CN105165464B - WPC active defense ecologic planting bags and preparation method thereof - Google Patents

WPC active defense ecologic planting bags and preparation method thereof Download PDF

Info

Publication number
CN105165464B
CN105165464B CN201510421980.7A CN201510421980A CN105165464B CN 105165464 B CN105165464 B CN 105165464B CN 201510421980 A CN201510421980 A CN 201510421980A CN 105165464 B CN105165464 B CN 105165464B
Authority
CN
China
Prior art keywords
plastic composite
wood
wood plastic
sleeve pipe
maleic anhydride
Prior art date
Application number
CN201510421980.7A
Other languages
Chinese (zh)
Other versions
CN105165464A (en
Inventor
钟培金
其他发明人请求不公开姓名
Original Assignee
南京大源生态建设集团有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南京大源生态建设集团有限公司 filed Critical 南京大源生态建设集团有限公司
Priority to CN201510421980.7A priority Critical patent/CN105165464B/en
Publication of CN105165464A publication Critical patent/CN105165464A/en
Application granted granted Critical
Publication of CN105165464B publication Critical patent/CN105165464B/en

Abstract

WPC active defense ecologic planting bags are made up of wood plastic composite opening frame, depression bar, sleeve pipe, non-woven bag and Nutrition Soil, there is depression bar in open inframe portion, sleeve pipe is arranged at bottom, open frame and depression bar are an entirety, sleeve pipe is fixed by screws in open frame bottom, non-woven bag is bonded in by adhesive on the sleeve pipe of open frame bottom, loads Nutrition Soil inside non-woven bag, below inside pipe casing and open inframe portion, depression bar, the depression bar in open inframe portion is pressed in the upper surface of Nutrition Soil.The present invention is reasonable in design, simple in construction, and it is convenient to manufacture, and production cost is low, and installation is easy, and plant growth environment is good.It can be widely applied to the ecological recoveries of bare rock caused by occasion such as stone pit, open circuit massif.

Description

WPC active defense ecologic planting bags and preparation method thereof

Technical field

The present invention relates to a kind of ecologic planting bag, more particularly to a kind of WPC active defenses ecologic planting bag and its preparation Method.Suitable for the ecological recovery of bare rock caused by open circuit etc. stone pit, massif.

Background technology

In recent years, with the fast development of communication, during building highway, generally required in some mountain areas Dig massif;During economic construction, cut into a mountain for quarrying for various buildings and many recurrent things in place.Dig Massif, which is repaired the roads, cut into a mountain for quarrying etc., frequently can lead to that rock is exposed, these exposed rocks both influenceed it is attractive in appearance, meanwhile, if too late Shi Jinhang ecological recoveries, go down to also result in its weathering for a long time and come off, cause the natural calamities such as mud-rock flow, landslide, to vehicle, OK The composition such as people and neighboring buildings potentially threatens.Thus, it is particularly significant that ecological protection is carried out in time to these exposed rocks.

The ecological protection of bare rock have at present one of a variety of trial methods, the more method used be with junked tire simultaneously Row are emitted on rock hillside, then inject soil thereto, plant flowers and plants;The method that another kind more often uses is to use linked network Slope is sprayed, wire netting, then soil of jet band vegetable seeds etc. thereto are fixed on massif.These trial methods have it can Part is taken, such as, using waste and used rubber tyre technology, one side waste and used rubber tyre is easy to get, and cost is low, can also realize in addition useless The recycling of old tire, reduce environmental pollution caused by discarding;Linked network spray slope operating efficiency is higher, directly that vegetable seeds is pre- It is embedded in soil, growth of then being rooted on hillside.But though in this way, also all there is certain office in these traditional methods It is sex-limited, such as, using rubber tyre technology, on the one hand, rubber tyre more difficult fixation on inclined-plane, even in steep hills slopes, It is limited with the plant growth that rubber tyre directly contacts, on the other hand, rubber tyre easy aging, time under exposing to the weather It can come off long, so as to cause wherein to be enclosed being scattered for soil, plant roots and stems are exposed, or even withered;Linked network spray slope technology need by The equipment of sprinkling soil is transported to scene, increases cost of transportation, meanwhile, for some precipitous or higher hillside, soil and rock Between combine loosely, easily come off, in addition some positions because be too high to realize spray.Thus, invent a kind of WPC active defenses Ecologic planting bag, the defects of overcoming conventional art and deficiency, the restoration of the ecosystem for bare rock are very necessary.

In recent years, it is a kind of with waste or used plastics, wood powder etc. be Raw material processing make wood plastic composite increasingly by people Attention.It is by waste or used plastics and the wood fibre having no value for use(Wood chip, bamboo powder, rice husk, straw obstruct etc.)By certain ratio Example mixing, and special auxiliary agent is added, the section bar of definite shape is made through techniques such as high-temperature fusion, mixing, shapings.It has same The similar processing characteristics of timber, it can saw, can follow closely, can dig, excellent solvent resistant, corrosion resistant performance, bacterial growth, is not easy by worm Moth, not long fungi, by adding different auxiliary agents, can change the characteristics such as the density of Wood-plastic material, may also reach up anti-aging, anti- The particular/special requirement such as electrostatic, fire-retardant.Meanwhile wood plastic composite has the outward appearance, the hardness higher than plastic products, material of timber equal Matter, size are stable compared with timber, are not likely to produce crackle and the features such as without timber knot, twill;It has the processing of thermoplastic Property, and equipment attrition is small;It is not required to be handled using toxic chemical substance, without formaldehyde;Reusable and recovery after discarded Recycle, and can be biodegradable, many advantages, such as being advantageous to environmental protection.

The needs of rock ecological recovery can both have been met by making WPC active defense ecologic plantings bag using wood plastic composite, Also the plurality of advantages of wood plastic composite can be played, it is ensured that the effect and persistence of ecological recovery.

The content of the invention

The present invention be directed to above-mentioned purpose to provide a kind of WPC active defenses ecologic planting bag and preparation method thereof, the WPC master There is dynamic protective ecological planting bag repeatable processing use, easy-formation to process, transport easy, easy for installation, ecological recovery effect The features such as good, durable in use.

The preparation method of WPC active defense ecologic planting bags takes following scheme to realize:

WPC active defense ecologic planting bags are by wood plastic composite opening frame, wood plastic composite depression bar, wood and plastic composite Expect that sleeve pipe, non-woven bag and Nutrition Soil are formed, there is wood plastic composite depression bar in wood plastic composite opening inframe portion, and wood is arranged at bottom Plastic composite materials sleeve pipe, wood plastic composite opening frame and wood plastic composite depression bar are an entirety, wood plastic composite set Pipe is fixed by screws in wood plastic composite opening frame bottom, and non-woven bag is bonded in wood plastic composite by adhesive and opened On the wood plastic composite sleeve pipe of mouth frame bottom, non-woven bag the inside, wood plastic composite inside pipe casing and wood plastic composite Nutrition Soil, the wood and plastic composite in wood plastic composite opening inframe portion are loaded below open inframe portion, wood plastic composite depression bar Material depression bar is pressed in the upper surface of Nutrition Soil.

The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)By wood powder, titanium dioxide, chopped glass fiber, plastic pellet, maleic anhydride grafted plastic particle, haloflex, hard Resin acid, calcium stearate, antioxidant in mass ratio 100:1~3:1~3:30~50:3~10:0.3~1.2:0.4~0.8:0.4~0.8: 0.25 ~ 0.35 mechanical mixture is uniform, then has the wood plastic composite of wood plastic composite depression bar open in integral extrusion shaping Frame, 170 ~ 190 DEG C of forming temperature;

(2)By wood powder, plastic pellet, maleic anhydride grafted plastic particle, haloflex, stearic acid, calcium stearate, carbon Sour calcium powder in mass ratio 50:30~50:3~10:0.3~1.2:0.4~0.8:0.4~0.8:50 mechanical mixtures are uniform, then extruded It is molded wood plastic composite sleeve pipe, 170 ~ 190 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)By minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle, water-loss reducer according to mass ratio 2: 2: 1: 1:0.05~ 0.10:0.01 ~ 0.03 it is well mixed form Nutrition Soil, successively insert non-woven bag, wood plastic composite sleeve pipe and wood plastics composite WPC active defense ecologic planting bags are made untill wood plastic composite depression bar bottom in material opening inframe portion.

Described wood powder particle diameter is 40 ~ 200 mesh.

Described titanium dioxide is anatase thpe white powder, the mesh of particle diameter 600 ~ 1000.

Described 0.1 ~ 0.5mm of chopped glass fiber length.

Described plastic pellet is one kind in polyethylene, polypropylene, ABS and polystyrene.

Described maleic anhydride grafted plastic particle is maleic anhydride grafted polyethylene, maleic anhydride inoculated polypropylene, horse One kind in maleic anhydride grafted ABS and maleic anhydride grafted polystyrene.Its selection is corresponding with plastic pellet used, that is, works as plastics When particle is polyethylene, from maleic anhydride grafted polyethylene, when plastic pellet is polypropylene, it is grafted from maleic anhydride poly- Propylene, when plastic pellet is ABS, from maleic anhydride grafted ABS, when plastic pellet is polystyrene, from maleic acid Acid anhydride grafted polystyrene.

Described antioxidant is β-positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid, two fourth hydroxyl first One kind in benzene, four [β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid] pentaerythritol esters.

Described Paris white is heavy calcium carbonate, the mesh of particle diameter 800 ~ 1200.

Described Controlled Release Fertilizer particle is chemical Controlled-release nitrogen, phosphorus, one kind in potash fertilizer or nitrogen, phosphorus, K composite fertilizer.

Described water-loss reducer is polyacrylie-type water-loss reducer.

WPC active defenses ecologic planting bag of the present invention, reasonable in design, simple in construction, it is convenient to manufacture, production cost Low, installation is easy, and plant growth environment is good.It is extensive that rock massif ecology is carried out using WPC active defenses ecologic planting bag of the present invention It is multiple, compared with using waste and used rubber tyre technology, without collecting a large amount of junked tires, planting environment is good with plant compatibility, no Aging, easy for installation, service life is longer;Compared with linked network spray slope technology, convenient transportation, bigger height can be carried out to rock massif Degree, the covering of wider area, it is simple to operate, thus can be widely applied to the exposed rocks caused by occasion such as stone pit, open circuit massif The ecological recovery of stone.

In use, wire netting is hung up properly in advance on rock hillside, then by the non-woven fabrics of WPC active defense ecologic planting bags Bag is inserted into inside metal grill, and the wood plastic composite casing clamp of WPC active defense ecologic planting bags is protected in metal grill Hold the wood plastic composite opening frame of WPC active defense ecologic planting bags outwardly.

Brief description of the drawings

Below with reference to accompanying drawing, the invention will be further described.

Fig. 1 is WPC active defense ecologic planting bag structural representations.

Fig. 2 is A-A cross-sectional views in Fig. 1.

Fig. 3 is wood plastic composite opening frame, the structural representation of wood plastic composite depression bar in Fig. 1.

Fig. 4 is the structural representation of wood plastic composite sleeve pipe in Fig. 1.

1- wood plastic composite opening frames, 2- wood plastic composite depression bars, 3- wood plastic composite sleeve pipes, 4- non-woven fabrics Bag, 5- Nutrition Soils, 6- screws, 7- adhesives, 8- wood powders, 9- titanium dioxides, 10- chopped glass fibers, 11- plastic pellets, 12- maleic acids Acid anhydride grafted plastic particle, 13- haloflexes, 14- stearic acid, 15- calcium stearates, 16- antioxidant, 17- Paris whites.

Embodiment

Referring to the drawings 1, accompanying drawing 2, WPC active defense ecologic planting bags are by wood plastic composite opening frame 1, wood and plastic composite Material depression bar 2, wood plastic composite sleeve pipe 3, non-woven bag 4 and Nutrition Soil 5 are formed, and have wood inside wood plastic composite opening frame 1 Wood plastic composite sleeve pipe 3, wood plastic composite opening frame 1 and wood plastic composite depression bar are arranged at plastic composite materials depression bar 2, bottom 2 be an entirety, and wood plastic composite sleeve pipe 3 is fixed on the bottom of wood plastic composite opening frame 1, non-woven bag 4 by screw 6 7 are glued by adhesive to be connected on the wood plastic composite sleeve pipe 3 of the bottom of wood plastic composite opening frame 1, the inside of non-woven bag 4, Inside the inside of wood plastic composite sleeve pipe 3 and wood plastic composite opening frame 1, nutrition is loaded below wood plastic composite depression bar 2 Soil 5, the wood plastic composite depression bar 2 inside wood plastic composite opening frame 1 are pressed in the upper surface of Nutrition Soil 5.

Embodiment 1:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(120 mesh), titanium dioxide(800 mesh), chopped glass fiber(0.3mm), plastic pellet(Poly- second Alkene), maleic anhydride grafted plastic particle(Maleic anhydride grafted polyethylene), haloflex, stearic acid, calcium stearate, antioxygen Agent(Butyl hydroxy toluene)100kg, 2kg, 2kg, 40kg, 6.5kg, 0.75kg, 0.6kg, 0.6kg, 0.3kg mechanical mixture are equal It is even, then there are the wood plastic composite opening frame of wood plastic composite depression bar, 180 DEG C of forming temperature in integral extrusion shaping;

(2)Wood powder is weighed respectively(120 mesh), plastic pellet(Polyethylene), maleic anhydride grafted plastic particle(Maleic anhydride Grafted polyethylene), haloflex, stearic acid, calcium stearate, Paris white(1000 mesh)50kg、40kg、6.5kg、 0.75kg, 0.6kg, 0.6kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, forming temperature 180℃;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical controlled release phosphate fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.075kg, 0.02kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood and plastic composite Sleeve pipe and wood plastic composite opening inframe portion are expected untill wood plastic composite depression bar bottom, and the life of WPC active defenses is made State planting bag.

Embodiment 2:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(40 mesh), titanium dioxide(600 mesh), chopped glass fiber(0.1mm), plastic pellet(Polypropylene)、 Maleic anhydride grafted plastic particle(Maleic anhydride inoculated polypropylene), haloflex, stearic acid, calcium stearate, antioxidant(β- The positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid)100kg、1kg、1kg、30kg、3kg、0.3kg、 0.4kg, 0.4kg, 0.25kg mechanical mixture are uniform, then there is the wood plastics composite of wood plastic composite depression bar in integral extrusion shaping Material opening frame, 170 DEG C of forming temperature;

(2)Wood powder is weighed respectively(40 mesh), plastic pellet(Polypropylene), maleic anhydride grafted plastic particle(Maleic anhydride Graft polypropylene), haloflex, stearic acid, calcium stearate, Paris white(800 mesh)50kg、30kg、3kg、0.3kg、 0.4kg, 0.4kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, 170 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical Controlled Release Nitrogen Fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.05kg, 0.01kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood plastic composite WPC active defenses ecology is made untill wood plastic composite depression bar bottom in sleeve pipe and wood plastic composite opening inframe portion Planting bag.

Embodiment 3:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(200 mesh), titanium dioxide(1000 mesh), chopped glass fiber(0.5mm), plastic pellet(ABS)、 Maleic anhydride grafted plastic particle(Maleic anhydride grafted ABS), haloflex, stearic acid, calcium stearate, antioxidant(Two fourths Hydroxy-methylbenzene)100kg, 3kg, 3kg, 50kg, 10kg, 1.2kg, 0.8kg, 0.8kg, 0.35kg mechanical mixture are uniform, then whole There are the wood plastic composite opening frame of wood plastic composite depression bar, 190 DEG C of forming temperature in body extrusion molding;

(2)Wood powder is weighed respectively(200 mesh), plastic pellet(ABS), maleic anhydride grafted plastic particle(Maleic anhydride connects Branch ABS), haloflex, stearic acid, calcium stearate, Paris white(1200 mesh)50kg、50kg、10kg、1.2kg、0.8kg、 0.8kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, 190 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical controlled-release fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.1kg, 0.03kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood plastic composite WPC active defenses ecology is made untill wood plastic composite depression bar bottom in sleeve pipe and wood plastic composite opening inframe portion Planting bag.

Embodiment 4:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(40 mesh), titanium dioxide(800 mesh), chopped glass fiber(0.5mm), plastic pellet(Polyphenyl second Alkene), maleic anhydride grafted plastic particle(Maleic anhydride grafted polystyrene), it is haloflex, stearic acid, calcium stearate, anti- Oxygen agent(Butyl hydroxy toluene)100kg, 1kg, 3kg, 40kg, 3kg, 1.2kg, 0.6kg, 0.4kg, 0.35kg mechanical mixture are equal It is even, then there are the wood plastic composite opening frame of wood plastic composite depression bar, 180 DEG C of forming temperature in integral extrusion shaping;

(2)Wood powder is weighed respectively(120 mesh), plastic pellet(Polystyrene), maleic anhydride grafted plastic particle(Maleic acid Acid anhydride grafted polystyrene), haloflex, stearic acid, calcium stearate, Paris white(800 mesh)50kg、40kg、10kg、 0.3kg, 0.6kg, 0.8kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, forming temperature 170 ℃;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical Controlled Release Nitrogen Fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.075kg, 0.03kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood and plastic composite Sleeve pipe and wood plastic composite opening inframe portion are expected untill wood plastic composite depression bar bottom, and the life of WPC active defenses is made State planting bag.

Embodiment 5:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(120 mesh), titanium dioxide(600 mesh), chopped glass fiber(0.5mm), plastic pellet(Poly- third Alkene), maleic anhydride grafted plastic particle(Maleic anhydride inoculated polypropylene), haloflex, stearic acid, calcium stearate, antioxygen Agent(β-positive octadecanol the ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid)100kg、3kg、2kg、30kg、10kg、 0.3kg, 0.6kg, 0.8kg, 0.25kg mechanical mixture are uniform, then there is the wood of wood plastic composite depression bar in integral extrusion shaping Plastic composite materials opening frame, 180 DEG C of forming temperature;

(2)Wood powder is weighed respectively(200 mesh), plastic pellet(Polyethylene), maleic anhydride grafted plastic particle(Maleic anhydride Grafted polyethylene), haloflex, stearic acid, calcium stearate, Paris white(1000 mesh)By 50kg, 50kg, 3kg, 0.75kg, 0.8kg, 0.4kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, forming temperature 180℃;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical controlled release phosphate fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.1kg, 0.01kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood plastic composite WPC active defenses ecology is made untill wood plastic composite depression bar bottom in sleeve pipe and wood plastic composite opening inframe portion Planting bag.

Embodiment 6:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(120 mesh), titanium dioxide(800 mesh), chopped glass fiber(0.3mm), plastic pellet(ABS), horse Maleic anhydride grafted plastic pellet(Maleic anhydride grafted ABS), haloflex, stearic acid, calcium stearate, antioxidant(Four [β- (3,5- di-tert-butyl-hydroxy phenyls) propionic acid] pentaerythritol ester)100kg、3kg、3kg、30kg、3kg、0.3kg、0.6kg、 0.6kg, 0.3kg mechanical mixture are uniform, and the wood plastic composite for then having wood plastic composite depression bar in integral extrusion shaping opens Mouth frame, 190 DEG C of forming temperature;

(2)Wood powder is weighed respectively(200 mesh), plastic pellet(Polystyrene), maleic anhydride grafted plastic particle(Maleic acid Acid anhydride grafted polystyrene), haloflex, stearic acid, calcium stearate, Paris white(800 mesh)50kg、30kg、3kg、 1.2kg, 0.8kg, 0.8kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, forming temperature 190 ℃;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical controlled-release fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.05kg, 0.02kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood plastic composite WPC active defenses ecology is made untill wood plastic composite depression bar bottom in sleeve pipe and wood plastic composite opening inframe portion Planting bag.

Embodiment 7:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(200 mesh), titanium dioxide(600 mesh), chopped glass fiber(0.1mm), plastic pellet(Poly- third Alkene), maleic anhydride grafted plastic particle(Maleic anhydride inoculated polypropylene), haloflex, stearic acid, calcium stearate, antioxygen Agent(β-positive octadecanol the ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid)100kg、2kg、1kg、50kg、6.5kg、 1.2kg, 0.4kg, 0.8kg, 0.25kg mechanical mixture are uniform, then there is the wood of wood plastic composite depression bar in integral extrusion shaping Plastic composite materials opening frame, 180 DEG C of forming temperature;

(2)Wood powder is weighed respectively(40 mesh), plastic pellet(Polyethylene), maleic anhydride grafted plastic particle(Maleic anhydride Grafted polyethylene), haloflex, stearic acid, calcium stearate, Paris white(1200 mesh)50kg、40kg、10kg、0.3kg、 0.4kg, 0.6kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, 170 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical Controlled-release nitrogen, phosphorus, potassium are compound Fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.05kg, 0.03kg are well mixed forms Nutrition Soil, successively insert non-woven bag, wood WPC master is made untill wood plastic composite depression bar bottom in plastic composite materials sleeve pipe and wood plastic composite opening inframe portion Dynamic protective ecological planting bag.

Embodiment 8:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(120 mesh), titanium dioxide(1000 mesh), chopped glass fiber(0.1mm), plastic pellet(Polyphenyl second Alkene), maleic anhydride grafted plastic particle(Maleic anhydride grafted polystyrene), it is haloflex, stearic acid, calcium stearate, anti- Oxygen agent(Butyl hydroxy toluene)100kg, 2kg, 1kg, 50kg, 10kg, 0.3kg, 0.8kg, 0.4kg, 0.25kg mechanical mixture are equal It is even, then there are the wood plastic composite opening frame of wood plastic composite depression bar, 190 DEG C of forming temperature in integral extrusion shaping;

(2)Wood powder is weighed respectively(40 mesh), plastic pellet(Polyethylene), maleic anhydride grafted plastic particle(Maleic anhydride Grafted polyethylene), haloflex, stearic acid, calcium stearate, Paris white(1000 mesh)50kg、30kg、3kg、1.2kg、 0.8kg, 0.6kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, 180 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical controlled-release fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.1kg, 0.02kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood plastic composite WPC active defenses ecology is made untill wood plastic composite depression bar bottom in sleeve pipe and wood plastic composite opening inframe portion Planting bag.

Embodiment 9:The preparation method of WPC active defense ecologic planting bags, its preparation process are:

(1)Wood powder is weighed respectively(160 mesh), titanium dioxide(700 mesh), chopped glass fiber(0.4mm), plastic pellet(Poly- third Alkene), maleic anhydride grafted plastic particle(Maleic anhydride inoculated polypropylene), haloflex, stearic acid, calcium stearate, antioxygen Agent(Four [β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid] pentaerythritol esters)100kg、2.2kg、2.3kg、35kg、6kg、 0.8kg, 0.7kg, 0.5kg, 0.32kg mechanical mixture are uniform, then there is the wood of wood plastic composite depression bar in integral extrusion shaping Plastic composite materials opening frame, 178 DEG C of forming temperature;

(2)Wood powder is weighed respectively(100 mesh), plastic pellet(Polyethylene), maleic anhydride grafted plastic particle(Maleic anhydride Grafted polyethylene), haloflex, stearic acid, calcium stearate, Paris white(900 mesh)50kg、34kg、8kg、0.9kg、 0.7kg, 0.7kg, 50kg mechanical mixture are uniform, then extruded shaping wood plastic composite sleeve pipe, 182 DEG C of forming temperature;

(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;

(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;

(5)Minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle are weighed respectively(Chemical Controlled Release Nitrogen Fertilizer), water-loss reducer 2kg, 2kg, 1kg, 1kg, 0.06kg, 0.025kg are well mixed to form Nutrition Soil, successively inserts non-woven bag, wood and plastic composite Sleeve pipe and wood plastic composite opening inframe portion are expected untill wood plastic composite depression bar bottom, and the life of WPC active defenses is made State planting bag.

Claims (10)

1.WPC active defense ecologic planting bags, it is characterised in that by wood plastic composite opening frame, wood plastic composite depression bar, Wood plastic composite sleeve pipe, non-woven bag and Nutrition Soil are formed, and there is wood plastic composite pressure in wood plastic composite opening inframe portion Wood plastic composite sleeve pipe arranged at bar, bottom, and wood plastic composite opening frame and wood plastic composite depression bar are an entirety, wood moulding Composite sleeve is fixed by screws in wood plastic composite opening frame bottom, and non-woven bag is bonded in wood moulding by adhesive On the wood plastic composite sleeve pipe of composite opening frame bottom, non-woven bag the inside, wood plastic composite inside pipe casing and wood Nutrition Soil is loaded below plastic composite materials opening inframe portion, wood plastic composite depression bar, wood plastic composite opening inframe portion Wood plastic composite depression bar is pressed in the upper surface of Nutrition Soil.
2. the preparation method of WPC active defenses ecologic planting bag according to claim 1, it is characterised in that its preparation process For:
(1)By wood powder, titanium dioxide, chopped glass fiber, plastic pellet, maleic anhydride grafted plastic particle, haloflex, tristearin Acid, calcium stearate, antioxidant in mass ratio 100:1~3:1~3:30~50:3~10:0.3~1.2:0.4~0.8:0.4~0.8:0.25 ~ 0.35 mechanical mixture is uniform, then there is the wood plastic composite opening frame of wood plastic composite depression bar in integral extrusion shaping, into 170 ~ 190 DEG C of type temperature;
(2)By wood powder, plastic pellet, maleic anhydride grafted plastic particle, haloflex, stearic acid, calcium stearate, calcium carbonate Powder in mass ratio 50:30~50:3~10:0.3~1.2:0.4~0.8:0.4~0.8:50 mechanical mixtures are uniform, then extruded shaping Wood plastic composite sleeve pipe, 170 ~ 190 DEG C of forming temperature;
(3)Wood plastic composite sleeve pipe is fixed on wood plastic composite opening frame bottom using screw;
(4)Non-woven bag is bonded on wood plastic composite sleeve pipe using adhesive;
(5)By minishanny, garden mould, humus, plant ash, Controlled Release Fertilizer particle, water-loss reducer according to mass ratio 2: 2: 1: 1:0.05~ 0.10:0.01 ~ 0.03 it is well mixed form Nutrition Soil, successively insert non-woven bag, wood plastic composite sleeve pipe and wood plastics composite WPC active defense ecologic planting bags are made untill wood plastic composite depression bar bottom in material opening inframe portion.
3. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described wood powder Particle diameter is 40 ~ 200 mesh.
4. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described titanium white Powder is anatase thpe white powder, the mesh of particle diameter 600 ~ 1000.
5. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described is chopped 0.1 ~ 0.5mm of Length of Glass Fiber.
6. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described plastics Particle is one kind in polyethylene, polypropylene, ABS and polystyrene;Described maleic anhydride grafted plastic particle is maleic acid One in acid anhydride grafted polyethylene, maleic anhydride inoculated polypropylene, maleic anhydride grafted ABS and maleic anhydride grafted polystyrene Kind;It is from corresponding with plastic pellet used, i.e., when plastic pellet is polyethylene, from maleic anhydride grafted polyethylene, when When plastic pellet is polypropylene, from maleic anhydride inoculated polypropylene, when plastic pellet is ABS, it is grafted from maleic anhydride ABS, when plastic pellet is polystyrene, from maleic anhydride grafted polystyrene.
7. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described antioxygen Agent is β-positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid, butyl hydroxy toluene, four [β (3,5 2 tertiary fourths The hydroxy phenyl of base 4) propionic acid] one kind in pentaerythritol ester.
8. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described carbonic acid Calcium powder is heavy calcium carbonate, the mesh of particle diameter 800 ~ 1200.
9. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described controlled release Fertile particle is chemical Controlled-release nitrogen, phosphorus, one kind in potash fertilizer or composite fertilizer.
10. the preparation method of WPC active defenses ecologic planting bag according to claim 2, it is characterised in that described guarantor Aqua is polyacrylie-type water-loss reducer.
CN201510421980.7A 2015-07-19 2015-07-19 WPC active defense ecologic planting bags and preparation method thereof CN105165464B (en)