CN105153767A - 一种屋面防水涂料的制备方法 - Google Patents
一种屋面防水涂料的制备方法 Download PDFInfo
- Publication number
- CN105153767A CN105153767A CN201510709209.XA CN201510709209A CN105153767A CN 105153767 A CN105153767 A CN 105153767A CN 201510709209 A CN201510709209 A CN 201510709209A CN 105153767 A CN105153767 A CN 105153767A
- Authority
- CN
- China
- Prior art keywords
- waterproof paint
- heating
- waterproof coating
- stirring
- reaction pot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种屋面防水涂料的制备方法，包括以下步骤：a、将生石灰和异氰酸酯放入反应锅内并加水进行搅拌，同时加热反应锅，温度加热范围为80-120℃；b、反应锅加热6-18分钟后，向反应锅内加入沥青并进行搅拌，边搅拌边加热，加热温度范围为100-150℃，直至沥青完全熔化；c、上述沥青完全熔化后再加入增稠剂、消泡剂和银浆粉进行搅拌，持续加热反应锅20-30分钟，得到防水涂料；d、停止加热反应锅，冷却防水涂料至60℃后停止搅拌。本发明提供的屋面防水涂料的制备方法，操作简便，所制成的防水涂料用于屋面工程可以起到很好的防水效果，该防水涂料延伸性好，粘结力强，抗拉伸强度高，能克服基层开裂带来的渗漏。
Description
技术领域
本发明涉及工程建设的领域，特别是涉及一种屋面防水涂料的制备方法。
背景技术
涂料又称油漆。指涂布于物体表面在一定的条件下能形成薄膜而起保护、装潢或其他特殊功能(绝缘、防锈、防霉、耐热等)的一类液体或固体材料。因早期的涂料大多以植物油为主要原料，故又称作油漆。现在合成树脂已大部分或全部取代了植物油，故称为涂料。
建筑防水涂料是在常温下呈无固定形状的粘稠液态高分子合成材料。经涂布后，通过溶剂的挥发或水分的蒸发或反应固化后在基层面上形成坚韧的防水膜的材料的总称。
目前，国内广泛使用的涂料种类繁多，而用于建筑物表面，如屋顶、外墙等仍然使用三油二毡防水材料，施工时费时费工，而且使用范围受到了很大的局限。特别是这种方法五反光降温性能，每到夏天由于三油二毡得吸热作用，使得顶楼或者冷库、粮库的温度升高，要保持温度适宜，耗能较大。
发明内容
本发明主要解决的技术问题是提供一种屋面防水涂料的制备方法，操作简便，所制成的防水涂料用于屋面工程可以起到很好的防水效果，该防水涂料延伸性好，粘结力强，抗拉伸强度高，能克服基层开裂带来的渗漏。
为解决上述技术问题，本发明采用的一个技术方案是：提供了一种屋面防水涂料的制备方法，包括以下步骤：
a、将生石灰和异氰酸酯放入反应锅内并加水进行搅拌，同时加热反应锅，温度加热范围为80-120℃；
b、反应锅加热6-18分钟后，向反应锅内加入沥青并进行搅拌，边搅拌边加热，加热温度范围为100-150℃，直至沥青完全熔化；
c、上述沥青完全熔化后再加入增稠剂、消泡剂和银浆粉进行搅拌，持续加热反应锅20-30分钟，得到防水涂料；
d、停止加热反应锅，冷却防水涂料至60℃后停止搅拌。
在本发明一个较佳实施例中，所述的步骤a-c中的原料以及质量百分比为：
硅石灰粉30-60%；
沥青15-25%；
异氰酸酯10-15%；
增稠剂8-16%；
消泡剂2-4%；
银浆粉5-10%。
在本发明一个较佳实施例中，所述的消泡剂为机硅氧烷、聚醚、高碳醇或者含胺的一种。
在本发明一个较佳实施例中，所述的增稠剂为羟乙基纤维素或者羟丙基甲基纤维素。
本发明的有益效果是：本发明的屋面防水涂料的制备方法，操作简便，所制成的防水涂料用于屋面工程可以起到很好的防水效果，该防水涂料延伸性好，粘结力强，抗拉伸强度高，能克服基层开裂带来的渗漏。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其它的附图，其中：
图1是本发明的屋面防水涂料的制备方法一较佳实施例的流程图。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
如图1所示，本发明实施例包括：
一种屋面防水涂料的制备方法，包括以下步骤：
a、将生石灰和异氰酸酯放入反应锅内并加水进行搅拌，同时加热反应锅，温度加热范围为80-120℃；
b、反应锅加热6-18分钟后，向反应锅内加入沥青并进行搅拌，边搅拌边加热，加热温度范围为100-150℃，直至沥青完全熔化；
c、上述沥青完全熔化后再加入增稠剂、消泡剂和银浆粉进行搅拌，持续加热反应锅20-30分钟，得到防水涂料；
d、停止加热反应锅，冷却防水涂料至60℃后停止搅拌。
上述中，所述的步骤a-c中的原料以及质量百分比为：
硅石灰粉30-60%；
沥青15-25%；
异氰酸酯10-15%；
增稠剂8-16%；
消泡剂2-4%；
银浆粉5-10%。
进一步的，所述的消泡剂为机硅氧烷、聚醚、高碳醇或者含胺的一种；所述的增稠剂为羟乙基纤维素或者羟丙基甲基纤维素。
本发明揭示的屋面防水涂料的制备方法，操作简便，所制成的防水涂料用于屋面工程可以起到很好的防水效果，该防水涂料延伸性好，粘结力强，抗拉伸强度高，能克服基层开裂带来的渗漏。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种屋面防水涂料的制备方法，其特征在于，包括以下步骤：
a、将生石灰和异氰酸酯放入反应锅内并加水进行搅拌，同时加热反应锅，温度加热范围为80-120℃；
b、反应锅加热6-18分钟后，向反应锅内加入沥青并进行搅拌，边搅拌边加热，加热温度范围为100-150℃，直至沥青完全熔化；
c、上述沥青完全熔化后再加入增稠剂、消泡剂和银浆粉进行搅拌，持续加热反应锅20-30分钟，得到防水涂料；
d、停止加热反应锅，冷却防水涂料至60℃后停止搅拌。
2.根据权利要求1所述的屋面防水涂料的制备方法，其特征在于，所述的步骤a-c中的原料以及质量百分比为：
硅石灰粉30-60%；
沥青15-25%；
异氰酸酯10-15%；
增稠剂8-16%；
消泡剂2-4%；
银浆粉5-10%。
3.根据权利要求1所述的屋面防水涂料的制备方法，其特征在于，所述的消泡剂为机硅氧烷、聚醚、高碳醇或者含胺的一种。
4.根据权利要求1所述的屋面防水涂料的制备方法，其特征在于，所述的增稠剂为羟乙基纤维素或者羟丙基甲基纤维素。