CN105152568B - 一种立磨用液体水泥助磨剂 - Google Patents
一种立磨用液体水泥助磨剂 Download PDFInfo
- Publication number
- CN105152568B CN105152568B CN201510601182.2A CN201510601182A CN105152568B CN 105152568 B CN105152568 B CN 105152568B CN 201510601182 A CN201510601182 A CN 201510601182A CN 105152568 B CN105152568 B CN 105152568B
- Authority
- CN
- China
- Prior art keywords
- cement
- vertical mill
- trimerization
- styrene
- maleic anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种立磨用液体水泥助磨剂,其组成为:邻苯二甲酸的醇胺盐20%~30%,苯乙烯马来酸酐的共聚物10%~15%,三聚聚合甘油10%~15%,葡萄糖10%~15%,甘蔗糖蜜10%~15%,氢氧化钠1%,余量为水。本发明具有以下有益效果:相同的水泥立磨磨机工况,相同的水泥各种原材料,添加了本水泥助磨剂后,改善了水泥的颗粒级配、提高了水泥产品颗粒的球形度、降低了水泥产品的标准稠度用水量、提高了水泥产品与混凝土外加剂的适应性,水泥强度稍有提高。
Description
技术领域
本发明涉及建筑材料行业中的水泥制造领域,尤其是一种立磨用液体水泥助磨剂。
背景技术
目前,水泥粉磨工艺可分为立磨与管磨(球磨)工艺两种。立磨与管磨(球磨)工艺相比,有着显著的优越性,因为没有了钢球和钢段,立磨自然就避免了金属间的撞击与磨损,金属磨损量小、噪音低;又因为它是风扫式粉磨,自身的选粉功能,避免了过粉磨现象,因此减少了无用功的消耗,粉磨效率高,与管磨系统相比,粉磨电耗仅为后者的60%左右;还具有工艺流程简单、单机产量大,入料粒度大,密闭性能好,负压操作无扬尘等特点。
水泥助磨剂是在水泥粉磨时加入,起助磨作用而又不损害人体健康和水泥混凝土性能的外加剂。在管磨机系统中使用液体水泥助磨剂的技术已经成熟,这些水泥助磨剂的功能:(1)改善水泥粉磨工艺,解决糊球、磨内通风不畅,防止输送管道堵塞等生产工艺问题;(2)提高水泥磨机产量,一般可以提高台时产量5%~15%;(3)提高水泥质量,使用水泥助磨剂可不同程度地提高水泥的质量,尤其是使用增强型水泥助磨剂可使水泥3天抗压强度提高2~3MPa,28天抗压强度提高4~8MPa;(4)节约熟料。在保证相同的水泥强度等级下,保持相同的台时产量,使用水泥助磨剂可节约4%~6%的熟料。管磨用水泥助磨剂有粉体和液体二种,目前国内产品已经与国际接轨,主要以液体产品为主。复配的液体水泥助磨剂原料有以下几种:(1)链烷醇胺类:三乙醇胺(TEA)、三异丙醇胺(TIPA)、二乙醇异丙醇胺(DEIPA)、乙醇二异丙醇胺(EDIPA)、四(羟乙基)乙二胺(THEED)、四(羟丙基)乙二胺(THPED)、甲基二乙醇胺(MDEA)以及它们的混合物;(2)醇类:包括聚乙二醇(400)、二甘醇、丙二醇、二丙二醇、聚合甘油、生产生物柴油的副产物(例如,生物甘油)以及它们的混合物;(3)糖类:如葡萄糖、果糖、玉米糖浆、糖蜜等或碳水化合物,例如葡糖酸钠、葡糖酸钾。(4)无机盐类包括:盐酸盐(例如,氯化钙,氯化钠),亚硝酸盐(例如亚硝酸钙,亚硝酸钠),硝酸盐(例如,硝酸钙,硝酸钠),硫氰酸盐(如硫氰酸钠)等。液体水泥助磨剂就是以胺类、醇类、糖类、其它合成化工母液、无机盐等作为原料和水充分搅拌均匀后的混合物,生产工艺简单,产品通过计量泵计量后,送入水泥管磨(球磨机)与水泥物料一起粉磨作业。
通常情况下,使用立磨粉磨的水泥与管磨机(球磨机)生产的水泥相比,其水泥产品的颗粒分布特别是颗粒级配不是特别理想、水泥产品球形度不高、水泥产品的标准稠度用水量偏大、水泥产品与混凝土外加剂的适应性相对差一些。但是在水泥立磨中使用水泥助磨剂的技术目前还在研制摸索阶段。
发明内容
发明目的
本发明的目的是提供一种立磨用液体水泥助磨剂,它对改善水泥的颗粒级配、提高水泥产品颗粒的球形度、降低水泥产品的标准稠度用水量、提高水泥产品与混凝土外加剂的适应性方面均有较大益处。
发明概述
本发明提供一种立磨用液体水泥助磨剂,其组成为:邻苯二甲酸的醇胺盐20%~30%,苯乙烯马来酸酐的共聚物10%~15%,三聚聚合甘油10%~15%,葡萄糖10%~15%,甘蔗糖蜜10%~15%,氢氧化钠1%,余量为水,所述邻苯二甲酸的醇胺盐为50%含量的邻苯二甲酸的醇胺盐,所述苯乙烯马来酸酐的共聚物为33.5%含量的苯乙烯马来酸酐共聚物,数均分子量为2800,重均分子量为7000,所述三聚聚合甘油为75%含量的三聚聚合甘油,所述甘蔗糖蜜的总含糖量为48%,所述百分比为质量百分比。
优选的,所述立磨用液体水泥助磨剂的组成为:邻苯二甲酸的醇胺盐25%,苯乙烯马来酸酐的共聚物13%,三聚聚合甘油13%,葡萄糖13%,甘蔗糖蜜13%,氢氧化钠1%,余量为水。
将本发明的各组成原料混合均匀,得到溶液,即为所述立磨用液体水泥助磨剂。
由于采用了上述技术方案,本发明与现有的不加助磨剂的立磨水泥工艺相比,具有以下有益效果:相同的水泥立磨磨机工况,相同的水泥各种原材料,添加了本水泥助磨剂后,它改善了水泥的颗粒级配、提高了水泥产品颗粒的球形度、降低了水泥产品的标准稠度用水量、提高了水泥产品与混凝土外加剂的适应性,水泥强度稍有提高。
具体实施方式
下面结合实施例对本发明作进一步说明。
本发明中所述百分比均为质量百分比。
1)水泥配合比:熟料75%,脱硫石膏5%,石灰石10%,粉煤灰10%。
2)原材料:
熟料:海螺水泥集团中国水泥厂产,3天强度31.2MPa,28天强度58.6MPa;
脱硫石膏:南京一夫建材实业有限公司生产;
石灰石:镇江宝华联合采石厂,5-10mm碎石;
粉煤灰:南京江苏南热发电有限责任公司产原灰。
邻苯二甲酸的醇胺盐,浓度50%,南京神和新材料科技有限公司生产;
苯乙烯马来酸酐的共聚物,型号SMA1440H,浓度33.5%,清澈液体,广州市润奥化工材料有限公司生产;
三聚聚合甘油,浓度75%,南京神和新材料科技有限公司生产;
葡萄糖:粉体,工业级,苏州蓝翔化工科技有限公司生产;
甘蔗糖蜜:总含糖量48%,广西南宁川和贸易有限公司生产;
氢氧化钠:片碱,工业级,99%含量,山东省淄博市临淄红星化工厂生产;
水:自来水。
3)设备为某公司生产的L56.3+3C/S立磨,水泥产量为210-220t/h,电耗30-35kwh/t,水泥比表面积在340~350kg/m2。
具体实施例1~6,详细配方见表1。
表1
应用实施例1~6所得立磨用液体水泥助磨剂,并以空白和市售产品作为对照,按照上述配合比,采用上述立磨设备粉磨得出水泥。采用VISION 210-D颗粒图像检测仪测试水泥的颗粒球形度,依据标准GB 175-2007测试水泥标准稠度用水量及水泥强度;依据标准GB 50119-2013测试水泥净浆流动度及损失(脂肪族缓凝高效减水剂,南京聚昌建筑材料有限公司生产,型号JC-2,含固27%,按照水泥用量的2%掺量),具体数据见表2。
表2
Claims (2)
1.一种立磨用液体水泥助磨剂,其特征在于,其组成为:邻苯二甲酸的醇胺盐20%~30%,苯乙烯马来酸酐的共聚物10%~15%,三聚聚合甘油10%~15%,葡萄糖10%~15%,甘蔗糖蜜10%~15%,氢氧化钠1%,余量为水,所述邻苯二甲酸的醇胺盐为50%含量的邻苯二甲酸的醇胺盐,所述苯乙烯马来酸酐的共聚物为33.5%含量的苯乙烯马来酸酐共聚物,数均分子量为2800,重均分子量为7000,所述三聚聚合甘油为75%含量的三聚聚合甘油,所述甘蔗糖蜜的总含糖量为48%,所述百分比为质量百分比。
2.如权利要求1所述的一种立磨用液体水泥助磨剂,其特征在于,其组成为:邻苯二甲酸的醇胺盐25%,苯乙烯马来酸酐的共聚物13%,三聚聚合甘油13%,葡萄糖13%,甘蔗糖蜜13%,氢氧化钠1%,余量为水。