CN109293997A - A kind of waterproof degradation environment protection bag - Google Patents
A kind of waterproof degradation environment protection bag Download PDFInfo
- Publication number
- CN109293997A CN109293997A CN201811032195.2A CN201811032195A CN109293997A CN 109293997 A CN109293997 A CN 109293997A CN 201811032195 A CN201811032195 A CN 201811032195A CN 109293997 A CN109293997 A CN 109293997A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment protection
- protection bag
- microballoon
- modified xantham
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of waterproof degradation environment protection bag, its raw material includes: 40-50 parts of cornstarch, 15-28 parts of polyhydroxyalkanoates, 2-8 parts of polyurethane resin by weight, 2-10 parts of stearyl methacrylate, 3-7 parts of plasticizer, 1-2 parts of disproportionated rosin, N, 0.1-0.6 parts of penylene bismaleimide between N'-, 30-40 parts of filler, 0.2-1 parts of butyl titanate, 1-2 parts of UV absorbers UV-531.Filler includes: modified xantham gum microballoon, porous konilite, zeolite powder, talcum powder, microencapsulated powder oil.Modified xantham gum microballoon is prepared using following technique: xanthan gum, dimethylformamide are stirred; filtering; washing; vacuum drying is added methacrylic acid list sealing end polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water and is uniformly mixed; methyl methacrylate is added to stir under nitrogen protection; ultraviolet irradiation, centrifugation, is dried to obtain modified xantham gum microballoon.
Description
Technical field
The present invention relates to polybag technical fields, more particularly to a kind of waterproof degradation environment protection bag.
Background technique
A large amount of uses of plastics produce many irretrievable disposable plastic waste products, cause and get worse
" white pollution " seriously endangers the existence of the mankind and is good for if body of groundwater pollution and soil pollution, animal and plant resource are destroyed
Health.Starch has regeneration, cheap, easy to maintain and the characteristics of be readily transported, and can carry out various reactions under certain condition, derive
Numerous derivatives.And the good reproducible utilization of starch and biological degradability become the fabulous original of biodegradation material
Material.Although starch plastic goods cost is 10-30% higher than general plastics at present, with it is production-scale expansion and its technology into
Step, uses starch to have very big development potentiality as raw material next life generation degradation products to substitute partly plastic product.
Polyhydroxyalkanoates has excellent biocompatibility and absorbability, nontoxic, non-stimulated, it is in nature
It can be decomposed completely under the effects of microorganism, water, acid, alkali, final product is CO2And H2O, no pollution to the environment can be used as environmentally friendly material
Material replaces traditional polymer material, and polyhydroxyalkanoates plastics are although degradable at present, but that there is also waterproof performances is insufficient
Technical problem.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of waterproof degradation environment protection bags, can be complete
Degradation, does not cause white pollution, not only good water-proof effect, but also mechanical property is good, toughness is balanced with hardness, good toughness, anti-impact
Hit intensity is high.
The waterproof degradation environment protection bag of one kind proposed by the present invention, raw material include: cornstarch 40-50 by weight
Part, 15-28 parts of polyhydroxyalkanoates, 2-8 parts of polyurethane resin, 2-10 parts of stearyl methacrylate, 3-7 parts of plasticizer,
1-2 parts of disproportionated rosin, 0.1-0.6 parts of penylene bismaleimide between N, N'-, 30-40 parts of filler, butyl titanate 0.2-1
Part, 1-2 parts of UV absorbers UV-531.
Preferably, plasticizer includes: polyvinyl alcohol, pentaerythrite.
Preferably, polyvinyl alcohol, pentaerythrite weight ratio be 1-4:1-3.
Preferably, filler includes: that modified xantham gum microballoon, porous konilite, zeolite powder, talcum powder, microencapsulation are red
Phosphorus.
Preferably, modified xantham gum microballoon, porous konilite, zeolite powder, talcum powder, microencapsulated powder oil weight ratio be
4-8:10-18:12-24:4-12:1-2.
Preferably, modified xantham gum microballoon is prepared using following technique: xanthan gum, dimethylformamide are stirred, filtering,
Washing, vacuum drying, addition methacrylic acid list sealing end polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water mixing are equal
It is even, it adds methyl methacrylate and stirs under nitrogen protection, ultraviolet irradiation, centrifugation is dried to obtain modified xantham gum microballoon.
Preferably, in the preparation process of modified xantham gum microballoon, xanthan gum, dimethylformamide, methacrylic acid list envelope
Hold polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water, methyl methacrylate weight ratio be 12-20:50-90:
1-2.6:0.2-0.8:50-80:2-6.
Preferably, modified xantham gum microballoon is prepared using following technique: xanthan gum, dimethylformamide are stirred 15-
35min, whipping temp are 70-80 DEG C, are filtered, washing, 25-34 DEG C of vacuum drying 60-80h, vacuum degree 0.01-0.03MPa,
Methacrylic acid list sealing end polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water is added to be uniformly mixed, adds methyl
Methyl acrylate stirs 12-20min, ultraviolet irradiation 2-8min, irradiation intensity 5.5-6mw/cm under nitrogen protection, centrifugation,
It is dried to obtain modified xantham gum microballoon.
The present invention is prepared using following steps: each raw material is uniformly mixed, is molded using screw injection molding machine, screw rod
First segment heating temperature is 125-132 DEG C, and the second segment heating temperature of screw rod is 155-158 DEG C, and the third section of screw rod heats temperature
Degree is 165-184 DEG C, and the addition temperature of die head is 210-218 DEG C, and then blow molding obtains waterproof degradation environment protection bag.
The present invention is can absorb ultraviolet using the high molecular material-cornstarch and polyhydroxyalkanoates that are readily biodegradable
Photoinitiated reactions occur for light, weaken bond energy, split into the lower fragment of molecular weight, the fragment of lower molecular weight in air into
The oxidation of one step, generates free radicals chain-breaking reaction, and being further degraded to can be final to decompose by the low molecular weight compound of biological decomposition
For CO2And H2O is conducive to eliminate " white " pollution, protects environment.
In modified xantham gum microballoon of the invention, xanthan gum is sealed after being swollen in dimethylformamide with methacrylic acid list
End polyethylene glycol is uniformly dispersed each other, under the cooperation of 2,2- dimethoxy -2- phenyl acetophenone and methyl methacrylate
It is polymerize, not only mechanical property is good, and contained carbamate structures have preferable acidproof content alkaline hydrolysis properties, waterproof effect
Fruit is good, and dispersion performance is excellent, can rapid dispersion to cornstarch and polyhydroxyalkanoates surface, promote cornstarch and poly-
Hydroxyalkanoate and porous konilite, zeolite powder, talcum powder disperse, and cooperation butyl titanate effect, toughness is balanced with hardness, tough
Property is good, excellent in cushion effect, and has the vinyl of close polyhydroxyalkanoates on the strand of butyl titanate, can improve well
Interface compatibility between polyhydroxyalkanoates and other components, it is ensured that whole mechanical property, good toughness, and poly- hydroxyl can be reduced
The hydrophilicity of base alkanoic acid ester.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of waterproof degradation environment protection bag, raw material include: cornstarch 40kg, polyhydroxyalkanoates 28kg, poly- ammonia
Ester resin 2kg, stearyl methacrylate 10kg, plasticizer 3kg, penylene bismaleimide between disproportionated rosin 2kg, N, N'-
Amine 0.1kg, filler 40kg, butyl titanate 0.2kg, UV absorbers UV-531 2kg.
Plasticizer is made of by weight for 1:3 polyvinyl alcohol, pentaerythrite.Filler is by modified xantham gum microballoon, more
Hole konilite, zeolite powder, talcum powder, microencapsulated powder oil are 4:18:12:12:1 composition by weight.
Modified xantham gum microballoon is prepared using following technique: 20kg xanthan gum, 50kg dimethylformamide are stirred
35min, whipping temp are 70 DEG C, are filtered, washing, and 1kg methyl-prop is added in 34 DEG C of vacuum drying 60h, vacuum degree 0.03MPa
Olefin(e) acid list blocks polyethylene glycol, 0.8kg2, and 2- dimethoxy -2- phenyl acetophenone, 50kg water are uniformly mixed, and adds 6kg first
Base methyl acrylate stirs 12min, ultraviolet irradiation 8min, irradiation intensity 5.5mw/cm under nitrogen protection, centrifugation, dry
To modified xantham gum microballoon.
Embodiment 2
A kind of waterproof degradation environment protection bag, raw material include: cornstarch 50kg, polyhydroxyalkanoates 15kg, poly- ammonia
Ester resin 8kg, stearyl methacrylate 2kg, plasticizer 7kg, penylene bismaleimide between disproportionated rosin 1kg, N, N'-
0.6kg, filler 30kg, butyl titanate 1kg, UV absorbers UV-5311kg.
Plasticizer is made of by weight for 4:1 polyvinyl alcohol, pentaerythrite.Filler is by modified xantham gum microballoon, more
Hole konilite, zeolite powder, talcum powder, microencapsulated powder oil are 8:10:24:4:2 composition by weight.
Modified xantham gum microballoon is prepared using following technique: 12kg xanthan gum, 90kg dimethylformamide are stirred
15min, whipping temp are 80 DEG C, are filtered, washing, and 2.6kg methyl is added in 25 DEG C of vacuum drying 80h, vacuum degree 0.01MPa
Acrylic acid list blocks polyethylene glycol, 0.2kg2, and 2- dimethoxy -2- phenyl acetophenone, 80kg water are uniformly mixed, and adds 2kg
Methyl methacrylate stirs 20min, ultraviolet irradiation 2min, irradiation intensity 6mw/cm under nitrogen protection, centrifugation, dry
To modified xantham gum microballoon.
Embodiment 3
A kind of waterproof degradation environment protection bag, raw material include: cornstarch 44kg, polyhydroxyalkanoates 24kg, poly- ammonia
Ester resin 4kg, stearyl methacrylate 8kg, plasticizer 4kg, penylene bismaleimide between disproportionated rosin 1.7kg, N, N'-
Amine 0.2kg, filler 37kg, butyl titanate 0.4kg, UV absorbers UV-531 1.7kg.
Plasticizer is made of by weight for 2:2.5 polyvinyl alcohol, pentaerythrite.Filler by modified xantham gum microballoon,
Porous konilite, zeolite powder, talcum powder, microencapsulated powder oil are 5:16:16:10:1.3 composition by weight.
Modified xantham gum microballoon is prepared using following technique: 18kg xanthan gum, 60kg dimethylformamide are stirred
30min, whipping temp are 73 DEG C, are filtered, washing, and 1.6kg methyl is added in 32 DEG C of vacuum drying 65h, vacuum degree 0.025MPa
Acrylic acid list blocks polyethylene glycol, 0.6kg2, and 2- dimethoxy -2- phenyl acetophenone, 60kg water are uniformly mixed, and adds 5kg
Methyl methacrylate stirs 14min, ultraviolet irradiation 6min, irradiation intensity 5.6mw/cm under nitrogen protection, is centrifuged, dry
Obtain modified xantham gum microballoon.
Embodiment 4
A kind of waterproof degradation environment protection bag, raw material include: cornstarch 46kg, polyhydroxyalkanoates 18kg, poly- ammonia
Ester resin 6kg, stearyl methacrylate 4kg, plasticizer 6kg, penylene bismaleimide between disproportionated rosin 1.3kg, N, N'-
Amine 0.4kg, filler 33kg, butyl titanate 0.8kg, UV absorbers UV-531 1.3kg.
Plasticizer is made of by weight for 3:1.5 polyvinyl alcohol, pentaerythrite.Filler by modified xantham gum microballoon,
Porous konilite, zeolite powder, talcum powder, microencapsulated powder oil are 7:12:20:6:1.7 composition by weight.
Modified xantham gum microballoon is prepared using following technique: 14kg xanthan gum, 80kg dimethylformamide are stirred
20min, whipping temp are 77 DEG C, are filtered, washing, and 2kg methyl-prop is added in 28 DEG C of vacuum drying 75h, vacuum degree 0.015MPa
Olefin(e) acid list blocks polyethylene glycol, 0.4kg2, and 2- dimethoxy -2- phenyl acetophenone, 70kg water are uniformly mixed, and adds 3kg first
Base methyl acrylate stirs 18min, ultraviolet irradiation 4min, irradiation intensity 5.8mw/cm under nitrogen protection, centrifugation, dry
To modified xantham gum microballoon.
Embodiment 5
A kind of waterproof degradation environment protection bag, raw material include: cornstarch 45kg, polyhydroxyalkanoates 21kg, poly- ammonia
Ester resin 5kg, stearyl methacrylate 6kg, plasticizer 5kg, penylene bismaleimide between disproportionated rosin 1.5kg, N, N'-
Amine 0.3kg, filler 35kg, butyl titanate 0.6kg, UV absorbers UV-531 1.5kg.
Plasticizer is made of by weight for 2.5:2 polyvinyl alcohol, pentaerythrite.Filler by modified xantham gum microballoon,
Porous konilite, zeolite powder, talcum powder, microencapsulated powder oil are 6:14:18:8:1.5 composition by weight.
Modified xantham gum microballoon is prepared using following technique: 16kg xanthan gum, 70kg dimethylformamide are stirred
25min, whipping temp are 75 DEG C, are filtered, washing, and 1.8kg methyl is added in 30 DEG C of vacuum drying 70h, vacuum degree 0.02MPa
Acrylic acid list blocks polyethylene glycol, 0.5kg2, and 2- dimethoxy -2- phenyl acetophenone, 65kg water are uniformly mixed, and adds 4kg
Methyl methacrylate stirs 16min, ultraviolet irradiation 5min, irradiation intensity 5.7mw/cm under nitrogen protection, is centrifuged, dry
Obtain modified xantham gum microballoon.
The 5 waterproof degradation environment protection bag of gained of embodiment and commercially available common plastics bag are compared into Degrading experiment, tied
Fruit is as follows:
Time, the moon | 5 remaining weight of embodiment, g | Commercially available common plastics bag remaining weight, g |
0 | 1 | 1 |
3 | 0.94 | 0.98 |
6 | 0.78 | 0.87 |
9 | 0.46 | 0.71 |
12 | 0.11 | 0.62 |
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of waterproof degradation environment protection bag, which is characterized in that its raw material includes: 40-50 parts of cornstarch by weight, is gathered
15-28 parts of hydroxyalkanoate, 2-8 parts of polyurethane resin, 2-10 parts of stearyl methacrylate, 3-7 parts of plasticizer, disproportionation pine
0.1-0.6 parts of penylene bismaleimide between fragrant 1-2 parts, N, N'-, it is 30-40 parts of filler, 0.2-1 parts of butyl titanate, ultraviolet
1-2 parts of light absorber UV-531.
2. waterproof degradation environment protection bag according to claim 1, which is characterized in that plasticizer includes: polyvinyl alcohol, season penta
Tetrol.
3. waterproof degradation environment protection bag according to claim 2, which is characterized in that the weight of polyvinyl alcohol, pentaerythrite
Than for 1-4:1-3.
4. any one of -3 waterproof degradation environment protection bag according to claim 1, which is characterized in that filler includes: modification
Xanthan gum microballoon, porous konilite, zeolite powder, talcum powder, microencapsulated powder oil.
5. waterproof degradation environment protection bag according to claim 4, which is characterized in that modified xantham gum microballoon, periporate stone
English, zeolite powder, talcum powder, microencapsulated powder oil weight ratio be 4-8:10-18:12-24:4-12:1-2.
6. waterproof degradation environment protection bag according to claim 4 or 5, which is characterized in that modified xantham gum microballoon is using such as
Lower technique preparation: xanthan gum, dimethylformamide being stirred, filtered, is washed, and methacrylic acid list sealing end is added in vacuum drying
Polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water are uniformly mixed, and add methyl methacrylate in nitrogen protection
Lower stirring, ultraviolet irradiation, centrifugation are dried to obtain modified xantham gum microballoon.
7. waterproof degradation environment protection bag according to claim 6, which is characterized in that the preparation process of modified xantham gum microballoon
In, xanthan gum, dimethylformamide, methacrylic acid list sealing end polyethylene glycol, 2,2- dimethoxy -2- phenyl acetophenone, water,
The weight ratio of methyl methacrylate is 12-20:50-90:1-2.6:0.2-0.8:50-80:2-6.
8. waterproof degradation environment protection bag described according to claim 6 or 7, which is characterized in that modified xantham gum microballoon is using such as
Lower technique preparation: stirring 15-35min for xanthan gum, dimethylformamide, and whipping temp is 70-80 DEG C, is filtered, washing, 25-
34 DEG C of vacuum drying 60-80h, vacuum degree 0.01-0.03MPa are added methacrylic acid list and block polyethylene glycol, 2,2- diformazan
Oxygroup -2- phenyl acetophenone, water are uniformly mixed, and are added methyl methacrylate and are stirred 12-20min under nitrogen protection, purple
External irradiation 2-8min, irradiation intensity 5.5-6mw/cm, centrifugation, are dried to obtain modified xantham gum microballoon.