510597292 A CN201510597292 A CN 201510597292A CN 105174812 A CN105174812 A CN 105174812A
- Authority
- CN
- China
- Prior art keywords
- water
- spackling
- parts
- iron oxide
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种墙面环保填缝剂,制备基料:先将石英砂、石英砂粉碎300-500目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度6000-8000RPM,时间45min~90min,搅拌出料即为填缝剂。清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:(0.4-0.6)混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。
Description
技术领域
本发明涉及一种建筑用填缝剂,具体说是一种墙面环保填缝剂、制备方法和使用方法。
背景技术
由于填缝剂能完美的修补地表面的开裂或破损,还可自行配制颜色丰富色彩丰富,因而越来越受客人青睐。而现有的填缝剂大都采用水泥制备,配以水泥常用的添加剂,存在耐环境、环保上的缺陷,在应用场合和使用安全、寿命长局限性大。
发明内容
针对现有技术的不足,本发明提供了一种墙面用耐环境、环保的填缝剂、制备方法和使用方法。
本发明采用的技术方案是:一种墙面环保填缝剂,按质量份数包括石英砂40-50份、400目重晶石粉10-15份、乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、气相二氧化硅2-2.4份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、RTV有机硅胶1.5-1.9份、光亮剂0.4-0.6份和氧化铁颜料1.8-2.2份。
一种墙面环保填缝剂的制备方法,首先称量如下原料:按质量份数包括石英砂40-50份、400目重晶石粉10-15份、乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、气相二氧化硅2-2.4份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、RTV有机硅胶1.5-1.9份、光亮剂0.4-0.6份和氧化铁颜料1.8-2.2份;制备基料:先将石英砂、石英砂粉碎300-500目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度6000-8000RPM,时间45min~90min,搅拌出料即为填缝剂。
一种墙面环保填缝剂的使用方法,清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:(0.4-0.6)混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。
采用上述技术方案后,本发明的有益效果是:在填缝剂的中增加RTV有机硅橡胶,能够有效增强填缝剂的憎水性和憎水迁移性,使得填缝剂具有自清洁性,不易附着灰尘,保证了填缝剂的使用效果。乙烯-醋酸乙烯共聚物提高耐水性,其密闭泡孔结构、不吸水、防潮、耐水性能良好,提高耐腐蚀性:耐海水、油脂、酸、碱等化学品腐蚀,抗菌、无毒、无味、无污染,便于进行剪裁加工,具有良好的防震、缓冲性能,隔热,保温防寒及低温性能优异,可耐严寒和曝晒。玻化微珠作为填充骨料,进一步提高其绝热﹑防火﹑吸音﹑保温性能。重晶石粉能提高其吸附和净化功能,在墙面上填缝使用,空气接触面大,提高其绿色环保性能。气相二氧化硅用作防沉、增稠、防流挂的助剂,调节自由流动和作为抗结块剂来改善粉末性质,具有良好的补强、增稠、触变、消光、抗紫外线和杀菌等多种作用。丙烯酸树脂有效促进户外抗老化性能.羟丙基甲基纤维素作为增强剂、保水剂能使浆料在涂抹后不会因干得太快而龟裂,同时增强硬化后强度。无机铝盐防水剂提高其防水性能,结合硅酸镁铝悬浮增稠,同时提高填缝剂稳定性,确保使用安全卫生。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种墙面环保填缝剂,按质量份数包括石英砂40份、400目重晶石粉10份、乙烯-醋酸乙烯共聚物2份、玻化微珠8份、气相二氧化硅2份、丙烯酸树脂1份、羟丙基甲基纤维素3份、无机铝盐防水剂1份、硅酸镁铝0.5份、RTV有机硅胶1.5份、光亮剂0.4份和氧化铁颜料1.8份。
其制备方法为:首先称量如下原料:按质量份数包括石英砂40份、400目重晶石粉10份、乙烯-醋酸乙烯共聚物2份、玻化微珠8份、气相二氧化硅2份、丙烯酸树脂1份、羟丙基甲基纤维素3份、无机铝盐防水剂1份、硅酸镁铝0.5份、RTV有机硅胶1.5份、光亮剂0.4份和氧化铁颜料1.8份。
制备基料:先将石英砂、石英砂粉碎300目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;
制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;
按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度9000RPM,时间45min,搅拌出料即为填缝剂。
使用方法为:清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:0.4混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。
实施例二
一种墙面环保填缝剂,按质量份数包括石英砂50份、400目重晶石粉15份、乙烯-醋酸乙烯共聚物3份、玻化微珠12份、气相二氧化硅2.4份、丙烯酸树脂1.5份、羟丙基甲基纤维素6份、无机铝盐防水剂1.3份、硅酸镁铝1.5份、RTV有机硅胶1.9份、光亮剂0.6份和氧化铁颜料2.2份。
其制备方法为:首先称量如下原料:按质量份数包括石英砂50份、400目重晶石粉15份、乙烯-醋酸乙烯共聚物3份、玻化微珠12份、气相二氧化硅2.4份、丙烯酸树脂1.5份、羟丙基甲基纤维素6份、无机铝盐防水剂1.3份、硅酸镁铝1.5份、RTV有机硅胶1.9份、光亮剂0.6份和氧化铁颜料2.2份。
制备基料:先将石英砂、石英砂粉碎500目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;
制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;
按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度8000RPM,时间45min,搅拌出料即为填缝剂。
使用方法为:清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:0.6混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。
实施例三
一种墙面环保填缝剂,按质量份数包括石英砂45份、400目重晶石粉12份、乙烯-醋酸乙烯共聚物2.5份、玻化微珠11份、气相二氧化硅2.3份、丙烯酸树脂1.35份、羟丙基甲基纤维素5份、无机铝盐防水剂1.2份、硅酸镁铝1.2份、RTV有机硅胶1.8份、光亮剂0.5份和氧化铁颜料2份。
其制备方法为:首先称量如下原料:按质量份数包括石英砂45份、400目重晶石粉12份、乙烯-醋酸乙烯共聚物2.5份、玻化微珠11份、气相二氧化硅2.3份、丙烯酸树脂1.35份、羟丙基甲基纤维素5份、无机铝盐防水剂1.2份、硅酸镁铝1.2份、RTV有机硅胶1.8份、光亮剂0.5份和氧化铁颜料2份。
制备基料:先将石英砂、石英砂粉碎450目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;
制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;
按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度7000RPM,时间60min,搅拌出料即为填缝剂。
使用方法为:清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:0.5混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。
Claims (3)
1.一种墙面环保填缝剂,其特征在于:按质量份数包括石英砂40-50份、400目重晶石粉10-15份、乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、气相二氧化硅2-2.4份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、RTV有机硅胶1.5-1.9份、光亮剂0.4-0.6份和氧化铁颜料1.8-2.2份。
2.一种墙面环保填缝剂的制备方法,首先称量如下原料:按质量份数包括石英砂40-50份、400目重晶石粉10-15份、乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、气相二氧化硅2-2.4份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、RTV有机硅胶1.5-1.9份、光亮剂0.4-0.6份和氧化铁颜料1.8-2.2份;制备基料:先将石英砂、石英砂粉碎300-500目后加入玻化微珠、羟丙基甲基纤维素、无机铝盐防水剂、硅酸镁铝搅拌均匀;制备辅料:将乙烯-醋酸乙烯共聚物、丙烯酸树脂、气相二氧化硅、RTV有机硅胶和光亮剂混合搅拌均匀;按填缝剂颜色分类选取氧化铁颜料,将基料加入高速剪切搅拌机,在剪切搅拌状态下依次加入辅料和氧化铁颜料,剪切速度6000-8000RPM,时间45min~90min,搅拌出料即为填缝剂。
3.一种墙面环保填缝剂的使用方法,清理填缝空间,并在填缝接缝上喷洒依次水,以湿润即可,再将填缝剂与水按质量比1:(0.4-0.6)混合并调成粘稠状物料,填于瓷砖与瓷砖之间,待干燥后再喷洒一次水,自然干燥即可。